• Journal of the Korea institute for structural maintenance and inspection
• /
• v.24 no.2
• /
• pp.78-85
• /
• 2020

Shotcrete concrete is generally used in the form of ready-mixed concrete products using type I ordinary portland cement(hereinafter referred to as OPC) and about 5% of accelerator mixed separately in the field. In this study, we tested the effect of OPC fineness and SO₃ content on a penetration resistance, compressive strength of binder for shotcrete using calcium aluminate type accerlerator. And we analysed hydrates and pore structure effects on mortar performance. In the future, it is expected to be useful for manufacturing optimized OPC as a binder for shotcrete.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.4
• /
• pp.367-373
• /
• 2015

In this study, fundamental properties of cement were reviewed to apply high fineness cement at low temperature environment. The classified high fineness cement has large proportion of particles below $10{\mu}m$ which affects early hydration: an overall reaction of cement hydration faster. As a result of using high fineness cement, setting time of concrete was reduced and compressive strength was higher than OPC at all ages. Especially, compressive strength was more than double its value compared with OPC after three days curing in low temperature. Faster reaction and higher heat of hydration was verified by calorimetry early and maximum heat of hydration was analyzed by adiabatic temperature raising test. The analysis of this study confirmed that high fineness cement can be suitable to be used in low temperature environment.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.3
• /
• pp.313-319
• /
• 2017

In general, various factors such as grain size, chemical composition, amorphous amount, amorphous Si and Al content of fly ash affect the reaction with cement. In this study, we investigate the effect of fly ash particle characteristics on compressive strength. The standard sand was pulverized to a particle size similar to that of fly ash and the compressive strength was measured by blending with the cement as in fly. Using the measured compressive strength results, strength enhancement by cement hydration reaction and strength enhancement by particle filling effect were confirmed. Strength increment by pozzolanic reaction of fly ash was calculated by using the compressive strength results of mortar substituted with standard powder. As a result of comparison between compressive strengths and the particle characteristics of fly ash, the blaine showed a weak correlation with the compressive strength and the PI(Pozzolanic Index) showed good correlation with the 10% penetration diameter(D10) and the 50% Respectively. Therefore, it is expected that PI will be a good means to evaluate the fly ash characteristics together with the chemical characteristics of fly ash.

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.5
• /
• pp.413-419
• /
• 2016

In the cold-weathering concrete construction, it is important to ensure stable strength development of concrete in a low temperature environment. In this study, Non-curing cement(NCC) using the classified high fineness cement and self-heating powder was investigated for stable strength development without curing in a low temperature environment (less than $0^{\circ}C$). The actual size Mock-Up tests by various cement type and curing condition are performed to evaluate the strength development and hydration heat of concrete.

• Magazine of the Korea Concrete Institute
• /
• v.9 no.1
• /
• pp.115-121
• /
• 1997

This study deals with the suppressing characteristics of alkali-silica reaction by ground granulated blast-furnace slag(GGBS) in NaCl solution. NaCl contents used in the experiment ranges over 0%, 2.8% and 20%. Reactive aggregate used is Japanese andesite. Also, three GGBSs of about 4.000. 6, 000 and $8, 000cm^2/g$ were used in the experiment. The replacement proportions of portland cement by GGBSs were 40%. 60%, 70% and 80%. respectively. The specimens with GGBS were severely contracted according to the increasing replacement ratio in NaCl solution. The contraction rate increases according to the increasing in NaCl content. Also. it does with increasing the blaine fineness of GGRS. It is concluded that the suppression of alkali-silica reaction by GGBS in NaCl solution is complished by contraction of GGBS due to chloride ion induced chemical shrinkage.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.677-680
• /
• 2008

The surface of particles was energetically modified by inter-grinding OPC and BFS in vibration mill for improvement of the early strength and low-heat evolution of concretes. BFS was pre-grinding in ball-mill to 2535(BS2) and 3245 $cm^2/g$(BS3), in blaine surface area. The inter-grinding time in vibration mill was changed from 10 minutes to 30 minutes. And Mixing ration of BFS to OPC was changed in 60, 70, 80%. After inter-grinding, the change of specific surface area, particle size distribution, hydration heat of cement and compressive strength of mortar were measured. As the result of comparison test with LHC, it was found that the mixture and inter-grinding time satisfying the value of over 100% of compressive strength for 7 days and under 170J/g of heat of hydration for 72 hours. and it was confirmed that the possibility of low heat slag cement utilizing blast furnace slag(BS2, BS3) with the low fineness in high volumes.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.1
• /
• pp.37-44
• /
• 2014

Recently, many efforts related to the utilization of industrial by-products have been made to reduce carbon dioxide emissions in the construction industry. Of these various efforts, concrete incorporating ground granulated blast furnace slag (BFS) provides many advantages compared to conventional concrete, such as high long-term compressive strength, improved durability and economic benefits because of its latent hydraulic property, and low compressive strength at early curing age. This paper investigates the compressive strength of high-activated ground granulated blast furnace slag blended mortar with slag by-product S type(SBP-S). The results of the experiment revealed that incorporating high-activated ground granulated blast furnace slag would affect the compressive strength of mortar. It was found that increasing the Blaine fineness and replacement ratio of slag by-product S type shows high compressive strength of mortar at early curing age because of its high $SiO_2$ and CaO contents in the slag. It is confirmed that an increase of curing age does not affect the compressive strength of mortar made with slag by-product S type at a high curing temperature. Moreover, it is possible to develop and design concrete manufactured with high-activated ground granulated blast furnace slag as binder considering the acceleration curing conditions and mix proportions.