• 소성∙가공
• /
• 제21권8호
• /
• pp.506-511
• /
• 2012

Aluminum brazing normally requires a careful control of temperature due to the small interval between brazing and melting temperatures for base materials. Unsuitable processing conditions, including brazing temperature outside admissible range, gap between brazed materials or inadequate flux feeding, can lead to joining defects. In this study, A357 was used as a filler metal for the brazing of pure aluminum base materials and brazed at temperatures in the semi-solid state. Interface microstructures with base materials were observed using optical metallography(OM) and scanning electron microcopy(SEM) with energy dispersive spectroscopy(EDS), and compared to conventional aluminum brazing.

• 한국표면공학회지
• /
• 제26권2호
• /
• pp.71-81
• /
• 1993

Thed effects of Ar or Oxygen RF plasma treatment on the adhesion behavior of Cr films to polyimide sub-strates have been investigated by using SEM, XRD, AES, and $90^{\circ}$peel test. By applying RF plasma treatment of the polyimide surface prior to metal deposition, the peel adhesion strength of Cu/Cr films sputtered onto the fully cured BPDA-PDA polyimide was highly increased from about 3g/mm to 90 ~ 100g/mm. Improved peel adhesion strength of Cr/polyimide interfaces due to RF plasma treatment was attributed to the contributions from surface cleaning, Cr-polyimide bonding at the interface, and force required for plastic deformation of the film. While the surface topology change of the polyimide caused by RF plasma treatment makes a little contri-bution to the improved adhesion.

• 한국구조물진단유지관리공학회 논문집
• /
• 제1권1호
• /
• pp.89-96
• /
• 1997

The paper presents the results of experimental studies on two strengthening methods for reinforced concrete (RC) slabs. Bending tests on RC slabs have been carried out to investigate the influence of the increased thickness and externally bonded carbon fiber sheets. The interfaces of new and old concrete of increased thickness specimens have been chipped and treated with bonding agent. The conclusions have been reached as followings. (1) The behavior of specimens with chipped interface is good enough to calculate flexural strength of RC slabs for increased depth. (2) The flexural stiffness of increased depth specimen is severely increased and the deformation of RC slabs is controled. (3) The specimens with externally bonded carbon fiber sheets can be assumed to behave monolithically.

• 산업공학
• /
• 제20권2호
• /
• pp.121-132
• /
• 2007

The facility layout problem (FLP) involves the positioning of facilities within a given workplace in order to minimize the material flow distance between facilities. In this paper, we focus on the FLP in which the each facility has a rectangular shape and an input and output points. We develop a heuristic algorithm in which the facilities are arranged according to the layout algorithm using center of gravity and then simulated annealing algorithm is applied to improve the solution. A comparison of the computational results with exiting algorithms shows that the proposed algorithm provides better solutions in reasonable range of computational time.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.91-92
• /
• 2021

In the present work, we simulated and explained the bonding of three alkanethiols - hexanethiol (HT), decanethiol (DT), and 11-mercaptoundecanoic acid (MDA) - with Fe(110) surface and Fe2 clusters using Density Functional Theory (DFT) to probe the corrosion inhibition mechanisms. The interaction energies computed from periodic DFT calculations successfully predicted the experimental inhibition performance. We have found strong covalent bond formation between S(thiol) and Fe-atoms in both approaches, further confirmed by the projected density of states and electron density difference. Besides, natural bond orbital (NBO) charge distribution showed that DT had stronger electron-donation and back-donation synergic interactions with Fe-atoms.

• 한국진공학회지
• /
• 제8권1호
• /
• pp.20-25
• /
• 1999

여러 가지 방법의 plasma 표면 처리와 산화 공정이 $SiO_2-Si$(100) 계면에 미치는 물리적 영향을 angle resolved uv-photoelectron spectroscopy(ARUPS)를 이용하여 연구하였다. 표면은 ex situ 방법과 함께 in situ 수소 플라즈마를 이용하여 처리되어 졌으며, 이것은 고진공 고온 열 처리 방법과 비교되어졌다. ARUPS 빛띠 상에 나타난 산화물 가전자 띠에 대한 특징적인 peak 위치는 표면 처리 및 산화 공정 방법에 따라 이동하였다. 이러한 peak의 이동은 Si에서의 띠휨에 의한 것으로 분석되어졌다. 또한 peak 이동의 원인으로 Si-SiO2 계면에 형성된 결점과 표면 처리 공정에 따라 달라지는 표면 거칠기 등을 고려할 수 있었다. 여러 공정에 대한 ARUPS 결과를 비교함으로써 $Si--SiO_2$(계면 결합이 표면 처리 및 산화 방법에 깊이 관련되어 있음을 결론지을 수 있었다. 산소 plasma 공정은 가장 작은 band bending을 보여주었다.

• Geomechanics and Engineering
• /
• 제36권2호
• /
• pp.145-156
• /
• 2024

The mechanical properties of the concrete-frozen soil interface play a significant role in the stability and service performance of construction projects in cold regions. Current research mainly focuses on the precast concrete-frozen soil interface, with limited consideration for the more realistic cast-in-place concrete-frozen soil interface. The two construction methods result in completely different contact surface morphologies and exhibit significant differences in mechanical properties. Therefore, this study selects silty clay as the research object and conducts direct shear tests on the concrete-frozen soil interface under conditions of initial water content ranging from 12% to 24%, normal stress from 50 kPa to 300 kPa, and freezing temperature of -3℃. The results indicate that (1) both interface shear stress-displacement curves can be divided into three stages: rapid growth of shear stress, softening of shear stress after peak, and residual stability; (2) the peak strength of both interfaces increases initially and then decreases with an increase in water content, while residual strength is relatively less affected by water content; (3) peak strength and residual strength are linearly positively correlated with normal stress, and the strength of ice bonding is less affected by normal stress; (4) the mechanical properties of the cast-in-place concrete-frozen soil interface are significantly better than those of the precast concrete-frozen soil interface. However, when the water content is high, the former's mechanical performance deteriorates much more than the latter, leading to severe strength loss. Therefore, in practical engineering, cast-in-place concrete construction is preferred in cases of higher negative temperatures and lower water content, while precast concrete construction is considered in cases of lower negative temperatures and higher water content. This study provides reference for the construction of frozen soil-structure interface in cold regions and basic data support for improving the stability and service performance of cold region engineering.

• 한국산학기술학회논문지
• /
• 제16권12호
• /
• pp.8679-8683
• /
• 2015

세라믹은 고온에서 뛰어난 내마모성, 내부식성을 가지기 때문에 산업적 응용에 있어서 널리 사용된다. 세라믹은 금속과 비교해서 고온에서 더 큰 강도를 가지고 있고, 더 낮은 열전도도 및 열팽창 계수를 가진다. 그러나, 세라믹이 가진 취성의 성질은 전기전자산업과 고온에서의 구조적 적용에의 넓은 적용을 제한한다. Ti 활성금속과 STS304를 IBAD 기술을 이용해서 동시에 증착시켜 STS304 스테인레스강에 $Al_2O_3$(알루미나)의 브레이징 접합강도에 어떤 영향을 미치는지 알아보았으며, 시험편들은 Ti 타겟과 Ti+ STS304 타겟 두 종류를 이용하여 두께를 변화시켜가며 증착하였다. 브레이징 접합을 위한 삽입금속으로는 일반적으로 사용되는 Ag-Cu 공정조성의 합금이 사용되었다. 브레이징 접합품의 강도는 Ag-Cu 삽입금속과 알루미나 사이의 반응층의 두께와 반응 생성물 조직에 의해 결정되며, 본 실험에서는 계면 반응의 메커니즘을 보다 구체화하고 계면 반응에 의한 경사기능성의 접합계면을 더욱 향상시키는 결과를 얻고자 한다.

• 대한치과보철학회지
• /
• 제27권1호
• /
• pp.143-179
• /
• 1989

To observe the bonding behavior of palladium-based alloys to porcelain; 1. Pd-Co binary alloy with the higher cobalt content, 2. Pd-Co binary alloy with the lower cobalt content, 3. Pd-Ag-Sn ternary alloy, 4. Pd-Ag binary alloy, 5. Pd-Cu-Au ternary alloy and 6. Pd-Cu binary alloy were made as 6 groups of experimental alloys. Each group of alloy was divided into 4 sub-groups such as one sub-group that was not degassed and three sub-groups that degassed for 5 minutes, 10 minutes and 15 minutes. On each specimen, weight changes after degassing, morphological changes of oxide layer by changing the degassing time, compositional changes at metal-ceramic interface and bond strength of metal-ceramic measured with planar shear test were observed and compared. The results of the present study allow the following conclusions to be drawn: 1. The alloy showing the greatest bond strength was Pd-Cu alloy without gold and bond strength was decreased by alloying gold to them. 2. Although Pd-Co alloy showed the most prominent oxidation behavior, bond strength of them to porcelain was not greatly high by the formation of porosities at metal-ceramic interfaces. 3. Likewise tin, cobalt formed the peaks on line profiles at metal-ceramic interface, however copper did not exhibit such peaks on line profiles. 4. Mainly, oxide layer on Pd-Co alloy was composed with cobalt, and for Pd-Co alloy with higher cobalt content the rise of bond strength was not significant by increased degassing time. 5. On Pd-Ag alloy not containing tin, during degassing for 15 minutes silver content was increased at metal-ceramic interface. 6. As an oxidized element, tin formed the oxide layers that widen their area by increasing the degassing time, while cobalt and copper showed the morphological changes of particle or crystal on oxide layer.

• 한국전기전자재료학회논문지
• /
• 제20권7호
• /
• pp.606-610
• /
• 2007

This paper describes the Raman scattering characteristics of polycrystalline (poly) 3C-SiC thin films, in which they were deposited on the oxidized Si substrate by APCVD method according to growth temperature. Since the phonon modes were not measured for $0.4{\mu}m$ thick 3C-SiC, $2.0{\mu}m$ thick 3C-SiC deposited on the oxidized Si at $1180^{\circ}C$, in which TO (transverse optical mode) and LO (longitudinal optical mode) phonon modes were appeared at 794.4 and $965.7cm^{-1}$, respectively. The broad FWHM (full width half maximum) can explain that the crystallinity of 3C-SiC deposited at $1180^{\circ}C$ becomes polycrystalline instead of disorder crystal. Additionally, the ratio of intensity $I_{LO}/I_{TO}{\approx}1.0$ of 3C-SiC indicates that the crystal disorder of $3C-SiC/SiO_2/Si$ is small. Compared poly $3C-SiC/SiO_2$ with $SiO_2/Si$ interfaces, $1122.6cm^{-1}$ phonon mode was measured which may belong to C-O bonding and two phonon modes, 1355.8 and $1596.8cm^{-1}$ related to D and G bands of C-C bonding in the Raman range of 200 to $2000cm^{-1}$.