• Journal of Power System Engineering
• /
• v.15 no.6
• /
• pp.73-80
• /
• 2011

The experimental investigation focuses on an influence of artificial aging time in longitudinal butt welded Al 6013-T4 aluminum alloy on the fatigue crack growth resistance. The preferred welding processes for this alloy are frequently tungsten inert gas welding (TIG) process due to its comparatively easier applicability and better weldability than other gas metal arc welding. Fatigue crack growth tests were carried out on compact tension specimens (CT) in longitudinal butt TIG welded after T82 heat treatment was varied in three artificial aging times of 6 hours, 18 hours and 24 hours. Of the three artificial aging times, 24 hours of artificial aging time are offering better resistance against the growing fatigue cracks. The superior fatigue crack growth resistance preferred spatial variation of materials within each specimen in the Paris equation based on reliability theory and fatigue crack growth rate by crack length are found to be the reasons for superior fatigue resistance of 24 hours of artificial aging time was compared to other joints. The highest of crack propagation resistance occurs in artificial aging times of 24 hours due to the increase in grain size (fine grained microstructures).

• Journal of the Korean institute of surface engineering
• /
• v.50 no.5
• /
• pp.380-385
• /
• 2017

Mechanical characteristics of the STS 304 which is heat resistance steel were investigated after artificial aging at $650^{\circ}C$ with 1,000 hours. Tensile test specimens and small test pieces were done artificial aging up to 1,000 hours in the high temperature atmospheric environment. The results present that as the aging time increased, tensile properties were deteriorated. In the case of failure mechanism, the configuration of the fractography presented drastic change from ductile to brittle with aging time. $M_{23}C_6$ carbide leading to the change of the mechanical properties and fracture mode of the aged STS 304 steel continuously precipitated along the grain boundaries of austenite microstructure.

• International Journal of Highway Engineering
• /
• v.9 no.4
• /
• pp.45-54
• /
• 2007

This study was carried out for developing artificial short-term aging(SA) and long-term aging(LA) methods of asphalt mixtures in which the aging level is properly matched with those of RTFO and PAV aged binders, respectively. The specimens were made of the short-term aged loose asphalt mixture which was kept in a convection oven at $154^{\circ}C$ for 2 hours and were aged at $110^{\circ}C$ for 24, 48, 72 and 96 hours for SA. Large molecular size(LMS) were measured using GPC after SA and LA to evaluate aging extents of each mixture with aging time. It is shown that the LMS was increased with aging time increment and that from the LMS(%) change ratio, it was possible to suggest an appropriate artificial aging time which is corresponding level of aging with RTFO and PAV. It was found that SA was somewhat strong and LA for 48 hours at $110^{\circ}C$ would be appropriate if sort-term aging is properly controlled.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.22 no.3
• /
• pp.90-96
• /
• 2014

The conventional SnPb solders were widely used for several decades in the electronic packing system due to the superior mechanical properties such as low melting point, better wettavility and good mechanical fatigue. However, in recent years, owing to adverse effect on the human health and environment, conventional SnPb solders have been replaced by Lead-free solders. In this research, the shear punch(SP) test of Sn-4Ag-(Cu)/Ni pad was performed. Pb-free solder alloys which are the environmentally friendly of the electronic components were performed at $150^{\circ}C$ for 100hr~1000hr to artificial aging processing. In order to evaluate the mechanical properties of solder joints, the SP test was conducted at $30^{\circ}C$ and $50^{\circ}C$. As a result, the maximum shear strength of almost the whole specimens was decreased with the increase in aging time and temperature of SP test. The mechanical properties of Sn-4Ag-0.5Cu solder were most excellent in all Pb-free solder which were produced by the SP test at $30^{\circ}C$.

• Analytical Science and Technology
• /
• v.25 no.3
• /
• pp.197-206
• /
• 2012

Ambers are composed of polymer molecules which contain aromatic moieties such as benzene, naphthalene, phenanthrene and anthracene. They emit fluorescence when irradiated with ultraviolet light, which was used for confirming an amber. The fluorescence of amber, however, tends to decrease as the surface of amber is weathered with light, heat, oxygen for a long time. In this study, the reliability of confirming amber with its fluorescence by measuring the changes of fluorescence after artificial aging. Aging factors were UV light (${\lambda}$=340 nm), oxygen with heat (100%, $90^{\circ}C$) and heat ($90^{\circ}C$) and aging time was for 5, 15, 30 and 60 days, respectively. In the excitation and emission spectra of amber, the intensity decreased and the maximal wavelength was shifted to longer wavelength with artificial aging time. Especially, there was a drastic decrease in the intensity of spectra to 1.7% of initial value after 60 days aging under oxygen with heat. Only in Colombian amber there showed an increase of fluorescence intensity for a certain aging time, which could be explained by the production of aromatic ring in the presence of light and heat. Conclusively, the fluorescence can be lessened by the natural weathering with light, heat and oxygen and it is not accurate to recognize amber just with UV irradiation method.

• Journal of the Korean Society for Heat Treatment
• /
• v.14 no.6
• /
• pp.323-329
• /
• 2001

Artificial aging was performed to simulate the microstructural degradation in 2.25CrMo steel arising from long time exposure at $540^{\circ}C$. The carbide morphologies were classified as acicular, pipe and globular type, and the number of carbides per unit area was measured for each type of carbides. The fine acicular carbides were found to diminish drastically in the initial stage of aging. An attempt was made to evaluate the microstructural degradation in artificially aging heat treated 2.25CrMo steel by the magnetic property measurements such as saturation magnetization, coercivity and remanence. The saturation magnetization showed no distinct trend with aging time. However, the coercivity and remanence were observed to decrease rapidly in initial 920 hours of aging time and then decrease slowly afterwards.

• Journal of the Korean Society for Heat Treatment
• /
• v.14 no.2
• /
• pp.110-117
• /
• 2001

Artificial aging was performed to simulate the microstructural degradation in 2.25CrMo steel arising from long time exposure at $540^{\circ}C$. It was found that the carbides became coarser and spheroidized as aging time increased. An attempt was made to evaluate the microstructural degradation in artificially aging heat treated 2.25CrMo steel by the ultrasonic attenuation and velocity measurements. Ultrasonic velocity was found essentially insensitive to the microstructural changes resulting from aging heat treatment. However, the ultrasonic attenuation was observed to increase with increasing aging time. Also, it was noticed that the change of ultrasonic attenuation with aging time was more sensitive at high frequency regions.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.3
• /
• pp.183-190
• /
• 2015

PURPOSE. This study evaluated the fracture load of customized zirconia abutments with titanium insert according to preparation depths, with or without 5-year artificial aging. MATERIALS AND METHODS. Thirty-six identical lithium disilicate crowns (IPS e.max press) were fabricated to replace a maxillary right central incisor and cemented to the customized zirconia abutment with titanium insert on a $4.5{\times}10$ mm titanium fixture. Abutments were fabricated with 3 preparation depths (0.5 mm, 0.7 mm, and 0.9 mm). Half of the samples were then processed using thermocycling (temperature: $5-55^{\circ}C$, dwelling time: 120s) and chewing simulation (1,200,000 cycles, 49 N load). All specimens were classified into 6 groups depending on the preparation depth and artificial aging (non-artificial aging groups: N5, N7, N9; artificial aging groups: A5, A7, A9). Static load was applied at 135 degrees to the implant axis in a universal testing machine. Statistical analyses of the results were performed using 1-way ANOVA, 2-way ANOVA, independent t-test and multiple linear regression. RESULTS. The fracture loads were $539.28{\pm}63.11$ N (N5), $406.56{\pm}28.94$ N (N7), $366.66{\pm}30.19$ N (N9), $392.61{\pm}50.57$ N (A5), $317.94{\pm}30.05$ N (A7), and $292.74{\pm}37.15$ N (A9). The fracture load of group N5 was significantly higher than those of group N7 and N9 (P<.017). Consequently, the fracture load of group A5 was also significantly higher than those of group A7 and A9 (P<.05). After artificial aging, the fracture load was significantly decreased in all groups with various preparation depths (P<.05). CONCLUSION. The fracture load of a single anterior implant restored with lithium disilicate crown on zirconia abutment with titanium insert differed depending on the preparation depths. After 5-year artificial aging, the fracture loads of all preparation groups decreased significantly.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.119-122
• /
• 2000

Recently polymer insulators are being used for outdoor high voltage applications. Polymer insulators for transmission line have significant advantages over porcelain and glass insulators, especially for ultra-high voltage transmission lines. Their advantages are light weight, vandalism resistance and hydrophobicity. Polymer insulators are a relatively new technology, but their expected life is still unknown. Therefore these estimating technique are very important. Their life time is related to weathering and operating condition. Multi-aging test is requested because aging factor is occurred by multi-aging than unique aging. The aging test about polymer insulators have mainly carried out by IEC 61109. This paper presents multi-stress chamber experiments and tracking wheel test to examine the tracking and erosion performance of polymer insulator for transmission. Multi-stress testing is able to demonstrate deficiencies of polymer insulator materials and designs, including the nature of interfaces in insulation design. We have investigated IEC 61109 Annex C (5000h aging test) and CEA tracking wheel test as test methods of artificial accelerated aging. The aging degree of polymer insulator is estimated by leakage current, measurement of hydrophobicity degree, damage conditions of insulator surface, withstand voltage test etc.

• Journal of the Korean Society for Heat Treatment
• /
• v.15 no.2
• /
• pp.70-75
• /
• 2002

The depletion of solid solution elements from matrix and the change of carbides during artificial aging of 2.25CrMo steel at $630^{\circ}C$ were investigated. The Mo and Cr elements were found to be depleted drastically in the early stage of aging. The change of carbides was confirmed by analyzing the XRD patterns of electrolytically extracted carbides. Four type of carbides, $M_{23}C_6$, $M_3C$, $M_2C$ and $M_6C$, were found to exist in the specimen before aging. The amount of $M_6C$ carbides increased with aging time, while that of $M_3C$ carbides diminished after short aging time.