• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.262-264
• /
• 2005

$Bi_{2}Sr_{2}CaCu_{2}O_{x}$(Bi-2212) and $Bi_{2}Sr_{2}Ca_{2}Cu_{3}O_{y}$(Bi-2223) high-$T_{c}$ superconductor(HTS) coating have been prepared by plasma spraying and heaat treatment. The Bi-2212 HTS coating later is synthesized through the peritectic reaction between Sr-Ca-Cu oxide coating layer and Bi-Cu oxide coating later, and $Bi_{2}Sr_{2}CaCu_{2}O_{y}$(Bi-2212) superconducting phase grow by partial melting process. The superconducting characteristic depends strongly on the conditions of the partial melting process. the Bi-2212 HTS layer consists of the whiskers grown in the diffusion direction. Above the 2212 layer, Bi-2223 phase and secondary phase was observed. The secondary phase is distributed uniformly over the whole surface. This is caused to the microcrack on the coatings surface. Despite everything, the film shows superconducting with an onset $T_{c}$ of about 115K. There are two changes steps. One changes (1step) at 115K is due to the diamagnetism of the Bi-2223 phase and the other changes (2step) at 78K is due to the diamagnetism of the Bi-2212 phase.

• Korean Journal of Materials Research
• /
• v.24 no.2
• /
• pp.116-122
• /
• 2014

$Bi_2Sr_2CaCu_2O_x$(Bi-2212) and $Bi_2Sr_2Ca_2Cu_3O_y$(Bi-2223) high-Tc superconductors(HTS) have been manufactured by plasma spraying, partial melt process(PMP) and annealing treatment(AT). A Bi-2212/2223 HTS coating layer was synthesized through the peritectic reaction between a 0212 oxide coating layer and 2001 oxide coating layer by the PMP-AT process. The 2212 HTS layer consists of whiskers grown in the diffusion direction. The Bi-2223 phase and secondary phase in the Bi-2212 layer were observed. The secondary phase was distributed uniformly over the whole layer. As annealing time goes on, the Bi-2212 phase decreases with mis-orientation and irregular shape, but the Bi-2223 phase increases because a new Bi-2223 phase is formed inside the pre-existing Bi-2212 crystals, and because of the nucleation of a Bi-2223 phase at the edge of Bi-2212 crystals by diffusion of Ca and Cu-O bilayers. In this study the spray coated layer showed superconducting transitions with an onset Tc of about both 115 K, and 50 K. There were two steps. Step 1 at 115 K is due to the diamagnetism of the Bi-2223 phase and step 2 at 50 K is due to the diamagnetism of the Bi-2212 phase.

• Transactions on Electrical and Electronic Materials
• /
• v.2 no.1
• /
• pp.12-15
• /
• 2001

Bi-2212 and Bi-2223 thin films are prepared by IBS(ion beam sputtering) technique. Three phases of Bi-2201, Bi-2212 and Bi-2223 appear as stable ones in spite of the conditions for thin film fabrication of Bi-2212 and Bi-2223 compositions, depending on substrate temperature (T $_{sub}$) and ozone pressure(PO$_3$). It is found out that these phases are limited within very narrow temperature.e.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2007.06a
• /
• pp.536-539
• /
• 2007

BSCCO am films fabricated by using the evaporation method at various substrate temperatures, Tsub and ozone gas pressures $PO_3$. Despite setting the composition of thin film Bi2223, Bi2201, Bi2212 and Bi2223 phase were appeared. It was confirmed the obtained field of stabilizing phase was represented in the diagonal direction of the right below end in the Arrhenius plot of temperature of the substrate and $PO_3$, and it was distributed in the rezone. The XRD peak of the generated film continuously changed according to the substrate temperature. This demonstrates the existence of mixed crystal composition where the phases of Bi2201, Bi2212 and Bi2223 are mixed in the crystal structure; and the single-phase film of each phase exist in a very rezone of temperature and gas pressure.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2003.05a
• /
• pp.615-618
• /
• 2003

This paper presents Bi thin films have been fabricated by atomic layer-by-layer deposition and co-deposition at an IBS method. The growth rates of the films was set in the region from 0.17 to 0.27 nm/min. MgO(l00) was used as a substrate. In order to appreciate stable existing region of Bi 2212 phase with temperature and ozone pressure, the substrate temperature was varied between 655 and 820 $^{\circ}C$ and the highly condensed ozone gas pressure(PO$_3$) in vacuum chamber was varied between 2.0$\times$10$^{-6}$ and 2.3$\times$10$^{-5}$ Torr. Bi 2212 phase appeared in the temperature range of 750 and 795$^{\circ}C$ and single phase of Bi 2201 existed in the lower region than 785 $^{\circ}C$. Whereas, PO$_3$ dependance on structural formation was scarcely observed regardless of the pressure variation. And high quality of c-axis oriented Bi 2212 thin film with T$_{c}$(onset) of about 90 K and T$_{c}$(zero) of about 45 K is obtained. Only a small amount of CuO in some films was observed as impurity, and no impurity phase such as CaCuO$_2$ was observed in all of the obtained films.lms.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.104-105
• /
• 2000

High quality BSCCO thin films have been fabricated by means of an ion beam sputtering at various substrate temperatures, T$_{sub}$, and ozone gas pressures, PO$_3$. The correlation diagrams of the BSCCO phases appeared against T$_{sub}$ and PO$_3$are established in the 2212 and 2223 compositional films. In spite of 2212 compositional sputtering, Bi2201 and Bi2223 phases as well as Bi2212 one come out as stable phases depending on T$_{sub}$ and PO$_3$. From these results, the thermodynamic evaluations of ΔH and ΔS which are related with Gibbs'free energy change for single Bi2212 or Bi2223 phase are performed.ormed.i2212 or Bi2223 phase are performed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.589-590
• /
• 2005

BSCCO:2212-2223 thin films were fabricated by using the ion beam sputter with a evaporation method at various substrate temperatures, $T_{sub}$, and ozone gas pressures, $pO_3$. The correlation diagrams of the BSCCO phases with Tsub and $pO_3$ are established in the 2212 and 2223 compositional films. In spite of 2212 compositional sputtering, Bi2201 and Bi2223 as well as Bi2212 phases come out as stable phases depending on Tsub and $pO_3$. From these results, the thermodynamic evaluation of ${\Delta}H$ and ${\Delta}S$, which are related with Gibbs' free energy change for single Bi2212 or Bi2223 phase, was performed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.65-68
• /
• 1999

A well oriented Bi2212 superconductor thick films were fabricated by screen printing with a Cu-free Bi-Sr-Ca-O mixture powder on a copper plate and heat-treating at 820-88$0^{\circ}C$ for several minute in air. During the heat-treatment, the printing layer partially melted by reaction between the Cu-free precursor and CuO of the oxidizing copper plate. In the partial melting state, it is believed that the solid phase is Bi-free phase and Cu-rich phase and the composition of the liquid is around Bi : Sr : Ca : Cu = 2 : 2 : 0 : 1. Following the partial melting, the Bi2212 superconducting phase is formed at Bi-free phase/liquid interface by nucleation and grows. With decreasing the Bi composition in the precursor powder, the critical temperature(T$_{c}$) of the fabricated Bi2212 thick film increased to about 79 K.K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05a
• /
• pp.80-83
• /
• 2003

$SrSO_4$ were systematically added on Bi2212 from 0 to 10wt% to study the effect of Bi2212 superconductor tube characteristics. After mixing, the melted solution of Bi2212 and $SrSO_4$ was initially poured into the cylinder type of steel mold preheated at $550^{\circ}C$ for 30min and rotated at 1000rpm. Following that, tube was annealed at $840^{\circ}C$ for 72hrs. The tube dimension was 60 in diameter, 60mm in length and 2mm in thickness. XRD data suggests that there was no typical segregation phase related with $SrSO_4$. Well textured grain with typical 2212 phase was observed and average size was $20{\mu}m$. The measured critical current and critical current density of Bi2212 tube added by 5% $SrSO_4$ at 77K were 495A and $202A/cm^2$ respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.4
• /
• pp.343-350
• /
• 2003

Using Bi$_2$Sr$_2$Ca$_2$.$_2$Cu$_3$ $O_{x}$ powders prepared by solid state reaction and spray drying method, the nucleation and growth behaviors of superconducting and second phases were investigated during isothermal heat treatment. When the spray drying power was used in contrast with solid state reaction powder, Bi$_2$Sr$_2$Ca$_2$.$_2$Cu$_3$ $O_{x}$ (2223) phase could be formed at the relatively shot time and second phases were much bigger. Quantitative analysis showed that as the heat treatment time increased, more Bi$_2$Sr$_2$Ca$_2$.$_2$Cu$_3$ $O_{x}$ (2212) changed to 2223 and the major second phase was changed from (Sr,Ca)$_{14}$Cu$_{24}$ $O_{x}$(14:24) to (Sr,Ca)$_2$Cu$_1$ $O_{x}$ (2:l). The superconducting phase formed at the relatively short time 14:24 phase. Following the Bi-free phase of 14:24 Phase, but long time was needed in places far from the 14:24 phase. Following the formation of the 2212 phase near the 14:24 phase, the 2223 phase nucleated preferentially at the interface between the 2212 and 14:24 phases. The preferential nuclcation of 2223 was explained by its structural similarity and low Interfacial energy with both the Bi-free and 2212 Phases.12 Phases.