• Transactions of Materials Processing
• /
• v.21 no.8
• /
• pp.506-511
• /
• 2012

Aluminum brazing normally requires a careful control of temperature due to the small interval between brazing and melting temperatures for base materials. Unsuitable processing conditions, including brazing temperature outside admissible range, gap between brazed materials or inadequate flux feeding, can lead to joining defects. In this study, A357 was used as a filler metal for the brazing of pure aluminum base materials and brazed at temperatures in the semi-solid state. Interface microstructures with base materials were observed using optical metallography(OM) and scanning electron microcopy(SEM) with energy dispersive spectroscopy(EDS), and compared to conventional aluminum brazing.

• Journal of Welding and Joining
• /
• v.33 no.5
• /
• pp.1-8
• /
• 2015

Aluminium and its alloys are widely used in brazing various components in automotive industries due to their properties like lightweight, excellent ductility, malleability and formability, high oxidation and corrosion resistance, and high electrical and thermal conductivity. However, high machinability and strength of aluminium alloys are a serious concern during casting operations. The generation of porosity caused by dissolved gases and modifiers affects seriously the strength and quality of cast product. Brazing of Al and its alloys requires careful monitoring of temperature since theses alloys are brazed at around the melting temperature in most of the aluminium alloys. Therefore, the development of low temperature brazing filler alloys as well as superior strength Al alloys for various engineering applications is always in demand. In various heat exchangers and automotive applications, poor strength of Al alloys is due to the inherent porosities and casting defects. The unstable mechanical properties is therefore needed to be controlled by adding various additive elements in the aluminium and its alloys, by a change in the heat treatment procedure or by modifying the microstructure. In this regard, this article reports the effect of various elements added in aluminium alloys to improve microstructure, brazeability, machinability, castability as well as to stabilize the mechanical properties.

• Journal of Powder Materials
• /
• v.30 no.4
• /
• pp.339-345
• /
• 2023

This study investigates the melting point and brazing properties of the aluminum (Al)-copper (Cu)-silicon (Si)-tin (Sn) alloy fabricated for low-temperature brazing based on the alloy design. Specifically, the Al-20Cu-10Si-Sn alloy is examined and confirmed to possess a melting point of approximately 520℃. Analysis of the melting point of the alloy based on composition reveals that the melting temperature tends to decrease with increasing Cu and Si content, along with a corresponding decrease as the Sn content rises. This study verifies that the Al-20Cu-10Si-5Sn alloy exhibits high liquidity and favorable mechanical properties for brazing through the joint gap filling test and Vickers hardness measurements. Additionally, a powder fabricated using the Al-20Cu-10Si-5Sn alloy demonstrates a melting point of around 515℃ following melting point analysis. Consequently, it is deemed highly suitable for use as a low-temperature Al brazing material.

• Journal of Welding and Joining
• /
• v.17 no.3
• /
• pp.79-89
• /
• 1999

The study was carried out to examine in more detail metallurgical and mechanical properties of brazed joints of diamond cutting wheel. In this work, shank(mild steel) and sintered bronze-base tips were brazed with three different filler materials(W-40, BAgl and BAg3S). The machine used in this work was a high frequency induction brazing equipment. The joint thickness, porosities and microstructure of brazed joints with brazing variables(brazing temperature, holding time) were evaluated with OLM, SEM, EDS and XRD. Bending(torque) test was also performed to evaluate strength of brazed joints. Further wetting test was performed in a vacuum furnace in order to evaluate the wettability of filler metals on base metals9shank and tips). The brazing temperature had a strong influence on the joint strength and the optimum brazing temperature range was about $700~850^{\circ}C$ for the bronze/steel combinations. The strength of the brazed joint was found to be influenced by the three factors : degree of reaction region, porosity content, joint thickness. The reaction region was formed in the bronze-base tip adjacent to the joint. The reaction region resulted in a bad influence on the strength due to the formation of Cu5.6Sn, CuZn4, $\beta(CuZn)$ and CdAg, etc. Porosities increased as brazing variables(brazing temperature, holding time) increased, and the brazed joints with porosities of less than about 3-5% had an optimum strength for the bronze-base tip.

• Journal of Welding and Joining
• /
• v.30 no.6
• /
• pp.15-20
• /
• 2012

Brazing technology has been widely used among bonding technologies because it enables to bond various metals, even ceramics, dissimilar metals, and give higher bonding strength, cost down, automation, etc. However, there are many parameters to achieve optimal brazing joint such as brazing alloys, brazing atmospheres, designs and brazing methods, etc. The brazing parameters affect seriously on the characteristic of final brazing products. Stainless steel is broadly used in high temperature applications, chemical industry, heat exchangers, muffler of vehicles, and so on. Accordingly, in this article, brazing alloys, forms of brazing alloys, brazing methods and atmospheres for stainless steel were described.

• Journal of the Korean Ceramic Society
• /
• v.33 no.12
• /
• pp.1421-1425
• /
• 1996

Sintered Si3N4 and Inconel composed of Ni(58-63%) Cr(21-25%) Al(1-17%) Mn(<1%) fe(balance) were pressurelessly joined by using Ag-Cu-Ti brazing filler metal at 950℃ and 1200℃ under N2 gas atmosphere of 1atm and their interfacial structures were investigated. In case that the reaction temperature was low as 950℃ its interfacial structure was "Inconel metal/Ti-rich phase layer/brazing filler metal layer/Si3N4 " Ti used as reactive metal existed in between inconel steel and brazing metal and moved to the interface of between brazing filler metal nd Si3N4 according as reaction temperature increased up to 1200℃. The interfacial structure of inconel steel-Si3N4 reacted at 1200℃ was ' inconel metal/Ni-rich phase layer containing of Fe. Cr and Si/Cu-rich phase layer containing of Mn and Si/Si3N4 " Cr Mn, Ni and Fe diffused to the interface of between brazing filler metal and Si3N4 and reacted with Si3N4 The most reactive components of ingredients of inconel metal were Cr and Mn. On the other hand Ti added as reactive components to Ag-Cu eutectic segregated into Ni-rich phase layer,.

• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.96-105
• /
• 1995

An advantage offered by brazing over fusion welding is that strong joints may be produced at relatively low heat input. To minimize the thermal effects and maintain the desired dimension of assemblies. the CO$_{2}$ laser beam can be applied to the brazed joint of pin and plate as a micro heat source. This paper presents a analysis model of the laser brazing process considering the laser beam mode and heat flow in brazed parts by using the finite element method. The simulation results were compared with the experimental results obtained from the infrared temperature sensing system. Based on these results, the proper process parameters were investigated to get a good joining quality. The influence of the beam mode change was examined with respect to the temperature distribution and joint quality.

• Journal of Welding and Joining
• /
• v.9 no.4
• /
• pp.17-27
• /
• 1991

The direct brazing technology which could be used for the simplification of brazing process and the improvement of brazed joint quality was studied with $Al_2O_3$ and stainless steels. The brazing of $Al_2O_3$ to STS304 or STS430 was performed under different brazing conditions such as brazing filler metal, temperature, heating rate and brazing time. Microstructural observation and chemical analysis be SEM/EPAM were carried out to verify the quality of brazed joints. 4-point bending strength of brazed joints was also measured to find the optimal brazing conditions. The results showed that, in brazing of $Al_2O_3$, the mixed oxide layer resulted from the reaction between Ti in filler metal and oxide layer on the material surface to be brazed was found to be bery important for the joint quality. The width of oxide layer varied with the brazing conditions such as brazing time, heating rate and chemical composition of filler metals. The strength of brazed joints was more affected by the type of materials and their thermal properties than by brazing heat cycle.

• Journal of Welding and Joining
• /
• v.29 no.6
• /
• pp.40-44
• /
• 2011

Brazing of a stainless steel was described in this article. Brazing is a joining technology without melting a substrate and joining temperature is higher than $450^{\circ}C$. Brazing can be broadly applicable across industries. In particular, brazing of stainless steel is widely used in aircraft parts, car engines, heat exchangers, etc. due to its excellent strength, corrosion resistance and other suitable characteristics. Characteristics of the stainless steel depend on their classification like austenitic, ferritic and martensitic stainless steels. In addition, there are many processes in brazing and various parameters such as brazing heat source, filler metals, joint design, etc. Therefore, it is necessary to know basic knowledge about brazing to achieve good brazing joint. Accordingly, properties of stainless steel and design of brazing joint and related process were described in this article.

• Journal of the Korean Ceramic Society
• /
• v.56 no.4
• /
• pp.394-398
• /
• 2019

In this paper, the joining characteristics of GDC-LSM ceramics with Crofer 22 APU metal alloys was investigated at different brazing temperatures and holding times by reactive air brazing. Brazing was performed using Ag-10 wt% CuO filler, at three different temperatures (1000, 1050, and 1100℃ for 30 minutes) as well as for three different holding times (10, 30, and 60 minutes at 1050℃). The interfacial microstructures were examined by scanning electron microscopy and the joining strengths were assessed by measuring shear strengths at room temperature. The results show that with increasing brazing temperature and holding time, joint microstructure changed obviously and shear strength was decreased. Shear strength varied from a maximum of 100±6 MPa to a minimum of 18±5 MPa, depending on the brazing conditions. These changes were attributed to an increase in the thickness of the oxide layer at the filler/metal alloy interface.