• Proceedings of the KWS Conference
• /
• 2000.10a
• /
• pp.151-154
• /
• 2000

• Journal of Welding and Joining
• /
• v.33 no.2
• /
• pp.62-68
• /
• 2015

This study investigates the appropriate range of reverse bending load for the CTOD test of thick weld by observing improvement of pre-crack shape and determination of the limit applicable load. In order to do it, the effect of the amount of the reverse bending load on the maximum deviation of the pre-crack length was investigated by the extensive tests, and the variation of plastic zone size in way of the crack tip under reverse bending load were evaluated by FEA. With the results obtained by the experiments and FEA, the proper range of reverse bending load was suggested. The effectiveness of the reverse bending method was verified by examining the pre-crack straightness after CTOD tests of thick weld specimens with various thickness and strength.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.3
• /
• pp.528-536
• /
• 2002

As one step for the safety performance of LNG storage tank, the change in fracture toughness within the X-grooved weld heat-affected zone (HAZ) of newly developed 9% Ni steel, which was submerged arc (SA)-welded, was investigated. Both crack initiation fracture toughness and crack arrest fracture toughness were evaluated by the crack tip opening displacement (CTOD) tests and compact crack arrest (CCA) tests. As the evaluated region approached the fusion line, each test result shorted different tendency, that is, crack initiation toughness decreased while crack arrest toughness increased. The results were discussed through the observation of the microstructural change.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.13 no.5
• /
• pp.928-937
• /
• 1989

Applicability of $T_{\delta}$ proposed by Shin et al as an instability parameter for ductile material is investigated, Both general fracture test and instability fracture test are performed using compact tension specimens of structural alloy steel(SCM4), The values of ( $T_{\delta}$)$_{app}$(applied tearing modules) estimated from the real load vs. crack growth curve measured from experiments are compared with those estimated from the limit load vs. crack growth curve. The results are:(1) the $T_{\delta}$ parameter may be used as a crack instability parameter:(2) the use of ( $T_{\delta}$)$_{app}$ estimated from the load-crack growth curve, proposed in this study is reasonably justified.ified.d.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.3
• /
• pp.253-258
• /
• 2016

The effect of temperature on the fracture energy, crack propagation, and crack tip opening displacement (CTOD) was determined for particulate reinforced composites using the wedge splitting test. The materials that were used consisted of a polymer binder, an oxidizing agent, and aluminum particles. The test rate of the wedge splitting specimen was 50 mm/min, the temperature conditions were $50^{\circ}C$, room temperature, $-40^{\circ}C$, and $-60^{\circ}C$. The fracture energy, calculated from splitting load-crack mouth opening displacement(CMOD) curves, increased with decreasing temperature from $50^{\circ}C$ to $-40^{\circ}C$. In addition, the strength of the particulate reinforced composites increased sharply at $-60^{\circ}C$, and the composites evidenced brittle fracture due to the glass transition temperature. The strain fields near the crack tip were analyzed using digital image correlation.

• Journal of the Korean Society of Industry Convergence
• /
• v.26 no.5
• /
• pp.875-884
• /
• 2023

Hydrogen infiltration into metals has been reported to induce alterations in their mechanical properties under load. In this study, we conducted CTOD (Crack Tip Opening Displacement) tests on steel specimens designed for use in liquid hydrogen storage systems. Electrochemical hydrogen charging was performed using both FCC series austenitic stainless steel and BCC series structural steel specimens, while CTOD testing was carried out using a 500kN-class material testing machine. Results indicate a notable divergence in behavior: SS400 test samples exhibited a higher susceptibility to failure compared to austenitic stainless steel counterparts, whereas SUS 316L test samples displayed minimal changes in displacement and maximum load due to hydrogen charging. However, SEM (Scanning Electron Microscopy) analysis results presented challenges in clearly explaining the mechanical degradation phenomenon in the tested materials. This study's resultant database holds significant promise for enhancing the safety design of liquid hydrogen storage systems, providing invaluable insights into the performance of various steel alloys under the influence of hydrogen embrittlement.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.46 no.7
• /
• pp.535-541
• /
• 2018

In this study, wedge splitting tests were performed to evaluate fracture behavior of particle reinforced composite materials. Crack resistance was evaluated by using CTOD (crack tip opening displacement) and crack tip opening angle (CTOA). The particle reinforced composites were tested under various temperature ($-60^{\circ}C{\sim}50^{\circ}C$) and load speed (5~500mm/min). Also, digital image correlation method (DIC) was used to analyze the strain field at crack tip. Test results showed that the fracture energy increased with decreasing temperature and crack resistance increased with increasing load velocity.

• Journal of the Korean Institute of Gas
• /
• v.2 no.1
• /
• pp.7-13
• /
• 1998

In this study, for the safety performance of LNG storage tank, the fracture toughness in X-grooved weld HAZ(heat-affected zone) of $9\%$ Ni steel was evaluated qualitatively and quantitatively, and the relation with the change in microstructure was analyzed. The toughness assessment was peformed through the modified CTOD test proposed for thick weldment with X-groove. Additionally, microstructures of HAZ were evaluated by OM, SEM and XRD. From the results, HAZ toughness of SMA(shielded metal arc)-welded $9\%$ Ni steel decreased as the evaluated region approached the fusion line. The decrease in toughness was apparently caused by the increase in the fraction of coarse-grained zone within HAZ. On the other hand, toughness drop with decreasing test temperature in F.L.(fusion line) ${\~}$F.L.+3mm was larger than that in F.L.+5mm${\~}$F.L.+7mm region due to the fact that in the former regions, retained austenite had poor stability.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.40 no.12
• /
• pp.1021-1026
• /
• 2016

In this study, crack resistance is evaluated by the crack tip opening angle (CTOA) using a wedge splitting test (WST) on a viscoelastic particulate reinforced composite based on an HTPB binder. Generally, CTOA, as a function of crack extension, is used in order to determinate fracture resistance and has a steady state relative angle. Digital image correlation (DIC) is used to measure the crack tip opening displacement (CTOD) and crack extension for the critical crack tip opening angle (CTOAc). In these results, the CTOAc value of a particulate reinforced composite tends to approach a constant angle after a small amount of crack extension. The CTOAc value increases with decreasing temperature, from $50^{\circ}C$ to $-40^{\circ}C$. These CTOAc values may be used to measure fracture mechanics parameters for particulate reinforced composite.

• Journal of the Korean Institute of Gas
• /
• v.5 no.3 s.15
• /
• pp.15-22
• /
• 2001

Reliability evaluation of welded structures by mechanical testing of weld heat-affected zones (HAZs) has become general practice throughout the world. HAZs of steel welded Joints show a gradient of microstructure from the fusion line to the unaffected base metal. This study is concerned a correlation between the microstructural change and the fracture characteristics in HAZs of both seam and girth welds of API 5L X65 pipeline steel, which is generally used for natural gas transmission pipelines in Korea. The focus in this study is the investigation of macroscopic fracture behavior of the various regions within HAZ. Changes in microstructure and toughness were observed using actual HAZ specimens. To evaluate the macroscopic toughness of actual HAZ, Charpy V-notch impact test and CTOD test were performed.