• Journal of the Korean Society of Safety
• /
• v.12 no.2
• /
• pp.27-36
• /
• 1997

This paper evaluates the static and fatigue bending strengths of CFRP (carbon fiber reinforced plastic) laminates subjected to hygrothermals. The specimens which had different stacking composition, orthotropic and quasi-isotropic laminated plates, were prepared for this experiment. A steel ball launched by the air gun collides against CFRP laminates to generate impact damages, and the 3-point fatigue bending test is carried out by using the impacted laminates to investigate the influence of hygrothermals on the effect on the residual bending fatigue strength of CFRP laminates.

• Journal of Bio-Environment Control
• /
• v.27 no.4
• /
• pp.391-399
• /
• 2018

In this paper, experimental study performed on steel-pipe connections for structural members of a greenhouse is presented. By those experiments performed, bending moment, deformation and stress distribution of specimens were investigated under four point bending test. The bending performance according to connection method using pin and the stretching is also investigated. The results of bending performance of the no connection specimen were compared to those of other connection specimens. The pin and stretching connection specimens showed lower banding performance than the no connection specimen. The stretching connection method was relatively higher bending performance than the pin connection specimens. According to the results, we proposed the connection method with good bending performance that can be applied to steel-pipe connection in greenhouse.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.17 no.4
• /
• pp.59-66
• /
• 2008

This paper has proposed a new parameter to interpret the effects of plastic deformation in bending of strips in cylindrical die and punch. With reference to the parameter, we have provided an insight on the separation between strips and punches, the occurrence of the multi-point bending during the process of deformation, the final shapes of strips, and the springback ratios. Also using the parameter, we have considered the different effects between the bending deformation in the cylindrical die and the bending deformation due to pure bending.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.5
• /
• pp.486-496
• /
• 2018

This study was conducted to confirm an effect of span length on bending properties of larch dimensional lumber in the four point bending test. The size of specimen in this study was 38 (width) ${\times}$ 89 (depth) ${\times}$ 3,600 (length) $mm^3$, and average air-dry density and moisture content of the specimens was $543.5kg/m^3$ and 10.5%, respectively. Visually graded No. 1 dimensional lumbers of 248 were divided by two groups to compare modulus of rupture (MOR) and modulus of elasticity (MOE). One group was tested in the four point bending test with span length of 1,650 mm, and other was tested with span length of 3,000 mm. While MOE was not different according to span length in 5% significance level, MOR was different in accordance with span lengths and was in inverse proportion to change of span length. Fifth percentiles of MOR in span length of 1,650 and 3,000 mm were 28.65 and 25.70 MPa, respectively. It was confirmed that the difference between MORs in each case increased as normalized rank increased. This is because of size effect in Weibull weakest link failure theory. Therefore, KS F 2150, in which there is only regulation about span to depth ratio of 15 or more, is needed to be revised to contain a method considering size effect for MOR. From the method, various results of bending test with different size of lumber could be used to determine design value of lumber.

• Journal of the Korean Geotechnical Society
• /
• v.36 no.3
• /
• pp.25-36
• /
• 2020

In this research, three-point bending tests were performed using a rectangular frozen specimen with various fine contents and notch offset distance from the center of the specimen to investigate the fracture characteristic of the frozen sand. Based on the test results, mode I fracture toughness was calculated, and mixed-mode (mode I + II) fracture characteristics were investigated using the fracture energy which was calculated until the maximum point of the load-displacement curve. As the fine contents increase, the peak load and mode I fracture toughness increase until 10% fine contents. Furthermore, as the notch offset distance increases, the fracture energy required for crack start also increases due to the increase in mode II load at the crack tip.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.6
• /
• pp.1836-1842
• /
• 1996

In this paper, static and fatigue bending strengths of CFRP(carbon fiber reinforced plastic laminates having impact damage(FOD) are evaluated. Composite laminates used for this experiment are CF/EPOXY and CF/PEEK orthotropy laminated plates, which have two-interfaces[${0^0}_4{90^0}_4}$]$_sym$. A steel ball launched by the air gun colides against CFRP laminates to generate impact damages. The damage growth during bending fatigue test is observed by the scanning acoustic microscope(SAM). When the impacted side is compressed, the residual fatigue bending strength of CF/PEEK specimen P is greater that that of CF/EPOXY SPECIMEN B. On the other hand, when the impacted side is in tension, the residual fatigue bending strength of CF/PEEK speicemen P is smaller than that of CF/EPOXY specimen B. In the case of impacted-side compression, fracture is proposed from the transverse crack generated near impact point. On the other hand, fracture is developed toward the impact point from the edge of interface-b delamination in the case of impacted-side tension.

• Composites Research
• /
• v.30 no.3
• /
• pp.188-192
• /
• 2017

The mechanical properties of composites are significantly affected by external environment. It is essential to understand the degradation of material performance and judge the material's lifetime in advance. In the current research, changes in mechanical properties of glass fiber and unsaturated polyester composite materials (GFRP, Glass fiber reinforced plastic) were investigated under different bending stress and submerged in hot water at a temperature of $80^{\circ}C$. Loading time of 100 H (hours), 200 H, 400 H, 600 H, 800 H for testing under stresses equal to 0% (stress-free state), 30%, 50% and 70% of the ultimate strength was applied on the GFRP specimens. From the values of bending stress, obtained from three-point bending test, fracture energy, failure time, and life curve were analysed. Moreover, a normalized strength degradation model for this condition was also developed. It was observed that within 100 H, the decline rate of the bending strength was proportional to the pressure.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.10 no.1
• /
• pp.65-72
• /
• 1990

Comparison of acoustic emission, ultrasonic testing and crack gauge in 3-point bending testing have been studied. As the results, COD is indirectly assumed by strain gauge rate and grid pitch width when crack gauge grid is out. Acoustic emission is qualitatively able to measure crack growth by total count but ultrasonic testing has a difficulty in measuring it because of echo height fluctuation according to the change and pressure of UT. probe.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.3 no.1
• /
• pp.176-182
• /
• 2000

$360^{\circ}$ bending of Ti-6Al-4V large-diameter seamless tube(62.37 mm $OD {\times} 4.40mm$ wall thickness) has been achieved at room temperature without heating. The bending process comprised two steps : the first step is $360^{\circ}$ bending by an uniquely designed rotary bender allowing spring back, which is subsequently eliminated by the second or finishing step which comprised repeated bending processes by powered three roll bender, In odor to prevent collapse of tube during bending, Cerro $Tru^{TM}$(Trade name of a non-ferrous low melting point alloy)has been employed as a filler metal. The resultant ovality(out of roundness) obtained was 1.28%, as compared with 6~8% without applying Cerro $Tru^{TM}$.

• Journal of the Korean Society for Precision Engineering
• /
• v.17 no.5
• /
• pp.131-136
• /
• 2000

This paper is concerned with the surface roughness and the bending strength of ground workpiece in ZrO2 ceramic grinding. Surface roughness was measured with surface tracer and bending strength value was obtained by three-point bending test on machining center using tool dynamometer. Grinding experiments were carried out to examine the effects of grinding conditions including diamond mesh size, table speed, and depth of cut on ground surface roughness. The correlation between surface roughness and bending strength was also inspected. The experimental results indicate that the rougher surface is produced as the mesh size of diamond wheel is reduced and table speed is increased, but surface roughness is not affected by depth of cut. The values of bending strength decrease as the values of Ra, Rmax and Ku increase.