• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.450-455
• /
• 2002

Cu-cored Sn-Ag solder balls were fabricated by coating pure Sn and Ag on Cu balls. The melting behavior and the solderability of the BGA joint with the Ni/Au coated Cu pad were investigated and were compared with those of the commercial Sn-Ag and Sn-Ag-Cu balls. DSC analyses clarified the melting of Cu-cored solders to start at a rather low temperature, the eutectic temperature of Sn-Ag-Cu. It was ascribed to the diffusion of Cu and Ag into Sn plating during the heating process. After reflow soldering the microstructures of the solder and of the interfacial layer between the solder and the Cu pad were analyzed with SEM and EPMA. By EDX analysis, formation of a eutectic microstructure composing of $\beta$-Sn, Ag$_3$Sn, ad Cu$_{6}$Sn$_{5}$ phases was confirmed in the solder, and the η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer was found to form at the interface between the solder and the Cu pad. By conducting shear tests, it was found that the BGA joint using Cu-cored solder ball could prevent the degradation of joint strength during aging at 423K because of the slower growth me of η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer formed at the solder, pad interface. Furthermore, Cu-cored multi-component Sn-Ag-Bi balls were fabricated by sequentially coating the binary Sn-Ag and Sn-Bi solders on Cu balls. The reflow property of these solder balls was investigated. Melting of these solder balls was clarified to start at the almost same temperature as that of Sn-2Ag-0.75Cu-3Bi solder. A microstructure composing of (Sn), Ag$_3$Sn, Bi and Cu$_{6}$Sn$_{5}$ phases was found to form in the solder ball, and a reaction layer containing primarily η'-(Au, Co, Cu, Ni)$_{6}$Sn$_{5}$ was found at the interface with Ni/Au coated Cu pad after reflow soldering. By conducting shear test, it was found that the BGA joints using this Cu-core solder balls hardly degraded their joint shear strength during aging at 423K due to the slower growth rate of the η'-(Au, Cu, Ni)$_{6}$Sn$_{5}$ reaction layer at the solder/pad interface.he solder/pad interface.

• Journal of the Institute of Electronics Engineers of Korea SD
• /
• v.38 no.4
• /
• pp.243-250
• /
• 2001

This paper presents the structure of a $\mu$Spring package, its fabrication process and an analysis of its electrical characteristics compared to that of a $\mu$BGA. It was found that both $\mu$BGA and $\mu$Spring packages provide with outstanding high speed signal transmission characteristics due to their lower inductance of package interconnection lines, smaller than half of inductance of TSOP package lines. Even the worst case substrate trace of a Rambus DRAM $\mu$Spring package yields the line inductance of 2.9nH, which provides with 25% margin compared to the Rambus DRAM specification of 4nH. The fabrication cost of $\mu$Spring package is lower than that of $\mu$BGA by 50%, passes 1000 thermal cycles, meets JEDEC Level 1 specification whereas $\mu$BGA does not, and thereby yields high reliability and strong competing power.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.2
• /
• pp.39-43
• /
• 2002

The eutectic solder Sn-37Pb and the lead free solder alloys with the compositions of Sn-0.7Cu, Sn-3.5Ag, Sn-3.5Ag-0.75Cu, Sn-2.0Ag-0.7Cu-3.0Bi were applied to the 48 BGA packages, and then it was discussed for the shear strength at the solder joints as the hardness and the composition of the small solder ball. As a result of experiments, the high degree of hardness with the displacement of 0.043 mm was obtained in Sn-2.0Ag-0.7Cu-3.0Bi. The shear strength of the lead free solder was higher than that of Sn-37Pb solder, and it can be obtained the maximum value of about 52% in Sn-2.0Ag-0.7Cu-3.0Bi.

• Korean Journal of Materials Research
• /
• v.21 no.12
• /
• pp.650-654
• /
• 2011

In this paper, the effects of conventional and newly developed elastomer modified underfill materials on the mechanical shock reliability of BGA board assembly were studied for application in mobile electronics. The mechanical shock reliability was evaluated through a three point dynamic bending test proposed by Motorola. The thermal properties of the underfills were measured by a DSC machine. Through the DSC results, the curing condition of the underfills was selected. Two types of underfills showed similar curing behavior. During the dynamic bending reliability test, the strain of the PCB was step increased from 0.2% to 1.5% until the failure circuit was detected at a 50 kHz sampling rate. The dynamic bending reliability of BGA board assembly using elastomer modified underfill was found to be superior to that of conventional underfill. From mechanical and microstructure analyses, the disturbance of crack propagation by the presence of submicron elastomer particles was considered to be mainly responsible for that result rather than the shear strength or elastic modulus of underfill joint.

• Proceedings of the KWS Conference
• /
• 2003.11a
• /
• pp.86-88
• /
• 2003

The characteristic of induction heating solder bump(solder ball: Sn-37Pb, Sn-3.5Ag, Sn-3.0Ag-0.5Cu) has analyzed in this paper. The initial condition of induction heating depends on the time and current. The shape of lead-free solder bump is better than lead solder. The shear strength of lead solder bump has decreased with aging time. The average of shear strength of solder bump is about 10N, 11N, and 11N respectively. The lead-free solder bump's shear strength is better than lead solder and varies irregularly with aging time.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.463-468
• /
• 2002

This study investigates the variations of shear force, displacement, and fracture surface with the shear speed and the number of reflows. The experimental data of shear tests indicate that the shear force increases as increasing the number of reflows and the shear speed due to the formation of a kind of intermetallic compound, Ni$_3$Sn$_4$, on Au/Ni/Cu pad, and the work-hardening. However, general trends show that the shear force decreases due to increasing the thickness of the intermetallic compound over 4x reflow. It is observed that the intermetallic compound which is formed between solder and pad increases according to increasing the number of reflows, and the growth rate of the intermetallic compound at central region on the interface is faster than one at edge part. The general tendencies of shear force and displacement with different shear speeds are almost identical as an increase of the number of reflows.

• Proceedings of the KSME Conference
• /
• 2003.11a
• /
• pp.1027-1032
• /
• 2003

Thermo-mechanical behavior of flip-chip plastic ball grid array (FC-PBGA) packages are characterized by high sensitive $Moir{\acute{e}}$ interferometry. $Moir{\acute{e}}$ fringe patterns are recorded and analyzed for several temperatures. Deformation analysis of bending displacements of the packages and average strains in the solder balls for a single-sided package assembly and a double-sided package assembly are presented. The bending displacement of the double-sided package assembly is smaller than that of the single-sided one. The largest of effective strain occurred in the solder ball located at the edge of the chip and its magnitude of the double-sided package assembly is greater than that of single-sided one.

• Proceedings of the KWS Conference
• /
• 2005.11a
• /
• pp.231-233
• /
• 2005

Laser have been utilized as a heat source for the soldering of electronic components for the their capability of localized heating and faster heating rate. Laser soldering process, especially the diode laser soldering of BGA solderball was investigated. In this study, an attempt was made to investigate the possibility of laser soldering using Sn-37Pb and Sn-3Ag-0.5Cu solderball. The laser energy absorbed on the pad raised the temperature of the solderball forming a reflowed solder bump. The result were discussed based on the measurement of pull and shear strength of the bond.

• Journal of the Microelectronics and Packaging Society
• /
• v.2 no.1
• /
• pp.59-68
• /
• 1995

박막제조 기술 및 BGA패캐지를 이용하여 Wellcom 2000 system 소요 OCU Board 의 집적화를 구현하였다. 기존 PCB에 실장되는 소자 일부를 2 Channel BGA 패캐지로 모 듈화한 결과 약 1/6로 소형화시킬수 있었으며 8 Channel의 모율화는 현재 진행중인 다층 구조의 제조 기술 개발과 아울러 BGA 패캐지로 실현이 가능하며 1/10로집접화할수 있음을 알수 있었다. 또한 PCB위에 Bare Chip을 실장하여 Wire Bonding 한 COB를 구현하여 CBGGA의 PCB실장과 함께한 모듈을 형성해 보았다. CBGA패캐지에 Ball Shear Test, In Circuit Test 온도 환경주기시험(TCT) 진동시험을 통하여 신뢰성을 입증하였다. 이때 CBGA의 Coplanarity(3.2%) 증진을 위하여 Ceramic Pad에 선택적인 도금 방식을 개발적용 하였다.

• Journal of Welding and Joining
• /
• v.17 no.3
• /
• pp.90-95
• /
• 1999

The increase in high speed, multi-function and high I/O pin semiconductor devices highly demands high pin count, very thin, and high density packages. BGA is one of the solutions, but the package has demerits in package reliability, surface mounting problems due to the PCB warpage and solder joint crack related with TCE mismatch between the materials. On this study to verify the thermal fatigue lifetime of the solder joint FEM and experiments were performed after surface mounting BGA with different solder composition and reliability conditions. FEM showed optimum composition of Ag3.2-Sn96.5 and under the composition minimum creep deformation of the solder joint was calculated, and the thermal fatigue lifetime was improved. In view of temperature cycle condition, the conditions of $-65^{\circ}C$to $150^{\circ}C$ showed minimum lifetime and t was 1/3 of $0^{\circ}C$ to $125^{\circ}C$ condition. Test board was prepared and solder joint crack was verified. Until 1000cycle on soder joint crack was observed.