• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2008년도 춘계학술대회 논문집
• /
• pp.438-440
• /
• 2008

Effects of Ga contents of CIGS absorber layer on the performance of thin films solar cells were investigated. As Ga content increased, the grain size of CIGS films decreased presumably because Ga diffusion during 2nd stage of co-evaporation process is more difficult than In diffusion. Performances of corresponding solar cell show systematic dependence on Ga content in which open circuit voltage increases and short circuit current and fill factor decrease as Ga contents increases. At a optimal condition of Ga/(In+Ga)=0.27, the solar cell shows a conversion efficiency of 15.6% with $V_{OC}$ of 0.625 V, $J_{SC}$ of 35.03 mA/$cm^2$ and FF of 71.3%.

• 한국표면공학회지
• /
• 제44권6호
• /
• pp.264-268
• /
• 2011

The Molybedenium thin film is generally used on back contact material of CIGS solar cell due to low electrical resistivity and stable thermal expansion coefficient. The Mo thin films deposited on si wafer by the magnetron sputtering method. The research focused on the variation of electrical resistivity of films which deposited with various working pressure at the target power of 2.0 kW(8.4 W/). The lowest resistivity of Mo thin film showed $9.0{\mu}O$-cm at pressure of 1.5 mTorr. However, working pressure increasing up to 50 mTorr, resistivities were highly increased. The results showed that the conductivity of Mo films depended on growing structures and defects in deposition process. Surface morphology, porosity, grain size, oxidation, and bonding structures were analysed by SEM, AFM, spectroscopic ellipsometry (SE), XRD, and XPS.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.330-333
• /
• 2002

The substrate temperature is an important parameter in thin film deposition process. In this paper the effects of the substrate temperature on the properties of CuIn0.75Ga0.25Se2(CIGS) thin films are reported. Structure, surface morphology and optical properties of CIGS thin films deposited at various substrate temperatures have been investigated using a number of analysis techniques. X-ray diffraction (XRD) analysis shows that CIGS films exhibit a strong <112> preferred orientation. As expected, at higher substrate temperatures the films displayed a higher degree of crystallinity. The <112> peak was also enhanced and other CIGS peaks appeared simultaneously These results were supported by experimental work using Raman spectroscopy. The Raman spectra of the as-grown CIGS thin films show only the Al mode peak. The intensity of this peak was enhanced at higher deposition temperatures. Scanning electron microscopy (SEM) results revealed very small grains in films fabricated at 48$0^{\circ}C$ substrate temperature. When the substrate temperature was increased the average grain size also increased together with a reduction in the number and size of the voids. The deposition temperature also had a significant influence on the transmission spectra.

• Current Photovoltaic Research
• /
• 제3권2호
• /
• pp.65-70
• /
• 2015

We applied KF on CIGS film to modify CIGS surface with a wider-bandgap surface layer. With the KF deposition the surface of CIGS film had fine particle on the CIGS surface at 350 and $300^{\circ}C$. No fine particle was detected at 500 and $250^{\circ}C$. With the KF treatment, the Ga and O content increased at the surface, while the In and Cu content decreased. The valence band maximum was lowered with KF treatment. The composition profile and band structure were positive side of applying KF on the CIGS surface. However, the efficiency decreased with the KF treatment due to high series resistance, probably due to too thick surface layer. A smaller amount of KF should be supplied and more systematic analysis is necessary to obtain a reproducible higher efficiency CIGS solar cells.

• 한국전기전자재료학회논문지
• /
• 제27권4호
• /
• pp.203-208
• /
• 2014

In this study, Sputtering method was used to grow Al-dopes ZnO films on a CIGS absorber layer, in order to examine the effect of TCO on properties of CIGS solar cell devices. Structural, electrical and optical properties were investigated by varied thickness of Al-dopes ZnO films. Also, relation to the application as a window layer in CIGS thin film solar cell were studied. It was found that the electrical and structural properties of ZnO:Al film improved with increasing its thickness. However, the optical properties degraded. Jsc of the fabricated CIGS based solar cells was significantly influenced by the variation of the ZnO:Al window layer thickness. Because ZnO:Al window layer is one of the Rs factors in CIGS solar cell. Rs has the biggest influence on efficiency characteristic. In order to obtain high efficiency of CIGS solar cell, ZnO:Al window layer should be fabricated with electrically and optically optimized.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2011년도 춘계학술대회 초록집
• /
• pp.125.2-125.2
• /
• 2011

CuInGaSe2 (CIGS)을 포함한 Chalcopyrite계 물질은 직접천이형 반도체이면서, ${\sim}1{\times}10^5cm^{-1}$ 이상의 광흡수계수를 보이며, 조성제어를 통한 밴드갭 조절이 가능해 차세대 고효율 박막태양전지재료로 매우 주목받고 있다. 최근, CIGS 박막태양전지 제조를 위해 CIGS 흡수층의 여러 가지 박막제조 공정들이 개발되고 있으나, 동시증착법과 소위 2단계법이라 일컬어지는 금속 전구체 스퍼터링 증착 후 셀렌화 공정을 가장 대표적인 공정이라 말 할 수 있다. 동시증착법은 실험실 수준의 소면적 셀에서 20%에 가까운 높은 효율의 CIGS 박막태양전지 제조에 성공하였음에도 불구하고, 상용화를 위한 대면적 셀 제조를 위해 해결해야 할 문제들이 아직 남아있다. 또한, 2단계법의 경우는 스퍼터링 공정을 기반으로 대면적 셀 제조에는 용이하나, CIGS/Mo 계면에서의 Ga 응집현상의 발생 및 셀렌화 공정에 사용되는 독성가스($H_2Se$)의 문제 등이 남아 있어 새로운 시각에서의 접근 방법이 요구되고 있다. 본 연구에서는 CIGS 4성분계 단일 타겟을 사용, RF 스퍼터링 공정을 통해 $200{\times}200mm^2$ 기판 위에 CIGS 박막을 제조하여 그 특성을 분석하였다. XRD 분석결과, 동시증착법에서 일반적으로 관찰되는 CIGS/Mo 계면에서의 $MoSe_2$ 상의 존재는 관찰되지 않았으며, CIGS 단일상의 다결정 박막이 제조되었음을 알 수 있었다. 또한, CIGS 박막제조 후, RTA 공정을 통해 CIGS 박막의 결정성이 향상됨을 관찰 할 수 있었으며, SIMS 분석결과, Mo층의 공정 조건에 따라 CIGS/Mo 계면에서의 금속원소 (In, Ga, Mo)의 상호확산이 크게 억제됨을 알 수 있었다. 그 외의 특성평가 결과들을 통하여 CIGS 4성분계 단일 타겟을 사용한 CIGS 박막태양전지 제조의 유용성에 대해 논의하고자 한다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.45-46
• /
• 2015

Se 원소가 포함된 $CuIn_xGa_{1-x}Se_2$(CIGS) 단일 스퍼터링 타겟을 이용하여 후처리 공정없이 단일 스퍼터링 공정만으로 CIGS 흡수층 박막을 증착하여 소자 특성을 확인하였다. 단일 CIGS 흡수층 공정이 적용된 CIGS 박막태양전지 소자(유리기판/Mo/단일 CIGS 흡수층 박막/CdS/i-ZnO/Al-doped ZnO/Ni-Al grid)에서 10.0%의 태양광 변환 효을을 달성하였으며, 이는 기존의 복잡한 공정구조를 해결하여 대면적 양산화 CIGS 제조 공정에도 적용할 수 있음을 확인하였다.

• 한국신재생에너지학회:학술대회논문집
• /
• 한국신재생에너지학회 2005년도 춘계학술대회
• /
• pp.109-112
• /
• 2005

Cu계$I-III-VI_2$화합물은 직접천이형 반도체로 광흡수계수가 매우 높아 박막형 태양전지 제조에 매우 유리하다 또한 화학적으로 안정하며 Ga, A1등을 첨가하면 에너지 금지대폭을 조절할 수 있어 Wide Bandgap 태양전지 및 탠덤구조 태양전지를 제조하기에도 용이하다. $CuInSe_2(CIS)$ 물질에서 In을 $20-30\%$ 정도 치환한 $Cu(In,\;Ga)Se_2(CIGS)$ 태양전지의 경우 $19.5\%$의 세계 최고 효율을 보고하고 있으며 이는 다결정 실리콘 태양전지의 효율과 비슷한 수준이다. 본 연구에서는 동시 진공증발법을 이용하여 증착한 CIGS 박막 및 $CuGaSe_2(CGS)$ 박막을 이용하여 태양전지를 제조하였다. 공정의 재현성 및 결정립계가 큰 광흡수층 제조를 위하여 실시간 기판 온도 모니터링 시스템을 도입하였으며 버퍼층으로는 용액성장한 CdS 박막을 사용하였다. SLG/MO/CIGS(CGS)/CdS/ZnO/Al구조의 태양전지를 제조하여 면적 $0.5cm^2$에서 각각 $15\%$(CIGS)와 $7\%(CGS)$의 효율을 얻었다.

• 한국전기전자재료학회논문지
• /
• 제26권4호
• /
• pp.304-308
• /
• 2013

For the application to the window layer of $Cu(In,Ga)Se_2$(CIGS) solar cell, zinc oxide(ZnO) thin film was deposited at various temperatures by in-line pulsed DC sputtering. From the structural, optical, and electrical investigation and analysis, it was possible to obtain the lower thickness, the lower resistivity, and the higher transmittance at a higher process temperature. The energy band gap of ZnO was calculated using the transmittance data and was analyzed in terms of the dependency on temperature. From the X-ray diffraction(XRD) results, it was possible to conclude that a dominant peak was found about $34.2{\sim}34.6^{\circ}$(111) and crystallinity was obtained at a temperature above $150^{\circ}C$.

• 신재생에너지
• /
• 제1권2호
• /
• pp.6-10
• /
• 2005

[ $CulnSe2$ ]계 화합물은 직접천이형 반도체로 광흡수계수가 매우 높아 박막형 태양전지 제조에 매우 유리하다. 또한 화학적으로 안정하며 Ga, Al 등을 첨가하면 에너지 금지대폭을 조절할 수 있어 Wide Bandgap 태양전지 및 탠덤구조 태양전지를 제조하기에도 용이하다. CIS 물질에서 In을 $20-30\%$ 정도 치환한 $Cu(In,\;Ga)Se_2(CIGS)$ 태양전지의 경우 19.5%의 세계 최고 효율을 보고하고 있으며 이는 다결정 실리콘 태양전지의 효율과 비슷한 수준이다. 본 연구에서는 동시 질공증발법을 이용하여 증착한 CIGS 박막 및 $CuGaSe_2(CGS)$ 박막을 이용하여 태양전지를 제조하였다. 공정의 재현성 및 결정립계가 큰 광흡수층 제조를 위하여 실시간 기판 온도 모니터링 시스템을 도입하였으며 버퍼층으로는 용액성장한 CdS 박막을 사용하였다. SLG/MO/CIGS(CGS)/CdS/ZnO/Al 구조의 태양전지를 제조하여 면적 $0.5cm^2$에서 각각 $17\%(CIGS)$와 $7\%(CGS)$의 효율을 얻었다.