• 한국재료학회지
• /
• 제24권6호
• /
• pp.305-309
• /
• 2014

When sunlight irradiates a boron-doped p-type solar cell, the formation of BsO2i decreases the power-conversion efficiency in a phenomenon named light-induced degradation (LID). In this study, we used boron-doped p-type Cz-Si solar cells to monitor this degradation process in relation to irradiation wavelength, intensity and duration of the light source, and investigated the reliability of the LID effects, as well. When halogen light irradiated a substrate, the LID rate increased more rapidly than for irradiation with xenon light. For different intensities of halogen light (e.g., 1 SUN and 0.1 SUN), a lower-limit value of LID showed a similar trend in each case; however, the rate reached at the intensity of 0.1 SUN was three times slower than that at 1 SUN. Open-circuit voltage increased with increasing duration of irradiation because the defect-formation rate of LID was slow. Therefore, we suppose that sufficient time is needed to increase LID defects. After a recovery process to restore the initial value, the lower-limit open-circuit voltage exhibited during the re-degradation process showed a trend similar to that in the first degradation process. We suggest that the proportion of the LID in boron-doped p-type Cz-Si solar cells has high correlation with the normalized defect concentrations (NDC) of BsO2i. This can be calculated using the extracted minority-carrier diffusion-length with internal quantum efficiency (IQE) analysis.

• 신재생에너지
• /
• 제8권1호
• /
• pp.24-34
• /
• 2012

The main issue of boron doped p-type czochralski-grown silicon solar cells is the degradation when they are exposed to light or minority carriers injection. This is due to the meta-stable defect such as boron-oxygen in the Cz-Si material. Although a clear explanation is still researching, recent investigations have revealed that the Cz-Si defect is related with the boron and the oxygen concentration. They also revealed how these defects act a recombination centers in solar cells using density function theory (DFT) calculation. This paper reviews the physical understanding and gives an overview of the degradation models. Therefore, various methods for avoiding the light-induced degradation in Cz-Si solar cells are compared in this paper.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.985-988
• /
• 2004

The carrier lifetime of boron doped Cz silicon samples after light induced degradation could be improved by optimized rapid thermal processing (RTP). The important five different parameters varied in order to investigate which parameter is important for the stable lifetime after light induced degradation, $\tau_d$. The Plateau temperature and the Plateau time influenced on the lifetime after light induced degradation. Especially, the Plateau temperature showed a strong influence on the stable lifetime. The optimal plateau temperature is approximately $900^{\circ}C$ t for a plateau time of 120 s. The stable lifetime increased from $15\mu}s$ to $25.5{\mu}s$. The normalized defect concentration, $N_t^*$, decreased from $0.06{\mu}s^{-1}$ to $0.037{\mu}s^{-1}$ by RTP-process.

• 한국태양에너지학회 논문집
• /
• 제30권6호
• /
• pp.16-21
• /
• 2010

It is well-known that Boron-doped Cz Si solar cells suffer light-induced degradation due to boron-oxygen defect which is responsible of a reduction in lifetime and hence efficiency. In this paper, we assume that PV solar cell has been connected with variable load to account the real operating condition and it shows different light-induced degradation of Si solar cell. To evaluate the effect of light-induced degradation for solar cell with various load, Single crystalline solar cells are connected with open and short circuits during light exposure. Isc-Voc curve evaluate light induced degradation of solar cells and the reason is explained as a change for serial resistance. From the results, Electrical characteristics of solar cells show better performance under short circuit conditions, after light exposure.