• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 봄 학술논문 발표대회
• /
• pp.83-84
• /
• 2020

In present study, we have deposited the Zinc coating using arc thermal spray and plasma arc spray processes onto the steel substrate and durability of the deposited coating was evaluated. The bond adhesion result shows that plasma arc sprayed Zn coating exhibited higher in its value compared to arc thermal spray. SEM shows that Zn coating deposited by plasma arc process is more compact, less porous and adherent compare to arc spray process. The corrosion resistance properties are evaluated in artificial ocean water solution with exposure periods. EIS results show that total impedance at 0.01 Hz of plasma arc sprayed coating is higher than arc thermal spray owing to the compact and less porous morphology. It is concluded that plasma arc sprayed Zn coating is better than arc thermal spray process.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 가을 학술논문 발표대회
• /
• pp.17-18
• /
• 2021

In the present study, Al-Zn coating was deposited by Arc thermal (AT) and plasma arc thermal (PAT) spray processes, and their corrosion characteristics were studied in 3.5% NaCl through electrochemical impedance spectroscopy (EIS), scanning electron microscope (SEM) and mechanical tests. The bond adhesion result showed that plasma arc sprayed coating had a higher value attributed to compact, dense, and less porous coating compared to arc thermal spray coating which contains defects/pores and uneven morphology as revealed by scanning electron microscope analysis. Electrochemical results revealed that the plasma arc sprayed coating had a high polarization resistance at early stage of immersion, suggesting its excellent corrosion protection performance.

• 한국건축시공학회지
• /
• 제23권5호
• /
• pp.559-570
• /
• 2023

건설산업에서 사용되는 구조용 강재의 부식은 산업화로 인해 많은 공격적인 이온이 내포된 대기 환경에서 증가추세에 있다. 따라서 본 연구에서는 아크 및 플라즈마 아크용사로 Al 코팅을 용착하여 Cl^-와 CO₃^2-같은 공격적인 이온을 다량 함유한 Society of Automotive Engineering(SAE) J2334 용액의 모사대기환경에서 그 효과를 비교하였다. 다양한 분석기법으로 코팅 특성과 부식 메커니즘을 고찰하였다. 플라즈마 아크용사로 용착된 Al 코팅은 밀도 있고 균일하면 층층이 적층이 잘 되었고 높은 부착력이 나타났다. 이 공법으로 용착된 Al 코팅을 SAE J2334 용액에 기간별로 침지하여 측정한 개회로전위(OCP)는 아크용사로 용착된 Al 코팅보다 더 양전성(electropositive)한 값을 보여주었다. 플라즈마 아크용사는 총 임피던스가 아크용사보다 높게 나타났다. SAE J2334 용액에 23일 침지하였을 때 플라즈마 아크용사 Al 코팅의 부식속도는 아크용사에 비해 20% 감소하였다.

• 한국표면공학회지
• /
• 제48권6호
• /
• pp.343-348
• /
• 2015

In this paper, arc Zn thermal spray coating was carried out on the SS400 steel, and then various electrochemical characteristics and surface damage behavior of Zn thermal spray coating layer were analyzed. As the results, the potential of Zn thermal spray coating layer presented driving voltage above 300 mV compare to that of SS400 steel. The passivity characteristic in anodic polarization curve was not presented. It was adequate to as sacrificial anode material. In the surface damage after galvanostatic experiments, uniform corrosion tendency of Zn thermal spray coating layer was clearly observed with acceleration of the dissolution reaction. In conclusion, Zn thermal spray coating could be determined to represent the corrosion protection effect by stable sacrificial anodic cathodic protection method in seawater because it had sufficient driving voltage and uniform corrosion damage tendency for the SS400 steel.

• 한국표면공학회지
• /
• 제49권1호
• /
• pp.32-39
• /
• 2016

In this study, Al and Zn arc thermal spray coatings were carried out onto the substrate of SS400 steel to improve corrosion resistance and durability of hull structural steel for ship in marine environment. Therefore cavitation-erosion test was conducted to evaluate the durability of painted and thermal spray coated specimens. And then the damaged surface morphology and weight loss were obtained to compare with each other, respectively. As a result, the painted specimen was the poorest cavitation resistance characteristics because surface damage behavior appeared to be exfoliated in bulk shape during the cavitation experiment. And Zn thermal spray coating layer presented the significant surface damage depth due to relatively low surface hardness and local cavitation damage tendency. On the other hand, as a result of the weight loss analysis, the painting layer presented the poorest cavitation resistance and the Al thermal spray coating layer relatively showed the best results after cavitation experiment.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2020년도 가을 학술논문 발표대회
• /
• pp.52-53
• /
• 2020

The thermal spray coating process is being used to protect the metals and alloys from wear, abrasion, fatigue, tribology, and corrosion failure. Therefore, in the present study, Al and Zn was deposited by plasma arc thermal spray process onto the steel substrate and their performance was assessed. The bond adhesion result shows that Al coating has higher value attributed to compact, dense, and less porous compared to Zn coating which contain defects/pores and uneven morphology assessed by scanning electron microscopy (SEM). Electrochemical results show that the Al coating exhibited higher impedance value compared to Zn in artificial ocean water solution at prolonged exposure periods. However, both coatings show the increment in polarization resistance with exposure periods which reveal that porosity of coatings is filled by the corrosion products.

• 한국통신학회논문지
• /
• 제40권5호
• /
• pp.974-980
• /
• 2015

해양환경 하에서 강재에 대한 방식 목적으로 Al-3%Mg 용사선재를 이용하여 아크 용사코팅을 실시하였다. 그리고 Al-3%Mg 용사코팅 층의 내식성을 개선하기 위하여 유/무기 복합 세라믹 후처리를 실시하였다. 후처리 적용에 따른 용사코팅 층의 다양한 전기화학적 실험 결과, 양극분극과 음극분극 실험 시 모든 전위구간에서 후처리 적용 시 전류밀도가 작게 나타나 내식성 개선이 확인되었다. 그리고 후처리된 용사코팅 층의 표면에서 관찰된 마이크로 크랙의 영향으로 자연전위 계측 시 심한 전위변동이 나타났으며, 양극분극 실험 시에는 후처리 층의 탈리손상이 용이하게 발생하였다. 그럼에도 불구하고 타펠분석을 기반으로 외부 환경차단 효과를 나타내는 코팅 효율이 92.11%로 산출되어 Al-3%Mg 용사코팅 층의 내식성이 향상되었다.

• 한국표면공학회지
• /
• 제48권6호
• /
• pp.349-353
• /
• 2015

In this paper, arc thermal spray coating was conducted onto the SS400 steel using Inconel 625 wires in order to improve the durability of marine steel structures, and then investigated cavitation damage behavior of Inconel 625 coating layer in sea water. For the Inconel 625 coating layer, surface hardness appeared similar to that of existing high velocity oxy-fuel coating technology with 380~480 HV, but the porosity of about 6 % was larger relatively. During the cavitation experiment, pit damages were originated and grown at the rough surface and pore defect area of Inconel 625 coating layer. And, after the 72 hours of experimental time, weight loss of Inconel 625 coating layer exhibited gradually increasing tendency due to surface damage effect of the undercut.

• Corrosion Science and Technology
• /
• 제21권1호
• /
• pp.68-76
• /
• 2022

Several technologies are employed to protect substrates from corrosion and erosion damage. In particular, arc thermal spray coating technology is widely used as anti-corrosive technology for steel and concrete structures and is applied to offshore plants and petrochemical and drilling facilities. In this investigation, solid particle impingement erosion experiments were performed on an arc thermal spraying-coated specimen using 85% Al-14% Zn-1% Zr wire rod in KR-RA steel. This study investigated the effect of fluorosilicone sealing on the erosion resistance characteristics of the thermal spray coating layer. The erosion rates of the thermal spray-coated and sealed specimens were 4.1×10^-4 and 8.5×10^-4, respectively. At the beginning of the experiment, the fluorosilicone sealant was almost destroyed by the impact of the solid particles. The destruction time for the coating layer was 10 minutes for the thermal spray-coated specimen and 13 minutes for the sealed specimens, indicating that the sealed specimens had better erosion resistance characteristics to solid particle impingement.

• 한국분무공학회지
• /
• 제13권4호
• /
• pp.193-199
• /
• 2008

Spray coating is a versatile surface modification technology in which coating is built-up based on the successive deposition of micron-scaled particles. Depending on the coating materials, the coatings can meet the required mechanical properties, corrosion resistance, and other properties of base materials. Spraying processes are mainly classified into thermal and kinetic spraying according to their bonding mechanism and deposition characteristics. Specifically, thermal spraying process can be further classified into many categories based on the design and mechanism of the process, such as frame spraying, arc spraying, atmospheric plasma spraying (APS), and high velocity oxygen-fuel (HVOF) spraying, etc. Kinetic spraying or cold gas dynamic spraying is a newly emerging coating technique which is low-temperature and high-pressure coating process. In this paper, overall view of thermal and kinetic spray coating technologies is discussed in terms of fundamentals and industrial applications. The technological characteristics and bonding mechanism of each process are introduced. Deposition behavior and properties of technologically remarkable materials are reviewed. Furthermore, industrial applications of spray coating technology and its potentials are prospected.