• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.1
• /
• pp.45-49
• /
• 2014

We have fabricated white organic light-emitting diodes (OLEDs) using several thicknesses of electron-transport layer. The multi-emission layer structure doped with red and blue phosphorescent guest emitters was used for achieving white emission. 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline (BCP) was used as an electron-transport layer. The thickness of BCP layer was varied to be 20, 55, and 120 nm. The current efficiency, emission and recombination characteristics of multi-layer white OLEDs were investigated. The BCP layer thickness variation results in the shift of emission spectrum due to the recombination zone shift. As the BCP layer thickness increases, the recombination zone shifts toward the electron-transport layer/emission-layer interface. The white OLED with a 55 nm thick BCP layer exhibited a maximum current efficiency of 40.9 cd/A.

• Journal of Information Display
• /
• v.11 no.3
• /
• pp.123-127
• /
• 2010

Fluorescent white organic light-emitting diodes showing high color-rendering indices (CRIs) of up to 81 was demonstrated, with a silicon-cored anthracene derivative (PATSPA) doped with DPAVBi utilized as the deep-blue host and dye materials, and the commercial dyes rubrene and DCM2 utilized as the orange- and red-light-emitting dyes. The devices, consisting of three emissive layers, showed bright-white-light emission, but the ratio of the blue peak to the orange and red peaks changed with the current density and the thickness of the blue emissive layer. A high CRI was achieved with the use of a deep-blue emitter doped in a novel host and by optimizing the blue-layer thickness. The device with a blue-layer thickness of 10 nm showed the Commission Internationale de l'Eclairage (CIE) color coordinate of (0.33, 0.35), a high CRI of 81, and a moderate external quantum efficiency of 2% at a current density of $2.5\;mA/cm^2$.

• Transactions on Electrical and Electronic Materials
• /
• v.8 no.5
• /
• pp.218-221
• /
• 2007

High-efficiency white organic light-emitting diodes(WOLEDs) were fabricated with two emissive layers and an blocking layer was sandwiched between two phosphorescent dopants, bis(3,5-difluoro-2-(2-pyridyl)phenyl-(2-carboxypyridyl) iridium III(FIrpic) as the blue emission and a newly synthesized red phosphorescent material guest, bis(5-acetyl-2-phenylpyridinato-N,C2') acetylacetonate($(acppy)_2Ir(acac)$). This blocking layer prevented a T-T annihilation in a red emissive layer, and balanced with blue and red emission as blocking of hole carriers. The white device showed Commission Internationale d'Eclairage($CIE_{x,y}$) coordinates of (0.317, 0.425) at 22400 $cd/m^2$, a maximum luminance of 27300 $cd/m^2$ at 268 $mA/cm^2$, a maximum luminous efficiency and power efficiency of 26.9 cd/A and 18.6 lm/W.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.64-65
• /
• 2007

High-efficiency white organic light-emitting diodes (WOLEDs) were fabricated with two emissive layers and exciton blocking layer was sandwiched between two phosphorescent dyes which were, bis(3,5-Difluoro-2-(2-pyridyl)phenyl-(2-carboxypyridyl) iridium III (Flrpic) as blue emission and a newly synthesized red phosphorescent material guest, Bis(5-benzoyl-2-phenylpyridinato-C,N)iridium(III) (acetylacetonate) ((Bzppy)2Ir(III)acac). This exciton blocking layer prevents a triple-triple energy transfer between the two phosphorescent emissive layers with balanced emission of blue and red. The white device showed the Commission Internationale d'Eclairage (CIEx,y) coordinates of (0.34, 0.40) at the maximum luminance of $24100\;cd/m^2$ and maximum luminous efficiency of 22.4 cd/A, respectively.

• Proceedings of the KIEE Conference
• /
• 1999.11d
• /
• pp.997-999
• /
• 1999

We fabricated white light-emitting organic electroluminescent device which have a mixed single emitting layer containing poly(N-vinylcarbazole)[PVK], tris(8-hydroxyquinoline)aluminum[Alq3] and poly(3-hexylthiophene)[P3HT] and investigated the emission properties of it. We expect to obtain a blue light from PVK, green light from Alq3 and red light from P3HT The fabricated device emits white light over 18V with slight orange light. We think that the energy transfer in a mixed layer occurred from PVK to $Alq_3$ and P3HT resulted in decreasing the blue light intensity from PVK. With mixing of N, N'-diphenyl-N, N'-(3-methylphenyl)-[1,1'-biphenyl]-4, 4'-diamine[TPD], hole transport material, to the emitting layer, the luminance intensity of device was increased 50 times than that of the device which not contain TPD. We find that the efficiency of the white light electroluminescent device can be improved by injecting electron more effectively and blue light need to improve the color purity of white light.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.6
• /
• pp.451-456
• /
• 2013

To study emission properties of white phosphorescent organic light emitting devices (PHOLEDs), we fabricated white PHOLEDs of ITO(150 nm) / NPB(30 nm) / TcTa(10 nm) / mCP(7.5 nm) / light-emitting layer(25 nm) / UGH3(5 nm) / Bphen(50 nm) / LiF(0.5 nm) / Al(200 nm) structure. The total thickness of light-emitting layer with co-doping and blue-doping/co-doping using a host-dopant system was 25 nm and the dopant of blue and red was FIrpic and $Bt_2Ir$(acac) in UGH3 as host, respectively. The OLED characteristics were changed with position and thickness of blue doping layer and co-doping layer as light-emitting layer and the best performance seemed in structure of blue-doping(5 nm)/co-doping(20 nm) layer. The white PHOLEDs showed the maximum current density of $34.5mA/cm^2$, maximum brightness of $5,731cd/m^2$, maximum current efficiency of 34.8 cd/A, maximum power efficiency of 21.6 lm/W, maximum quantum efficiency of 15.6%, and a Commission International de L'Eclairage (CIE) coordinate of (0.367, 0.436) at $1,000cd/m^2$.

• Bulletin of the Korean Chemical Society
• /
• v.22 no.7
• /
• pp.743-747
• /
• 2001

New azomethine metal complexes were synthesized systematically and characterized. Beryllium, magnesium, or zinc ions were used as a central metal cation and aromatic azomethines (L1-L4) were employed as a chelating anionic ligand. Emission peaks o f the complexes in both solution and solid states were observed mostly at the region of 400-500 nm in the luminescence spectra, where blue light was emitted. Three of them (BeL1 (Ⅰ), ZnL2 (Ⅱ), and ZnL3 (Ⅲ)) were sublimable and thus were applied to the organic light-emitting devices (OLED) as an emitting layer, respectively. The device including the emitting layer of Ⅰ exhibited white emission with the broad luminescence spectral range. The device with the emitting layer of Ⅱ showed blue luminescence with the maximum emission peak at 460 nm. Their ionization potentials, electron affinities, and electrochemical band gaps were investigated with cyclic voltammetry. The electrochemical gaps of 2.98 for I, 2.70 for Ⅱ, and 2.63 eV for Ⅲ were found to be consistent with their respective optical band gaps of 3.01, 2.95 and 2.61 eV within an experimental error. The structure of OLED manufactured in this study reveals that these complexes can work as electron transporting materials as well.

• Journal of the Korean Applied Science and Technology
• /
• v.39 no.5
• /
• pp.589-595
• /
• 2022

The white OLED is fabricated with the anthracene-based blue emitting material, 9-(2-naphthyl)-10-(p-tolyl)anthracene (2-NTA) in various volume-ratios of orange dopant, rubrene, which results in pure white emission with C.I.E. coordinate of ~(0.32, 0.39). The devices with <1.5% rubrene show better EL properties (efficiency) than >3% devices. Furthermore the turn-on voltage of 2-NTA WOLED (3.7 V) is lower than that of 2-NTA blue OLED (5.4 V) at the same condition. Conclusively 2-NTA with rubrene less than 1.5% (v/v) could be utilized for the pure WOLED.

• Journal of the Korea Society of Computer and Information
• /
• v.10 no.1 s.33
• /
• pp.1-6
• /
• 2005

White light emission is very important for applying electroluminescent device to full display, backlight and illumination light source. In this letter, Multilayer molecular organic white-light-emitting device using thin nim of blue material nitro-DPVT with fluorescent dye Rubrene for an orange emission were fabricated. The basic structure of the fabricated device is a-NPD / nitro-DPVT / nitro- DPVT:Rubrene / BCP/ Alq3. Aluminum is used as the cathode material and ITO was anode material. The white light emission spectrum covers a wide range of the visible region and the Commission Internationale do I'E clairage (C.I.E.) coordinates of the emitted light was ((0.3347, 0.3515) at 14V. The turn voltage is as low as 2.5V and quantum efficiencies are $0.35\%$.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2008.10a
• /
• pp.565-568
• /
• 2008

In this study, a blue-emitting $Sr_2MgSi_2O_7:Eu^{2+}$ (SMS) phosphor for white light-emitting diodes is reported. Through transition of $4f{\rightarrow}5d$ in $Eu^{2+}$, SMS showed a strong blue emission under UV excitation. Additionally, the variation of emission wavelength of SMS is explained by crystal field effect and is supported by rietveld refinement.