• Journal of Powder Materials
• /
• v.4 no.2
• /
• pp.106-112
• /
• 1997

$Cu-Al_20_3 $ composite powders were prepared by hydrogen reduction of $Cu^{2+}$ from ammoniacal copper sulfate solution on alumina core using autoclave. The copper reduction rate and the properties of copper layer were investigated using Scanning Electron Microscope(SEM), X-ray diffractometer, size and chemical analyzers. The reduction rate of $Cu^{2+}$ showed the maximum value when the molar ratio of [$NH_3$]/[$Cu^{2+}$] was 2. In order to prevent the agglomeration of Cu powder and ethane reduction rate, $Fe^{2+}$ and anthraquinone which act as catalysis were added in the solution. Catalysis was effectively chanced with the addition of two elemerts at a time. Optimum conditions obtained in this study were hydrogen reduction temperature of 205$^{\cire}C$, stirring speed of 500 rpm and hydrogen partial pressure of 300 psi. Obtained $Cu-Al_20_3 $ composite Powders were found to have the uniform and continuous copper coating layer of nodule shape with 3~5 $\mu$m thickness.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.3C no.2
• /
• pp.66-69
• /
• 2003

Various semiconductor nanowires such as GaN, GaP, InP, Si$_3$N$_4$, SiO$_2$/Si, and SiC were coated conformally with aluminum oxide (Al$_2$O$_3$) layers by atomic layer deposition (ALD) using trimethylaluminum (TMA) and distilled water ($H_2O$) at a temperature of 20$0^{\circ}C$. Transmission electron microscopy (TEM) revealed that A1203 cylindrical shells conformally coat the semiconductor nanowires. This study suggests that the ALD of $Al_2$O$_3$ on nanowires is a promising method for preparing cylindrical dielectric shells for coaxially gated nanowire field-effect transistors.

• Tribology and Lubricants
• /
• v.19 no.5
• /
• pp.274-279
• /
• 2003

$Al-SiC_{p}$ composite layer was prepared by plasma thermal spray on aluminum substrate. The homogeneously dispersed composite powder for thermal spray was fabricated by mechanical alloying with ball mill. The friction tests of the composite layers and commercial aluminum alloys for comparison were performed in the temperature range of 20∼$260^{\circ}C$ with the interval of $40^{\circ}C$ with steel counter-face. Friction coefficient was recorded during test sequence, and the microstructure of surface and debris was investigated by optical and scanning electron microscope. Friction coefficients of composite and aluminum alloys at room temperature were similar except pure aluminum. As the temperature increase, friction coefficient was increased rapidly in AC4C, AC2A. But friction coefficient of $Al-SiC_{p}$ composite was not increased so much up to $220^{\circ}C$. Consequently, the reinforcement of $SiC_{p}$ into aluminum matrix increased the stability of friction coefficient as well as wear resistance.

• Journal of Welding and Joining
• /
• v.17 no.6
• /
• pp.62-69
• /
• 1999

The advantages of Thermal sprayed coatings as a replacement for cast iron liners are reduced weight, better heat transfer and reduced cost. One of the most important performance attributes of a cylinder bore coating is its wear resistance, since it must survive the abrasive sliding of both the piston rings and the piston skirt. In this study, composite powders were prepared by ball milling of Al-13Si-3Mg(wt%) alloy with SiC particles. The concentrations of SiC were 40 and 60wt%. The composite powders were sprayed using Metco-9MB plasma torch. Plasma sprayed coatings were heat-treated at 500℃ for 3 hours. The wear resistances of the plasma sprayed coatings were found to improve with heat treatment and superior to the commercially available G.C.I.(gray cast iron). AlSiMg-40SiC heat-treated coatings showed the best wear resistance in this study.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.144-144
• /
• 2015

본 연구에서는 PVD법 중의 하나인 스퍼터링(sputtering) 기술을 이용하여 향상된 희생양극(sacrificial anode)적 특성을 가지는 고내식 Al-Mg 막을 제작함은 물론 그 제작 조건에 따른 표면의 몰포로지, 성분 분포, 결정구조 등의 변화를 해석하였다. 또한 표면 및 단면에 대한 염수분무 노출시험을 통해 Mg 성분의 첨가에 따른 막의 내식특성을 평가하였다. 이상의 재료특성 분석 및 내식성 평가 결과간 연구-고찰을 통해 제작 조건과 막의 내식성에 대한 종합적인 연관성을 해석하였으며 이를 통해 최적의 Al-Mg 제작에 대한 기초적인 설계 조건을 제시하고자 하였다.

• Journal of the Korean Ceramic Society
• /
• v.27 no.8
• /
• pp.1043-1049
• /
• 1990

In this work, strength of ceramic fibers and monofilament composites were evaluated on the basis of Weibull's theory. The fibers used were β-SiC and γ-Al2O3 monofilament composites was fabricated by coating Al on the fiber surface by the use of vacuum evaporation method. Average tensile strength of ceramic fibers showed the tendency to linearly decrease with increasing gauge length. Also, Weibull moduli of ceramic fibers were decreased with increasing gauge length, Weibull modulus of β-SiC was 3.5 for 6-50mm, 2.8 for 100-200mm. Weibull modulus of γ-Al2O3 was 6.5 for 20-50mm, 6 for 100mm. Fibers in monofilament retained their original as-produced strength to exposure temperature of 400℃. However, tensile strength of both monofilament composites approved to remarkably degrade due to interfacial reaction-induced flaws on the fiber surface after thermal exposure of 600℃. In this case, Weibull modulus of monofilament composites was 2.7 for β-SiC and 5.2 for γ-Al2O3 respectively.

• Journal of the Korean institute of surface engineering
• /
• v.50 no.5
• /
• pp.421-426
• /
• 2017

Herein, we investigated surface morphological characteristics of anodic films on Al6061 alloy prepared by unipolar pulsed Micro-arc oxidation (MAO) in a mixed solution of $Na_2SiO_3$ + KOH. The number and size of pores as well as craters on anodic alumina surface were studied as a function of different voltages, duty cycles and applied anodic current densities. The morphological characteristics of all samples were investigated by scanning electron microscopy, conforming that the most uniform surface morphology of MAO films on Al1050 alloy was obtained at high applied current density with low duty cycle.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.125-125
• /
• 2015

Ti-Al-Cr-N thin layer was prepared on Fe-Si thin sheet by arc ion plating to improve corrosion and mechanical properties. The compositions ratios of Fe : Cr : Al : Ti : Si : N of the thin layers at $500^{\circ}C$ was 1.24 : 0.56 : 36.82 : 32.72 : 0.59 : 28.07 [wt.%], respectively. The higher arc ion plating temperature was, the higher corrosion resistance and nano-hardness were observed due to chromium content. Corrosion potential and corrosion rate in artificial sea water of the coating layer were in the range of $-39mV_{SHE}$ and $2mA/cm^2$, respectively. Passivity was not observed in the artificial sea water. Nano-hardnesses of the thin layers was increased by adding Cr from 23.6 to 25.8 [GPa]. The friction coefficients and fatigue limits of the layers were 0.388, 0.031, respectively.

• Korean Journal of Materials Research
• /
• v.25 no.2
• /
• pp.107-112
• /
• 2015

The oxide films formed on etched aluminum foils play an important role as dielectric layers in aluminum electrolytic capacitors. $Y_2O_3$-doped $ZrO_2$ (YZ) films were coated on the etched aluminum foils by sol-gel dip coating, and the electrical properties of YZ-coated Al foils were characterized. YZ films annealed at $450^{\circ}C$ were crystallized into a cubic phase, and as the $Y_2O_3$ doping content increased, the unit cell of $ZrO_2$ expanded and the grain size decreased. The etch pits of Al foils were filled by YZ sol when it dried at atmospheric pressure after repeating for several times, but this step could essentially be avoided when being dried in a vacuum. YZ-coated foils indicated that the specific capacitance and dissipation factor were $2-2.5{\mu}F/cm^2$ and 2-4 at 1 kHz, respectively, and the leakage current and withstanding voltage of films approximately 200 nm thick were $5{\times}10^{-4}A$ at 21 V and 22 V, respectively. After being anodized at 500 V, the foils exhibited a specific capacitance and dissipation factor of $0.6-0.7{\mu}F/cm^2$ and 0.1-0.2, respectively, at 1 kHz, while the leakage current and withstanding voltage were $2{\times}10^{-4}-3{\times}10^{-5}A$ at 400 V and 420-450 V, respectively. This suggests that YZ film is a promising dielectric that can be used in high voltage Al electrolytic capacitors.

• Corrosion Science and Technology
• /
• v.4 no.6
• /
• pp.242-249
• /
• 2005

A lot of parts in FGD (Flue Gas Desulfurization) systems of fossil-fuel power plants show the environments in which are highly changeable and extremely acidic corrosive medium according to time and locations, e.g. in duct works, coolers and re-heaters etc. These conditions are formed when system materials are immersed in fluid that flows on them or when exhausted gas is condensed into thin layered acidic medium to contact materials of the system walls and roofs. These environments make troublesome corrosion and air pollution problems that are occurred from the leakage of the condensed solution. To cathodically protect the metallic structures in extremely acidic fluid, the properties of the protective coatings on the metal surface were very important, and epoxy Novolac coating was applied in this work. On the base of acid immersion tests, hot sulfuric acid decreased the hardness of the coatings and reduced greatly the content of $Na_2O$, $Al_2O_3$, and $SiO_2$ among the main components of the coating. A special kind of CP(Cathodic Protection) system has been developed and tested in a real scale of the FGD facility. Applied coating for this CP system was peeled off and cracked in some parts of the facility. However, the exposed metal surface to extremely acidic fluid by the failure of the coatings was successfully protected by the new CP system.