• Journal of the Korean Ceramic Society
• /
• v.25 no.1
• /
• pp.66-72
• /
• 1988

The effect of salts on the formation of ${\alpha}$-hemihydrated gypsum at boiling temperature under atmospheric pressure was studied by the solubility measurement method, and the formation of ${\alpha}$-hemihydrated gypsum from by-product gypsum of phosphoric acid process in the salts solution were investigated. The order of catalytic effect of salt on the formation of ${\alpha}$-hemihydrated gypsum are as follows: NH4Cl>NaCl>NaNO3. In the salts solution of sodium nitrate, sodium chloride, and ammonium chloride, prismatic ${\alpha}$-hemihydrated gypsum was obtained and the crystal form was converted to needle form in complex solution with sulfuric acid. The P2O5 content in gypsum was largely decreased in this atmosphoric solution process.

• Resources Recycling
• /
• v.15 no.3 s.71
• /
• pp.20-29
• /
• 2006

This study was carried out for to recover the purified crystalline gypsum from phosphogypsum by means of using it's crystallographical Properties. The dehydration of hydrated phosphogypsum to $\alpha$-hemihydrate is completed with the 2 hours treatment of it in $99^{\circ}C$ waterrs. The purified crystalline gypsum having the maximum size of $200{\mu}m$ was obtained by 325# wet screening after recrystallization of the $\alpha$-hemihydrate gypsum at the condition of $Na_2SO_4$ 10 wt%, slurry density 20%, $pH\;5{\sim}6,\;65^{\circ}C$ and 4hr. In this process, the yield of gypsum was 93.9% and its grade was 99%.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.26 no.1
• /
• pp.67-72
• /
• 2022

Concrete prevents corrosion of reinforcing bars due to its strong alkalinity. However, in the sea, strong alkali components with a pH of 12 to 13 are eluted, which adversely affects the ecological environment and growth of marine organisms. In this study, the mechanical properties and durability of the low alkali mortar were evaluated for the development of a low alkali mortar for the 3D printed artificial reefs. As a result of evaluation of strength characteristics, the α-35 mixture, which were produced with fly ash, silica fume and α-hemihydrate gypsum, satisfied the strength requirement 27 MPa in terms of compressive strength. As a result of pH measurement, it was found that mixing with alpha-type hemihydrate gypsum resulted in minimizing pH due to the the formation of calcium sulfate instead of calcium hydroxide production. As a result of the chloride ion penetration resistance test, the α-35 mixture exhibited the best performance, 3844C. As a result of measuring the length change over time, the α-35 mixture showed the shrinkage 33.5% less compared to the Plain mix.