Synthesis of Crystalline Calcium Sulfate Dihydrate from Phosphogypsum

This study was carried out for to recover the purified crystalline gypsum from phosphogypsum by means of using it's crystallographical Properties. The dehydration of hydrated phosphogypsum to $\alpha$-hemihydrate is completed with the 2 hours treatment of it in $99^{\circ}C$ waterrs. The purified crystalline gypsum having the maximum size of $200{\mu}m$ was obtained by 325# wet screening after recrystallization of the $\alpha$-hemihydrate gypsum at the condition of $Na_2SO_4$ 10 wt%, slurry density 20%, $pH\;5{\sim}6,\;65^{\circ}C$ and 4hr. In this process, the yield of gypsum was 93.9% and its grade was 99%.

인산부생석고(燐酸副生石膏)로부터 결정질(結晶質) 이수석고(二水石膏)의 제조(製造)

본 연구는 인산부생석고를 결정성장시켜 고순도의 결정질 이수석고를 제조하여 다용도의 석고를 얻고자 하였다. $99^{\circ}C$의 수중에서 약 2시간 동안에 이수석고는 $\alpha$형의 반수석고로 탈수가 완료되었다. 수중탈수된 반수석고를 매정제 $Na_2SO_4$를 10wt%, 슬러리 농도는 20%, pH가 $5{\sim}6$, 결정성장온도 $65^{\circ}C$의 조건에서 4시간 동안 결정성장 시키면 장경이 $200{\mu}m$정도인 결정을 얻을 수 있었다. 결정성장이 끝난 슬러리를 325#로 습식사분하여 사상산물로 고순도 결정성장 석고를 얻었으며, 이 때 석고의 회수율은 약 93.9%, 순도는 99% 정도 였다.