• Journal of Korea Foundry Society
• /
• v.42 no.5
• /
• pp.273-281
• /
• 2022

In order to understand the solidification behavior and microstructural evolution of the Al-Cu-Si ternary eutectic alloy system, changes of the microstructure of the Al-Cu-Si ternary eutectic alloy with different cooling rates were investigated. When the mold preheating temperature is 500℃, primary Si and Al2Cu dendrites are observed, with (α-Al+Al2Cu) binary eutectic and needle-shaped Si subsequently observed. In addition, even when the mold preheating temperature is 300℃, primary Si and Al2Cu dendrites can be observed, and both (α-Al+Al2Cu+Si) areas observed and areas not observed earlier appear. When the mold preheating temperature is 150℃, bimodal structures of the binary eutectic (α-Al+Al2Cu) and ternary eutectic (α-Al+Al2Cu+Si) are observed. When the preheating temperature of the mold is changed to 500℃, 300℃, and 150℃, the greatest change is in the Si phase, and upon reaching the critical cooling rate, the ternary eutectic of (α-Al+Al2Cu+Si) forms. If the growth of the Si phase is suppressed upon the formation of (α-Al+Al2Cu+Si), the growth of both Al and Cu is also suppressed by a cooperative growth mechanism. As a result of analyzing the Al-27wt%Cu-5wt%Si ternary eutectic alloy with a different alloy design simulation programs, it was confirmed that different results arose depending on the program. A computer simulation of the alloy design is a useful tool to reduce the trial and error process in alloy design, but this effort must be accompanied by a task that increases reliability and allows a comparison to microstructural results derived through actual casting.

• Journal of Korea Foundry Society
• /
• v.21 no.2
• /
• pp.119-126
• /
• 2001

Al/15%Gr. composite have been manufactured by mixing, compacting, and extruding aluminium powder and graphite powder. Then, Al-6%Si/x%Gr., Al-12%Si/x%Gr., and Al-18%Si/x%Gr.(x: 0, 2, 4, 6, 8) composites have been manufactured by remelting the extruded materials(Al/15%Gr.), Al-33.3%Si alloy, and Al ingot, etc. We conducted experiments to chracterize the microstructure, and damping properties and hardness. The result of microstructure experiment on Al-x%Si/y%Gr. composites reveals the good dispersion of graphite. As to Al-Si/y%Gr. composites, the more the graphite contents, the less the tensile strength. And the tensile strength varied according to contents of Si: with its highest value in Al-18%Si/y%Gr. composites and lowest in Al-6%Si/y%Gr. composites. As to Al-x%Si/y%Gr. composites, the more the contents of graphite, the more the vibration damping properties. And we can get the highest vibration damping rate in Al-12%Si/y%Gr. composites which matrix structure is an eutectic component.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.2
• /
• pp.110-115
• /
• 2018

The Na low temperature gettering in $SiO_2/PSG/SiO_2/Al-1%Si$ and $SiO_2/TEOS/SiO_2/Al-1%Si$ multilevel thin films was investigated using dynamic SIMS(secondary ion mass spectrometry) analysis. DC magnetron sputter, APCVD and PECVD techniques were utilized for the deposition of Al-1%Si thin films, $SiO_2/PSG/SiO_2$ and $SiO_2/TEOS/SiO_2$ passivations, respectively. Heat treatment was carried out at $300^{\circ}C$ for 5 h in air. SIMS depth profiling was used to determine the distribution of Na, Al, Si and other elements throughout the $SiO_2/PSG/SiO_2/Al-1%Si$ and $SiO_2/TEOS/SiO_2/Al-1%Si$ multilevel thin films. XPS was used to analyze chemical states of Si and O elements in $SiO_2$ passivation layers. Na peaks were observed throughout the $PSG/SiO_2$ and $TEOS/SiO_2$ passivation layers on the Al-1%Si thin films and especially at the interfaces. Na low temperature gettering in $SiO_2/PSG/SiO_2/Al-1%Si$ and $SiO_2/TEOS/SiO_2/Al-1%Si$ multilevel thin films is considered to be caused by a segregation type of gettering.

• Journal of the Korean Ceramic Society
• /
• v.43 no.10 s.293
• /
• pp.595-600
• /
• 2006

The preparation of $\beta$-SiAlON powder by SHS in the system of $Si-Al-SiO_2-NH_4F(\beta-Si_3N_4)$ was investigated in this study. In the preparation of SiAlON powder, the effect of gas pressure, compositions such as Si, $NH_4F$, \beta-Si_3N_4$ and additive in mixture on the reactivity were investigated. At 50 atm of the initial inert gas pressure in reactor, the optimum composition for the preparation of pure $\beta$-SiAlON was $3Si+Al+2SiO_2+NH_4F$. The $\beta$-SiAlON powder synthesized in this condition was a single phase $\beta$-SiAlON with a rod like morphology.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.2
• /
• pp.109-115
• /
• 2003

Quaternary Ti-Al-Si-N films were deposited on WC-Co substrates by a hybrid deposition system of arc ion plating (AIP) method for Ti-Al source and DC magnetron sputtering technique for Si incorporation. The synthesized Ti-Al-Si-N films were revealed to be composites of solid-solution (Ti, Al, Si)N crystallites and amorphous Si3N4 by instrumental analyses. The Si addition in Ti-Al-N films affected the refinement and uniform distribution of crystallites by percolation phenomenon of amorphous silicon nitride, similarly to Si effect in TiN film. As the Si content increased up to about 9 at.%, the hardness of Ti-Al-N film steeply increased from 30 GPa to about 50 GPa. The highest microhardness value (~50 GPa) was obtained from the Ti-Al-Si-N film haying the Si content of 9 at.%, the microstructure of which was characterized by a nanocomposite of nc-(Ti,Al,Si) N/a$-Si_3$$N_4$.

• Journal of Powder Materials
• /
• v.21 no.6
• /
• pp.460-466
• /
• 2014

Al-Si-SiC composite powders with intra-granular SiC particles were prepared by a gas atomization process. The composite powders were mixed with Al-Zn-Mg alloy powders as a function of weight percent. Those mixture powders were compacted with the pressure of 700 MPa and then sintered at the temperature of $565-585^{\circ}C$. T6 heat treatment was conducted to increase their mechanical properties by solid-solution precipitates. Each relative density according to the optimized sintering temperature of those powders were determined as 96% at $580^{\circ}C$ for Al-Zn-Mg powders (composition A), 97.9% at $575^{\circ}C$ for Al-Zn-Mg powders with 5 wt.% of Al-Si-SiC powders (composition B), and 98.2% at $570^{\circ}C$ for Al-Zn-Mg powders with 10 wt.% of Al-Si-SiC powders (composition C), respectively. Each hardness, tensile strength, and wear resistance test of those sintered samples was conducted. As the content of Al-Si-SiC powders increased, both hardness and tensile strength were decreased. However, wear resistance was increased by the increase of Al-Si-SiC powders. From these results, it was confirmed that Al-Si-SiC/Al-Zn-Mg composite could be highly densified by the sintering process, and thus the composite could have high wear resistance and tensile strength when the content of Al-Si-SiC composite powders were optimized.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2007.11a
• /
• pp.128-129
• /
• 2007

Cr-Al-N, Cr-Si-N 그리고 Cr-Al-Si-N 코팅막을 WC-Co 모재위에 AIP법과 DC 마그네트론 스퍼터링 법을 결합한 하이브리드 시스템을 이용하여 합성하였으며, Si함량에 따른 Cr-Al-Si-N 코팅막의 미세구조, 기계적 특성과 마찰 거동에 관해 비교 연구하였다. Cr-Si-N(${\sim}35GPa$)과 Cr-Al-Si-N(${\sim}55GPa$) 코팅막의 경도값은 CrN(${\sim}23GPa$)과 Cr-Al-N(${\sim}25GPa$) 코팅막과 비교하여 각각 증가하였고, CrN(${\sim}0.50$)과 Cr-Al-N(${\sim}0.84$)의 평균 마찰계수는 Si 함량이 9 at.% 일때, Cr-Si-N(${\sim}0.30$)과 Cr-Al-Si-N(${\sim}0.57$)으로 각각 감소하였다.

• 연구논문집
• /
• s.26
• /
• pp.103-112
• /
• 1996

$Al_2O_3/SiC$ Hybrid-Composite has been fabricated by conventional powder process. The addition of $\alpha-Al_2O_3$ as seed particles in the transformation of $\gamma-Al_2O_3 to $\alpha-Al_2O_3$ provided a homogeneity of the microstructure, resulting in increase of mechanical properties. The grain growth of $Al_2O_3$ are significantly surpressed by the addition of nano-sized. SiC particles, increasing in fracture strength. The addition of SiC plates to $Al_2O_3$ nano-composite decreased the fracture strength, but increased the fracture toughness. Coated SiC plates with nitrides such as BN and /SiC$Si_3N_4$ enhanced fracture toughness much more than uncoated SiC plates by inducing crack deflection.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.535-543
• /
• 1997

The surface of SiC particles were partially oxidized to produce SiO2 layers on the SiC particles to prepare Al2O3/SiC composite by formation of mullite bonds between the grains of Al2O3 and SiC during sintering at 1$600^{\circ}C$. This process is considered to enable the sintering of Al2O3/SiC composite at lower temperature and also to relieve the stress, produced by thermal expansion mismatch between Al2O3 and SiC. In fact, Al2O3/SiC composite prepared by oxidation of SiC was observed to be more effectively sintered and densified at lower temperature. Maximum density, flexural strength and microhardness were obtained with 5.65 vol% of mullite content in Al2O3/SiC composite.

• Journal of Korea Foundry Society
• /
• v.20 no.2
• /
• pp.89-96
• /
• 2000

The effects of modification processing on the refinement of primary Si and the wear behavior of hyper-eutectic Al-Si alloys have been mainly investigated. Refining effects of primary Si in Al-17%Si alloy was more efficient than that of B.390 alloy. Optimum condition of getting the finest primary Si microstructure was when AlCuP modifier is added into the melt at $750^{\circ}C$ and held it at $700^{\circ}C$ for 30 minutes. Wear loss in the specimens of as-cast condition decreases as the size of primary Si decreases, in the order of B.390 alloy, B.390 alloy with AlCuP addition, Al-17%Si alloy and Al-17%Si alloy with AlCuP addition. Wear loss in the aged condition of Al-17%Si alloy, B.390 alloy and B.390 alloy with AlCuP addition decreased due to the increase of compressive residual stress in the matrix by the aging treatment. While, wear loss increased in the aged specimens of Al-17%Si alloy with AlCuP addition and Hepworth addition in which compressive residual stress decreases by the aging treatment. Therefore, it is assumed that higher compressive residual stress in the matrix can reduce the wear loss in composite materials such as hyper-eutectic Al-Si alloys.