• Journal of Powder Materials
• /
• v.28 no.2
• /
• pp.134-142
• /
• 2021

In this study, AlSi10Mg powders with average diameters of 44 ㎛ are additively manufactured into bulk samples using a selective laser melting (SLM) process. Post-heat treatment to reduce residual stress in the as-synthesized sample is performed at different temperatures. From the results of a tensile test, as the heat-treatment temperature increases from 270 to 320℃, strength decreases while elongation significantly increases up to 13% at 320℃. The microstructures and tensile properties of the two heat-treated samples at 290 and 320℃, respectively, are characterized and compared to those of the as-synthesized samples. Interestingly, the Si-rich phases that network in the as-synthesized state are discontinuously separated, and the size of the particle-shaped Si phases becomes large and spherical as the heat-treatment temperature increases. Due to these morphological changes of Si-rich phases, the reduction in tensile strengths and increase in elongations, respectively, can be obtained by the post-heat treatment process. These results provide fundamental information for the practical applications of AlSi10Mg parts fabricated by SLM.

• Progress in Superconductivity and Cryogenics
• /
• v.11 no.2
• /
• pp.7-10
• /
• 2009

Effects of $BaCO_3$ purity on the superconducting properties of top seeded melt growth (TSMG) processed $Y_{1+x}Ba_2Cu_3O_{7-y}$ (Y1+x, x=0.1 and 0.2) superconductors were investigated. $YBa_2Cu_3O_{7-y}$ (Y123) powder prepared using $BaCO_3$ with 99.75% purity and commercially available Y123 powder of 99.9% were used for the fabrication of single Y123 grain superconductors. $T_c$ values of the Y1+x samples prepared using low purity Y123 powder were slightly lower than those of the samples prepared using a high purity powder. In addition to the lower $T_c$, an anomalous peak effect in the intermediate magnetic fields was observed in Y1+x samples prepared using the low purity $BaCO_3$ powder. The slight decrease in $T_c$ and the anomalous peak effect are ascribed to the possible incorporation of a Y123 phase with impurity elements such as strontium and calcium included in the $BaCO_3$powder of 99.7%. The result suggests that the low purity $BaCO_3$ powder of a low price can be used as a raw power for the fabrication of single grain YBCO bulk superconductors.

• The Sea:JOURNAL OF THE KOREAN SOCIETY OF OCEANOGRAPHY
• /
• v.5 no.4
• /
• pp.320-334
• /
• 2000

Deep-sea surface sediment were analyzed for their geotechnical properties, and the sediment samples were collected with a multiple-corer from 31 stations along the track line (131$^{\circ}$30'W, 5-12$^{\circ}$N) in the northeast equatorial Paciflc. Most of the sediments from the northern part (8-12$^{\circ}$N) showed typical properties of siliceous sediments, whereas the southern part (5-6$^{\circ}$N) showed calcareous characteristics due to high biogenic carbonate productivity in the surface waters, where its water depth was shallower than the carbonate compensation depth (CCD: 4,400 m). Geotechnical properties changed sharply at the boundary of 7$^{\circ}$N. Calcareous sediments from the southern part had low water contents, low porosity, low shear strength, high bulk density and high specific grain density, whereas siliceous sediments from the northern part attained high water content, high porosity, high shear strength, low bulk density and low specific grain density. Higher sediment activities were observed in the northern sediment samples than the southern sediment samples. The core samples of the northern sediments were divided into a semi-liquid upper layer and a consolidated lower layer with a boundary at 5-8 cm. These sediment samples showed a rapid increasing pattern along the downcore in original shear strength when an opposite trend was observed in the southern samples. The results showed that sediment variabilities in geotechnical properties between the northern and southern parts such as productivities of surface water, grain solubility due to water depth variation, sedimentation rate, erosion and redistribution of sediment, and combined sedimentary processes were distinctly different along the latitude.

• Smart Structures and Systems
• /
• v.12 no.1
• /
• pp.55-71
• /
• 2013

Structural health monitoring (SHM) is vital for detecting the onset of damage and for preventing catastrophic failure of civil infrastructure systems. In particular, piezoelectric transducers have the ability to excite and actively interrogate structures (e.g., using surface waves) while measuring their response for sensing and damage detection. In fact, piezoelectric transducers such as lead zirconate titanate (PZT) and poly(vinylidene fluoride) (PVDF) have been used for various laboratory/field tests and possess significant advantages as compared to visual inspection and vibration-based methods, to name a few. However, PZTs are inherently brittle, and PVDF films do not possess high piezoelectricity, thereby limiting each of these devices to certain specific applications. The objective of this study is to design, characterize, and validate piezoelectric nanocomposites consisting of zinc oxide (ZnO) nanoparticles assembled in a PVDF copolymer matrix for sensing and SHM applications. These films provide greater mechanical flexibility as compared to PZTs, yet possess enhanced piezoelectricity as compared to pristine PVDF copolymers. This study started with spin coating dispersed ZnO- and PVDF-TrFE-based solutions to fabricate the piezoelectric nanocomposites. The concentration of ZnO nanoparticles was varied from 0 to 20 wt.% (in 5 % increments) to determine their influence on bulk film piezoelectricity. Second, their electric polarization responses were obtained for quantifying thin film remnant polarization, which is directly correlated to piezoelectricity. Based on these results, the films were poled (at 50 $MV-m^{-1}$) to permanently align their electrical domains and to enhance their bulk film piezoelectricity. Then, a series of hammer impact tests were conducted, and the voltage generated by poled ZnO-based thin films was compared to commercially poled PVDF copolymer thin films. The hammer impact tests showed comparable results between the prototype and commercial samples, and increasing ZnO content provided enhanced piezoelectric performance. Lastly, the films were further validated for sensing using different energy levels of hammer impact, different distances between the impact locations and the film electrodes, and cantilever free vibration testing for dynamic strain sensing.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.11
• /
• pp.941-948
• /
• 2009

The present study aims at the examination of the effects of 1 mol% NiO addition on the reaction, microstructure development, resultant electrical properties, and especially the bulk trap and interface state levels of $ZnO-Bi_2O_3-Sb_2O_3$ (Sb/Bi=0.5, 1.0, and 2.0) systems (ZBS). The samples were prepared by conventional ceramic process, and characterized by density, XRD, SEM, I-V, impedance and modulus spectroscopy (IS & MS) measurement. The sintering and electrical properties of Ni-doped ZBS (ZBSN) systems were controlled by Sb/Bi ratio. Pyrochlore ($Zn_2Bi_3Sb_3O_{14}$) was decomposed more than $100^{\circ}C$ lowered in ZBS (Sb/Bi=1.0) by Ni doping. The reproduction of pyrochlore was suppressed by the addition of Ni in ZBS. Between two polymorphs of $Zn_7Sb_2O_{12}$ spinel ($\alpha$ and $\beta$), microstructure of ZBSN (Sb/Bi=0.5) composed of a-spinel was more homogeneous than $Sb/Bi{\geq}1.0$ composed of $\beta$-spinel phase. In ZBSN, the varistor characteristics were not improved drastically (non-linear coefficient $\alpha\;=\;6{\sim}11$) and independent on microstructure according to Sb/Bi ratio. Doping of Ni to ZBS seemed to form ${V_0}^{\cdot}$ (0.33 eV) as dominant bulk defect. From IS & MS, especially the grain boundaries of Sb/Bi=0.5 systems were divided into two types, i.e. sensitive to oxygen and thus electrically active one and electrically inactive intergranular one with temperature.

• Asian Journal of Atmospheric Environment
• /
• v.4 no.3
• /
• pp.189-197
• /
• 2010

An orchestrated attempt was made to analyze samples of bulk and individual particulate matters (PM) collected at the Gosan ground-based station on the west coast of Jeju, Korea. A two-stage filter pack sampler was operated to collect particles in both large (> $1.2\;{\mu}m$) and small size fractions (< $1.2\;{\mu}m$) between the Asian dust (hereafter called "AD") storm event and non-Asian dust period. Elemental components in bulk and individual particles were determined by PIXE and synchrotron XRF analysis systems, respectively. To assess the transport pathways of air parcels and to determine the spatial distribution of PM, the backward trajectories of the Meteorological Data Explorer (Center for Global Environmental Research, 2010) and the NOAA's HYSPLIT dispersion-trajectory models were applied. In line with general expectations, Si and other crustal elements in large size particles showed considerably higher mass loading on AD days in comparison with non-AD days. Computation of the crustal enrichment factors [(Z/Si)$_{particle}$/(Z/Si)$_{desert}$ sand] of elements in large size particles (> $1.2\;{\mu}m$) allowed us to estimate the source profile and chemical aging of AD particles as well as to classify the soil-origin elements. On the basis of a single particle analysis, individual AD particles are classified into three distinct groups (neutralized mineral particles, S-rich mineral particles, and imperfectly neutralized particles).

• Journal of Powder Materials
• /
• v.22 no.3
• /
• pp.163-168
• /
• 2015

Ti alloys are extensively used in high-technology application because of their strength, oxidation resistance at high temperature. However, Ti alloys tend to be classified very difficult to cut material. In this paper, The powder synthesis, spark plasma sintering (SPS), bulk material properties such as electrical conductivity and thermal conductivity are systematically examined on $Ti_2AlN$ and $Ti_2AlC$ materials having most light-weight and oxidation resistance among the MAX phases. The bulk samples mainly consisted of $Ti_2AlN$ and $Ti_2AlC$ materials with density close to theoretical value were synthesized by a SPS method. Machining characteristics such as machining time, surface quality are analyzed with measurement of voltage and current waveform according to machining condition of micro-electrical discharge machining with micro-channel shape.

• Journal of Korea Foundry Society
• /
• v.26 no.2
• /
• pp.77-84
• /
• 2006

The effect of alloy composition on the glass forming ability (GFA) of the Ca-rich Ca-Mg-Zn alloys has been investigated in $Ca_{65}Mg_{5+x}Zn_{30-x}$ and $Ca_{55+x}Mg_{15}Zn_{30-x}$ (x=0, 5, 10, 15, 20) alloys. In a wide composition range of 15-25% Zn and 10-20% Mg bulk metallic glass (BMG) samples with the diameter larger than 6 mm are fabricated by conventional copper mold casting method in air atmosphere. Among the alloys investigated, the $Ca_{65}Mg_{15}Zn_{20}$ alloy exhibits the highest GFA enabling to form BMG sample with the diameter of at least 15 mm. The crystalline phase formed during solidification of $Ca_{65}Mg_{15}Zn_{20}$ ($D_{max}=15\;mm$) could be identified as a mixture of $Ca_3Zn$ and $CaMg_2$ cause by the redistribution of the constituent elements on long-range scale. The compressive fracture strength and fracture elongation of the $Ca_{65}Mg_{15}Zn_{20}$ BMG are 602 MPa and 2.08% respectively. The ${\sigma}$ parameter which has been recently proposed for evaluating GFA exhibits better correlation with GFA of Ca-Mg-Zn alloys than other parameters suggested so far such as ${\Delta}T_x$, $T_{rg}$, K, ${\gamma}$, and ${\Delta}T^*$ parameters.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.34 no.9
• /
• pp.1235-1240
• /
• 2010

Wire-woven Bulk Kagome (WBK) is fabricated by assembling helically formed wires in six directions. To date, WBK samples have been assembled manually. For industrial application, the assembly process must be automated. Furthermore, if WBK is to be fabricated using flexible wires that cannot maintain their helical shape during fabrication, a specialized automatic machine, i.e., a loom needs to be developed. In this work, we designed and constructed a loom for fabricating WBKs using flexible wires. This loom is operated by one rotation of the upper plate, two translations of the insertion device, and insertion of wires. So-called "comb devices" are placed between multiple layers of Kagome nets to prevent the wires that are already in place from getting entangled with those that are being inserted. This loom can be also used to fabricate semi-WBKs composed of helically formed wires and rigid straight wires.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.57 no.7
• /
• pp.1208-1212
• /
• 2008

In this study, both structural and microwave dielectric properties of the $Ba_5B_4O_{15}$ (B=Ta, Nb) cation-deficient perovskite ceramics with sintering temperature were investigated. All samples of the $Ba_5B_4O_{15}$ (B=Ta, Nb) ceramics were prepared by the conventional mixed oxide method and sintered at $1325^{\circ}C{\sim}1575^{\circ}C$. The bulk density and dielectric constant of the $Ba_5Ta_4O_{15}$ ceramics were increased continuously with increasing of sintering temperature. The quality factor of the $Ba_5Ta_4O_{15}$ ceramics was increased in as the sintering temperature increases from $1375^{\circ}C{\sim}1475^{\circ}C$ but decreased at the temperatures above $1475^{\circ}C$. And the bulk density, dielectric constant and quality factor of the $Ba_5Nb_4O_{15}$ ceramics were increased in as the sintering temperature increases from $1325^{\circ}CP{\sim}1400^{\circ}C$ but decreased at the temperatures above $1400^{\circ}C$. In the case of the $Ba_5Ta_4O_{15}$ sintered at $1475^{\circ}C$ and $Ba_5Nb_4O_{15}$ ceramics sintered at $1400^{\circ}C$, the dielectric constant, quality factor, and temperature coefficient of the resonant frequency (TCRF) were 25.15, 53,105 GHz, -3.06 $ppm/^{\circ}C$ and 39.55, 28,052 GHz, +5.7 ppm/$^{\circ}C$, respectively.