• Journal of the korean academy of Pediatric Dentistry
• /
• v.45 no.3
• /
• pp.344-353
• /
• 2018

The purposes of this study were to evaluate microleakage of Biodentine, one of the tricalcium silicate based pulp-capping materials, and to compare the shear bond strength between composite resin and Biodentine with different setting times. For microleakage evaluation, 70 bovine teeth were used. Cavities were formed on the labial surfaces and filled with Biodentine. The teeth were divided into seven groups, each consisting of 10 teeth. The specimens were prepared by applying the composite resin on the upper side after different setting times. To evaluate shear bond strength, 210 acrylic resin blocks with central grooves were prepared, and the grooves were filled with Biodentine. The acrylic resin blocks were divided into seven groups of 30 specimens each, and the specimens were prepared by applying the composite resin on the upper side after different setting times. In samples with setting time of 24 hours or longer period, the microleakage between composite resin and Biodentine was reduced significantly while the shear bond strength increased to offset the polymerization shrinkage of the composite resin. Setting Biodentine for more than 24 hours before composite resin restoration would lead to more favorable clinical result.

• Restorative Dentistry and Endodontics
• /
• v.39 no.2
• /
• pp.120-125
• /
• 2014

Use of an apical plug in management of cases with open apices has gained popularity in recent years. Biodentine, a new calcium silicate-based material has recently been introduced as a dentine substitute, whenever original dentine is damaged. This case report describes single visit apexification in a maxillary central incisor with necrotic pulp and open apex using Biodentine as an apical barrier, and a synthetic collagen material as an internal matrix. Following canal cleaning and shaping, calcium hydroxide was placed as an intracanal medicament for 1 mon. This was followed by placement of small piece of absorbable collagen membrane beyond the root apex to serve as matrix. An apical plug of Biodentine of 5 mm thickness was placed against the matrix using pre-fitted hand pluggers. The remainder of canal was back-filled with thermoplasticized gutta-percha and access cavity was restored with composite resin followed by all-ceramic crown. One year follow-up revealed restored aesthetics and function, absence of clinical signs and symptoms, resolution of periapical rarefaction, and a thin layer of calcific tissue formed apical to the Biodentine barrier. The positive clinical outcome in this case is encouraging for the use of Biodentine as an apical plug in single visit apexification procedures.

• The Journal of the Korean dental association
• /
• v.57 no.5
• /
• pp.264-268
• /
• 2019

Objectives: This study aimed to measure the water sorption / solubility of Biodentine, composite resin and glass ionomer cement. Materials and Methods: The materials used in this study were Biodentine(BD), Filtek Z250(FZ) and Ketac Molar(KM). Twenty disc-shaped specimens of each material were prepared of 6mm diameter and 1mm thickness. All specimens were desiccated for 24 hours and weighed(m1). After then, They were immersed in distilled water and stored at $37^{\circ}C$. 1 week later, They were washed with running water, wiped with absorbent paper and weighed(m2). Finally, They were dried for 24 hours and weighed(m3). Water sorption and solubility, net water uptake were calculated. Results: KM and BD showed high water sorption than FZ(P<0.05). KM and BD exhibited similar water sorption(P<0.05). BD exhibited high solubility than KM(P=0.012). BD exhibited high net water uptake than FZ(P=0.008). Conclusion: Biodentine showed higher water sorption, solubility and net water uptake than Filtek Z250 and Ketac Molar. Within limitation of this study, it is not recommended to use Biodentine for permanent restoration.

• Restorative Dentistry and Endodontics
• /
• v.46 no.1
• /
• pp.3.1-3.14
• /
• 2021

Objectives: This study aimed to evaluate the interface between a calcium silicate cement (CSC), Biodentine and dental adhesives in terms of sealing ability. Materials and Methods: Microleakage test: 160 standardized class II cavities were prepared on 80 extracted human molars. The cavities were filled with Biodentine and then divided into 2 experimental groups according to the time of restoration: composite resin obturation 15 minutes after Biodentine handling (D0); restoration after 7 days (D7). Each group was then divided into 8 subgroups (n = 5) according to the adhesive system used: etch-and-rinse adhesive (Prime & Bond); self-etch adhesive 2 steps (Optibond XTR and Clearfil SE Bond); self-etch adhesive 1 step (Xeno III, G-aenial Bond, and Clearfil Tri-S Bond); and universal used as etch-and-rinse or self-etch (ScotchBond Universal ER or SE). After thermocycling, the teeth were immersed in a silver nitrate solution, stained, longitudinally sectioned, and the Biodentine/adhesive percolation was quantified. Scanning electron microscopic observations: Biodentine/adhesive interfaces were observed. Results: A tendency towards less microleakage was observed when Biodentine was etched (2.47%) and when restorations were done without delay (D0: 4.31%, D7: 6.78%), but this was not significant. The adhesives containing 10-methacryloyloxydecyl dihydrogen phosphate monomer showed the most stable results at both times studied. All Biodentine/adhesive interfaces were homogeneous and regular. Conclusions: The good sealing of the CSC/adhesive interface is not a function of the system adhesive family used or the cement maturation before restoration. Biodentine can be used as a dentine substitute.

• Restorative Dentistry and Endodontics
• /
• v.45 no.1
• /
• pp.5.1-5.8
• /
• 2020

Objectives: The obturation quality of MTA, Biodentine, Total Fill BC root canal sealer (RCS), and warm gutta-percha (WGP) in teeth with simulated internal root resorption (IRR) was evaluated by using micro-computed tomography. Materials and Methods: Standardized IRR cavities were created using 40 extracted maxillary central incisor teeth and randomly assigned into 4 groups (n = 10). IRR cavities were filled with MTA, Biodentine, Total Fill BC RCS (bulk-fill form) and WGP + Total Fill BC RCS. Percentage of voids between resorptive cavity walls and obturation material (external void), and inside the filling materials (internal voids) were measured. Results: Total Fill BC sealer in the bulk-fill form presented significantly highest values of external and internal void percentages (p < 0.05). Biodentine showed a significantly lowest external void percentage (p < 0.05). WGP + Total Fill BC RCS presented significantly lower values of internal void percentages than all groups (p < 0.05), except Biodentine (p > 0.05). Conclusion: None of the filling materials were created void-free obturation in resorption cavities. Biodentine may favor its application in teeth with IRR over Angelus MTA and bulkfill form of Total Fill BC.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.43 no.1
• /
• pp.36-43
• /
• 2016

The aim of this study was to evaluate the effect of blood contamination on the push-out bond strength and surface morphology of tricalcium silicate materials; Biodentine$^{(R)}$, Theracal$^{(R)}$ and mineral trioxide aggregate. The standardized lumens of root slices prepared from extracted single-root human teeth were filled with Biodentine$^{(R)}$, Theracal$^{(R)}$ and mineral trioxide aggregate by manufacturer's instruction. The specimens were randomly divided into 2 groups (n = 20) for each material and then incubated for 4 days at $37^{\circ}C$; control group (phosphate buffered saline solution) and experimental group (fetal bovine serum). The push-out bond strengths were then measured by a universal testing machine and the surface morphology of each experimental group was analyzed by scanning electron microscope. Biodentine$^{(R)}$ and Theracal$^{(R)}$ showed higher push-out bond strength compared with mineral trioxide aggregate after exposure to fetal bovine serum. A substantial change in the surface morphology of each material was observed after exposure to fetal bovine serum. In conclusion, the push-out bond strengths of Biodentine$^{(R)}$ and Theracal$^{(R)}$ were higher than mineral trioxide aggregate when exposed to blood contamination. Therefore, it is supposed that the use of Biodentine$^{(R)}$ and Theracal$^{(R)}$ is appropriate in the presence of blood.

• Restorative Dentistry and Endodontics
• /
• v.41 no.1
• /
• pp.29-36
• /
• 2016

Objectives: The purpose of this study was to assess the ability of two new calcium silicate-based pulp-capping materials (Biodentine and BioAggregate) to induce healing in a rat pulp injury model and to compare them with mineral trioxide aggregate (MTA). Materials and Methods: Eighteen rats were anesthetized, cavities were prepared and the pulp was capped with either of ProRoot MTA, Biodentine, or BioAggregate. The specimens were scanned using a high-resolution micro-computed tomography (micro-CT) system and were prepared and evaluated histologically and immunohistochemically using dentin sialoprotein (DSP). Results: On micro-CT analysis, the ProRoot MTA and Biodentine groups showed significantly thicker hard tissue formation (p < 0.05). On H&E staining, ProRoot MTA showed complete dentin bridge formation with normal pulpal histology. In the Biodentine and BioAggregate groups, a thick, homogeneous hard tissue barrier was observed. The ProRoot MTA specimens showed strong immunopositive reaction for DSP. Conclusions: Our results suggest that calcium silicate-based pulp-capping materials induce favorable effects on reparative processes during vital pulp therapy and that both Biodentine and BioAggregate could be considered as alternatives to ProRoot MTA.

• Restorative Dentistry and Endodontics
• /
• v.46 no.4
• /
• pp.59.1-59.14
• /
• 2021

Objectives: This study compared the Biodentine, MTA Repair HP, and Bio-C Repair bioceramics in terms of bond strength to dentin, failure mode, and compression. Materials and Methods: Fifty-four slices obtained from the cervical third of 18 single-rooted human mandibular premolars were randomly distributed (n = 18). After insertion of the bioceramic materials, the push-out test was performed. The failure mode was analyzed using stereomicroscopy. Another set of cylindrically-shaped bioceramic samples (n = 10) was prepared for compressive strength testing. The normality of data distribution was analyzed using the Shapiro-Wilk test. The Kruskal-Wallis and Friedman tests were used for the push-out test data, while compressive strength was analyzed with analysis of variance and the Tukey test, considering a significance level of 0.05. Results: Biodentine presented a higher median bond strength value (14.79 MPa) than MTA Repair HP (8.84 MPa) and Bio-C Repair (3.48 MPa), with a significant difference only between Biodentine and Bio-C Repair. In the Biodentine group, the most frequent failure mode was mixed (61%), while in the MTA Repair HP and Bio-C Repair groups, it was adhesive (94% and 72%, respectively). Biodentine showed greater resistance to compression (29.59 ± 8.47 MPa) than MTA Repair HP (18.68 ± 7.40 MPa) and Bio-C Repair (19.96 ± 3.96 MPa) (p < 0.05). Conclusions: Biodentine showed greater compressive strength than MTA Repair HP and Bio-C Repair, and greater bond strength than Bio-C Repair. The most frequent failure mode of Biodentine was mixed, while that of MTA Repair HP and Bio-C Repair was adhesive.

• Restorative Dentistry and Endodontics
• /
• v.40 no.4
• /
• pp.276-285
• /
• 2015

Objectives: The purpose of this study was to evaluate the efficacy of mineral trioxide aggregate (MTA), Biodentine and Propolis as pulpotomy medicaments in primary dentition, both clinically and radiographically. Materials and Methods: A total of 75 healthy 3 to 10 yr old children each having at least one carious primary molar tooth were selected. Random assignment of the pulpotomy medicaments was done as follows: Group I, MTA; Group II, Biodentine; Group III, Propolis. All the pulpotomized teeth were evaluated at 3, 6, and 9 mon clinically and radiographically, based on the scoring criteria system. Results: The clinical success rates were found to be similar among the three groups at 3 and 6 mon where as a significant decrease in success rate was observed in Group III (84%) compared to both Group I (100%) and Group II (100%) at 9 mon. Radiographic success rates over a period of 9 mon in Groups I, II, and III were 92, 80, and 72%, respectively. Conclusions: Teeth treated with MTA and Biodentine showed more favorable clinical and radiographic success as compared to Propolis at 9 mon follow-up.

• Restorative Dentistry and Endodontics
• /
• v.44 no.1
• /
• pp.5.1-5.9
• /
• 2019

Objectives: The aim of this in vitro study was to evaluate the push-out bond strength of a novel calcium silicate-based root repair material-BIOfactor MTA to root canal dentin in comparison with white MTA-Angelus (Angelus) and Biodentine (Septodont). Materials and Methods: The coronal parts of 12 central incisors were removed and the roots were embedded in acrylic resin blocks. Midroot dentin of each sample was horizontally sectioned into 1.1 mm slices and 3 slices were obtained from each root. Three canal-like standardized holes having 1 mm in diameter were created parallel to the root canal on each dentin slice with a diamond bur. The holes were filled with MTA-Angelus, Biodentine, or BIOfactor MTA. Wet gauze was placed over the specimens and samples were stored in an incubator at $37^{\circ}C$ for 7 days to allow complete setting. Then samples were subjected to the push-out test method using a universal test machine with the loading speed of 1 mm/min. Data was statistically analyzed using Friedman test and post hoc Wilcoxon signed rank test with Bonferroni correction. Results: There were no significant differences among the push-out bond strength values of MTA-Angelus, Biodentine, and BIOfactor MTA (p > 0.017). Most of the specimens exhibited cohesive failure in all groups, with the highest rate found in Biodentine group. Conclusions: Based on the results of this study, MTA-Angelus, Biodentine, and BIOfactor MTA showed similar resistances to the push-out testing.