• The Journal of Korean Academy of Prosthodontics
• /
• v.48 no.2
• /
• pp.122-127
• /
• 2010

Purpose: The objective of this study was to investigate the effects of calcium phosphate coated titanium implant surface on bone response and implant stability at early stage of healing period of 3 weeks and later healing period of 6 weeks. Material and methods: A total of 24 machined, screw-shaped implants (Dentium Co., Ltd., Seoul, Korea) which dimensions were 3.3 mm in diameter and 5.0 mm in length, were used in this research. All implants (n = 24), made of commercially pure (grade IV) titanium, were divided into 2 groups. Twelve implants (n = 12) were machined without any surface modification (control). The test implants (n = 12) were anodized and coated with thin film (150nm) of calcium phosphate by electron-beam deposition. The implants were placed on the proximal surface of the rabbit tibiae. The bone to implant contact (BIC) ratios was evaluated after 3 and 6 weeks of implant insertion. Results: The BIC percentage of calcium phosphate coated implants ($70.8{\pm}18.9%$) was significantly higher than that of machined implants ($44.1{\pm}16.5%$) 3 weeks after implant insertion (P = 0.0264). However, there was no significant difference between the groups after 6 weeks of healing (P > .05). Conclusion: The histomorphometric evaluation of implant surface revealed that; 1. After 3 weeks early healing period, bone to implant contact (BIC) percentage of calcium phosphate coated implants (70.8%) was much greater than that of surface untreated machined implants (44.1%) with P = 0.0264. 2. After 6 weeks healing period, however, BIC percentage of calcium phosphate coated implants group (79.0%) was similar to the machined only implant group (78.6%). There was no statistical difference between two groups (P = 0.8074). 3. We found the significant deference between the control group and experimental group during the early healing period of 3 weeks. But no statistical difference was found between two groups during the later of 6 weeks.

• Journal of Periodontal and Implant Science
• /
• v.33 no.4
• /
• pp.651-671
• /
• 2003

The influence of calcium phosphate (Ca-P) coating on the bone response of titanium implants was investigated two types of titanium implants, i.e. as -machined ,as -machined with Ca-P coating, were prepared. The Ca-P coating produced by OCT Inc technique. These implants were inserted into the left and right femur of beagle dog, After implantation periods of 3 days, 1weeks, weeks, 4weeks, 8weeks, 12weeks. 24weeks, the bone-implant interface was evaluated histologically, histomorphometrically , and removal torque. Histological evaluation revealed no new bone formation around different implant materials after 2weeks of implantation. After 4 weeks, Ca-P coated implants showed a higher amount of bone contact than either of the non coated implants. After 12weeks, bone healing was almost completed. And implant were removed by reverse torque rotation with torque-measuring device. Mean torque values for 4weeks control were 2.375Kgf.cm and experimental were 2.725Kgf.cm. And mean torque values for 8weeks control were 1.25Kgf.cm and experimental were 1.0Kgf.cm On the basis of these findings, we concluded that deposition of a Ca-P coating on an implant has a beneficial effect on the bone response to this implant during the healing phase. Besides implant surface conditions the bone response is also determined by local implant site condition.

• Journal of dental hygiene science
• /
• v.11 no.5
• /
• pp.405-410
• /
• 2011

The aim of this study was to evaluate antibacterial effect of Cl coated titanium. To coat the Cl on the titanium, first, the titanium was modified by blasting treatment with hydroxyapatite and alumina powder. Anodization process was completed using electrolyte solution of 0.04 M ${\beta}$-glycerol phosphate disodium salt n-hydrate, 0.4 M calcium acetate n-hydrate and 1 M NaCl on the condition of 250 voltages for 3 min. Surface morphology and elements' observation were performed with scanning electron microscopy and energy dispersive spectroscopy and surface profiler was used to analyze the surface roughness. Antibacterial effect was evaluated by film adhesion method. The anodized titanium after blasting showed dimpled surface contained the Cl. Surface average roughness of these surfaces had significantly higher compared to polished titanium. Result of antibacterial test showed that anodized titanium after blasting had an enhanced antibacterial effect compared to the polished titanium. Therefore, these results suggested that titanium contained Cl by anodization after blasting had a rough surface as well as antibacterial effect.