• Journal of Radiation Industry
• /
• v.6 no.2
• /
• pp.119-123
• /
• 2012

The detection properties of gamma-irradiated (0~10 kGy) dried seaweed, dried shrimp, and seasoned dried filefish were investigated by photo-stimulated luminescence (PSL) and electron spin resonance (ESR). PSL could be used as a detection method on irradiated dried seaweed and dried shrimp as they showed photon counts greater than 5,000 counts/60 s (positive) in the irradiated samples with doses above l kGy. However, PSL could not be applied to detect irradiated seasoned dried filefish, because gamma-irradiated sample at 10 kGy even yielded photon counts less than 700 counts/60 s (negative). The ESR spectroscopy for only dried shrimp revealed specific signals derived from free radicals captured in the shell of shrimp. As a result, it is considered that PSL or ESR methods for detection of gamma-irradiated dried shrimp and only PSL can be used to detect gamma-irradiated seaweed. Furthermore, it is considered that hydrocarbon analysis of seasoned dried filefish containing fat by GC/MS and Thermo Luminance (TL) analysis of dried seaweed should be studied for detection of irradiation.

• Journal of the Mineralogical Society of Korea
• /
• v.24 no.4
• /
• pp.301-312
• /
• 2011

The study on the atomic structure of iron-bearing silicate glasses has significant geological implications for both diverse igneous processes on Earth surface and ultra-low velocity zones at the core-mantle boundary. Here, we report experimental results on the effect of iron content on the atomic structure in iron-bearing alkali silicate glasses ($Na_2O-Fe_2O_3-SiO_2$ glasses, up to 16.07 wt% $Fe_2O_3$) using $^{29}Si$ and $^{17}O$ solid-state NMR spectroscopy. $^{29}Si$ spin-lattice ($T_1$) relaxation time for the glasses decreases with increasing iron content due to an enhanced interaction between nuclear spin and unpaired electron in iron. $^{29}Si$ MAS NMR spectra for the glasses show a decrease in signal intensity and an increase in peak width with increasing iron content. However, the heterogeneous peak broa-dening in $^{29}Si$ MAS NMR spectra suggests the heterogeneous distribution of $Q^n$ species around iron in iron-bearing silicate glasses. While nonbridging oxygen ($Na-O-Si$) and bridging oxygen (Si-O-Si) peaks are partially resolved in $^{17}O$ MAS NMR spectrum for iron-free silicate glass, it is difficult to distinguish the oxygen clusters in iron-bearing silicate glass. The Lorentzian peak shape for $^{29}Si$ and $^{17}O$ MAS NMR spectra may reflect life-time broadening due to spin-electron interaction. These results demonstrate that solid-state NMR can be an effective probe of the detailed structure in iron-bearing silicate glasses.

• Journal of Radiation Industry
• /
• v.7 no.2_3
• /
• pp.149-154
• /
• 2013

In this study, the simple preparation of poly(sodium 4-styrenesulfonate) (PSS)-patterned substrate via a selective ion irradiation was investigated to manipulate cell adhesion. PSS thin films spin-coated onto the hydrophobic polystyrene (PS) was patterned through masked 150 keV proton irradiation followed by developing with deionized water. The characteristics of the resulting PSS-patterned surfaces were investigated by using microscope, surface profiler, FT-IR, XPS, and contact angle analyzer. These analytical results revealed that the resolved $100{\mu}m$ PSS patterns were formed on the hydrophobic PS surface above the fluence of $1{\times}10^{15}ions\;cm^{-2}$ and the chemical structure, composition, and wettability of the PSS patterns were dependant on a fluence. Moreover, the results of the in-vitro cell culture and proliferation assay exhibited that H1299 cells preferentially adhered and proliferated onto the more hydrophilic PSS part of the PSS-patterned PS and the well-aligned cell patterns was formed on the PSS-patterned PS particularly at the fluence of $1{\times}10^{15}ions\;cm^{-2}$.

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.33 no.9
• /
• pp.1522-1528
• /
• 2004

Electron spin resonance (ESR) and hydrocarbon characteristics were analyzed to establish identification conditions for irradiated dried red pepper. The ESR spectroscopy for 4 different parts (powder, pericarp, seed, stem) of the samples showed that irradiated samples signaled (g=2.024, 2.006, 1.987) a pair of peaks from a cellulose radical at intervals of 6 mT, which were not found on the non-irradiated samples. The ESR signals increased in directly proportion to the irradiation doses, which were still detectable after 12 weeks of storage at room temperature. The GC-MS analysis of hydrocarbons after fat extraction and separation by florisil column chromatography revealed that hydrocarbons, such as 1-tetradecene (14:1), 1,7,10-hexadecatriene (16:3), 1,7-hexadecadiene (16:2), 1-hexadecene (16:1), 6,9-heptadecadiene (17:2), and 8-heptadecene (17:1), were detected only from the irradiated samples immediately after irradiation and 8 months of storage. They linearly increased with the dose of irradiation, suggesting them as radiation-induced markers for irradiated dried red pepper.

• Food Science and Preservation
• /
• v.13 no.1
• /
• pp.50-54
• /
• 2006

The identification characteristics of inadiated dried onion and garlic at 1, 4 and 7 kGy were investigated by analyzing their photostimulated luminescence (PSL), thermoluminescence (TL) and electron spin resonance (ESR). The PSL results showed that the photon counts of non-irradiated dried onion were less than 700 (negative) and those of irradiated samples at 1kGy or more were over 5000 (positive), making it possible to discriminate non-irradiated onions from irradiated ones. However, the intermediate counts (700-5000) were observed in irradiated garlic at 1 and 4 kGy, even though positive counts were measured in 7 kGy group. Radiation-induced TL glow curves $(TL_1)$ were measured at $150^{\circ}C$ range in both irradiated onion and garlic samples at 1 kGy or more, which could identify irradiated groups. Furthermore, determination of TL ratios $(TL_1/TL_2)$ for both samples could verify the above results. It was found, however, that ESR spectroscopy was not suitable for the detection of irradiated dried onion and garlic.

• Macromolecular Research
• /
• v.16 no.8
• /
• pp.725-733
• /
• 2008

Polyimide (PI) multilayer thin films were prepared by spin-coating from a poly(amic acid) (PAA) and poly(amic acid) ammonium salt (PAAS). PI was prepared from pyromellitic dianhydride (PMDA) and 4,4'-oxydianiline (ODA) PAA. Different compositions of PAAS were prepared by incorporating triethylamine (TEA) into PMDA-ODA PAA in dimethylacetamide. PI multilayer thin films were spin-coated from PMDA-ODA PAA and PAAS. The PAAS comprising cationic and anionic moieties were spherical with a particle size of $20{\sim}40\;nm$. Some particles showed layers with ammonium salts, despite poor ordering. Too much salt obstructed the interaction between the polymer chains and caused phase separation. A small amount of salt did not affect the interactions of the interlayer structure but did interrupt the stacking between chains. Thermogravimetric analysis (TGA) showed that the average decomposition temperature of the thin films was $611^{\circ}C$. All the films showed almost single-step, thermal decomposition behavior. The nanostructure of the multilayer thin films was confirmed by X -ray reflectivity (XRR). The LF 43 film, which was prepared with a 4:3 molar ratio of PMDA and ODA, was comprised of uniformly spherical PAAS particles that influenced the nanostructure of the interlayer by increasing the interaction forces. This result was supported by the atomic force microscopy (AFM) data. It was concluded that the relationship between the uniformity of the PAAS particle shapes and the interaction between the layers affected the optical and thermal properties of PI layered films.

• Journal of the Korean Magnetics Society
• /
• v.8 no.5
• /
• pp.288-294
• /
• 1998

Effect of degree of intermixing at the Ta/NiFe interface induced by varying applied substrate bias voltage during NiFe free layer deposition on change of magnetoresistance in Substrate/Ta/NiFe/Cu/NiFe/FeMn/Ta spin valve multilayers was investigated. It was found that the optimum NiFe free layer thickness showing a maximum MR increase with increasing the bias voltage. The increase of the optimum thickness was due to the increase of the intermixed layer thickness with a bias voltage. The weak ferromagnetic or non ferromagnetic intermixed layer plays as a spin-independent scattering region and does not contribute on spin-dependent scattering. The existence of the intermixed layer was proved by the means of electrical resistivity and magnetization changes. In the present study, the optimum "effective" free layer thickness which gives the highest MR ratio was a constant independent of the magnitude of the bias voltage we have used.have used.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.1
• /
• pp.7-11
• /
• 2020

Carbon solubility on the paste deposition methods in the carbon-doped TiZrN coating was investigated in terms of lattice distortion and atomic concentration. After depositing the carbon paste by the dip coating, spin coating and screen printing, the laser was ablated to form the carbon gradient layer. Thickness and the concentration of doped carbon depended on the paste deposition method. Crystal structure analysis indicated that more lattice distortion occurred when coating layers were doped with spin coating and screen printing than when coating layers were doped with dip coating. The XPS depth profile showed that the thickness of carbon gradient layer by dip coating was about 30 nm, spin coating and screen printing are approximately 100 nm, formed more gradient layer. The hardness before laser carburization was about 30 GPa, and the hardness of 31 GPa with dip coating and 37 GPa with spin coating and screen printing. It was indicated that paste deposition methods for laser carburization contributed to lattice distortion and gradient layer.

• Journal of Magnetics
• /
• v.14 no.4
• /
• pp.172-174
• /
• 2009

Nanolithography by atomic force microscope local oxidation was applied to the fabrication of planar-type Ni/Ni oxide/Ni junctions from 10 nm-thick Ni films. The junction characteristics were sensitive to the lithography conditions such as the bias voltage. Successful oxidation produced junctions of nonlinear current-voltage characteristics, implying the formation of oxide barriers. Magnetoresistance (MR) at low temperatures resembled that of spin valves.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.306-306
• /
• 2011

Three dimensional(3D) topological insulators(TIs) of Bi binary alloys are characterized by a bulk energy gap with strong spin-orbit coupling and metallic surface states protected by time-reversal symmetry. It was reported that film forms of such materials were advantageous over bulk forms due to less defect density and better crystallinity. So far, the films have been prepared on several substrates including semiconductors and graphene. But, there were no studies on metal substrates. For electronic transport experiments and device applications, it is necessary to know epitaxial relation between TIs and metal electrodes. In this study, Atomically flat films of Bi2Se3 were grown on a Au(111) metal substrate by in-situ molecular beam epitaxy. Using home-built scanning tunneling microscope, we observed hexagonal atomic structures which corresponded to the outmost selenium atomic layer of Bi2Se3. Triangular-shaped defects known as Selenium vacancy were also found.