• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 가을 학술발표회 논문집
• /
• pp.417-420
• /
• 2003

Concrete with low water to binder ratio (W/B) is prone to large autogenous shrinkage. Early age cracking of concrete would be caused by tensile stress induced by large autogenous shrinkage under restrained condition. Therefore, it is necessary to measure autogenous shrinkage to control the early age cracking of concrete. An objective of this study is to investigate the effects of W/B and blast furnace slag (BFS) on autogenous shrinkage of concrete. Autogenous shrinkage of concrete with various W/B ranging from 0.42 to 0.27 and BFS contents of 0, 30 and 50% were measured. Test results show that the autogenous shrinkage of concrete increases as the W/B decreases, and all BFS concretes showed larger autogenous shrinkage than OPC concretes with the same W/B. Moreover, the higher BFS content, the larger autogenous shrinkage.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 추계 학술발표회 제20권2호
• /
• pp.915-918
• /
• 2008

수화열 및 자기수축은 동일한 수화반응에 의해 필연적으로 발생되는 현상으로서 여러 연구자들에의해 수화온도와 자기수축의 깊은 상관성은 언급되어 왔으나, 아직까지 수화온도와 자기수축의 구체적인 관계에 대한 연구보고는 거의 없는 실정이다. 이에 본 연구에서는 시험체의 단면크기를 달리하여 초기 수화발열 및 자기수축의 특성을 구체적으로 분석한 후, 내부 수화온도와 자기수축의 상관성을 검토하였다. 그 결과, 시험체 단면이 증가할수록 전체적인 내부온도와 자기수축은 증가하였으며, 수화발열상승구간 및 자기수축증가구간에서 발생하는 수화온도 상승량 및 상승률, 자기수축 증가량 및 증가율은 증가하였다. 수화발열상승속도 및 자기수축증가속도가 증가할수록 구간에서 발생하는 수화온도상승량과 자기수축증가량은 증가한 반면, 수화온도상승률과 자기수축증가율은 유사하게 나타났으며, 수화발열상승 속도가 증가할수록 자기수축증가구간의 자기수축증가량과 자기수축증가속도는 증가하였다.

• 한국구조물진단유지관리공학회 논문집
• /
• 제10권3호
• /
• pp.97-105
• /
• 2006

고성능 콘크리트의 자기수축은 초기균열을 유도할 수 있기 때문에 내구성 측면에서 매우 중요하다. 이에 따라, 본 연구에서는 실험을 통해 혼화재료를 혼입한 고성능 콘크리트의 자기수축 특성을 분석한 후 예측모델을 제안하였다. 이를 위해 다양한 실험변수를 가진 시편에 대해 광범위한 실험을 수행하였다. 주요 실험변수는 혼화재료의 종류 및 혼입률로 설정하였으며 물-시멘트비는 30%로 고정하였다. 실험결과 플라이애시를 치환한 경우에는 자기수축량이 다소 감소하였으며, 고로슬래그를 사용한 경우에는 자기수축이 증가하였다. 또한, 수축저감제 및 팽창재의 혼입량이 클수록 고성능 콘크리트의 자기수축은 감소하는 경향을 보였다. 한편, 본 논문에서는 회귀분석을 통해 혼화재료를 사용한 고성능 콘크리트의 자기수축 예측식을 제안하였으며, 제안된 자기수축 예측식은 실험결과와 비교적 일치하였다

• 콘크리트학회논문집
• /
• 제17권5호
• /
• pp.853-856
• /
• 2005

A low water/cement ratio leads to autogenous shrinkage of cement paste at an early age. This autogenous shrinkage is related to the change of relative humidity in the pore structure that is formed during the hydration process. The relationship between autogenous shrinkage and relative humidity change are relatively well defined today, but the effects of temperature on autogenous shrinkage, relative humidity, and pore structures have been studied less systematically. This study focused on correlating alterations of these properties of cement paste hydrated at constant temperatures of 20, 40, and $60^{\circ}C$. The test results clearly indicate that increasing curing temperature resulted in increased porosity, particularly for pores between 5 to 50 nm as measured by MIP, and increased autogenous shrinkages, as a consequence of a reduction of relative humidity at early ages.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 봄 학술발표회 논문집
• /
• pp.95-100
• /
• 2003

The shrinkage of high strength/high performance concrete is very important property for the good working of a structure since it very often generates early age cracking due to thermal and autogenous shrinkage. Autogenous shrinkage occurs as a result of internal moisture depletion due to hydration and temperature-induced effects. The level of autogenous shrinkage occurring due to hydration also depends on temperature history at very early age. It is necessary that effect of temperature on autogenous shrinkage is investigated since the stress generated due to autogenous shrinkage is quantified. In this study, Effect of hydration heat evolution on autogenous shrinkage of high strength concretes with W/C=25-40% was investigated.

• 한국건축시공학회지
• /
• 제11권6호
• /
• pp.538-546
• /
• 2011

This paper is to experimentally investigate the strength and autogenous shrinkage of high strength mortar with the 20 % of water?binder ratio(W/B). In this study, the water substituting liquid(WSL) was used including gasoline, light oil, lamp oil, edible oil, HFE, ethanol, methanol and acetone in order to explore changes in strength and autogenous shrinkage depending on WSL type and replacement. For fresh properties, the replacement of WSL did not affect the fluidity of mortar mixtures considerably, except for ethanol and methanol. However, the replacement of WSL resulted in a slight decrease in flexural and compressive strength. For autogenous shrinkage, the replacement of WSL led to reduce autogenous shrinkage, and especially, the replacement of edible oil led to reduce autogenous shrinkage significantly due to saponification between edible oil and cement.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 봄 학술발표회 논문집
• /
• pp.101-106
• /
• 2003

This study is to capture autogenous shrinkage in reinforced concrete. The experiment was carried out on total 13 beams. The experiment parameters are a method of curing and reinforcement ratio. Autogenous shrinkage in reinforced concrete beam was experimentally measured. Also, the distribution of autogenous shrinkage and self stress on cross section in reinforced concrete beams were calculated. The experimental results showed that autogenous shrinkage of high strength concrete were significantly higher than that of nomal strength concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2002년도 가을 학술발표회 논문집
• /
• pp.385-390
• /
• 2002

Autogenous shrinkage of concrete has been defined as decrease in volume due to hydration cement, not due to other causes such as evaporation, temperature change and external load and so on. For ordinary concretes, autogenous shrinkage is so little compared to the other deformations that it has been dignored. It has recently been proved, however, that autogenous shrinkage considerably increase with decrease in water to cement ratio. And it has been reported that cracking can be caused by autogenous shrinkage, when high- strength concretes were used. In this study, we propose an analytical system to represent autogenous shrinkage in cement paste in order to control crack due to autogenous shrinkage. The system is composed with the hydration model and pore structure model. Contrary to the usual assumption of uniform properties in the hydration progress, the hydration model to refine Tomosawa's represents the situation that inner and outer products are made in cement paste. The pore structure model is based upon the physical phenomenon of ion diffusion in cement paste and chemical phenomenon of hydration in cement particle. The proposed model can predict the pore volume ratio and the pore structure in cement paste under variable environmental conditions satisfactorily The autogenous shrinkage prdiction system with regard to pore structure development and hydration at early ages for different mix-proportions shows a reasonable agreement with the experimental data.

• Archives of Plastic Surgery
• /
• 제38권3호
• /
• pp.222-227
• /
• 2011

Purpose: Autogenous particulate bone grafting is a type of autogenous bone graft that consists of small particles of cortical and cancellous bone. Autogenous particulate bone grafting has been used for calvarial bone defect after calvarial defect of craniosynostosis and prevention of temporal depression after fronto-orbital advancement. The results were followed up and studied for effectiveness of autogenous calvarial particulate bone grafting. Methods: Cranial vault remodeling and fronto-orbital advancement was performed for six craniosynostosis patient from August 2005 to October 2007. Autogenous particulate bone grafting was harvested from endocortex of separated cranial vault and if insufficient, from extocortex of occipital region using Hudson brace & D'Errico craniotomy bit and was grafted on the calvarial bone defect of cranial vault and temporal hollow. Fibrin glues were added to the harvested particulated bone for adherence and shaping of paticles. Results: Autogenous particulate bone grafting was followed-up at least longer than I year. The calvarial bony defects following primary cranial remodeling were successfully covered and postoperative temporal depressions after fronto-orbital advancement were also well prevented by grafted particulated bone. Conclusion: Autogenous calvarial particulate bone graft can be harvested in infants and young children with minimal donor site morbidity. It effectively heals cranial defects in children and during fronto-orbital advancement reduces the prevalence of osseous defects independent of patient age. It's easy and effective method of reconstruction of calvarial defect.

• Structural Engineering and Mechanics
• /
• 제49권6호
• /
• pp.763-773
• /
• 2014

The recently developed Ultra High Performance Concrete (UHPC) displays outstanding compressive strength and ductility but is also subjected to very large autogenous shrinkage. In addition, the use of forms and reinforcement to confine this autogenous shrinkage increases the risk of shrinkage cracking. Accordingly, this study adopts a combination of shrinkage reducing admixture and expansive admixture as a solution to reduce the shrinkage of UHPC and estimates its appropriateness by evaluating the compressive and flexural strengths as well as the autogenous shrinkage according to the age. Moreover, the coefficient of thermal expansion known to experience sudden variations at early age is measured in order to evaluate exactly the autogenous shrinkage and the thermal expansion is compensated considering these measurements. The experimental results show that the compressive and flexural strengths decreased slightly at early age when mixing 7.5% of expansive admixture and 1% of shrinkage reducing admixture but that this decrease becomes insignificant after 7 days. The use of expansive admixture tended to premature the setting of UHPC and the start of sudden increase of autogenous shrinkage. Finally, the combined use of shrinkage reducing admixture and expansive admixture appeared to reduce effectively the autogenous shrinkage by about 47% at 15 days.