• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.859-866
• /
• 2003

When calcium sulfoaluminate-based expansive cement was hydrated, ettringite and monosulfate were mainly formed. The crack of hardened cement was prevented by compensating drying shrinkage due to formation of the above hydrates. In order to study the hydration properties of calcium sulfoaluminate-based expanding cement, 3CaOㆍ3Al$_2$O$_3$ㆍCaSO$_4$(C$_4$A$_3$S) was prepared by chemical synthesis, and then the hydration of $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$.$2H_2O$-C$_3$A system_was characterized. Good $C_4$A$_3$S phase was prepared at $1300^{\circ}C$ by chemical synthesis, and the main hydration product of $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$.2$H_2O$ system was ettringite. In the case of hydration $C_4$A$_3$S-Ca(OH)$_2$-CaSO$_4$ㆍ 2$H_2O$-C$_3$A system, ettringite was formed in the early period and it was transformed into monosulfate while consumed gypsum.

• Journal of Korean Society of Environmental Engineers
• /
• v.28 no.3
• /
• pp.265-269
• /
• 2006

This study was to investigate the effect of acidic leachate on the landfill liner system and healing of cracks by using industrial by-products; BFS(Blast Furnace Slag) and FA(Fly Ash). From the results of pH measurement, for OPC(Ordinary Portland Cement) and DM(Dredged Mud) mixtures immersed acidic leachate, the initial pH($4.5{\sim}5.5$) was heavily increased to approximately 10 after 60 days experiment due to the production of 2 mole $OH^-$ which was occurred by hydrolysis of CaO and MgO etc.. Meanwhile, the initial pH of acidic leachate immersed DM mixtures with BFS and FA respectively was lasted for longer period as compared to the comparison. The reason was that production of low Ca C-S-H hydrates which stabilized in acidic liquid. The physical properties(compressive strength, hydraulic conductivity) of DM mixtures added BFS and FA was improved. It was concluded that the dissolution of hydrates was disturbed by high alkalinity of BFS and FA.

• The Korean Journal of Ceramics
• /
• v.2 no.3
• /
• pp.147-151
• /
• 1996

By adding borax into the raw mix, Modified Belite Cement clinker and cements were prepared. Clinkerization and hydration reactions were investigated in order to better understand. Borax-bearing MBC clinker sintered at 1300℃ for 1 hour showed excellent burnability. Borax stabilized α'and β-C2S at room temperature. In the hydration of the cement prepared with the borax-bearing clinker, ettringite, monosulphate, C-S-H hydrates and CH were formed. The hydration of calcium sulphoaluminate was less reactive than the cement prepared with the controlled clinker at early hydration time. But, as hydration time elapsed, this cement showed more active hydraulicity and higher compressive strength development.

• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1507-1512
• /
• 1994

High strength cement hardened body was prepared by ordinary portland cement, silica-fume, super-plasticizer and the industrial by-product powder such as tailing, paper sludge ash and granulated slag. These raw materials were mixed and formed with w/c=0.18. The cement hardened body is cured in the autoclave at 18$0^{\circ}C$, 10atm. These admixtures made the compressive strength of all specimens develope by 170~230%. The highest compressive strength could be obtained by 236 MPa when mix composition was 14 wt% of silica-fume and 26 wt% of granulated slag. The compressive strength increased with decreasing the average pore size and the amount of the poe over the size of 50 nm by which the appearance of high compressive strength of the cement hardened body were mainly influenced. In the result, the hydration products were C-S-H, tobermorite and ettringite and it was realized that the reason why the cement hardened body became dense and revealed the higher strength was that those hydrates were formed inside of the pore and filled in it and the unhydrated materials played the role of an inner-filler.

• Journal of the Korea Concrete Institute
• /
• v.26 no.3
• /
• pp.369-375
• /
• 2014

This study examined the changes of microstructural compositions in cement matrix according to the depth from the surface of a reinforced concrete (RC) column exposed to fire. The RC column was exposed to a standard fire for 180 minutes. After the fire test, core samples passing through the column section were obtained. Using the core samples, the remaining fractions of calcium-silicate-hydrates (C-S-H) and calcium hydroxide in cement matrix at the surface, the depth of 40 mm and 80 mm and the center (175 mm) were examined using thermal gravimetric analysis (TGA) and X-ray diffraction analysis (XRDA). Using nuclear magnetic resonance (NMR) technique, the silicate polymerization of C-S-H in cement matrix was also evaluated. The experimental results indicated that the amount of C-S-H loss at the center of column experiencing the transferred fire temperature of $236^{\circ}C$ has been underestimated as the TGA results showed the highest C-S-H contents are located at the depth of 80 mm, where the transferred fire temperature is $419^{\circ}C$. Moreover, the destruction of silicate connections at the center was observed as similar as that at the depth of 40 mm, where the transferred fire temperature was $618^{\circ}C$. This might be attributed to the temperature changes during cooling time after the fire test was neglected. Due to the relatively low thermal conductivity of concrete, the high temperature, which can affect the change of microstructure in cements, will hold longer at the center of the column than other depth.

• Journal of the Korean Geotechnical Society
• /
• v.31 no.1
• /
• pp.37-46
• /
• 2015

In this study, a blast furnace slag with the alkaliphilic microorganism (Bacillus halodurans) alkaline activator was used to cement natural soils in the field. A low-cost and massive microbial solution for cementation of field soils was produced and compared with existing microbial culture in terms of efficiency. A field soil was prepared for three different cementation areas: a cemented ground with microbial alkaline activator (Microbially-treated soil), a cemented ground with ordinary Portland cement (Cement-treated soil), and untreated ground (Non-treated soil). The testing ground was prepared at a size of 2.6 m in width, 4 m in length, and 0.2 m in depth. After 28 days, a series of unconfined compression tests on the cement-treated and microbially-treated soils were carried out. On the other hand, a torvane test was carried out for non-treated soil. The strength of field soils treated with microorganism was 1/5 times lower than those of cement-treated soil but is 6 times higher than non-treated soil. The pH measured from microbially-treated soil was about 10, which is lower than that of cement-treated soil (pH = 11). Therefore, it is more eco-friendly than Portland cemented soils. The C-S-H hydrates were found in both cement- and microbially-treated soils through SEM-EDS analyses and cement hydrates were also found around soil particles through SEM analysis.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.1
• /
• pp.84-92
• /
• 2014

The purpose of study is to analyze mechanism with early high portland cement and hardening accelerator. As the result, it was concluded that hardening accelerator makes accelerates appearance of $Ca(OH)_2$ through experiment using TG-DTA when it hydrates with cement. On the result of compressive strength, as increasing the amount of hardening accelerator used, early compressive strength was improved. Also, as a result of hydration heat, hardening accelerator accelerates hydration of $C_3S$ that is cement's component. On the result of XRD's analyzation, hydration product for each age could be check and it was shown that as increasing the amount of hardening accelerator used, peak point of hydration product was recorded high. As the result of SEM, appearance of C-S-H was shown as the amount of $Ca(OH)_2$'s appearance and each age according to additive contents of hardening accelerator. Therefore hardening accelerator used on this study is effective on getting early compressive strength.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.4
• /
• pp.104-112
• /
• 2012

This study involves investigating the correlation between variation of internal structure and heating temperature of alkali-activated fire protection materials using fly ash. Dehydration and micro crack thermal expansion occur in cement hydrates of cementitious materials heated by fire. Internal structure difference due to both the dehydration of cement hydrates and pore solution causes and influences changes in the properties of materials. Also, this study is concerned with change in microstructure and dehydration of the alkali-activated fire protection materials at high temperatures. The testing methods of alkali-activated fire protection materials in high temperature properties are make use of TG-DSC and mercury intrusion porosimetry measurements. The study results show that the alkali-activated fire resistant finishing material composed of potassium hydroxide, sodium silicate and fly ash has the high temperature thermal stability. These thermal stability is caused by the ceramic binding capacity induced by alkali activation reaction.

• International conference on construction engineering and project management
• /
• 2009.05a
• /
• pp.1630-1636
• /
• 2009

Nine alkali-activated (AA) mortars were mixed and cured at water or air-dried conditions to explore the significance and limitation for the application of the combination of Ba and Ca ions as an alkali-activator. Ground granulated blast-furnace slag (GGBS) was used for source materials, and calcium hydroxide (Ca(OH)₂) and barium hydroxide (Ba(OH)₂) were employed as alkali activators. Test results clearly showed that the water curing condition was more effective than the air-dried curing condition for the formation of the denser calcium silicate hydrate (C-S-H) gels that had a higher molar Si/Ca ratio, resulting in a higher strength development. At the same time, the introduction of Ba(OH)₂ led to the formation of 2CaO·Al₂O₃·SiO₂·8H₂O (C₂ASH₈) hydrates with higher molar Si/Al and Ca/Al ratios. Based on the test results, it can be concluded that the developed cementless mortars have highly effective performance and high potential as an eco-friendly sustainable building material.

• Bulletin of the Korean Chemical Society
• /
• v.12 no.2
• /
• pp.214-219
• /
• 1991

To study the effect of solvents and counterions in Z-DNA crystal of d(5BrC-G-5BrC-G-5BrC-G), we performed the local energy analysis and then molecular dynamics simulations. Since counterions raise serious caging problems in crystal simulations, it is very important to search for the possible positions before simulations. For this purpose, the local energy analysis was done for the whole crystal volume. It is shown from our simulation that counterions along with water molecules play a bridging role to bind adjacent oligomers so as to form the crystal. In this crystal, each water molecule bound to Gua-N2H, either directly or indirectly, hydrates the adjacent anionic phosphate oxygen, and thus assists Gua to be in a syn position. From the simulation, the average root-mean-square deviation of allthe DNA heavy atom coordinates from the X-ray data is $0.99{\AA}$ . The bases are less deviated from the X-ray positions than the phosphates. The temperature factors from the simulation are consistent with those from the X-ray refinement, showing that the phosphates are more mobile than the bases.