• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.05a
• /
• pp.239-240
• /
• 2021

In this study, we conducted a study to evaluate the more accurate mechanical properties of concrete damaged by fire. In relation to this, in this study, the results of compressive strength and biaxial flexural strength were compared for concrete that received high temperature heat. As a result, both the compressive strength and the biaxial bending strength decreased as the heating temperature increased. As a result of examining the correlation between the compressive strength and the biaxial flexural strength, the biaxial flexural strength was smaller than the compressive strength.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.33 no.3
• /
• pp.901-907
• /
• 2013

In this study, flexural strength properties of concrete under biaxial stress state were experimentally investigated. Tests for size effect and fatigue behaviour of concrete under biaxial stress were carried out by the ASTM C 1550 and the biaxial flexure test(BFT). The results given by the biaxial tests were compared to those by the third-point bending test. Test results showed that biaxial flexural strengths obtained from the ASTM C 1550 and the biaxial flexure test are greater than the strength by the third-point bending test. As the size increases, the uniaxial and biaxial flexural strength decreases. However, the slope of the size effect of the biaxial strength was greater than that of the uniaxial strength. Finally, the fatigue response of concrete under the biaxial stress state was similar with that for uniaxial stress state.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.23 no.4
• /
• pp.269-281
• /
• 2007

Fluoric acid etching is an essential procedure in cementation of reinforced ceramics to tooth surface. But there have been few studies about the changes of surface structure and flexural strength of IPS $Empress^{(R)}$ 2 ceramic according to the etching time. The objectives of this study were to examine the surface structure changes and the difference in biaxial flexural strength of IPS $Empress^{(R)}$ 2 ceramic according to various etching times. Sixty one disk-shaped specimens of IPS $Empress^{(R)}$ 2 ceramic($14mm{\times}1.2mm$) were fabricated for the biaxial flexural strength test and SEM analysis according to the manufacturer's recommendations. Sixty specimens were divided into 6 groups(n=10) according to the time of HF acid etching(0, 20, 180 and 300s)and silane/resin cement application. Each disk was loaded using a piston-on-3 ball biaxial configuration in a universal testing machine. The failure loads(N) were recorded, and the biaxial flexural strength for each disk was calculated. A one-way analysis of variance and independent t-test on transformed fracture strength data were used to determine significant differences between groups. The groups of no cementation showed a trend toward progressive weakening with increasing the etching time. However, this was not statistically significant at p=0.05 level. The groups of resin cementation exhibited no apparent trend in their mean strength values. SEM photomicrographs showed very different results of etching. Within the conditions of this study, alteration of surface topography by acid etching does not have a deleterious effect on the biaxial flexural strength of IPS $Empress^{(R)}$ 2 ceramic.

• Journal of Technologic Dentistry
• /
• v.30 no.1
• /
• pp.41-47
• /
• 2008

This study was to evaluate the biaxial flexural strength of zirconia ceramics after glass-infiltration on zirconia core. The zirconia specimens were made with diameter-15mm, thickness-0.6mm using zirconia block which divided into 1) sintered group, 2) heat - treated group, 3) Glass - infiltrated group and experimented fracture strength by each 10 specimens in experimental group. The biaxial flexural test was performed at crosshead speed of 0.1${\beta}\;{\AE}$ min. The experiment result average fracture strength was shown 541.0${\beta}\acute{A}$ in sintered group and glass-infiltrated group as 662.2${\beta}\acute{A}$ river of 22.4% rise appear. Weibull coefficient sintered group is 3.462 and glass-infiltrated group improved believability about fracture strength from melting permeation processing of glass by 4.716.

• Journal of the Korea Concrete Institute
• /
• v.20 no.2
• /
• pp.139-146
• /
• 2008

The characteristics of the biaxial flexural tensile strength of concretes was compared to that of the uniaxial strength. The uniaxial and biaxial strengths in this study were obtained from the classical modulus of rupture test and the biaxial flexural test recently developed by Zi and Oh and Zi et al., respectively. Three different sizes were considered to investigate the effect of the size of aggregates. To estimate the stochastic aspect of the strength, 32 specimens were used for each test. The average biaxial flexural fracture strength was about 20% greater than the uniaxial test. At the same time, the coefficient of variation for the biaxial test was 18% greater than the uniaxial test. This means that the probability of the biaxial cracking can be greater than the uniaxial cracking.

• Journal of the Korea Concrete Institute
• /
• v.23 no.4
• /
• pp.479-486
• /
• 2011

In this study, we conducted experiment and finite element analysis on the flexural behavior of the round concrete panels according to the evaluation method of biaxial flexural tensile strengths. The Round Panel Test (RPT) and the Biaxial Flexure Test (BFT) were used to determine the biaxial flexural strength of round plain concrete panels. In order to understand the stress distribution on the panels, we measured load-strain relationship at the center of the panels' bottom surface. Test results show that fracture pattern in RPT and BFT panels are similar, and the tensile stress distribution is uniform in all directions at the center of the bottom surface of the panels for both RPT and BFT. The distribution of stresses in two test specimens coincided with the analysis result. The average biaxial flexural strength of RPT is about 29% greater than those of the BFT. The coefficient of variations (COV) of the RPT and BFT for the biaxial flexure strength is 8%, 6%, respectively, which indicates that BFT method is useful and reliable for determining biaxial flexural strengths of the concrete.

• The Journal of Advanced Prosthodontics
• /
• v.6 no.3
• /
• pp.224-232
• /
• 2014

PURPOSE. The purpose of the present study was to evaluate the effect of thermocycling and mechanical loading on the biaxial flexural strength and the phase transformation of one Ce-TZP/$Al_2O_3$ and two Y-TZP core materials. MATERIALS AND METHODS. Thirty disc-shaped specimens were obtained from each material. The specimens were randomly divided into three groups (control, thermocycled, and mechanically loaded). Thermocycling was subjected in distilled water for 10000 cycles. Mechanical loading was subjected with 200 N loads at a frequency of 2 Hz for 100000 times. The mean biaxial flexural strength and phase transformation of the specimens were tested. The Weibull modulus, characteristic strength, 10%, 5% and 1% probabilities of failure were calculated using the biaxial flexural strength data. RESULTS. The characteristic strengths of Ce-TZP/$Al_2O_3$ specimens were significantly higher in all groups compared with the other tested materials (P<.001). Statistical results of X-ray diffraction showed that thermocycling and mechanical loading did not affect the monoclinic phase content of the materials. According to Raman spectroscopy results, at the same point and the same material, mechanical loading significantly affected the phase fraction of all materials (P<.05). CONCLUSION. It was concluded that thermocycling and mechanical loading did not show negative effect on the mean biaxial strength of the tested materials.

• Restorative Dentistry and Endodontics
• /
• v.38 no.3
• /
• pp.134-140
• /
• 2013

Objectives: There has been a growing interest in glass ceramic systems with good esthetics, high fracture resistance and bonding durability, and simplified fabrication techniques using CAD/CAM. The aim of this study is to compare flexural strength before and after heat treatment of two lithium disilicate CAD/CAM blocks, IPS e.max CAD (Ivoclar Vivadent) and Rosetta SM (Hass), and to observe their crystalline structures. Materials and Methods: Biaxial flexural strength was tested according to ISO 6872 with 20 disc form specimens sliced from each block before and after heat treatment. Also, the crystalline structures were observed using field-emission scanning microscopy (FE-SEM, Hitachi) and x-ray diffraction (XRD, Rigaku) analysis. The mean values of the biaxial flexural strength were analyzed by the Mann-Whitney U test at a significance level of p = 0.05. Results: There were no statistically significant differences in flexural strength between IPS e.max CAD and Rosetta SM either before heat treatment or after heat treatment. For both ceramics, the initial flexural strength greatly increased after heat treatment, with significant differences (p < 0.05). The FE-SEM images presented similar patterns of crystalline structure in the two ceramics. In the XRD analysis, they also had similar patterns, presenting high peak positions corresponding to the standard lithium metasilicate and lithium disilicate at each stage of heat treatment. Conclusions: IPS e.max CAD and Rosetta SM showed no significant differences in flexural strength. They had a similar crystalline pattern and molecular composition.

• The Journal of Korean Academy of Prosthodontics
• /
• v.59 no.2
• /
• pp.190-200
• /
• 2021

Purpose. The aim of this study was to evaluate biaxial flexural strength and hardness of colored monolithic zirconia after dipping in different time intervals of coloring solution. Materials and Methods. Disk shaped specimens were prepared from monolithic zirconia (Eclipse V2.0, AMS, Gimpo, Korea). Four experimental groups were categorized (n = 12) due to coloring time (PU (0s); ST (8s); OV (1 min); PS (preshade)), to evaluate biaxial flexural strength and Vickers hardness. After fracture, X-ray diffraction analysis was performed using fractured specimens. Results were analyzed with one-way ANOVA test. Results. There was no significant difference between groups in the biaxial flexural strength test. However, in the Vickers hardness test, the group with standard dipping time (ST) showed significantly higher value than the group without dipping in coloring liquid (PU)(P=.038). Also, there was no significant difference in the rest of the groups (P>.05). As a result of X-ray diffraction analysis, specific peaks of tetragonal phase were shown and the volume of monoclinic phase fraction was lower than 25%. Conclusion. Although this study has several limitations, coloring liquids had no significant effect on biaxial flexural strength. Vickers hardness was significantly different between the group to which the coloring liquid was applied and the group to which the coloring solution was not applied, but there was no significant difference between the other groups. Also, the flexural strength of monolithic zirconia corresponds to Class 5 of the minimal flexural strength standard according to the use of dental ceramics.

• The Journal of the Korea Contents Association
• /
• v.15 no.9
• /
• pp.384-394
• /
• 2015

The purpose of this study was to evaluate the push-shear bond strength between five commercial zirconia veneering ceramics and zirconia core cylinder, and to investigate the effect of biaxial flexural strength and zirconia liner glass treatments. The biaxial flexural strengths of the veneering ceramics were evaluated by a piston-on-three-ball test. The bond strengths between the Y-TZP cylinder and zirconia veneering ceramics were evaluated using the push-shear bond strength test. The data was analyzed using two-way ANOVA and Scheffe's test. The biaxial flexural strength of Cercon ceram kiss (CE) was higher than those of the other groups. The glass-treated and Triceram zirconia groups showed the highest value and the Creation ZI(CR) showed the lowest. In all groups, the liner glass treatment groups showed significantly higher push-shear bond strength than those without(P<0.05). The liner glass treatments of zirconia can improve the bond strength between the zirconia ceramic core and veneering ceramics.