• Proceedings of the Materials Research Society of Korea Conference
• /
• 1997.05a
• /
• pp.49-49
• /
• 1997

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1997.05a
• /
• pp.50-50
• /
• 1997

• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.816-819
• /
• 1995

(Ba$_{1-x}$ , Sr$_{x}$)TiO/$_3$thin films on Pt/Ti/SiO$_2$/Si substrates were prepared by LP MOCVD(Low Pressure Metal-Organic Chemical Vapor Deposition). The crystalinity of BST deposit had a (100) preferred orientation with increasing deposition temperature due to surface diffusion. BST films deposited at 90$0^{\circ}C$ showed a dielectric constant of 365 and a dissipation factor of 0.052 at a frequency of 100kHz. The chance of capacitance of the films with applied voltage was small, showing paraelectric properties. BST film deposited at 90$0^{\circ}C$ had a charge storage density of 60 fc/${\mu}{\textrm}{m}$$^2$at a field of 0.2MV/cm and the leakage current density of 20 nA/$\textrm{cm}^2$ at a field of 0.15 MV/cm.cm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.866-869
• /
• 2001

In this study, (Ba,Sr)TiO$_3$(BST) thin films were etched with a magnetically enhanced inductively coupled plasma(MEICP). Etching characteristics of BST thin films including etch rate and selectivity were evaluated as a function of the etching parameters such as gas mixing ratio, rf power, dc bias voltage and chamber pressure. The maximum etch rate of the BST films was 1700 $\AA$/min at Ar(90)/CF$_4$(10), 600 W/350 V and 5 mTorr. The selectivity of BST to PR was 0.6, 0.7, respectively. To analyze the composition of surface residue remaining after the etching, samples etched with different CF$_4$/Ar gas mixing ratio were investigated with X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectrometry (SIMS). From the results of XPS and SIMS, there are chemical reaction between Ba, Sr, Ti and C, F radicals during the etching and remained on the surface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.834-837
• /
• 2004

BST thin films were etched with inductively coupled $CF_4(C1_2+Ar)$ Plasmas. The maximum etch rate of the BST thin films was 53.6 nm/min for a 10 % $CF_4$ to the $Cl_2/Ar$ gas mixture at RF power of 700 W, DC bias of -150 V, and chamber pressure of 2 Pa. Small addition of $CF_4$ to the $Cl_2/Ar$ mixture increased chemical effect. Consequently, the increased chemical effect caused the increase in the etch rate of the BST thin films. To clarify the etching mechanism, the surface reaction of the BST thin films was investigated by X-ray photoelectron spectroscopy.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.73-76
• /
• 2001

We deposited epitaxial $Ba_{0.6}Sr_{0.4}TiO_{3}(BST)$ films having thickness of 400 nm on MgO(001) substrates, where a 10 nm thick $Ba_{1-x}Sr_{x}TiO_{3}$ (x = 0.1 - 0.7) interlayer was inserted between BST and MgO to manipulate the stress of the BST films. Since the main difference of those epitaxial BST films was the lattice constant of the interlayers, we were very successful in controlling the stress of the BST films. BST films under small tensile stress showed larger dielectric constant than that without stress as well as those under compressive stress. Stress relaxation was investigated using epitaxial BST films with various thicknesses grown on different interlayers. For BST films grown on $Ba_{0.7}Sr_{0.3}TiO_{3}$ interlayers, the critical thickness was about 600 nm. On the other hand, the critical thickness of single-layer BST film was less than 100 nm.

• Proceedings of the KIEE Conference
• /
• 2004.07c
• /
• pp.1621-1623
• /
• 2004

The $Pb(Zr_{0.52}Ti_{0.48})O_3/(Ba_{0.6}Sr_{0.4})TiO_3$ [PZT(52/48)/BST(60/40)] heterolayered thin films were deposited on Pt/Ti/$SiO_2$/Si substrates by using the RF sputtering method with RF powers of 60,70,80,90[W]. All thin films showed the peaks of the tetragonal phase. Increasing the RF power, dielectric constant and loss of the PZT(52/48)/BST(60/40)] heterolayered thin films were decreased. The thickness ratio of PZT and BST thin films was 1/1. The relative dielectric constant and the dielectric loss of the PZT(52/48)/ BST(60/40) heterolayered thin films were 562 and 13%, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.377-380
• /
• 2001

The BST thin films to composite (Ba$\sub$x/Sr$\sub$l-x/)TiO$_3$ using sol-gel method were fabricated on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric materials was investigated by structural and electrical properties. BST solution was composited by moi ratio, and then spin-coated (from 3 times to 5 times coating on Pt/SiO$_2$/Si substrate. Thickness of BST ceramics thin films are about 2600∼2800[${\AA}$] in 3 times deposition. The property of leakage current was stable when the applied voltage was 3[V]. Leakage current of 3 times coated BST thin film was 10$\^$-9/∼10$\^$-11/[A] at 0∼3[V].

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.04b
• /
• pp.22-25
• /
• 2004

In this study, BST thin films were etched with inductively coupled $CF_4/(Cl_2+Ar)$ plasmas. The etch characteristics of BST thin films as a function of $CF_4/(Cl_2+Ar)$ gas mixtures were analyzed using quadrupole mass spectrometry (QMS) and optical emission spectroscopy (OES). The maximum etch rate of the BST thin films was 53.6 nm/min because small addition of $CF_4$ to the $Cl_2/Ar$ mixture increased chemical effect. The optimum condition appears to be under a 10 % $CF_4/(Cl_2+Ar)$ gas mixture in the present work.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.43-46
• /
• 2000

In this study, (Ba, Sr)$TiO_3$ (BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/$TiO_2$/Si substrate at 4000 [rpm] for 10 seconds. Coated specimens were dried at 150[$^{\circ}C$] for 5 minutes. Coating process was repeated 3 times and then sintered at 750[$^{\circ}C$] for 30 minutes. Structure and electrical characteristics of specimen was analyzed by Fractal Process. Thickness of BST ceramics thin films are about 2800[$\AA$]. Dielectric constant and loss of thin films was little decreased at 1[kHz]~1[MHz]. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. The property of leakage current as the relation between the current and the voltage was that change of the leakage current was stable when the applied voltage was 0~3[V].