'Yeobong' strawberries were stored at $2^{\circ}C$ under controlled atmosphere (CA) containing the combinations of $O_2{\;}(3.8%)$ and $CO_2{\;}(10,{\;}15,{\;}20%)$ and air as control. Atmospheres of $3%{\;}O_2+15%{\;}CO_2$ and $8%{\;}O_2+15%{\;}CO_2$ reduced respiration and ethylene production rates. Fruits kept under CA conditions of 10% and 15% $CO_2$ were harder than those stored under 20% $CO_2$ and air. The CA conditions of 10% or 15% $CO_2$ maintained approximately 80% of vitamin C for 24 days. Redness were increased and then decreased, but the changing trends were not clear among the storage conditions. Anthocyanin contents in $3%{\;}O_2+15%{\;}CO_2$ and $8%{\;}O_2+15%{\;}CO_2$ were slightly increased for 16 days and then decreased thereafter, while anthocyanin content in air was rapidly increased for 8 days. After 16 days of storage, off-flavor were perceived in all CA storage. And strawberries stored in 20% $CO_2$ conditions were unacceptable after 20 days. The 20% $CO_2$ significantly affected off-flavor of strawberries, but there was no significant difference between 10% $CO_2$ and 15% $CO_2$ conditions. Ethanol which is in relation to off-flavor was higher with elevated $CO_2$ levels. Although CA conditions under $3%{\;}O_2+15%{\;}CO_2$ was effective in delaying the quality changes, there was high ethanol content compared to $8%{\;}O_2+15%{\;}CO_2$ condition. Strawberry kept under $8%{\;}O_2+15%{\;}CO_2$ was maintained the shelf-life for 24 days and the condition prolonged more $4{\sim}8$ days and 12 days than the other CA conditions and air, resectively.

• Journal of the Korean Ceramic Society
• /
• v.55 no.2
• /
• pp.160-165
• /
• 2018

This paper investigates the reaction rate of $CO_2$ storing carbonation hybrid reaction by comparing the behavior of carbonation between $Ca(OH)_2$ and fly ash with that of CFBC (Circulating Fluidized Bed Combustion) containing plenty of Free-CaO. Because fly ash with CFBC contains a lot of unreacted CaO, it cannot be used as a raw material for concrete admixtures and its usages are limited. To reuse such material, we stabilized unreacted CaO by carbonation and investigated the carbonation rate. We used a pH meter and a thermometer to check the rate of the carbonization. Also, we set the contents of fly ash with CFBC, $Ca(OH)_2$, flow and fluid of $CO_2$, respectively, to 100 g, 50 g, 100 ~ 1000 cc/min and 400 g based on the content of Free-CaO. We used carbonated water instead of water, and added an alkaline activator to promote the carbonation rate. As a result, the addition of the alkaline activator and carbonated water promoted the rate of carbonation via a hybrid reaction.

• Journal of the Korean Ceramic Society
• /
• v.30 no.1
• /
• pp.7-16
• /
• 1993

Effect of sulfate on the reactionof C3S formation in presence of clinker melt and its appearance in clinker were investigated, using (NH4)2SO4 and CaSO4 as sulfate sources. When (NH4)2SO4 and CaSO4 were added, both showed the similar results, 1.0wt% of sulfate could promoted the reaction of C3S formation, however for its content of more than 2.0wt%, the formation of C3S was prevented. Residual limit of sulfate to C3S formation is about 1.4wt%. Appearances of sulfate were C4A3l and CaSO4 in interstitial phase. For the addition of (NH4)2SO4 or CaSO4 of 20wt%~4.0wt%, C3S grains showed the hypertrophic growth. We might consider that, because sulfate reduced the surface tension and viscosity of the clinker melt, C3S crystals were precipitated below 140$0^{\circ}C$, and the crystlas of C3S were coalesced and linked in the same crystallographical direction with increasing temperature becuase of their rapid growth rate.

• Horticultural Science & Technology
• /
• v.19 no.2
• /
• pp.145-148
• /
• 2001

This research was conducted to find out whether controlled atmosphere(CA) can maintain Satsuma Mandarin fruit fresh longer compared to cold storage. Fruit harvested in Nov. 1998 at Jeju Province were stored in three different CA condition including cold storage. The CA treatments consisted of combinations of 3%, 5% and 10.9% $CO_2$ with 1% and 3-3.9% $O_2$, respectively. Weight and firmness were maintained higher in static CA chambers than in the cold storage. Soluble solid content in fruit of cold storage increased until 2 months of storage and thereafter sharply decreased, whereas that of CA-stored fruit increased slowly throughout the storage period of 120 days. Citric acid decreased obviously in all the treatments with a partially longer retention in CA chambers during storage. Sensory evaluation clearly showed that CA could extend market period of Satsuma Mandarin fruit.

• Journal of the Korean Ceramic Society
• /
• v.26 no.4
• /
• pp.559-567
• /
• 1989

Bioglasses have been known to be as one of the promising biomateials, which can be used for replacing defective hard and soft tissue. There have been many reports on biological results for this type of glass, but no systematic work has carried out on the structures and properties of the bioglass itself. In the present study, the effect of P2O5 in bioglasses on their structures and properties was examined. Infrared and Raman spectroscopy for the glass structural analysis, differential thermal and X-ray diffraction analysis for the crystallization of the bioglass were performed, and several physical properties were measured. When the glasses were heat-treated, Na2O.2CaO.3SiO2 was the major crystalline phase and $\beta$-NaCaPO4 crystal was found for the glass with high P2O5 content. The added P2O5 in the glasses enhanced the polymerization of silicate glass structure and it changed the chain-like glass structure to a sheet-like structure, and some P2O5 may stay as phosphate monomer. With addition of P2O5 in the glass the density of the glasses decreased, but not much changes in their thermal expansion coefficient, softening point and microhardness were observed.

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.438-445
• /
• 2002

In this study, the glass frit of $PbO-TiO-2-SiO_2-BaO-ZnO-Al_2O-3-CaO-B_2O_3-Bi_2O_3-MgO$ system was manufactured. The glass was melted at $1,400{\circ}C$, quenched and attrition-milled. The glass frit powder was pressed and fired for 2h at the range of $750~1,000{\circ}C$. The crystallization of glass frit began at about $750{\circ}$ and at low temperature, the main crystal phases were hexagonal celsian($BaAl_2Si_2O_8$) and alumina. As the firing temperature increased, the crystal phases of monoclinic celsian, zinc aluminate, zinc silicate, calcium titanium silicate and titania appeared. And the increase of firing temperature led to transformation of hexagonal celsian to monoclinic. The only glass frit containing 15wt% PbO had the crystal phase of solid solution of $PbTiO_3-CaTiO_3$. At the frequency of 1 MHz, the dielectric constant of glass frit crystallized was in the range of 11~16 and the dielectric loss less than 0.020. But the glass frit containing 15wt% PbO had the dielectric constant of 17~26 and loss of 0.010~0.015 because of crystal phase of solid solution of $PbTiO_3-CaTiO_3$.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.4
• /
• pp.321-327
• /
• 2018

Blast furnace slag has been actively used as a substitute for cement in the construction field with high value-added through resource recycling research. However, most of the slag cannot find a clear recycling purpose. This is because some slags contain unstable materials and are used for road-use asphalt and embankment, which are low value-added materials. Electric arc furnace reduction slag(ERS) has been reported to contain a large amount of unstable free CaO due to deoxidation and component adjustment. In this study, free CaO of ERS which is generated in Korean steelmakers is quantitatively evaluated by using ethylene glycol method. As a result of free CaO quantitative evaluation of ERS, it was confirmed that there is a big difference according to the location of each field. In addition, ERS generally existed in powder form as undifferentiated characteristics, but it was confirmed that free CaO content was different due to hydration product in aggregate form due to water treatment. In addition, free CaO is an amorphous material and its crystallization characteristics are different due to the influence of temperature when it is cooled. ERS requires a long-term aging period as it contains a lot of free CaO.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.406-409
• /
• 2001

In this paper, the microstructure and the dielectric properties of the Sr$_{1-x}$ Ca$_{x}$TiO$_3$(0$\leq$$\chi$$\leq$0.2) -based grain boundary layer ceramics were investigated. The specimens were sintered from 142$0^{\circ}C$ to 152$0^{\circ}C$ for 4hr. in $N_2$ gas. The 2nd phase formed by thermal diffusing from the surface lead to a very high apparent dielectric constant, $\varepsilon$$_{r}$>50000. The structural properties of the specimens were studied by X-ray diffraction and SEM, EDX. All specimens exhibited cubic structure. Increasing content of Ca, the peak intensity were decreased.ed.d.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.697-700
• /
• 2001

In this paper, the structural and electrical properties of the Sr$_{1-x}$ Ca$_{x}$TiO$_3$ (0$\leq$x$\leq$0.2) (0$\leq$r$\leq$0.2)-based grain boundary layer ceramics were investigated by X-ray, SEM and V-I system. Increasing the Ca content, the average grain size and the lattice constant were decreased. The relative density of all specimens was >96%. The 2nd phase formed by thermal diffusing from the surface lead to a very excellent electrical properties, that is, $\varepsilon$$_{r}$>50000, tan$\delta$<0.05, $\Delta$C< $\pm$ 10%.\pm$ 10%.%.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.09a
• /
• pp.72-75
• /
• 2001

In this paper, the $Sr_{1-x}Ca_{x}TiO_{3}(0{\leq}x{\leq}0.2)$ 2)-based grain boundary layer ceramics were fabricated to measured dielectric properties and voltage-current properties. The sintering temperature and time were $1420\sim1520^{\circ}C$, 4hours, in $N_{2}$ gas, respectively. The structural and the dielectric properties were investigated by SEM, X-ray, HP4194A and K6517. The 2nd phase formed by thermal diffusion from the surface lead to a very high apparent dielectric constant, $\varepsilon_r$ > 50000. X-ray diffraction patterns exhibited cubic structure for all specimens. Increasing content of Ca, the peak intensity were decreased.ﱇﶖ⨀ਆᘍ܀㘱㔮㠹㬅K䍄乍