• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.11
• /
• pp.2328-2335
• /
• 2002

A hybrid composite material has many potential usage due to the high specific strength and the resistance to fatigue, when compared to other composite materials such as fiber reinforced plastic(FRP) and metal matrix composite(MMC). However, the fracture mechanism of hybrid composite material is extremely complicated because of the bonding structure of metals and FRP. In this study, Al 7075 sheets and carbon epoxy preprags were used to fabricate the hybrid composite. Recently, nondestructive technique has been used to evaluate the fracture mechanism of these composite materials. AE technique was used to clarify the microscopic damage behavior and failure mechanism of A17075/CFRP hybrid composite. It was found that AE paralneters such as AE event, energy and amplitude were effective to evaluate the failure process of Al 7075/CFRP composite. In addition, the relationship between the AE signal and the characteristics of fracture surface using optical microscope was discussed.

• Composites Research
• /
• v.19 no.1
• /
• pp.36-42
• /
• 2006

MWNT(multi-walled carbon nanotube)-filled plain-weave glass/epoxy composites were fabricated and electromagnetic characteristics of the composites were investigated. The observation of the microstructures of the composites revealed that MWNTs are mostly distributed in matrix rich region and the interface between glass fiber yarns in warp and fill direction. The permittivity of the composites, measured in X-band (8.2-12.4 GHz) frequency range, increased with weight fraction of MWNTs and remained almost constant with frequency. The measured permittivity was used to investigate the reflection loss of radar absorbing structures (RAS) composed of MWNT-filled composites according to thickness and a RAS were constructed with 10 dB absorbing bandwidth 4.2 GHz and 3.3 mm in thickness.

• Polymer(Korea)
• /
• v.36 no.5
• /
• pp.612-616
• /
• 2012

In this work, the effect of chemical treatments of multi-walled carbon nanotubes (MWNTs) on the mechanical interfacial properties of carbon fiber fabric-reinforced composites was investigated. The surface properties of the MWNTs were determined by acid and base values, Fourier transform infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS) analyses. The mechanical interfacial properties of the composites were assessed by interlaminar shear stress (ILSS) and critical stress intensity factor ($K_{IC}$). The chemical treatments based on acid and base reactions led to a significant change of surface characteristics of the MWNTs, especially A-MWNTs/carbon fibers/epoxy composites had higher mechanical properties than those of B-MWNTs and non-treated MWNTs/carbon fibers/epoxy composites. These results were probably due to the improvement of interfacial bonding strength, resulting from the acid-base interaction and hydrogen bonding between the epoxy resins and the MWNT fillers.

• Composites Research
• /
• v.19 no.1
• /
• pp.29-35
• /
• 2006

The avoidance of enemy's radar detection is very important issue in the modem electronic weapon system. Researchers have studied to minimize reflected signals of radar. In this research, two types of radar absorbing structure (RAS), 'C'-type shell and 'U'-type shell, were fabricated using fiber-reinforced composite materials and their radar cross section (RCS) were evaluated. The absorption layer was composed of glass fiber reinforced epoxy and nano size carbon-black, and the reflection layer was fabricated with carbon fiber reinforced epoxy. During their manufacturing process, undesired thermal deformation (so called spring-back) was observed. In order to reduce spring-back, the bending angle of mold was controlled by a series of experiments. The spring-back of parts fabricated by using compensated mold was predicted by finite element analysis (ANSYS). The RCS of RAS shells were measured by compact range and predicted by physical optics method. The measured RCS data was well matched with the predicted data.

• Composites Research
• /
• v.29 no.6
• /
• pp.336-341
• /
• 2016

This paper conducted the study on the electromagnetic and mechanical applicability of CNT-coated glass fiber for wind blades. Large-size wind blade has the serious pending problems to meet the target, such as interfering radar signals, increasing weights, and increasing repair costs. In this paper, we are suggesting the CNT-coated glass fiber in order to overcome these problems. First, the CNTs were strongly coated on the surfaces of glass fiber by suggested coating process, and the CNT-coated glass fiber/epoxy composites were fabricated by Va-RTM process. We designed and fabricated a radar absorbing structure using the CNT-coated glass fiber, which showed over 90% radar absorbing performance between 8.3 and 12.1 GHz frequency. In addition, we confirmed the improvement of mechanical properties on the strength and modulus of tensile, compressive, and in-plane shear.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2001.05a
• /
• pp.172-175
• /
• 2001

The co-cured Joining method, which is regarded as an adhesively bonded Joining method, is an efficient joining technique because both curing and bonding processes for the composite structures can be achieved simultaneously. It requires neither surface treatment onto the composite adherend nor an additional adhesive joining process because the excess resin, which is extracted from composite materials during consolidation, accomplishes the co-cured Joining process. Since the adhesive of the co-cured joint is the same material as the resin of the composite adherend, the analysis and design of the co-cured joint for composite structures are simpler than those of an adhesively bonded joint, which uses an additional adhesive. In this paper, effects of the manufacturing parameters, namely surface roughness, stacking sequence of the composite adherend, and manufacturing pressure in the autoclave during curing process, on the tensile load bearing capacity of the co-cured single lap joint will be experimentally investigated.

• Composites Research
• /
• v.12 no.3
• /
• pp.84-90
• /
• 1999

High alumina cement(HAC) and polyvinyl alcohol(PVA) based macro-defect-free(MDF) cement composites were reinforced using short carbon fibers, 3mm in length, 1-4% in weight fraction and insoluble polymers such as polyurethane, epoxy, phenol resin, in order to increase mechanical properties and water stability. The specimens were manufactured by the low heat-press(warmpress) method. In addition, the interface and the cross-linking reaction of cement and polymers was also studied by the SEM and TEM. Flexural strength of HAC/PVA based MDF cementitious composites was proportionally decreased with increasing fiber contents due to the undensified structure around fibers. The flexural strength of insoluble polymer added specimen was decreased with increasing fiber contents, while water stability was dramatically improved. Epoxy resin added specimen showed the highest strength with increasing fiber contents, compared with other specimens. The water stability of fiber content 4% added specimen immersed in water presented about 95%, 87% at 3 and 7 days immersed in water, respectively. The interfacial adhesive strength of fiber-matrix was very much improved due to cross linking reaction of polymer and metal ions of cement. Tensile strength of insoluble polymers added composites as linearly increased with increasing the fiber contents. The epoxy resin added specimen also showed highest tensile strength. The 4% fiber added specimen presented 30~80% higher strength than controlled specimen.

• Steel and Composite Structures
• /
• v.48 no.3
• /
• pp.305-320
• /
• 2023

The mechanical properties of polymeric composites are degraded under elevated temperatures due to the effect of temperature on the mechanical behavior of the resin and resin fiber interfaces. In this study, the effect of temperature on the impact response of the carbon fiber reinforced plastics (CFRP) was investigated at low-velocity impact (LVI) using a drop-weight impact tester machine. All the composite plates were fabricated using a vacuum infusion process with a stacking sequence of [45/0_2/-45/90_2]s, and a thickness of 2.9 mm. A group of the specimens was exposed to an environment with a temperature cycling at the range of -30 ℃ to 65 ℃. In addition, three other groups of the specimens were aged at ambient (28 ℃), -30 ℃, and 65 ℃ for ten days. Then all the conditioned specimens were subjected to LVI at three energy levels of 10, 15, and 20 J. To assess the behavior of the damaged composite plates, the force-time, force-displacement, and energy-time diagrams were analyzed at all temperatures. Finally, radiography, optical microscopy, and scanning electron microscopy (SEM) were used to evaluate the effect of the temperature and damages at various impact levels. Based on the results, different energy levels have a similar effect on the LVI behavior of the samples at various temperatures. Delamination, matrix cracking, and fiber failure were the main damage modes. Compared to the samples tested at room temperature, the reduction of temperature to -30 ℃ enhanced the maximum impact force and flexural stiffness while decreasing the absorbed energy and the failure surface area. The temperature increasing to 65 ℃ increased the maximum impact force and flexural stiffness while decreasing the absorbed energy and the failure surface area. Applying 200 thermal cycles at the range of -30 ℃ to 65 ℃ led to the formation of fine cracks in the matrix while decreasing the absorbed energy. The maximum contact force is recorded under cyclic temperature as 5.95, 6.51 and 7.14 kN, under impact energy of 10, 15 and 20 J, respectively. As well as, the minimum contact force belongs to the room temperature condition and is reported as 3.93, 4.94 and 5.71 kN, under impact energy of 10, 15 and 20 J, respectively.

• Composites Research
• /
• v.28 no.4
• /
• pp.232-238
• /
• 2015

As a new method to predict the degree of dispersion in carbon nanocomposites, the electrical resistance (ER) method has been evaluated. After CNT epoxy resin was dropped on CF tow, the change in electrical resistance of carbon fiber tow was measured to evaluate dispersion condition in CNT epoxy resin. Good dispersion of CNTs in carbon nanocomposite exhibited low change in ER due to wetted resin penetrated on CF tow. However, because CNT network was formed among CFs, non-uniform dispersion occurred due to nanoparticle filtering effect by CF tow. The change in ER for poor dispersion exhibited large ER signal change. The change in ER was used for the dispersion evaluation of CNT epoxy resin. Correlation between interlaminar shear strength (ILSS) and dispersion condition by ER method was established. Good CNT dispersion in nanocomposites led to good interfacial properties of fiberreinforced nanocomposites.

• Composites Research
• /
• v.20 no.2
• /
• pp.1-9
• /
• 2007

To evaluate and investigate the aging characteristics and the structural service lifetime of the CFV(carbon fiber pressure vessel), natural aging tests were carried out using the CFVs, which had been placed and aged at outdoor and indoor laboratories for 10 and 15 years, respectively. To obtain the probabilistic characteristics of ageing characteristics in aged CFVs, inner pressure loading test was conducted with ring specimens taken from aged CFVs. And, to observe the interface morphology of aged CFVs, the micro-photographs were taken by SEM microscope and the fractured interfaces between the carbon fiber and the matrix resin were scrutinized. Based on the Weibull parameters of the tensile failure strain of aged CFVs, the degradation of the 10 and the 15 year aged CFV occur by 19% and 23%, respectively, and the effect of the placement, whether being placed inside the laboratory or not, is not so significant. However, the outer layer protection, such as painting, is found very advantageous to prevent CFV from aging.