• 대한치과기공학회지
• /
• 제31권4호
• /
• pp.15-23
• /
• 2009

The aim of this study was to evaluate the bond strength of using a Au bonding agent applied on cp-Ti and nonprecious metal-gold-ceramic system. Metallic frameworks(diameter: 5mm, height: 20mm)(N=56, n=7per group) cast in Ni-Cr alloy, Co-Cr alloy and cp-Ti were obtained using acrylic templates and airborne particle abraded with $110{\mu}m$ aluminum oxide. Au bonding agent was applied on wash opaque firing as intermediate layer. SEM and SEM/EDS line profile were performed on the cutting the cross-section of the metal substrate-porcelain with intermediate Au coating. Groups were tested using shear bond strength(SBS) testing at 0.5mm/min. The mean SBS values for the ceramic-Au layer-metal combination were significantly higher than those ceramic-metal combination. While ceramic-Au layer-cp-Ti combinations failed to increase bond strength instead of using a titanium bonding porcelain. The appication of using Au intermediate layer significantly improve the bond strength combination with metal-ceramic system.

• 대한치과기공학회지
• /
• 제33권3호
• /
• pp.185-192
• /
• 2011

Purpose: This study was to evaluate the shear bond strength of the ceramic fused to Ni-Cr alloy(Bellabond plus) and Co-Cr alloy(Wirobond C) by heat treatment. Methods: Metal specimens were divided into 5 groups for each alloy according to heat treatment conditions prior to porcelain application. Fifteen specimens from each group were subjected to a shear load a universal testing machine using a 0.1mm/min cross-head speed and one specimen from each group was observed with EDX line profile. Results: The diffusion of metal oxide observed far in the specimen heat treated than no heat treated in the opaque layer. The shear bond strength measured highest to BP3(50.50MPa), WC2(50.49MPa) groups and measured lowest from BP1(35.1MPaa), WC1(39.66MPa) groups which were not treated with heat, and there was a significant difference (p<0.05). Conclusion: The shear bond strength of Ni-Cr alloy(Bellabond plus) and Co-Cr alloy(Wirobond C) measured similar 5 groups all.

• 대한치과기공학회지
• /
• 제38권2호
• /
• pp.69-77
• /
• 2016

Purpose: This study was to evaluate the shear bond strength of ceramic fused to Ni-Cr alloy(Alophaloy) by heat treatment. Methods: The specimens were divided into 5 groups according to heat treatment conditions prior to porcelain application. Eighteen specimens from each group were subjected to the shear load a universal testing machine using a 0.1mm/min cross-head speed and two specimens from each group were observed with SEM and EDX line profile. Results: The observation of the oxide film on the metal surface by SEM photograph showed a coarsening with an increasing degassing hold time. The diffusion of metal oxide was observed farther from the opaque layer in the heat treated specimen than no heat treated specimen. The shear bond strength measured highest to A5(55.23MPa) in the 10min holding group and measured lowest from A1(24.38MPa) in the no heat treated group, and there was a significant difference(p<0.05). Conclusion: The shear bond strength of Ni-Cr alloy improved in the heat treatment compared to the no heat treatment specimen.

• 대한치과기공학회지
• /
• 제39권2호
• /
• pp.101-107
• /
• 2017

Purpose: The purpose of this study was to compare the shear bond strength of the metal-heat pressed glass ceramic bilayer structure. Methods: Metal framework specimens were prepared and surface is spreaded opaque(IPS InLine system opaque, IvoclarVivadent, Liechtenstein). There were 10 specimens for each bilayer dental ceramic group. The first group was porcelain fused metal, Press on metal IPS Inline press group, and press on metal HASS prototype group. Specimens measured for the shear bond strength on Schwickerath test by Instron universal testing machine(Instron3345, Instron Corp., USA). Mean average bond strength values of each specimen group were analyzed using a one-way ANOVA analysis of variance Saphiro-wilk's test. Statistical analysis were performed using IBM SPSS 23.0(IBM Co., Armonk, USA) Results: $RMS{\pm}SD$ The highest mean average HASS POM showed a bond strength value ($47.55{\pm}12.80Mpa$). The lowest mean average values Porcelain fused metal ($33.30{\pm}2.00Mpa$). Independent t-test was conduct to analysis the significant difference (p<0.05) (Table 3). Conclusion: Three kinds of Metal/ glass bilayer dental ceramics bond strength were clinical acceptability. Especially, as lithium disilicate containing represents higher bond strength.

• Journal of Welding and Joining
• /
• 제31권6호
• /
• pp.96-106
• /
• 2013

In this study, the effect of laser source($CO_2$ and Nd:YAG) on the microstructure and tensile properties of laser welded Al-Si coated boron steel(1.2mmt) was investigated with before and after hot-stamping. In case of as welds condition, fracture occurred in base metal unrelated to the laser source. It could be explained that tensile strength of fusion zone composed of martensite and bainite is higher than that of base metal that contains a lot of ferrite despite dilution of Al and Si from coating layer to fusion zone. In case of hot-stamping condition, the fracture occurred in fusion zone irrelevant to laser source and the tensile strength was lower than hot stamped base metal. In the $CO_2$ laser welds, $Fe_3$(Al,Si) formed near the bond line was transformed into ferrite during hot-stamping. Therefore tensile strength of bond line is lower than that of base metal and center of fusion zone and the fracture occurred in the bond line. On the other hand, in the Nd:YAG laser welds, the higher concentration of Al formed the ferrite in the fusion zone during hot-stamping treatment. Also, the thickness of centerline was thinner than that of base metal. Therefore, it is considered that fracture occurred in centerline of fusion zone due to effect of concentration stress, and it leaded to a lower tensile strength and elongation.

• Journal of the Korean Wood Science and Technology
• /
• 제52권4호
• /
• pp.301-318
• /
• 2024

Contrary to other materials like metals, glass, etc., wood continuously interacts with the environment, increasing and decreasing its moisture content according to the humidity of the air and changing its dimensions by swelling or shrinking. Water diffusion through laminated solid wood is crucial in wood bonding processes. The adhesive layer might block the diffusion if the water vapor diffusion is perpendicular to the bond line. As a result of this blockage, different proportions of deformation appear on the two sides of the bond line, which causes stresses in the bonded assembly. The question arises of how long the bonded structure will keep its integrity due to moisture diffusion blockage, inevitable tensions appearing in the glue line, and how these stresses could be avoided. With cross laminated timber (CLT) solid wood panel production, this question gains new importance. Despite the relevance, only a limited number of publications are available. Comprehensive research would also be necessary considering both the molecular structure and diffusion properties of the adhesive adjusted to the wood species (covering possible substituting wood species, too). Overall, this review serves as a resource for enhancing our understanding of water vapor diffusion through wood adhesive layers and provides insights that have implications for reducing stresses in bonded wood assemblies and the performance of the bonded group over time. Furthermore, identifying knowledge gaps is necessary to establish the basis for investigating the diffusion property of CLT panels.

• 대한치과보철학회지
• /
• 제30권4호
• /
• pp.508-525
• /
• 1992

The purpose of this study was to evaluate the effect of some resistance form designs on the bond strength of resin-retained prosthesis. Six sub-groups are designed in natural teeth group and resin teeth group . The framework designs in natural teeth group: 1) no groove preparation 2) groove at the center of distal surface 3) groove at the distobuccal line angle 4) 45 degree lateral load with no groove 5) 45 degree lateral load with center groove 6) splint two teeth with no groove. The framework designs in resin teeth group: 1) no groove preparation 2) groove at the center of distal surface 3) groove at the distobuccal line angle 4) metal covered the 1/2 of distal surface 5) metal covered the 1/2 of mesial surface 6) metal extended over the 114 of buccal surface. Specimens were treated electrolytic etching by Oxy-Etch and cemented with Panavia EX. Failure load was measured by Instron. Another 30 specimens were carried out fatigue tests by MTS 810 fatigue testing machine for 5000 cycles at different load level. The following results were obtained from this study. 1. The failure load was significantly increased by resistance forms. 2. The failure load was not increased by increase of total surface area bonded with teeth. The distal surface area played an important role in failure load. 3. In 45 degree lateral load group, the failure load was decreased significantly than that of in vertical load group. 4. Bond failure modes between static test and fatigue test exhibited no differences.

• Journal of the Korean Wood Science and Technology
• /
• 제43권1호
• /
• pp.60-67
• /
• 2015

국내산 낙엽송 집성재와 봉형 GFRP의 접착성능을 평가하기 위해 집성재에 선공을 한 후 봉형 GFRP를 삽입하고 접착제로 목재와의 간극을 충진시켜 인발시험편을 제작하였다. 인발시험편은 접착 깊이, 접착층 두께, 접착제 종류를 다르게 적용하여 실험하였다. 봉형 GFRP를 삽입접착한 캔틸레버형 라멘구조 시험체는 인발시험 결과를 토대로 제작, 강판삽입형 시험체와 모멘트 저항 성능을 비교검토 하였다. 인발시험결과 봉형 GFRP의 삽입깊이가 봉형 GFRP 직경의 5배일 때 가장 우수한 접착력이 측정되었으며, 접착층 두께는 1 mm일 경우 2 mm일 때보다 17%~29% 향상된 접착력이 측정되었다. 또한 폴리우레탄(poly-urethane) 접착제를 사용한 시험편이 레조시놀(resorcinol) 접착제를 사용한 시험편보다 2.9~4.0배 높은 성능을 발휘하였다. 봉형 GRFP로 접합한 캔틸레버형 라멘구조 시험체는 드리프트 핀을 사용한 강판삽입형 시험체와 비교하여 평균 0.82배 낮은 모멘트 저항 성능이 측정되었지만 초기강성은 0.93배로 대등한 성능을 보였다.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2005년도 춘계학술발표대회 개요집
• /
• pp.384-386
• /
• 2005

Initial oxide layer on the butt surface fragments during friction stir welding (FSW) and then often remains as a faint zigzag-line pattern on the cross section. When remnant of the oxide layer often adversely affects the mechanical properties in the weld, it is called as 'kissing-bond'. The present study systematically examines effect of oxide array on bend property in the root of friction stir (FS) welded Al alloy 1050 by transmission electron microscopy (TEM), and then clarifies identity of the kissing-bond.

• 전기학회논문지
• /
• 제58권2호
• /
• pp.308-313
• /
• 2009

This paper presents a reliability analysis of S-bonds for AF track circuits, which detect train movement and transmit a speed control signal to the train. Field survey shows that S-bonds are exposed to very large vibrations transferred from rail, and suffer from frequent failures when they were installed on ballasted track. We collected the time-to-failure data of S-bonds from the maintenance field of Seoul metro line 2, and made a parametric approach to estimate the statistical distribution that fits the time-to-failure data. The analysis shows that S-bonds have time-to-failure characteristics described by Weibull distribution. The estimated shape parameter of Weibull distribution is 1.1, which means the distribution has constant failure rate characteristics like exponential distribution. The reliability function, hazard function, percentiles and mean lifetime are derived for maintenance support.