• Transactions on Electrical and Electronic Materials
• /
• v.8 no.6
• /
• pp.241-245
• /
• 2007

[ $(Ba_{0.9-x}Sr_xCa_{0.10})TiO_3$ ] (x=0.33, 0.36) powders were prepared by sol-gel method. $(Ba,Sr,Ca)TiO_3$(BSCT) thick films, undoped and doped with $MnCO_3$ and $Yb_2O_3(0.1{\sim}0.7mol%)$, were fabricated by the screen printing method on the alumina substrate. The coating and drying procedure was repeated 6-times. The Pt bottom electrode was screen printing method on the alumina substrate. These BSCT thick films were annealed at $1420^{\circ}C$ for 2 hr in atmosphere. The upper electrodes were fabricated by screen printing the Ag paste and then firing at $590^{\circ}C$ for 10 min. And then the structured and dielectric properties as a function of the doping amount of $Yb_2O_3$ were studied. As a result of the TG-DTA, exothermic peak was observed at around $670^{\circ}C$ due to the formation of the polycrystalline perovskite phase. All BSCT thick films showed XRD patterns of typical cubic peroveskite structure. The average thickness of BSCT thick films was about $70^{\mu}m$. The curie temperature and the dielectric constant decreased with increasing $Yb_2O_3$ doped content and the relative dielectric constant of the specimen, doped with 0.5 mol% $Yb_2O_3$ at BSCT(54/36/10), showed a best value of 5018 at curie temperature.

• Korean Journal of Materials Research
• /
• v.15 no.12
• /
• pp.756-759
• /
• 2005

A lead free piezoelectric material, bismuth sodium barium titanate $(Bi_{0.5}Na_{0.5})_{0.94}Ba_{0.06}TiO_3$ (BNBT), was considered as an environment-friendly alternatives for the current PZT system. A perovskite BNBT was synthesized by conventional bulk ceramic processing technique. In order to improve piezoelectric properties, $La_2O_3$ as a dopant was incorporated into the BNBT system up to 0.025 moi, ana the effects on subsequent the piezoelectric ana dielectric properties were systematically investigated. With increasing $La_2O_3$ contents, the equilibrium grain shape was remarkably evidenced and sintered density was increased. Piezoelectric and dielectric properties were s]town to have maximum values at the $La_2O_3$ contents of 0.02 mol. $La^{3+}$ ions seemed to act as a softener in the BNBT system and to enhance dielectric and piezoelectric properties in this study.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.377-380
• /
• 2001

The BST thin films to composite (Ba$\sub$x/Sr$\sub$l-x/)TiO$_3$ using sol-gel method were fabricated on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric materials was investigated by structural and electrical properties. BST solution was composited by moi ratio, and then spin-coated (from 3 times to 5 times coating on Pt/SiO$_2$/Si substrate. Thickness of BST ceramics thin films are about 2600∼2800[${\AA}$] in 3 times deposition. The property of leakage current was stable when the applied voltage was 3[V]. Leakage current of 3 times coated BST thin film was 10$\^$-9/∼10$\^$-11/[A] at 0∼3[V].

• Electrical & Electronic Materials
• /
• v.9 no.5
• /
• pp.439-444
• /
• 1996

0.15(B $a_{0.95}$ S $r_{0.05}$)O-0.15(S $m_{2(1-x}$/N $d_{2x}$) $O_{3}$-0.7Ti $O_{2}$(x=0-10[m/o]) ceramics were fabricated by mixed oxide method. Microwave dielectric properties were investigated with contents of N $d_{2}$ $O_{3}$. In the case of specimen with N $d_{2}$ $O_{3}$(6[m/o]), dielectric constant, quality factor and temperature coefficient of resonant frequency were 78.14, 2938(at 3[GHz]) and +14.19[ppm/.deg. C], respectively. By comparison its properties with undoped specimen, dielectric constant and quality factor were highly improved, but the temperature coefficient of resonant frequency was increased to positive value......

• Journal of Fisheries and Marine Sciences Education
• /
• v.19 no.1
• /
• pp.1-7
• /
• 2007

The purpose of this study was to investigate geochemical characteristics of surface sediments in the Keum river estuary adjacent to coastal area. For this study we collected the 21 surface sediments samples. Mean size of surface samples was $3.24{\sim}6.65{\phi}$ on inner estuary and was $2.15{\sim}3.42{\phi}$ on outside estuary. Surface samples were composed of silt on inner estuary and were composed of sand which was more larger than $4{\phi}$ on outside estuary. Most major elements except CaO, $Na_2O$ showed good relationships between variation of contents and grain size. Contents of $Al_2O_3$, $Fe_2O_3$, MgO, $K_2O$, $TiO_2$, $P_2O_5$ and $M_nO$ were increased predominately owing to the variation of mean size of surface samples. Contents of Co, Cr, Cu, Li, Sr, Zn, La, Ce, Pb, Rb, Nd have a good relationships with grain size but Ba, Th, Sm have not. All of major and minor elements contents except $K_2O$ and Ba were less than world mean contents of shallow surface sediments but apprehend a high pollution possibility on silt sediments in the estuaries.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.1
• /
• pp.20-25
• /
• 2001

To develop the piezoelectric actuator, the structural, dielectric and piezoelectric properties and electric fieldinduced strain of the ceramics(Pb$\_$1-2/Ba$\_$x/)[Mg$\_$1/2/W$\_$1/2/)$\_$0.03/-Ni$\_$1/3/Nb$\_$2/3/)$\_$0.12/-(Zr$\_$0.5/Ti$\_$0.5/)$\_$0.85/]O$_3$(x=0, 0.01, 0.03, 0.05, 0.07, 0.1) were investigated with the substitution of Ba. The tetragonality of crystal structure and grain size decreased by the substitution of Ba. Curie temperature decreased due to the decrease of the tetragonality, and dielectric constants increased with the substitution of Ba. The coercive field, remnant polarization and electromechanical coupling factor also decreased, whereas the piezoelectric constatns d$\_$33/ and d$\_$31/ were showed the highest value of 430 and 209(x10$\^$-12/C/N), respectively, because of the increase of dielectric constant. The strain induced by 60Hz AC electric field had the maximum value of 204x10$\^$-6/Δℓ/ℓ at the substitution of Ba 3mol%. As the applied electric field approaches to the coercive field, the piezoelectric element is depolarized and the electric field induced strain revealed non-linearity.

• Proceedings of the KIEE Conference
• /
• 1996.07c
• /
• pp.1621-1623
• /
• 1996

The dielectric and polarizable properties of 0.85Pb$Mg_{1/3}Nb_{2/3}$)$O_3$-$0.125PbTiO_3$-$0.25BaTiO_3$ Ceramics have been investigated as a addition of the amount of $La_{2}O_{3}$($0{\leq}x{\geq}0.05$). The Temperature-dependant electrostictive characteristics of 0.85PMN-0.125PT-0.25BT relaxor ferroelectic system were improved by enhencing the extent of the diffuse phase transition(DPT). This was achieved using PMN-PT-BTceramics by the partial substitution of La at the Pb site. The curie temperature and the maximum dielectic permittivity decreased by substituting $La_{2}O_{3}$ and the electic field-related hysteresis phenomena decreased with increasing $La_{2}O_{3}$ substitution amount. It is showed decreasing in induced strain for electric field with increasing $La_{2}O_{3}$ substitution.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.410-411
• /
• 2009

The multi-component ceramic proton conductor, $BaZr(Y)O_3-SiO_2-TiO_2-ZrO_2$ (BZY-STZ) and $LaPO_4-SiO_2-TiO_2-ZrO_2$ (LP-STZ), were synthesized by micro-emersion and sol-gel technique. The characterization of proton conductors were carried out using X-ray diffraction(XRD), thermogravimetric analysis(TGA), differential thermal analysis(DTA), impedance analysis. The proton conductors indicate the possibility of application for the intermediate temperature up to $700^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.34 no.3
• /
• pp.323-329
• /
• 1997

Particle growth of BT-oxalate was investigated in aging with various additives such as glycerine, chloro-form and NaCl. Their effects on size and morphlogy of particle was examined. It can be known that particle size distributions of BT-oxalate precipitate varied with amounts of these additivies. With small amounts of these additives, particle growth of nonuniform distribution was occurred, but above 1 mole percent of those additives, uniform size distributions of about 0.4 ${\mu}{\textrm}{m}$ could be obtain. There was little difference among the effects by the kinds of additives. From the decomposition of uniform BT-oxalate, BaTiO3 powders of about 0.3${\mu}{\textrm}{m}$ could be obtained.

• Smart Structures and Systems
• /
• v.22 no.3
• /
• pp.259-276
• /
• 2018

This paper studies the energies and energy release rate (ERR) for the initially rotationally symmetric compressed (or stretched) in the inward (outward) radial direction of the PZT/Elastic/PZT sandwich circular plate with interface penny-shaped cracks. The investigations are made by utilizing the so-called three-dimensional linearized field equations and relations of electro-elasticity for piezoelectric materials. The quantities related to the initial stress state are determined within the scope of the classical linear theory of piezoelectricity. Mathematical formulation of the corresponding problem and determination of the quantities related to the stress-strain state which appear as a result of the action of the uniformly normal additional opening forces acting on the penny-shaped crack's edges are made within the scope of the aforementioned three-dimensional linearized field equations solution which is obtained with the use of the FEM modelling. Numerical results of the energies and ERR and the influence of the problem parameters on these quantities are presented and discussed for the PZT- 5H/Al/PZT-5H, PZT-4/Al/PZT-4, $BaTiO_3/Al/BaTiO_3$ and PZT-5H/StPZT-5H sandwich plates. In particular, it is established that the magnitude of the influence of the piezoelectricity and initial loading on the ERR increases with crack radius length.