• Journal of the Korean Ceramic Society
• /
• v.32 no.12
• /
• pp.1401-1407
• /
• 1995

Zirconia powder coated with alumina was prepared by hydrolysis of alumina butoxide. The coated powder was obtained by a hydrolysis reaction between the adsorbed water on the surface of zirconia particles and aluminum sec-butoxide. Amorphous aluminum hydroxide was uniformly coated on the surface of zirconia particles with the thickness of about 30 nm. The shape and distribution of aluminum hydroxide was varied with an existence of surfactant. The coated layer of aluminum hydroxide consists of the fine particle size, and the zirconia powder coated by alumina hydroxide have the large specific surface area of 120 $m^2$/g, compared with that of starting zirconia powder.

• Journal of the Korean Ceramic Society
• /
• v.31 no.4
• /
• pp.347-358
• /
• 1994

Creep densification and grain growth of alumina powder compacts during high temperature processing were investigated. The creep densification and grain growth of alumina powder compacts during various sintering processes were analyzed by employing the consitutive model by Kwon and Kim. Theoretical results from the constitutive model were compared with various experimental data of alumina powder compacts in the literature including pressureless sintering, sinter forging and hot pressing. The proposed constitutive equations were implemented into finite element analysis program (ABAQUS) to simulate densification for more complicated geometry and loading conditions. The effects of friction between die and powder compact or punch and powder compact during sinter forging and hot pressing are investigated by using the finite element method. Also, high temperature forming processing of alumina compact with complicated shape was simulated.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.403-409
• /
• 2015

Porous alumina ceramics are involved in many industrial applications due to the exceptional properties of these products. This study addresses the preparation of porous alumina ceramics using hollow microspheres as a pore-forming agent and slip casting as a green-body-forming technique. A uniform distribution of pores is a basic requirement of a porous material. This study investigates three different slurry systems, i.e., as-prepared alumina slurry, alumina slurry electrostatically dispersed by hydrochloric acid (HCl), and slurry dispersed by the commercial dispersant 'Darvan C-N'. At a low viscosity, the hollow microspheres in the slurry tend to float, which causes a non-uniform pore distribution. To avoid this phenomenon, the viscosity of the slurry was increased to the extent that the movement of hollow microspheres ceased in the slurry. As a result, a uniform pore distribution was achieved.

• Journal of the Korean Ceramic Society
• /
• v.35 no.12
• /
• pp.1308-1315
• /
• 1998

Effects of particle size of alumina on densification behavior during liquid-phase sintering of alumina-talc system were investigated with emphasis on particle rearrangement process. In the case of using coarse alu-mina powder densiication of specimens was rapidly accelerated after formation of liquid phase due to easy particle rearrangement process with addition of talc and increase of sintering temperature. On the contrary when fine alumina powder was used premature densification of alumina matrix region formed before for-mation of liquid phase rigid skeleton structure and then it seemed to inhibit rearrangement process during crease of sintering temperature. As results the densification of specimens using coarse alumina powder was higher than that of the case of using fine one.

• Journal of the Korean Ceramic Society
• /
• v.54 no.4
• /
• pp.331-339
• /
• 2017

Porous alumina-based ceramics are of special interest due to their outstanding mechanical properties and their thermal and chemical stability. Nevertheless, the high electrical resistance of alumina-based ceramics, due to the generation of static electricity, leads to difficulty in applying a vacuum chuck in the semi-conductor process. Therefore, development of alumina-based ceramics for applications with vacuum chucks aims to have primary properties of low electrical resistance and high air permeability. In this study, we tailored the electrical resistance of porous alumina-based ceramics by adjusting the amount of $MnO_2$ (with $TiO_2$ fixed at an amount of 2 wt%) and by using coarse alumina powder for high air permeability. The characteristics of the specimens were studied using scanning electron microscopy, mercury porosimeter, capillary flow porosimetry, universal testing machine, X-ray diffraction and high-resistance meter.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1994.03a
• /
• pp.159-166
• /
• 1994

A constitutive model was proposed to analyze creep densification and grain growth of alumina powder compacts during high temperature processing. Theoretical results from the constitutive model were compared with various experimental data of alumina powder compacts in the literature including pressureless sintering, sinter forging and hot pressing. The proposed constitutive equations were implemented into finite element analysis program (ABAQUS) to simulate densification for more complicated geometry and loading conditions. High temperature forming processing of alumina compact with complicated shape was simulated. Processing of Alumina Powder Compacts

• Journal of the Korean Ceramic Society
• /
• v.32 no.4
• /
• pp.482-488
• /
• 1995

The phase transformation temperature from $\theta$- to $\alpha$-alumina was lowered from 1214$^{\circ}C$ to 114$0^{\circ}C$ in DSC by treating ${\gamma}$-alumina obtained by calcination of boehmite at $700^{\circ}C$ for 2hrswith $\alpha$-Al2O3 seeds (d50=0.36${\mu}{\textrm}{m}$) and 3wt% of the alumina sol. $\alpha$-Al2O3 seeds seemed to lower to the transformation temperature and the alumina sol suppressed the high temperature agglormeration. The effect was increased as the amount of the sol was increased, which was supported by TEM and particle size distribution. For an example, spherical ${\gamma}$-alumina powder with d50=0.54${\mu}{\textrm}{m}$ was prepared by treating the ${\gamma}$-alumina with 9 wt% of the alumina sol and 3wt% of the $\alpha$-Al2O3. It sintered to 99% of the theoretical density at 150$0^{\circ}C$ for 2hrs. and it had relatively homogeneous microstructure with 2~3${\mu}{\textrm}{m}$ sized grains.

• Korean Journal of Materials Research
• /
• v.23 no.4
• /
• pp.250-254
• /
• 2013

In order to increase the toughness of ZTA(zirconia toughened alumina) ceramics, the present study focused on rearrangement and densification of particles according to the particle size of the parent material. When rough alumina was used for production of ZTA, densification behavior was observed in the specimen sintered at a temperature over $1550^{\circ}C$. However, it was found that the densification behavior was occurred in the specimen sintered at $1450^{\circ}C$ when fine alumina powder was used. High relative density exceeding 98% was obtained when fine alumina powder was mixed with 15 wt% of 3Y-TZP and sintered at $1600^{\circ}C$. Also, a hardness of 1820.2 Hv was obtained when a specimen containing 10 wt% of 3Y-TZP was sintered at $1600^{\circ}C$. In the case of 3Y-TZP containing rough alumina powder that had been sintered the hardness value was around 1720.3 Hv. It was predicted that an improved toughening effect in ZTA could be achieved by using finer alumina powder as the parent material.

• Journal of the Korean Ceramic Society
• /
• v.43 no.12 s.295
• /
• pp.859-864
• /
• 2006

For the pressure compaction process of the ceramic powder, the green density is very different with both the ceramic body shape and the processing conditions. The density difference cause non-uniform shrinkages and deformations, and make cracks in the sintered ceramics. In this paper, Material properties of the alumina powder mixed with binder and the friction coefficient between the powder and the tool set were determined through the simple compaction experiments: Also the powder flow characteristics were simulated and the green density was analyzed during the powder compaction process with Finite Element Method (FEM). The results show that the density distributions of the green body were improved at the optimized processing condition and both the possibility of the farming crack generation and rho deformation of the sintered Alumina body were reduced.

• Journal of the Korean Ceramic Society
• /
• v.36 no.6
• /
• pp.662-670
• /
• 1999

Porous alumina was fabricated from pressureless powder packing forming method using powders granulated by spray drying. It was investigated the pore size distribution of fabricated porous alumina. The results of microstructural observation showed that intraganular pore size and intragranular pore size. At 1700$^{\circ}C$ there were no intragranular pores but it showed homogeneous distribution of intergranular pore size. The bending strength and shrinkage increased as porosity decreased. In case of thermal shock resistance sudden decrease of bending strength to $\Delta$T was not shown because intergranular large pore prevented sudden crack propagation.