Effect of High Temperature Aging Time on Mechanical Characteristics Degradation of STS 304 Steel

STS 304 강의 기계적 특성에 미치는 고온 열화 시간의 영향

  • Jung, Kwang-Hu (Division of Marine Engineering, Mokpo National Maritime University) ;
  • Kim, Seong-Jong (Division of Marine Engineering, Mokpo National Maritime University)
  • 정광후 (목포해양대학교 기관시스템공학부) ;
  • 김성종 (목포해양대학교 기관시스템공학부)
  • Received : 2017.08.30
  • Accepted : 2017.09.20
  • Published : 2017.10.31
Download PDF
⟨ Previous Next ⟩

Abstract

Mechanical characteristics of the STS 304 which is heat resistance steel were investigated after artificial aging at $650^{\circ}C$ with 1,000 hours. Tensile test specimens and small test pieces were done artificial aging up to 1,000 hours in the high temperature atmospheric environment. The results present that as the aging time increased, tensile properties were deteriorated. In the case of failure mechanism, the configuration of the fractography presented drastic change from ductile to brittle with aging time. $M_{23}C_6$ carbide leading to the change of the mechanical properties and fracture mode of the aged STS 304 steel continuously precipitated along the grain boundaries of austenite microstructure.

Keywords

References

  1. D. B. Lee, High-temperature Corrosion by Chlorides in Biomass-fired Plants. J. Kor. Inst. Surf. Eng., 49 (2016) 14-19. https://doi.org/10.5695/JKISE.2016.49.1.14
  2. P. Viklund, Superheater corrosion in biomass and waste fired boilers: characterisation, causes and prevention of chlorine-induced corrosion. Diss. KTH Royal Institute of Technology, (2013) 6.
  3. S. M. Bruemmer, B. W. Arey and L. A. Charlot. Influence of chromium depletion on intergranular stress corrosion cracking of 304 stainless steel, Corros., 48 (1992) 42-49. https://doi.org/10.5006/1.3315917
  4. S. Zhang, T. Shibata and T. Haruna, Initiation and propagation of IGSCC for sensitized type 304 stainless steel in dilute sulfate solutions, Corros. Sci., 39 (1997) 1725-1739. https://doi.org/10.1016/S0010-938X(97)00078-4
  5. A. Y. Kina, V. M. Souza, S. S. M. Tavares, J. M. Pardal and J. A. Souza, Microstructure and intergranular corrosion resistance evaluation of AISI 304 steel for high temperature service, Mater. charact., 59 (2008) 651-655. https://doi.org/10.1016/j.matchar.2007.04.004
  6. K. G. Nam, Y. S. He, J. C. Chang and K. S. Shin, Microstructural Evolution of Super304H Steel upon Long-Term Aging, Key Eng. Mater., 727 (2017) 36-42. https://doi.org/10.4028/www.scientific.net/KEM.727.36
  7. X. Bai, J. Pan, G. Chen, J. Liu, J. Wang, T. Zhang, and W. Tang, Effect of high temperature aging on microstructure and mechanical properties of HR3C heat resistant steel, Mater. Sci. and Tech., 30 (2014) 205-210. https://doi.org/10.1179/1743284713Y.0000000347
  8. A. Iseda, H. Okada, H. A. Semba and M. Igarashi, Long term creep properties and microstructure of SUPER304H, TP347HFG and HR3C for A-USC boilers, Energy Mater., 2 (2007) 199-206. https://doi.org/10.1179/174892408X382860
  9. M. Farooq, Strengthening and degradation mechanisms in austenitic stainless steels at elevated temperature, Diss. KTH Royal Institute of Technology (2013) 26.
  10. E. A. Trillo and L. E. Murr, Effects of carbon content, deformation, and interfacial energetics on carbide precipitation and corrosion sensitization in 304 stainless steel, Acta materialia, 47 (1998) 235-245. https://doi.org/10.1016/S1359-6454(98)00322-X
  11. E. A. Trillo, R. Beltran, J. G. Maldonado, R. J. Romero, L. R. Murr, W. W. Fisher and A. H. Advani, Combined effects of deformation (strain and strain state), grain size, and carbon content on carbide precipitation and corrosion sensitization in 304 stainless steel, Mater. Charact., 35 (1995) 99-112. https://doi.org/10.1016/1044-5803(95)00072-0
  12. H. Tanaka, M. Murata, F. Abe and H. Irie, Microstructural evolution and change in hardness in type 304H stainless steel during long-term creep, Mater. Sci. and Eng., A 319 (2001) 788-791.
  13. X. Xiao, G. Liu, B. Hu, J. Wang, and W. Ma, Coarsening behavior for $M_{23}C_6$ carbide in 12% Cr-reduced activation ferrite/martensite steel: experimental study combined with DICTRA simulation, J. Mater. Sci., 48 (2013) 5410-5419. https://doi.org/10.1007/s10853-013-7334-5
  14. W. Wang, Z. Wang, W. Li, J. Tian, W. Zhong and J. Lin, Evolution of $M_{23}C_6$ phase in HR3C steel aged at $650^{\circ}C$." Mater. High Temp., 33 (2016) 276-282. https://doi.org/10.1080/09603409.2016.1189023