• Journal of the Korean Ceramic Society
• /
• v.27 no.3
• /
• pp.337-344
• /
• 1990

As a function of sintering temperature and time, the electrical properties of ruthenium based thick film resistors were investigated with microstructure. The variatio of resistivity and TCR(temperature coefficient of resistance)trends of sintered speciman at various sintering temperature were different low resistivity paste(Du Pont 1721) from high one(Du Pont 1741). These phenomena are deeply relative to microstructure of sintered film. With increasing the sintering temperature for 1721 system, the electrical sheet resistivity decreased, but again gradually increased above 80$0^{\circ}C$. And TCR trends in 1721 system are all positive. On the other hand the electrical sheet resistivity of 1741 resistor system decreased with sintering temperature. And TCR trends variable according to sintering temperature. TCR of speciman sintered at $700^{\circ}C$ was negative value, and TCR of 80$0^{\circ}C$ sintered speciman coexisted negative and positive value. But in case of speciman sintered at 90$0^{\circ}C$, TCR was positive value. As results of this fact, it was well known that the charge carrier contributied to electrical conduction in 1741 resistor system varied with sintering temperature.

• The Journal of Advanced Prosthodontics
• /
• v.2 no.2
• /
• pp.33-38
• /
• 2010

PURPOSE. Marginal fit is a very important factor considering the restoration's long-term success. However, adding porcelain to copings can cause distortion and lead to an inadequate fit which exposes more luting material to the oral environment and causes secondary caries. The purpose of this study was to compare the marginal fit of 2 different all-ceramic crown systems before and after porcelain veneering. This study was also intended to verify the marginal fit of crowns originated from green machining of partially sintered blocks of zirconia (Lava CAD/CAM system) and that of crowns obtained through machining of fully sintered blocks of zirconia (Digident CAD/CAM system). MATERIALS AND METHODS. 20 crowns were made per each system and the marginal fit was evaluated through a light microscope with image processing (Accura 2000) at 50 points that were randomly selected. Each crown was measured twice: the first measurement was done after obtaining a 0.5 mm coping and the second measurement was done after porcelain veneering. The means and standard deviations were calculated and statistical inferences among the 2 groups were made using independent t-test and within the same group through paired t-test. RESULTS. The means and standard deviations of the marginal fit were $61.52{\pm}2.88{\mu}m$ for the Digident CAD/CAM zirconia ceramic crowns before porcelain veneering and $83.15{\pm}3.51{\mu}m$ after porcelain veneering. Lava CAD/CAM zirconia ceramic crowns showed means and standard deviations of $62.22{\pm}1.78{\mu}m$ before porcelain veneering and $82.03{\pm}1.85{\mu}m$ after porcelain veneering. Both groups showed significant differences when analyzing the marginal gaps before and after porcelain veneering within each group. However, no significant differences were found when comparing the marginal gaps of each group before porcelain veneering and after porcelain veneering as well. CONCLUSION. The 2 all-ceramic crown systems showed marginal gaps that were within a reported clinically acceptable range of marginal discrepancy.

• Journal of Korean society of Dental Hygiene
• /
• v.14 no.4
• /
• pp.447-452
• /
• 2014

With the increase of esthetic demands, most patients want to have restorations which are not only functional but also esthetic. For the esthetic restoration, many ceramic systems have been introduced and applied in dentistry. Among those ceramic restorations, IPS e.max system composed of lithium disilicate glass ceramic is one of the most commonly used systems because it has strength and esthetic characteristics. IPS e.max system is divided into IPS e.max Press and IPS e.max CAD according to the manufacturing methods. IPS e.max Press is fabricated through heat-pressed technique with ceramic ingot, which is very simple. The restorations which are made using IPS e.max system can apply to 3 units restoration for the anterior teeth and premolar, and single posterior tooth restoration. Cementation is one of the most important clinic procedure for the longevity of the restorations. All ceramics are bonded by resin cements, it is classified into three groups including adhesive, self-adhesive, and conventional. Variolink N, which is an adhesive resin cement and manufactured by same company with IPS e.max, is recommended for the bonding of IPS e.max restoration. Conventional and self-adhesive resin cement is also available. The aim of this review article is to provide the understanding of material properties, production procedure and clinical application of IPS e.max system.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.3
• /
• pp.224-232
• /
• 2015

PURPOSE. The purpose of this study was to find out the effect of immediate dentin sealing (IDS) on bond strength of ceramic restoration under various thermocycling periods with DBA (dentin bonding agent system). MATERIALS AND METHODS. Fifty freshly extracted human mandibular third molars were divided into 5 groups (1 control and 4 experimental groups) of 10 teeth. We removed enamel layer of sound teeth and embedded them which will proceed to be IDS, using All Bond II. A thermocycling was applied to experimental groups for 1, 2, 7, 14 days respectively and was not applied to control group. IPS Empress II for ceramic was acid-etched with ceramic etchant (9.5% HF) and silane was applied. Each ceramic disc was bonded to specimens with Duo-link, dual curable resin cement by means of light curing for 100 seconds. After the cementation procedures, shear bond strength measurement and SEM analysis of the fractured surface were done. The data were analyzed with a one-way ANOVA and Tukey multiple comparison test (${\alpha}$=.05). RESULTS. There were no statistically significant differences between 4 experimental groups and control group, however the mean value started to decrease in group 7d, and group 14d showed the lowest mean bond strength in all groups. Also, group 7d and 14d showed distinct exposed dentin and collapsed hybrid layer was observed in SEM analysis. CONCLUSION. In the present study, it can be concluded that ceramic restorations like a laminate veneer restoration should be bonded using resin cement within one week after IDS procedure.

• Restorative Dentistry and Endodontics
• /
• v.23 no.1
• /
• pp.413-423
• /
• 1998

Dental ceramics exhibit excellent esthetic property, compressive strength, chemical durability, biocompatibility and translucency. This study evaluated the shear bond strength of composite resin to the new heat-pressed ceramic material (IPS-Empress System) depending on the surface treatments and bonding agents. The surface treatments were etching with 4.0% hydrofluoric acid, application of silane, and the combination of the two methods. Composite resin was bonded to ceramic with four kinds of dentin bonding agents(All-Bond 2, Heliobond, Scotch bond Multi-purpose and Tenure bonding agents). The ceramic specimen bonded with composite resin was mounted in the testing jig, and the universal testing machine(Zwick 020, Germany) was used to measure the shear bond strength with the cross head speed of 0.5 mm/min. The results obtained were as follows 1. The mean shear bond strength of the specimens of which the ceramic surface was treated with the combination of hydrofluoric acid and silane before bonding composite resin was significantly higher than those of the other surface treatment groups(p<0.05). 2. In the case of All-Bond 2 and Scotchbond Multi-purpose bonding agent group, the surface treatment methods did not influenced significantly on the shear bond(p>0.05). 3. Of the four bonding agents tested, the shear bond strength of Heliobond was significantly lower than those of other bonding agents regardless of the surface treatment methods(p<0.05). 4. The highest shear bond strength($12.55{\pm}1.92$ MPa) was obtained with Scotchbond Multipurpose preceded by the ceramic surface treatment with the combination of 4% hydrofluoric acid and silane.

• Journal of dental hygiene science
• /
• v.12 no.2
• /
• pp.123-129
• /
• 2012

The aim of study was to compare the color parameters and mean color difference of porcelain specimens by different veneering technique in order to examine the effect of veneering technique on esthetics of yttria-stabilized tetragonal zirconia polycrystalline(Y-TZP) all ceramic restoration. Three groups of square-shaped core ceramic specimens(14mm in diameter and 0.3, 0.5, 0.7 mm) and two groups of veneering ceramic specimen were prepared for analysis. Color parameter($L^*,a^*,b^*$) and color difference of zirconia core squares and core-veneer specimens were measured with ShadeEye $NCC^{(R)}$ spectrophotometer, respectively. Mean color difference(${\Delta}E^*$)were calculated using color difference formula. Two-way analysis of variance(ANOVA) combined with a Tukey multiple-range test were used to analysis the data(${\alpha}=0.05$). ${\Delta}E^*$ values were not significantly affected by core thickness and veneering porcelain(p=0.083). The color differences(${\Delta}E^*$) of core-veneer specimens with 0.5, 0.7 mm-A1,A2,A3.5 shade were mostly below 3.7 which was within the clinically acceptable range, while color differences between 0.3 mm-A1,A2 showed more than 3.7. All-ceramic system has color characteristics that clinicians have to consider when selecting materials. Also, manufacturers of different porcelain systems must make every effort to achieve color reproducibility.

• The Journal of Korean Academy of Prosthodontics
• /
• v.40 no.3
• /
• pp.262-268
• /
• 2002

Statement of problem. In-Ceram system is one of the all-ceramic crowns that can be used in anterior 3 unit fixed partial dentures and posterior single crowns. The alumina core used in In-Ceram system is manufactured using slip-casting technique. The slip-casting technique is difficult and technique sensitive. To improve this problem, tape-casting method was introduced into dentistry. There were no studies to examine the effect of margin design on the margin fitness of all-ceramic crowns fabricated from alumina tape. Purpose. The purpose of this study was to compare the marginal fitness of glass infiltrated alumina core fabricated from aqueous-based alumina tape according to different margin types ($90^{\circ},\;110^{\circ},\;135^{\circ}$ shoulder margin). Material and method. Three upper central resin incisors were prepared with $90^{\circ},\;110^{\circ}$, and $135^{\circ}$ shoulder margins for all-ceramic crowns, respectively. The resin teeth were duplicated and master die and special plaster die were made as usual. After alumina cores were fabricated from aqueous-based alumina tape, cores were cemented to each 15 epoxy dies replicated from three resin teeth with resin cement. These cemented cores were embedded in epoxy resin. Specimens were cut mesiodistally and buccolingually. Marginal gap and discrepancy were measured under microscope. Results. The marginal gap and discrepancy of $90^{\circ}$ marginal angle was $75.1{\mu}m,\;86.6{\mu}m,\;110^{\circ}$ marginal angle was $41.5{\mu}m,\;50.7{\mu}m$ and $135^{\circ}$ marginal angle was $51.7{\mu}m,\;54.2{\mu}m$, respectively. The smallest value was seen in 110 (angle, which was statistically significant compared to that of $90^{\circ}$ angle (p<0.05). Conclusion. Marginal fitness of alumina cores made of alumina tape with $110^{\circ}$ shoulder margin was best and others were clinically acceptable.

• Journal of the Korean Ceramic Society
• /
• v.47 no.5
• /
• pp.457-460
• /
• 2010

$SmCoO_3$ system was investigated for their application to themoelectric materials. All specimens showed p-type semiconducting behavior and their electrical conductivity ($\sigma$), Seebeck coefficient (S) and power factor were measured at high temperature. And the effect of dopant ions on their thermoelectrical properties were also investigated. $Fe^{3+}$ ion doped into $Co^{3+}$ site enhanced the Seebeck coefficient and decreased the electrical conductivity simultaneously. The maximum Seebeck coefficient value for 60% doping case reached to 780 ${\mu}V$/K at $240^{\circ}C$. However $Fe^{3+}$ doped system cause an negative effect on power factor value. In case of the pure phase, the maximum Seebeck coefficient value reached to 290 ${\mu}V$/K at $240^{\circ}C$ and the maximum electrical conductivity was obtained 748 1/(ohm$\times$cm) at $960^{\circ}C$. As a result, the maximum power factor was obtained $1.49\times10^{-4}$ W/$mK^2$ at $550^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.41 no.12 s.271
• /
• pp.873-879
• /
• 2004

In all major industries ranging from powder industries and advanced ceramics, to the food and pharmaceutical manufacture powder industries, the main production process is the spray dryers. In this paper, a systematic approach is used and six rules are obtained for the basis of the fuzzy model. A fuzzy model is based on the past behavior of the target system and expected to be able to reproduce the behavior of the target system. The output of the developed fuzzy model shows, graphically and statistically, a high level of face validity. Therefore, it is concluded that the developed fuzzy model mimics the actual process and can be considered, with confidence, as a reliable model to study, analyze, and improve the existing process.

• Journal of the Korean Ceramic Society
• /
• v.46 no.6
• /
• pp.689-694
• /
• 2009

Layer-structured $Na_xCo_2O_4$ was synthesized from $Na_2CO_3\;and\;Co_3O_4$ powders. The chemical concentrations of Na and additive were controlled to enhance the thermoelectric properties over the temperature range from 400 K to 1,150 K. As a result, we obtained the maximum thermoelectric properties at a single phase region with Na content of x=1.5. When Na content was smaller than x=1.5, the thermoelectric properties was low due to formation of second phases of CoO and other oxides. Additionally, Mn was doped to improve thermoelectric properties by means of decreasing thermal conductivity. The results showed that the concentrations of both Na and Mn are all governing factors to determine the thermoelectric properties of $Na_xCo_2O_4$ system.