• Journal of the Korean Vacuum Society
• /
• v.15 no.4
• /
• pp.427-433
• /
• 2006

We have fabricated nanodot arrays by using phase separated (PS- b- PMMA) diblock copolymer film and anodic aluminum oxide (AAO) membrane as templates with hexagonal arrays of cylindrical microdomains perpendicular to the substrate. Pulsed laser deposition technique was used to deposit various kinds of materials including Ag, Ni, ZnO, Si:Er, and Co/Pt onto Si substrates. The size and separation of nanodots correspond to those of the templates used, The density of nanodots was estimated to be $6{\times}10^{11}/cm^2$ and $1{\times}10^{10}/cm^2$ when the diblock copolymer and AAO were used, respectively. In particular, the optical properties of ZnO and Si: Er nanodot arrays were investigated and the strong photoluminescence at 380 nm and $1.54{\mu}m$ was observed from ZnO and Si:Er nanodot arrays, respectively.

• Journal of the Microelectronics and Packaging Society
• /
• v.26 no.1
• /
• pp.35-39
• /
• 2019

To date, porous alumina structures have been implemented by electrochemical anodization technique. The anodizing methods can easy to make a porous aluminum oxide film with a regular arrangement, but oxide film with complex structure type such as pillar-on-pore is relatively difficult to implement. Therefore, this study aims to observe the change of anodized oxide pore size, thickness, and structure in a phosphoric acid solution according to applied anodization voltage conditions. For the implementation of hybrid composite oxide structures, it is possible to create by modulating anodization voltage. The experimental conditions were performed at the applied anodization voltage of 100 V and 120 V in 10% phosphoric acid solution, respectively. The experimental results were able to observe the structure of oxides in the form of porous and composite structures (pillar-on-pore), depending on each condition.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.1
• /
• pp.34-39
• /
• 2018

Steel crucible used for molten Al has a problem of very limited lifetime because of the interaction between Fe and molten Al. This study was performed to improve the lifetime of steel crucible for molten Al by coating metallic Al and by further anodizing treatment to form thick and uniform anodic oxide films. The lifetime of the steel crucible was improved slightly by Al coating from 30 to 40 hours by metallic Al coating and largely to 120 hours by coating the surface with anodic oxide film. The improved lifetime was attributed to blocking of the reaction between Fe and molten Al with the help of anodic oxide layer with more than 20 um thickness on the crucible surface. The failure of the steel crucible arises from the formation of intermetallic compounds and pores at the steel/Al interface.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.195-195
• /
• 2010

In recent years, Anodic aluminum oxide(AAO) has become popular and attractive materials. It can be easily fabricated and self-organized pore structures. It has been widely used as a biosensor membrane, photonic crystal for optical circuit and template for nanotube growth etc. In previous papers, the theory was developed that AAO shows anisotropic optical properties, since it has anisotropic structure with numerous cylindrical pores. It gives rise to the anisotropy of the refractive index called as birefringence. It can be used as conventional polarizing elements with high efficiency and low cost. Therefore, we would like to compare the theory and experimental results in this study. One method which can measure effective refractive index of thin film is the prism coupling technique. It can give accurate results fast and simply. Furthermore, we can also measure separately the refractive index with different polarization using polarization of the laser (TE mode and TM mode). We calculated the effective refractive index with effective medium approximations (EMAs) by pore size in the SEM image. EMAs are physical models that describe the macroscopic system as the homogeneous and typical method of all mean field theories.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.106-107
• /
• 2007

We fabricated anodic aluminium oxides (AAO) on Si and sapphire substrates from the electrochemical reactions of thin AI films in an aqueous solution of oxalic acid. The thin AI films have deposited on Si and Sapphire substructure by using E-beam evaporation and thermal evaporation, respectively. The formation of AAO structures has investigated from FE-SEM measurement image and showed randomly distributed phase of nanoholes instead of the periodic lattice of photonic crystals. The AAO structure on sapphire shows the double layers of nanoholes.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.153-153
• /
• 2016

Aluminum alloys have poor corrosion resistance compared to the pure aluminum due to the additive elements. Thus, anodizing technology artificially generating thick oxide films are widely applied nowadays in order to improve corrosion resistance. Anodizing is one of the surface modification techniques, which is commercially applicable to a large surface at a low price. However, most studies up to now have focused on its commercialization with hardly any research on the assessment and improvement of the physical characteristics of the anodized films. Therefore, this study aims to select the optimum temperature of sulfuric electrolyte to perform excellent corrosion resistance in the harsh marine environment through electrochemical experiment in the sea water upon generating porous films by variating the temperatures of sulfuric electrolyte. To fabricate uniform porous film of 5083 aluminum alloy, we conducted electro-polishing under the 25 V at $5^{\circ}C$ condition for three minutes using mixed solution of ethanol (95 %) and perchloric (70 %) acid with volume ratio of 4:1. Afterward, the first step surface modification was performed using sulfuric acid as an electrolyte where the electrolyte concentration was maintained at 10 vol.% by using a jacketed beaker. For anode, 5083 aluminum alloy with thickness of 5 mm and size of $2cm{\times}2cm$ was used, while platinum electrode was used for cathode. The distance between the two was maintained at 3 cm. Afterward, the irregular oxide film that was created in the first step surface modification was removed. For the second step surface modification process (identical to the step 1), etching was performed using mixture of chromic acid (1.8 wt.%) and phosphoric acid (6 wt.%) at $60^{\circ}C$ temperature for 30 minutes. Anodic polarization test was performed at scan rate of 2 mV/s up to +3.0 V vs open circuit potential in natural seawater. Surface morphology was compared using 3D analysis microscope to observe the damage behavior. As a result, the case of surface modification presented a significantly lower corrosion current density than that without modification, indicating excellent corrosion resistance.

• 한국신재생에너지학회:학술대회논문집
• /
• 2011.11a
• /
• pp.84.1-84.1
• /
• 2011

Typical solid oxide fuel cells (SOFCs) have limited applications because they operate at high temperature due to low ionic conductivity of electrolyte. Thin film solid oxide fuel cell with yttria stabilized zirconia (YSZ) electrolyte is developed to decrease operating temperature. Pt/YSZ/Pt thin film SOFC was fabricated on anodic aluminum oxide (AAO). The crystalline structure of YSZ electrolyte by sputter is heavily depends on the roughness of porous Pt layer, which results in pinholes. To deposit YSZ electrolyte without pinholes and electrical shortage, it is necessary to deposit smoother and denser layer between Pt anode layer and YSZ layer by sputter. Atomic Layer Deposition (ALD) technique is used to deposit pre-YSZ layer, and it improved electrolyte quality. 300nm thick Bi-layered YSZ electrolyte was successfully deposited without electrical shortage.

• Tribology and Lubricants
• /
• v.26 no.1
• /
• pp.14-20
• /
• 2010

Tribological properties of nanoporous structured alumina film was investigated. Alumina film (AAO: anodic aluminum oxide) of $60{\mu}m$ thickness having nanopores of 45 nm diameter with 105 nm interpore-diatance was fabricated by mild anodization process. Reciprocating ball-on-flat sliding friction tests using 1 mm diameter steel ball as a counterpart were carried out with wide range of normal load from 1 mN to 1 N in an ambient environment. The morphology of worn surfaces were analyzed using scanning electron microscopy. The friction coefficient was strongly influenced by the applied normal load. Smooth layer patches were formed on the worn surface of both AAO and steel ball at relatively high load (100 mN and 1 N) due to tribochemical reaction and compaction of wear debris. These tribolayers contributed to the lower friction at high loads. Extremely thin layer patches, due to mild plastic deformation of surface layer, were sparsely distributed on the worn surface of AAO at low loads (1 mN and 10 mN) without the evidence of tribochemical reaction. Delaminated wear particles were generated at high loads by fatigue due to repeated loading and sliding.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.65-69
• /
• 2002

An Al film deposited on the Kovar alloy substrate was anodically-bonded to the borosilicate glass, and the bond interfaces was closely investigated by transmission electron microscopy. Al oxide was found to form a layer ~l0 nm thick at the bond interface, and fibrous structure of the same oxide was found to grow epitaxially in the glass from the oxide layer. The fibrous structure grew with the bonding time. The mechanism of the formation of this fibrous structure is proposed on the basis of the migration of Al ions under the electric field. Penetration of Al into glass beyond the interfacial Al oxide was not detected. The comparison of the amount of excess oxygen ions generated in the alkali depletion layer with that incorporated in the Al oxide suggests that the growth of the alkali-ion depletion layer is controlled by the consumption of excess oxygen to form the interfacial Al oxide.

• Journal of the Korean institute of surface engineering
• /
• v.53 no.1
• /
• pp.29-35
• /
• 2020

In this study, five different specimen preparation methods were introduced and their advantages and disadvantages were presented. One of them, an epoxy mounting method has advantages of constant exposure area, ease of surface preparation without touching the specimen surface during polishing or cleaning, use of small amount of material and ease of specimen reuse by polishing or etching. However, in order to eliminate unexpected errors resulting from preferable reaction at the specimen/epoxy interface and contact resistance between the specimen and copper conducting line for electrical connection, it is recommended to cover the wall side of the specimen with porous anodic oxide films and to remain the contact resistance lower than 1 ohm. The increased contact resistance between the specimen and Cu conducting line appeared to result in increases of anodizing voltage and solution temperature during anodizing by which thickness and hardness of anodizing film on Al2024 alloy were drastically decreased and color of the films became more brightened.