• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.402-405
• /
• 2001

(Ba$\_$0.6-x/Sr$\_$0.4/Ca$\_$x/)TiO$_3$(x=0.10, 0.15, 0.20) ceramics were fabricated by the mixed-oxide method and their structural and dielectric properties were investigated with variation of composition ratio and an amount of Al$_2$O$_3$(0.5, 1.0, 1.5, 2.0, 3.0 wt%) doping content. As a result of the X-ray diffraction BSCT specimens showed dense and homogeneous structure without presence of the second phase. The sintered density was decreased with increase an Al$_2$O$_3$ doping content. The Curie temperature and relative dielectric constant at room temperature were decreased with increasing an amount of Al$_2$O$_3$ doping content. The dielectric loss is minimum for BSCT doped with 1.5wt% Al$_2$O$_3$ content. The tunability was decreased with increasing an Ca content and is about 4.2% for BSCT(50/40/10) doped with 2.0wt% Al$_2$O$_3$ content.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.42-45
• /
• 2001

$(Ba_{0.6}Sr_{0.4}Ca_{x})TiO_{3}+yZrO_{2}$ wt% (x=0.10, 0.15, 0.20, y=0.5~3.0) specimens were fabricated by the mixed-oxide method and then the structural and dielectric properties as a function of the composition ratio and $ZrO_2$ contents were studied. All BSCT specimens showed dense and homogeneous structure without the presence of the seconds phase. The Curie temperature and the dielectric constant at room temperature decreased with increasing the Ca/Ba composition ratio and $ZrO_2$ content. The BSCT(50/40/10) specimens showed the excellent tunability property. And the tunability were increased with increasing the contents of $ZrO_2$.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2007년도 제38회 하계학술대회
• /
• pp.1275-1276
• /
• 2007

For fabrication of $BaTiO_3$ system Ferroelectric thick films, (Ba,Sr,Ca)$TiO_3$ (BSCT) powders, prepared by using the alkoxide-based sol-gel method, were doped $MnCO_3$ as acceptor and $Dy_{2}O_{3}$ as donor. $MnCO_3$ and $Dy_{2}O_{3}$-doped (Ba,Sr,Ca)$TiO_3$ thick films were fabricated by screen printing techniques on high purity alumina substrates. The structure and dielectric properties were investigated with variation of $Dy_{2}O_{3}$ amount. As a result of the differential thermal analysis(DTA), exothermic peak was observed at around $670^{\circ}C$ due to the formation of the polycrystalline perovskite phase. All the BSCT thick films, sintered at $1420^{\circ}C$ for 2h, showed the typical XRD patterns of perovskite polycrystalline structure and no pyrochlore phase was observed. The average grain size and thickness of specimens no doped with $Dy_{2}O_{3}$ was 1.32mm, 52mm, respectively. The relative dielectric constant decreased and dielectric loss increased with increasing amount of $Dy_{2}O_{3}$ dopant, the values of the BSCT thick films no doped with $Dy_{2}O_{3}$ were 4043 and 0.4% at 1 kHz, respectively. The relative dielectric constant gradually decreased in the measured frequency range from 0.1 to 100 kHz

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 추계학술대회 논문집
• /
• pp.33-36
• /
• 1998

BST(66/34) and BSCT(60/30/10) ceramics were prepared by mixed oxide method and studied about the microstructural and dielectric properties with $Y_2$O$_3$, Dy$_2$O$_3$, La$_2$O$_3$, MnCO$_3$. The grain size of undoped BST was 20~30 ${\mu}{\textrm}{m}$, but that of BST, doped content of MnCO$_3$ was 0.1 mol%, was decreased with increasing the contents of $Y_2$O$_3$. As the content of $Y_2$O$_3$ was Increased, Tc was shifted to lower temperature and dielectric constant at Tc was decreased. The dielectric constant of doped BSCT(60/30/10) ceramics ( 0.9 mol% $Y_2$O$_3$. and 0.1 mol% MnCO$_3$) was about 8, 000 at Tc( 22$^{\circ}C$ ).

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2001년도 하계학술대회 논문집 C
• /
• pp.1493-1495
• /
• 2001

$(Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3+yAl_2O_3$ wt% (x=0.10, 0.15, 0.20, y=0.5 $\sim$ 3.0) specimens were fabricated by the mixed-oxide method and then the structural properties as a function of the composition ratio and $Al_2O_3$ contents were studied. All BSCT specimens showed dense and homogeneous structure without the presence of the seconds phase. The sintered density was decreased with increase ad $Al_2O_3$ content. The Curie temperature and dielectric constant at room temperature decreased with increasing $Al_2O_3$ content. The dielectric constant and dielectric loss of the doped-0.5 wt% $Al_2O_3$ BSCT(50/40/10) specimen were about 3131 and 0.932% at 1KHz, respectively.