• 한국세라믹학회지
• /
• 제51권5호
• /
• pp.459-465
• /
• 2014

In this study, Si-SiC composites were fabricated using a Si melt infiltration method using ${\beta}$-SiC/C composite powders synthesized by the carbothermal reduction of $SiO_2-C$ precursors made from a TEOS and a phenol resin. The purity of the synthesized SiC-C composite powders was higher than 99.9993 wt% and the average particle size varied from 4 to $6{\mu}m$ with increasing carbon contents of the $SiO_2-C$ precursors. It was found that the Si-SiC composites fabricated in this study consist of ${\beta}$-SiC and residual Si, without any trace of ${\alpha}$-SiC. The 3-point bending strengths of the fabricated Si-SiC composites were measured and found to be higher than 550 MPa, although the density of the fabricated Si-SiC composite was less than $2.9g/cm^3$. The bending strengths and the densities of the fabricated Si-SiC composites were found to decrease with increasing C/Si mole ratios in the SiC-C composite powders. The specific resistivities of the Si-SiC composites fabricated using the SiC-C composite powders were less than $0.018{\Omega}cm$. With increasing C content in the SiC-C composite powders used for the fabrication of Si-SiC composites, the specific resistivity of the Si-SiC composites was found to slightly increase from 0.0157 to $0.018{\Omega}cm$.

• 한국결정성장학회지
• /
• 제9권2호
• /
• pp.212-216
• /
• 1999

SiC(3C) 광다이오드는 p-형 Si 위에 tetramethylsilane (TMS)를 열분해아여 화학기상증착법으로 성장된 SiC(3C) 에피층을 성장하여 제작되었다. SiC(3C)의 전기적 특성은 홀 측정(Hall measurement) 및 전류-전압(I-V) 특성으로 조사되었다. SiC(3C) 에피층의 전도형은 n-형이었다. 저항성 접촉은 마스크 (shadow-mask)를 통해서 Al을 열증착하여 형성하였다. SiC(3C)광다이오드의 광학적 이득(photovoltaic detection)를 해석하기 위하여 SiC(3C) 에피층의 Spectral response (SR)를 전기적 변수(electrical parameter) 및 광다이오드의 기하학적 구조(geometric structure)를 고려하여 계산하였다. 적절히 선정된 변수들로부터 계산된 SR의 최대값은 550 nm에서 약 0.75이었고, 파장영역 400~600 nm 사이에서 청색 및 근자외선 광검지기로서 매우 유용하다.

• ALGAE
• /
• 제26권2호
• /
• pp.153-165
• /
• 2011

Species of the diatom genus Chaetoceros with special intercalary setae are uncommon. For this study, we collected Chaetoceros species from August 2008 to September 2009 in Korean coastal waters and examined the ultra structures of the Chaetoceros species C. coarctatus, C. compressus var. hirtisetus, C. contortus, C. diversus, and C. messanensis, using light and scanning electron microscopy. C. coarctatus, in the subgenus Phaeoceros, showed longer and stronger spines than those found in other species. C. coarctatus and C. diversus had special intercalary setae with spines in straight arrangements, whereas C. compressus var. hirtisetus, C. contortus, and C. messanensis had special intercalary setae with spines arranged in spirals. The setae of C. coarctatus had spines that were robust toward the tips and, overall, longer and stronger than were those of other species. C. coarctatus and C. diversus were straight, and C. compressus var. hirtisetus, C. contortus, and C. messanensis spiraled. C. messanensis had two types of special intercalary setae, both forked: 1 with spines in spirals and 1 lacking spines. We did not find spines on the anterior part of divergent point of the special intercalary setae of C. messanensis. Foramina shapes of these 5 Chaetoceros species varied as follows: very small or no foramina in C. coarctatus, relatively wide and slightly centrally constricted foramina in C. compressus var. hirtisetus and C. contortus, quite narrowly slitted or no foramina in C. diversus, and lanceolate or hexagonal foramina in C. messanensis. We found rimoportula in both intercalary and terminal valves of C. coarctatus, but C. compressus var. hirtisetus, C. contortus, C. diversus, and C. messanensis only had rimoportula in terminal valves. In addition, C. compressus var. hirtisetus and C. contortus were new to Korean coastal waters.

• 한국가축번식학회지
• /
• 제16권1호
• /
• pp.63-76
• /
• 1992

This study was carried out to investigate the appearance time of the second polar body for producing Gynogenesis or Triploid which could be obtained by arresting the second polar body by cold shock, and then blastoderm was used to measure fertility that revealed the nature of oogenesis, the effects of water temperature on fertility, hatchability, abnormality, viability and growth rate, and the water temperature and the breeding methods to prevent early death of larvae in Korean loach(Misgurnus anguillicaudatus) ; the results obtained in this study were summarized as follows. The second polar body was observed ont he surface of plasma disc close to micropyle within 10~40 min after fertilization at 29$^{\circ}C$. Artificial inseminatin had to be done immediately after the egg spawning because the spermatozoa of loach their mobility within 2 minutes when they were exposed to water. The amount of time needed to reach at blastoderm stage was 12 hours if fertilized eggs were incubated at 16$^{\circ}C$, 8 hours at 19$^{\circ}C$, 6 hours at 21$^{\circ}C$, 5 hours at 23$^{\circ}C$, 4 hours at 26$^{\circ}C$ and 3 hours 30 min at 29$^{\circ}C$ showing the shorter time for development of eggs at higher temperature. Fertilization rates in water temperatures of 19$^{\circ}C$, 21$^{\circ}C$, 23$^{\circ}C$, and 26$^{\circ}C$ were higher than those of water temperatures, 16$^{\circ}C$ and 29$^{\circ}C$. Water temperatures at 19$^{\circ}C$, 21$^{\circ}C$, and 23$^{\circ}C$ showed higher hatching rates that those of 16$^{\circ}C$, 26$^{\circ}C$, and 29$^{\circ}C$, while abnormal rates in 16$^{\circ}C$, 19$^{\circ}C$, 21$^{\circ}C$ and 23$^{\circ}C$ were lower than that of 26$^{\circ}C$ and 29$^{\circ}C$. Water temperatures at 16$^{\circ}C$, 19$^{\circ}C$, 21$^{\circ}C$, 23$^{\circ}C$ and 26$^{\circ}C$ respectively, were more different than 29$^{\circ}C$ in survival rates. The embryos were hatched at 72 hours after fertilization in 16$^{\circ}C$ water temperature, 48 hours in 19$^{\circ}C$, 40 hours in 21$^{\circ}C$, 32 hours in 23$^{\circ}C$, 25 hours in 26$^{\circ}C$, and 16 hours in 29$^{\circ}C$. Within three days after hatched out, the larvage grew 3mm in total length, the yolk granules were entirely consumed and the head and the trunk became thicker. Within 45 days after hatched out, the larva grew 25mm at 29$^{\circ}C$, 21mm at 26$^{\circ}C$, 16mm at 23$^{\circ}C$, 15mm at 21$^{\circ}C$, 12mm at 16$^{\circ}C$ in a 30 litreglass aquarium.

• 대한방사선치료학회지
• /
• 제31권1호
• /
• pp.57-65
• /
• 2019

목 적: 전자선 치료에서 저 용융점 납합금과 순수 납을 이용한 차폐 시 두께증가에 따른 블록 가장자리의 산란선 영향을 알아보고자 한다. 대상 및 방법: $10{\times}10cm^2$ 어플리케이터의 Insert Frame 절반을 차폐하도록 블록을 제작하였고, 두께는 각 재질당 3, 5, 10, 15, 20 (mm)로 하였다. 공통 조건을 에너지 6 MeV, 선량률 300 MU/Min, 갠트리 각도 0, 부여선량 100 MU으로 설정하였고, 블록의 위치와 측정점의 위치, 블록재질을 각각 달리하여 블록 두께증가에 따른 상대적인 산란비율을 평행평판형 전리함과 고체팬텀으로 측정하였다. 결 과: (측정 깊이 / 블록 위치 / 블록 재질)이 (표면 / 어플리케이터 / 순수 납)일 때 블록 두께가 3, 5, 10, 15, 20 (mm) 순으로 증가함에 따라 상대선량은 15.33 nC, 15.28 nC, 15.08 nC, 15.05 nC, 15.07 nC로 측정되었다. (표면 / 어플리케이터 / 합금 납)일 때 15.19 nC, 15.25 nC, 15.15 nC, 14.96 nC, 15.15 nC로 측정되었다. (표면 / 팬텀 위 / 순수 납)일 때 15.62 nC, 15.59 nC, 15.53 nC, 15.48 nC, 15.34 nC로 측정되었다. (표면 / 팬텀 위 / 합금 납)일 때 15.56 nC, 15.55 nC, 15.51 nC, 15.42 nC, 15.39 nC로 측정되었다. (심부 / 어플리케이터 / 순수 납)일 때 16.70 nC, 16.84 nC, 16.72 nC, 16.88 nC, 16.90 nC로 측정되었다. (심부 / 어플리케이터 / 합금 납)일 때 16.83 nC, 17.12 nC, 16.89 nC, 16.77 nC, 16.52 nC로 측정되었다. (심부 / 팬텀 위 / 순수 납)일 때 17.41 nC, 17.45 nC, 17.34 nC, 17.42 nC, 17.25 nC로 측정되었다. (심부 / 팬텀 위 / 합금 납)일 때 17.45 nC, 17.44 nC, 17.47 nC, 17.43 nC, 17.35 nC로 측정되었다. 결 론: 차폐블록을 이용하여 전자선 치료를 진행할 때 블록위치는 환자 체표면보다는 어플리케이터에 삽입하고 두께는 각 사용 에너지에 해당되는 최소 적정차폐두께로 제작해야 한다. 또한 블록 가장자리 경계선으로부터 떨어진 거리에 따라 변화하는 산란선의 영향을 충분히 고려하여 치료를 시행하는 것이 바람직하다고 사료된다.

• 한국균학회지
• /
• 제30권1호
• /
• pp.56-60
• /
• 2002

1998년 병든 화본과작물, 목초, 잔디 및 야생잡초의 잎점무늬와 마름병징으로부터 Curvularia spp. 16균주를 분리하였다. 이들 균주를 균학적 특징을 기초로 동정한 결과 C. cymbopogonis, C. inaequalis, C. intermedia, C. lunata, C. lunata var. aeria, C. ovoidea, C. pallescens C. senegalensis로 동정되었다. 이중에서 C. cymbopogonis, C. lunata var. aeria, C. ovoidea, C. senegalensis는 국내에서 처음 보고되는 미기록종들이다.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.859-860
• /
• 2006

TiC-$TiB_2$-SiC system was a ternary eutectic, whose eutectic composition was 34TiC-$22TiB_2$-44SiC (mol%). TiC-$TiB_2$-SiC ternary eutectic composite were synthesized by a floating zone method using TiC, $TiB_2$ and SiC powders as starting materials. The TiC-$TiB_2$-SiC eutectic composite showed a lamellar texture. TiC(022), $TiB_2(010)$ and SiC(111) of the eutectic composite were perpendicular to the growth direction. TiC-$TiB_2$-SiC ternary eutectic composite had specific relationship among the crystal planes: TiC[011]//$TiB_2[010]$//SiC[112], TiC(200)//$TiB_2$(001)//SiC(402) and $TiC(1\bar{1}1)$//$TiB_2(101)$//SiC(220).

• 대한기계학회논문집A
• /
• 제31권2호
• /
• pp.205-210
• /
• 2007

SiC/SiC composites and monolithic SiC materials have been fabricated by the melt infiltration process, through the creation of crystallized SiC phase by the chemical reaction of C and Si. The reinforcing material used in this system was a braided Hi-Nicalon SiC fiber with double interphases of BN and SiC. The microstructures and the mechanical properties of RS-SiC based materials were investigated through means of SEM, TEM, EDS and three point bending test. The matrix morphology of RS-SiS/SiC composites was greatly composed of the SiC phases that the chemical composition of Si and C is different. The TEM analysis showed that the crystallized SiC phases were finely distributed in the matrix region of RS-SiC/SiC composites. RS-SiC/SiC composites also represented a good flexural strength and a high density, accompanying a pseudo failure behavior.

• Composites Research
• /
• 제32권3호
• /
• pp.148-157
• /
• 2019

본 연구에서는 탄소섬유, 탄화규소섬유 그리고 하이브리드섬유를 강화재로 하여 TGCVI와 PIP 혼합 공정으로 $C_f/SiC$, $SiC_f/SiC$, $C_f-SiC_f/SiC$의 세라믹복합재를 제조하였다. 열충격싸이클시험, 3점 굴곡시험과 Oxy-Acetylene 토취 시험후에 그들의 기계적물성, 산화저항성과 내삭마성을 평가하였다. $C_f/SiC$복합재는 온도 증가에 따라서 기계적물성의 감소와 준 연성의 파단모드, 그리고 높은 삭마량을 보였다. $SiC_f/SiC$복합재는 $C_f/SiC$ 복합재에 비하여 강한 기계적물성, 낮은 삭마량을 그리고 취성의 파단모드를 나타냈다. 한편 하이브리드 복합재는 가장 우수한 기계적물성과 $SiC_f/SiC$보다는 연성의 파단모드 그리고 $C_f/SiC$ 보다 낮은 삭마량의 결과를 나타냈다. Oxy-Acetylene 토취 시험 중에 SiC매트릭스는 산화되어 $SiO_2$층을 형성하였으며, 특히 이 층은 $C_f-SiC_f/SiC$와 $SiC_f/SiC$ 복합재에서 섬유의 추가적인 삭마를 막는 역할을 하는 것으로 나타났다. 결론적으로 낮은 기공율을 갖는 하이브리드 복합재를 제조한다면, $C_f/SiC$의 산화로 인한 기계적물성의 감소와 $SiC_f/SiC$ 복합재의 취성 파단모드의 개선으로 고온 산화분위기에서 고온열구조재로의 적용이 높을 것으로 기대한다.

• Applied Biological Chemistry
• /
• 제27권4호
• /
• pp.278-284
• /
• 1984

복숭아씨기름 및 살구씨기름의 triglyceride 조성(組成)을 밝히기 위하여 시료유(試料油)로부터 TLC에 의하여 triglyceride를 분리하고, 이것을 HPLC에 의하여 PN 별(別)로 triglyceride를 분획(分劃)하여 분취(分取)하였다. 분취(分取)한 각분획(各劃分)을 GLC에 의하여 acyl 탄소수별(炭素數別)로 재분획(再分劃)하는 한편, 각획분(各劃分)의 지방산조성(脂肪酸組成)을 분석(分析)하였다. 이들 결과로부터 시료유(試料油)의 triglyceride조성(組成)을 산정(算定)하였는데, 산정(算定)할 수 있었던 복숭아씨기름의 triglyceride는 15종류였으며, 이중(中) 주요(主要) triglyceride는 다음과 같다. $(3{\times}C_{18:1},\;30.9%)$, $(2{\times}C_{18:1},\;C_{18:2},\;21.2%)$, $(C_{18:1},\;2{\times}C_{18:2},\;10.6%)$, $(3{\times}C_{18:2},\;3.8%)$, $(C_{18:0},\;2{\times}C_{18:1},\;1.8%)$, $(C_{16:0},\;C_{18:1},\;C_{18:2},\;1.5%)$, $(C_{18:0},\;C_{18:1},\;C_{18:2},\;1.1%)$ 등이다. 또한 살구씨기름의 정우는 산정(算定)할 수 있었던 triglyceride 는 13종류였고, 주요(主要) triglyceride는 다음과 같다. $(3{\times}C_{18:1},\;39.5%)$, $(2{\times}C_{18:1},\;C_{18:2},\;24.5%)$, $(C_{18:1},\;2{\times}C_{18:2},\;14.2%)$, $(3{\times}C_{18:2},\;2.0%)$ 등이다.