Ultra-high temperature ceramics (UHTC) such as $ZrB_2$, ZrC, $HfB_2$, HfC and TaC has been recently actively investigated for the application as components such as nose-cone, rocket nozzle and leading edge of hypersonic systems. However, the application has been limited by various reasons. The brittleness of the materials and consequent low thermal shock resistance is one of the reasons. The property can be improved through the fabrication of ceramic matrix composites. In this paper, the concept of UHTC and the fabrication process and testing of UHTC-based ceramic matrix composites (UHTC-CMC) were briefly reviewed. Also, international activities regarding the fabrication of UHTC-CMC were summarized and a UHTC-CMC project, which was performed in Korea, was introduced.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2016.02a
• /
• pp.134-134
• /
• 2016

CMC(Ceramic Matrix Composites)는 $1500^{\circ}C$ 이상의 고온에서 내열성, 내산화성, 내식성이 우수하여, 초음속 비행체, 가스터빈 엔진 및 원자로용 초고온 부품 등에 수요가 증가하고 있다. 하지만 이러한 특성은 비산소 환경에 국한되는 것으로 약 $400^{\circ}C$ 이상의 산화 분위기에는 탄소섬유가 산화되는 문제로 인하여 적용의 한계를 가지고 있다. 따라서 CMC의 적용범위 확대를 위하여 내산화 코팅으로 CMC의 초고온 산화특성을 개선하는 것이 필수적이며, 장시간 초고온 산화환경 분위기에서 사용되기 위하여 안정적인 코팅기술이 최근 기술개발의 핵심현안으로 부각되고 있다. 본 연구에서는 pack cementation 공정을 이용하여 내산화성이 우수한 SiC 코팅층을 제조하였다. Pack cementation 공정에 사용된 코팅 분말은 57wt.% SiC, 30wt.% Si, 3wt.% B, 10wt.% Al2O3의 비율로 혼합된 것이다. 실험은 3D 직조된 CMC 모재를 혼합분말 내에 침적한 후, Ar 분위기에서 $1600^{\circ}C$, 4~12시간 반응시켜 수 마이크론 두께의 SiC 코팅층을 형성하였다. 더 우수한 산화 특성을 부여하기 위하여 pack 처리된 CMC 표면에 초고온 세라믹인 TaC 소재를 진공플라즈마 코팅 공정으로 적층시켰다. 제조된 코팅층을 SEM, XRD를 이용하여 미세구조 및 결정구조를 분석하였으며, pack cementation에 따른 내산화 특성을 비교 분석하고자 $2000^{\circ}C$에서 산화 실험을 진행하였다. 산화 실험 이후 미세구조 및 결정구조 분석으로 산화거동을 규명하고자 하였다.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 1996.10a
• /
• pp.52-57
• /
• 1996

Conductive Ceramic Matrix Composite(CMC) of TIC/Al2O3 and Metal Matrix Composite (MMC) of SiC/Al were experienced by the die sinking Electrical Discharge Machining(EDM) for different current and duty factor according to negative polarity. Inthis experimental study Material Removal Rate(MRR) maximum surface roughness four point bending stress distribution and Scanning Electron Microscopy(SEM) Photographs were analysed. the higher MRR was obtained for CMC than MMC but slowly decreased around duty factor of 0.67 for MMC and better surface morphology was found CMC than MMC. The SEM photographs of discharge traces for CMC showe uniform shape about 100 to 200${\mu}{\textrm}{m}$ in diameter but MMC showed irregular shape.

• The Korean Journal of Ceramics
• /
• v.6 no.3
• /
• pp.201-205
• /
• 2000

Fiber reinforced plastic (FRP) composites and ceramic matrix composites (CMC) which contain electrically conductive phases have been designed and fabricated to introduce the detection capability of damage/fracture detection into these materials. The composites were made electrically conductive by adding carbon and TiN particles into FRP and CMC, respectively. The resistance of the conductive FRP containing carbon particles showed almost linear response to strain and high sensitivity over a wide range of strains. After each load-unload cycle the FRP retained a residual resistance, which increased with applied maximum stress or strain. The FRP with carbon particles embedded in cement (mortar) specimens enabled micro-crack formation and propagation in the mortar to be detected in situ. The CMC materials exhibited not only sensitive response to the applied strain but also an increase in resistance with increasing number of load-unload cycles during cyclic load testing. These results show that it is possible to use these composites to detect and/or fracture in structural materials, which are required to monitor the healthiness or safety in industrial applications and public constructions.

• Journal of Ceramic Processing Research
• /
• v.20 no.1
• /
• pp.48-53
• /
• 2019

Carbon fiber reinforced SiC composites (C/SiC) have high-temperature stability and excellent thermal shock resistance, and are currently being applied in extreme environments, for example, as aerospace propulsion parts or in high-performance brake systems. However, their low thermal conductivity, compared to metallic materials, are an obstacle to energy efficiency improvements via utilization of regenerative cooling systems. In order to solve this problem, the present study investigated the bonding strength between carbon fiber and matrix material within ceramic matrix composite (CMC) materials, demonstrating the relation between the microstructure and bonding, and showing that the mechanical properties and thermal conductivity may be improved by treatment of the carbon fibers. When fiber surface was treated with a nitric acid solution, the observed segment crack areas within the subsequently generated CMC increased from 6 to 10%; moreover, it was possible to enhance the thermal conductivity from 10.5 to 14 W/m·K, via the same approach. However, fiber surface treatment tends to cause mechanical damage of the final composite material by fiber etching.

• Journal of the Korean Ceramic Society
• /
• v.46 no.3
• /
• pp.301-305
• /
• 2009

The novel carbon coating process for interlayer of fiber reinforced ceramic composites between fiber and matrix was performed by carbonizing phenolic resin solution that coated on fiber surface in $N_2$ atmosphere at $600^{\circ}C$ to improve the strength and fracture toughness of CMC(ceramic matrix composite). 160 nm carbon layer was coated on fiber surface with 5 vol% of phenolic resin solution. Since the process temperature ($600^{\circ}C$) is lower than chemical vapor deposition($900{\sim}1000^{\circ}C$), the strength and toughness could be preserved. Furthermore the coating thickness uniformity was improved to 8% of deviation along the stacking sequence. Therefore, prevention from fiber degradation during coating process and controlling coating thickness uniformity along the preform depth were achieved by coating with phenolic resin carbonizing method.

• Composites Research
• /
• v.27 no.4
• /
• pp.123-129
• /
• 2014

Ceramic matrix composites (CMCs) consist of such reinforcements as carbides, nitrides, borides and oxides, which have high melting points, low density, high modulus and high strength, for the purpose of increasing toughness. These materials are used for heat shielding systems for aerospace vehicles, high-temperature gas turbine combustion chambers, turbine blades, stator vane parts, etc. Oxide CMCs are used for the components of burner and flame holder and the high-temperature gas duct. CMCs are also applied to brake disks, which are subjected to severe thermal shock, and slide bearing parts under heavy loads. The research and development of the CMC are progressed for the strategic purpose in defense and energy industry; for instance, for aerospace applications in the U.S., and for hyper-speed aircraft, gas turbines, and atomic fissions in U.S., Japan, and Europe.

• Journal of the Korean Society for Precision Engineering
• /
• v.16 no.8
• /
• pp.9-15
• /
• 1999

Die-sinking electrical discharge machining(EDM) for conductive ceramic matrix composite(CMC) of Tic/$Al_2O_3$ was experienced with addition of ultrasonic emission, and the results were compared with ones obtained by the EDM only. From this experimental study, the values of material removal rate(MRR) and surface roughness($R_{max}$), scanning electron microscope(SEM) micrographs, and weibull probability distribution of bending strength for the specimens were obtained and compared. The trend of MRR was found to be increased slightly with the current and the duty factor for both EDM only and EDM with ultrasonic emission. The MRR values were found to be increased for EDM with ultrasonic emission. The SEM micrographs of EDMed surface by under various operating conditions showed less micro cracks in various places. Although smaller bending strength value was obtained by EDMed surface with ultrasonic emission by weibull probability distribution analysis of bending strength.

• Journal of the Korean Ceramic Society
• /
• v.55 no.4
• /
• pp.392-399
• /
• 2018

$C_f/SiC$ composites were prepared via a process combining chemical vapor infiltration (CVI) and precursor infiltration pyrolysis (PIP), wherein silicon carbide matrices were infiltrated into 2.5D carbon preforms. The obtained composites exhibited porosities of 20 vol % and achieved strengths of 244 MPa in air at room temperature and 423 MPa at $1300^{\circ}C$ under an Ar atmosphere. Carbon fiber pull-out was rarely observed in the fractured surfaces, although intermediate layers of pyrolytic carbon of 150 nm thickness were deposited between the fiber and matrix. Fatigue fracture was observed after 1380 cycles under 45 MPa stress at $1000^{\circ}C$. The fractured samples were analyzed by transmission electron microscopy to observe the distributed phases.