• Corrosion Science and Technology
• /
• 제14권6호
• /
• pp.261-266
• /
• 2015

The capacity of passive metal to repassivate after film damage determines the development of local corrosion and the resistance to corrosion failures. In this work, the repassivation kinetics of 316L stainless steel (316L SS) was investigated in borate buffer solution (pH 9.1) using a novel abrading electrode technique. The repassivation kinetics was analyzed in terms of the current density flowing from freshly bare 316L SS surface as measured by a potentiostatic method. During the early phase of decay (t < 2 s), according to the Avrami kinetics-based film growth model, the transient current was separated into anodic dissolution ($i_{diss}$) and film formation ($i_{film}$) components and analyzed individually. The film reformation rate and thickness were compared according to applied potential. Anodic dissolution initially dominated the repassivation for a short time, and the amount of dissolution increased with increasing applied potential in the passive region. Film growth at higher potentials occurred more rapidly compared to at lower potentials. Increasing the applied potential from 0 $V_{SCE}$ to 0.8 $V_{SCE}$ resulted in a thicker passive film (0.12 to 0.52 nm). If the oxide monolayer covered the entire bare surface (${\theta}=1$), the electric field strength through the thin passive film reached $1.6{\times}10^7V/cm$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.922-925
• /
• 2003

The interest of self-organization materials that have uniform and regular structure in nano scale has been grown due to their utilization in various fields of nanotechnology. An attractive candidate among these materials is anodic aluminum oxide film, which are formed by anodization of aluminum in an appropriate acid solution. The anodic aluminum oxide film has a highly ordered porous structure with very uniform and nearly parallel pores that can be organized in an almost precise close-packed hexagonal structure. In this study, we attempt to make Au dot arrays, which were fabricated using anodic aluminum oxide film as an evaporation mask. The Au dot arrays have a uniform sized dots and spacing to its neighbors and the average diameter of Au dots is about 60 nm corresponding to them of the mask.

• 한국표면공학회지
• /
• 제50권5호
• /
• pp.308-314
• /
• 2017

Anodic film formation behavior of AZ31 Mg alloy was studied as a function of NaOH concentration in 1 M $Na_2CO_3$ + 0.5 M $Na_2SiO_3$ solution under the application of a constant anodic current density, based on the analyses of voltage-time curves, surface appearances and morphologies of the anodically formed PEO (plasma electrolytic oxidation) films. The anodic film formation voltage and its fluctuations became largely lowered with increasing added NaOH concentration in the solution. Two different types of film defects, large size dark spots indented from the original surface and locally extruded white spots, were observed on the PEO-treated surface, depending on the concentration of added NaOH. The large size dark spots appeared only when added NaOH concentration is less than 0.2 M and they seem to result from the local detachments of porous PEO films. The white spots were observed to be very porous and locally extruded and their size became smaller with increasing added NaOH concentration. The white spot defects disappeared completely when more than 0.8 M NaOH is added in the solution. Concludingly it is suggested that the presence of enough concentration of $OH^-$ ions in the carbonate and silicate ion-containing electrolyte can prevent local thickening and/or detachment of the PEO films on the AZ31 Mg alloy surface and lower the PEO film formation voltage less than 70 V.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 하계학술대회 논문집 Vol.8
• /
• pp.375-375
• /
• 2007

In the conventional crystallization method, thepoly-Si TFTs show poor device-to-device uniformity because of the random location of the grain boundaries. However, our new crystallization method introduced in this paper employed substrate-embedded seeds on the highly ordered anodic alumina template to control both the location of seeds and the number of grain boundaries intentionally. In the process of excimer laser crystallization (ELC), a-Si film deposited on the anodic alumina by low pressure chemical vapor deposition (LPCVD) is transformed into fine poly-Si grains by explosive crystallization (XC) prior to primary melting. At the higher energy density, the film is nearly completely melted and laterally grown by super lateral growth (SLG) from remained small part of the fine poly-Si grains as seeds at the Si/anodic alumina interface. Resultant grain boundaries have almost linear functions of the number of seeds in concavities of anodic alumina which have a constant spacing. It reveals the uniformity of. device can be enhanced prominently by controlling location and size of pores which contains fine poly~Si seeds under artificial anodizing condition.

• 한국수산과학회지
• /
• 제14권2호
• /
• pp.94-102
• /
• 1981

해수에서 전기 전도성이 있는 산화 피막전극을 사용하여 금속 산화피막 전극들의 특성과 발암성 원인물질인 DBNA의 전극 반응성을 규명하는데 필요한 기초자료를 potential drop방법과 galvanostatic방법으로 얻어서 다음과 같은 결론을 내렸다. 1) $9\%_{\circ}$해수에 음극반응 억제제 DBNA를 첨가한 경우 알루미늄 산화피막 전극과 아연 산하피막 전극은potential drop현상을 나타내지 못 했으나 납 산화피막 전극과 구리 신화피막 전극은 피막전극으로서 적합한 기능을 가졌음을 알았다. 2) 제1단계 음극반응의 transition time이 $0.22\sim1.40sec$범위의 1분이내 값이므로 산화피막을 통과한 양성자는 확산$\rightarrow$흡착과정의 음극반응을 했다. 3) 0.5M NaCl수용액과 $9\%_{\circ}$해수에서 얻어진 transition time 값들이 대체로 일치한 것은 금속의 종류에 관계없이 산화피막을 통과한 양성자의 확산속도가 인정전류밀도 범위에서 인정하였기 때문이다. 4) $1.9\times10^{-4}\sim5.0\times10^{-6}\;amp/cm^2$의 전류밀도 범위에서 해수와 해수에 억제제 DBNA를 첨가했을때 얻어진 $\tau_{1}/4$값들의 $E_{1}/4$값들의 차가 각각 0.06sec와 0.53v있으므로, 억제 DBNA의 음극반응은 주로 흡착$\rightarrow$확산과정 이었다. 5) 알루미늄 산화피막과 아연 산화피막의 표면에 흡착된 전재질의 흡착량이 납 산화피막과 구리 산화피막보다 많은 것은 피막표면에 생성된 불규칙한 기공 생성 수가 증가하였기 때문이다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제29권1호
• /
• pp.107-115
• /
• 2005

The effects on the formation of anodic oxide films on Mg-Al alloy (AZ91) in 1M-NaOH solution was investigated using parameters of current density and time during anodizing The general tendency has been confirmed that the increase of anodizing time improves the corrosion resistance. It is considered that the formation of anodic oxide film was increased by increasing the applied current and the anodizing time to generate active dissolution reaction In anodizing at constant current density. passivity potentials shifted to noble direction with increasing current densities. It was confirmed that oxygen quantify in anodic oxide films increased with anodizing time. The compact films above 4 $mA/cm^2$ were formed with the shape of an island in grooves at early stage and then grew with combination of the islands

• 한국진공학회지
• /
• 제8권4A호
• /
• pp.465-469
• /
• 1999

In this paper, spacer process for FED (Field Emission Display ) was developed with the glass to glass anodic bonding technology using Al film as an interlayer. Characteristics, current density-time curves and force of the anodic boding were measured on various thickness of Al film; 1000$\AA$, 2000$\AA$, 3000$\AA$, 4000$\AA$ and 500$\AA$. Holders for spacer were fabricated with photosensitive glass and (110) Si wafer by bulk micromachining. Spacers was formed on glass substrate by spacer glass to glass anodic bonding and an evacuated panel was fabricated to prove the potential of application for FED.

• 한국조명전기설비학회:학술대회논문집
• /
• 한국조명전기설비학회 2002년도 학술대회논문집
• /
• pp.207-211
• /
• 2002

Anodizing film was prepared by anodic oxidation of pure aluminum(purity > 99.50) using DC power supply for constant current mode in an electrolytic solution of surface of sulfuric acid. Effects of pre-treatment process such as chemical polishing, acid cleaning, alkali etching before anodic oxidation, were studied to microstructures and surface morphologies. A roughness on surface of anodizing film had to be decreased for amorphous phase by anodic oxidation. A roughness on surface of anodizing film decrease as annealing temperature increased in chemical polishing.

• 한국표면공학회지
• /
• 제50권1호
• /
• pp.17-23
• /
• 2017

This work demonstrates arc generation and anodic film formation behaviors on Al1050 alloy during PEO (plasma electrolytic oxidation) treatment under a constant direct current in an alkaline electrolyte containing silicate, carbonate and borate ions. Only one big arc more than 2 mm diameter was generated first at the edges and it was moving on the fresh surface or staying occasionally at the edges, resulting in the local burning due to generation of an extremely big orange colored arc at the edges. Central region of the flat surface was not fully covered with PEO films even after sufficiently long treatment time because of the local burning problem. The anodic oxides formed on the flat surface by arcing once were found to consist of a number of small oxide nodules with spherical shape of $3{\sim}6{\mu}m$ size and irregular shapes of about $5{\sim}10{\mu}m$ width and $10{\sim}20{\mu}m$ length. The anodic oxide nodules showed uniform thickness of about $3{\mu}m$ and rounded edges. These experimental results suggest that one big arc observed on the specimen surface under the application of a constant direct current is composed of a number of small micro-arcs less than $20{\mu}m$ size.

• 한국재료학회지
• /
• 제22권1호
• /
• pp.1-7
• /
• 2012

Thin film electrode consisting purely of porous anodic tin oxide with well-defined nano-channeled structure was fabricated for the first time and its electrochemical properties were investigated for application to an anode in a rechargeable lithium battery. To prepare the thin film electrode, first, a bi-layer of porous anodic tin oxides with well-defined nano-channels and discrete nano-channels with lots of lateral micro-cracks was prepared by pulsed and continuous anodization processes, respectively. Subsequent to the Cu coating on the layer, well-defined nano-channeled tin oxide was mechanically separated from the specimen, leading to an electrode comprised of porous tin oxide and a Cu current collector. The porous tin oxide nearly maintained its initial nano-structured character in spite of there being a series of fabrication steps. The resulting tin oxide film electrode reacted reversibly with lithium as an anode in a rechargeable lithium battery. Moreover, the tin oxide showed far more enhanced cycling stability than that of powders obtained from anodic tin oxides, strongly indicating that this thin film electrode is mechanically more stable against cycling-induced internal stress. In spite of the enhanced cycling stability, however, the reduction in the initial irreversible capacity and additional improvement of cycling stability are still needed to allow for practical use.