• 한국표면공학회지
• /
• 제46권6호
• /
• pp.242-247
• /
• 2013

Zr-Al-N coatings were synthesized by the hybrid coating system combining arc ion plating and DC magnetron sputtering from a Zr and an Al target in argon-nitrogen atmosphere, respectively. By changing the power applied on the Al cathodes, the Zr-Al-N coatings with various Al contents were deposited. The microstructure and chemical compositions of the Zr-Al-N coatings were studied by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM). With increasing of Al content in the coatings, the solid solution (Zr, Al)N crystallites were observed in the Zr-Al-N coatings. The nanohardness of the Zr-Al-N coatings exhibited a maximum value of 42 GPa for the Zr-Al (7.9 at.%)-N, and decreased with further increase in Al content in the coatings. The oxidation and corrosion behavior of the Zr-Al-N coatings revealed better properties compared than those of ZrN coatings due to the formation of a solid solution.

• 한국표면공학회지
• /
• 제37권3호
• /
• pp.152-157
• /
• 2004

Ti-Al-N ($Ti_{75}$ $Al_{25}$ N) and Ti-Al-Si-N ($Ti_{69}$ $Al_{23}$ $Si_{8}$N) coatings synthesized by a DC magnetron sputtering technique were studied comparatively with respect to phase characterization and high-temperature oxidation behavior. $Ti_{69}$ $Al_{23}$ $Si_{ 8}$N coating had a nanocomposite microstructure consisting of nanosized(Ti,Al,Si)N crystallites and amorphous $Si_3$$N_4$, with smooth surface morphology. Ti-Al-N coating of which surface $Al_2$$O_3$ layer formed during oxidation suppressed further oxidation. It was sufficiently stable against oxidation up to about $700^{\circ}C$. Ti-Al-Si-N coating showed better oxidation resistance because both surface Ab03 and near-surface $SiO_2$ layers suppressed further oxidation. XRD, GDOES, XPS, and scratch tests were performed.

• 한국세라믹학회지
• /
• 제48권2호
• /
• pp.160-167
• /
• 2011

Plasma sprayed ceramic coatings inherently contain pores and usually also cracks. Post-treatment of the plasma sprayed coatings is a way to close the connected pores and cracks. In this study, post-sealing treatment in plasma sprayed $Al_2O_3$ coatings was employed to overcome the reduction of coating properties. $Al_2O_3$ plasma thermal spray coating was made on aluminum alloys plate, $CrO_3$ post coating and heat treatment at $550^{\circ}C$ was carried out in order for final $Cr_2O_3$ to be saturated through phase transformation. Chromia sealing began at the fine defect in coated microstructure, while larger pores were permeated later. The increase in concentration and treatment frequency of sealing solution resulted in the decrease of porosity of coating layer, while cracks occurred partially after the third treatment. After twice treatment of 10M $CrO_3$ solution, microhardness and breakdown voltage of $Al_2O_3$ coatings were found to increase by ${\fallingdotseq}$ 50% and ${\fallingdotseq}$ 390% respectively than without post-treatment.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.826-829
• /
• 2004

An increasing interest in fire safety engineering can currently be identified in Korea and overseas. The fire-resistant characteristics of spray coating material for fire protection with or without nano $Al(OH)_3$ colloid has been experimentally investigated and the results are presented in this paper. The fire-resistance characteristics of spray coating material with nano $Al(OH)_3$ were superior to those without $Al(OH)_3$. Especially, spray coating material with nano material showed that thermal characteristic in the early days was remarkably excellent.

• 동력기계공학회지
• /
• 제12권3호
• /
• pp.60-65
• /
• 2008

This study aims at investigating the wear properties of thermally sprayed $Al/Al_2O_3$ metal matrix composite(MMC) coating against different counterparts. $Al/Al_2O_3$ MMC coatings were fabricated using a flame spray system on an Al 6061 substrate. Dry sliding wear tests were performed using the sliding speeds of 0.2m/s and the applied loads of 1 and 2 N. AISI 52100, $Al_2O_3$, $Si_3N_4\;and\;ZrO_2$ balls(diameter: 8mm) were used as counterpart materials. Wear properties of $Al/Al_2O_3$ MMC coatings were analyzed using a scanning electron microscope(SEM) and energy dispersive X-ray spectroscopy (EDX). It was revealed that wear properties of $Al/Al_2O_3$ composite coatings were much influenced by counterpart materials. In the case of AISI 52100 used as counterparts, the wear rate of composites coating layer increased according to the increase of the applied load. On the contrary, in the case of ceramics used as counterparts, the wear rate of composites coating layer decreased according to the increase of the applied load.

• 한국세라믹학회지
• /
• 제32권10호
• /
• pp.1147-1161
• /
• 1995

When ceramic membrance was made from metal salt solution in place of metal akoxide solution, crack free and good adhesion to supporter was optimized for sol stability and good adhesion force. A starting sol was prepared from aluminum oxychloride aqueous solutjion in order to inhibit the grain growthof Al2O3 during heat treatment. The crack free dip coating can't be achieved in 1mol/ι zirconium oxychloride solution because of the high viscosity which interferes with the hydration copolymerization between Al3+ ion and Zr4+ ion. Thus Al2O3-ZrO2 sol stability and viscosity for dip coating was effective when 0.01 mol/ι zirconium oxychloride was added. The minimizing of crack and achieving better adhesion to the supporter wa obtained by microwave drying, surfactant addition and ultrasonic dip coating in wet atmosphere. The result seems to minimize the capillary force and improve the adhesive ability to supporter during the process. Where the average pore size of Al2O3-ZrO2 ultrafilter ceramic membrane measured 17 Å by the BET method and observed γ-Al2O3 phase with tetragonal zirconia after firing at 700℃.

• Corrosion Science and Technology
• /
• 제9권6호
• /
• pp.233-238
• /
• 2010

Hot-dipped Al-Mg-Si coatings to alternate Zn and Zn alloy coatings for steel were examined on metallographic structure, corrosion resistance, sacrificial ability, formation and growth of inter-metallic compounds, and mechanical properties. Near the eutectic composition of quasi-binary system of Al-$Mg_2Si$, very fine eutectic structure of ${\alpha}$-Al and $Mg_2Si$ was obtained and it showed excellent corrosion resistivity and sacrificial ability for a steel in sodium chloride solutions. Formation and growth of Al-Fe inter-metallic compounds at the interface of substrate steel and coated layer was suppressed by addition of Si. The inter-metallic compounds layer was usually brittle, however, the coating layer did not peel off as long as the thickness of the inter-metallic compounds layer was small enough. During sacrificial protection of a steel, amount of hydrogen into the steel was more than ten times smaller than that of Zn coated steel, suggesting to prevent hydrogen embrittlement. Al-Mg-Si coating is expected to apply for several kinds of high strength steels.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 추계학술대회 논문집
• /
• pp.307-310
• /
• 2009

Nowadays, the usage of high strength steel has been growing in automobile industry mainly as structural parts since for its lightweight and high strength properties the oil crisis happened. Owing to poor formability, complex-shaped high-strength steel components are invariably produced through hot press forming. The high-strength steel sheets are in so me instances used with an Al-Si-coating with a view to prevent scaling of components during hot press forming. How ever, friction and fracture characteristics of Al-Si-coated high-strength steel during hot press forming process have not yet been investigated. In this paper, the formed parts which were formed in hot bending process were investigated by using EDS. SEM and nano indenter in order to analysis the coating layer behavior.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2008년도 추계학술대회 초록집
• /
• pp.47-47
• /
• 2008

Cr and AlSi (Si=20 and 66 at.%) target들을 이용하여 Closed-field unbalanced magnetron sputtering (CFUBMS)으로 증착된 주기($\Lambda$)가 2.3 nm에서 8.0nm인 CrN/AlSiN multilayer coatings의 crystal structure, 화학적 조성, 및 기계적 특성을 glow discharge optical emission spectroscopy (GDOES), X-ray diffractometry (XRD), X-ray photoelectron spectroscopy (XPS) and nano-indenter 등의 분석장비를 이용하여 분석하였다. 고온안정성을 시험하기 위하여 $800^{\circ}C$와 $1000^{\circ}C$ 공기중 에서 30분 열처리하였다. CrN/AlSiN multilayer coatings의 고온안정성은 Si조성이 증가함에 따라 향상되었다. Si이 18.2 at.%함유된 coating이 가장 우수한 고온안정성을 갖고 있다.

• 한국윤활학회:학술대회논문집
• /
• 한국윤활학회 2000년도 제32회 추계학술대회 정기총회
• /
• pp.80-88
• /
• 2000

The plasma spray technics has known as one of the surface modification methods to improve the mechenical properties or the functional charactristics of materials. This paper has been aimed to investigate the effects of plasma sprayed conditions, such as spray distance and arc power level, on sliding wear properties of plasma sprayed $Al_2$O$_3$-40%TiO$_2$coating layer. The sliding wear test using pin-on-disc type wear machine, has been conducted in several sliding speed for coating layer sparyed under different conditions. The result of this paper is that the wear resistance of plasma sprayed $Al_2$O$_3$-40%TiO$_2$coating layer is fluctuated with tile spray distance and the arc power level. The wear resiatance could be improved with decreasing the spray distance and with increasing the arc power level.