• Journal of Korea Foundry Society
• /
• v.29 no.4
• /
• pp.169-175
• /
• 2009

Effect of iron and manganese contents on die soldering reaction has been studied in Al-9wt.%Si-0.3wt.%Mg alloy. Ternary ${\alpha}_{hcp}-Al_8Fe_2Si$ and ${\alpha}_{bcc}-Al_8Fe_2Si$ intermetallic compounds formed by interaction diffusion between Al-Si-Mg system alloy melt and SKD61 die steel surface. Thickness of soldering reaction layer in die steel surface decreased as Fe and Mn contents of the melts increased : When Fe content of Al-9wt.%Si-0.3wt.%Mg melts at constant 0.5wt%Mn content was 0.15wt.%, 0.45wt.% and 0.6wt.%, thickness of soldered layer of each alloy was $64.5{\mu}m,\;57.3{\mu}m$ and $46.9{\mu}m$ respectively. For Mn content of the alloy melts at constant 0.45wt.%Fe content was 0.30wt.%, 0.50wt.% and 0.70wt.%, thickness of soldered layer of each alloy was $66.1{\mu}m,\;57.3{\mu}m$ and $48.3{\mu}m$ respectively.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2002.05a
• /
• pp.78-78
• /
• 2002

• Proceedings of the KWS Conference
• /
• 1998.05a
• /
• pp.108-111
• /
• 1998

• Transactions of Materials Processing
• /
• v.26 no.5
• /
• pp.306-313
• /
• 2017

This study investigated the microstructure, tensile strength, and high cycle fatigue properties of ADC12 aluminum alloys with different $Mg+Al_2Ca$ contents manufactured using die casting process. Microstructural observation identified the presence of ${\alpha}-Al$, eutectic Si, $Al_2Cu$, and Fe-intermetallic phases. The increase of $Mg+Al_2Ca$ content resulted in finer pore size and decreased pore distribution. Room temperature tensile strength tests were conducted at strain rate of $1{\times}10^{-3}/sec$. For 0.6%Mg ADC12, measured UTS, YS, and El were 305.2MPa, 157.0MPa, and 2.7%, respectively. For 0.8%Mg ADC12, measured UTS, YS, and El were 311.2 MPa, 159.4 MPa, and 2.4%, respectively. Therefore, 0.8% ADC12 alloy had higher strength and slightly decreased elongation compared to 0.6% Mg ADC12. High cycle fatigue tests revealed that 0.6% Mg ADC12 alloy had a fatigue limit of 150 MPa while 0.8% Mg ADC12 had a fatigue limit of 160MPa. It was confirmed that $Mg+Al_2Ca$ added ADC12 alloy achieved finer, spherical eutectic Si particles, and $Al_2Cu$ phases with greater mechanical and fatigue properties since size and distribution of pores and shrinkage cavities decreased as $Mg+Al_2Ca$ content increased.

• Journal of the Korean Society for Heat Treatment
• /
• v.34 no.5
• /
• pp.226-232
• /
• 2021

The relationship between precipitation and coefficient of thermal expansion of Al-6%Si-0.4%Mg-0.9%Cu-(Ti) alloy (in wt.%) after various heat treatments were studied by the thermodynamic analyzer (TMA) and differential scanning calorimetry (DSC). Solution heat treatment of the alloy was carried out at 535℃ for 6 h followed by water quenching, and the samples were artificially aged in the air at 180℃ and 220℃ for 5 h. The coefficient of thermal expansion (CTE) curve showed some residual strain and decreased with increasing aging temperature. The CTE curves changed sharply in the temperature range of 200℃ to 400℃, and the corresponding peak shifted for the aged samples due to the change in the precipitation behavior of the secondary phase. These transformation peaks in the aged sample are related to the volume of the precipitation of the Si phase as determined by DSC analysis. The change in CTE is mainly caused by the precipitation of the Si phase in the Al-Si alloy, and the size of the change occurs simultaneously with the size of the precipitate.

• Journal of Powder Materials
• /
• v.16 no.4
• /
• pp.275-279
• /
• 2009

The aging characteristics of gas atomized Mg-6 wt.% Al-1 wt.% Zn alloy were investigated and compared to those of cast Mg-6 wt.% Al alloy. The gas atomized Mg-6 wt.% Al-1wt.% Zn alloy powders had spherical morphology between 1 and 100 $\mu m$ in diameter. After compaction under the pressure of 700 MPa at $320^{\circ}C$ for 10 min, the Mg-6 wt.% Al-1 wt.% Zn alloy showed a grain size of approximately 40 $\mu m$ which is smaller than that of the cast Mg-6 wt.% Al alloy, and a relative compact density of approximately 93%. After ageing, the Mg-6 wt.% Al-1 wt.% Zn alloy showed much faster peak hardness than cast Mg-6 wt.% Al alloy. The Mg-6 wt.% Al-1 wt.% Zn alloy showed the new fine precipitations with ageing time, while the cast Mg-6 wt.% Al alloy was almost similar morphology.

• Journal of Powder Materials
• /
• v.21 no.6
• /
• pp.460-466
• /
• 2014

Al-Si-SiC composite powders with intra-granular SiC particles were prepared by a gas atomization process. The composite powders were mixed with Al-Zn-Mg alloy powders as a function of weight percent. Those mixture powders were compacted with the pressure of 700 MPa and then sintered at the temperature of $565-585^{\circ}C$. T6 heat treatment was conducted to increase their mechanical properties by solid-solution precipitates. Each relative density according to the optimized sintering temperature of those powders were determined as 96% at $580^{\circ}C$ for Al-Zn-Mg powders (composition A), 97.9% at $575^{\circ}C$ for Al-Zn-Mg powders with 5 wt.% of Al-Si-SiC powders (composition B), and 98.2% at $570^{\circ}C$ for Al-Zn-Mg powders with 10 wt.% of Al-Si-SiC powders (composition C), respectively. Each hardness, tensile strength, and wear resistance test of those sintered samples was conducted. As the content of Al-Si-SiC powders increased, both hardness and tensile strength were decreased. However, wear resistance was increased by the increase of Al-Si-SiC powders. From these results, it was confirmed that Al-Si-SiC/Al-Zn-Mg composite could be highly densified by the sintering process, and thus the composite could have high wear resistance and tensile strength when the content of Al-Si-SiC composite powders were optimized.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2004.10a
• /
• pp.234-237
• /
• 2004

As an automotive industry's demand for lighter materials gets bigger and bigger, a lot of new strength Al alloys have been developed recently. In the present study, Al 6xxx series alloys were designed to get the strength level of 350MPa with the elongation of $12\%$. For that purpose, three alloy systems were selected based on the thermodynamics calculation. The effect of both $Mg_{2}Si$ precipitate and excess Si amount on the newly designed alloys was investigated. Also, heat treatment procedure was studied to optimize the mechanical properties.

• Korean Journal of Materials Research
• /
• v.33 no.1
• /
• pp.8-14
• /
• 2023

In order to broaden the range of application of light weight aluminum alloys, it is necessary to enhance the mechanical properties of the alloys and combine them with other materials, such as cast iron. In this study, the effects of adding small amounts of Cu and Zr to the Al-Si-Mg based alloy on tensile properties and corrosion characteristics were investigated, and the effect of the addition on the interfacial compounds layer with the cast iron was also analyzed. Although the tensile strength of the Al-Si-Mg alloy was not significantly affected by the additions of Cu and Zr, the corrosion resistance in 3.5 %NaCl solution was found to be somewhat lowered in this research. The influence of Cu and Zr addition on the type and thickness of the interfacial compounds layer formed during compound casting with cast iron was not significant, and the main interfacial compounds were identified to be Al₅FeSi and Al₈Fe₂Si phases, as in the case of the Al-Si-Mg alloys.

• Korean Journal of Materials Research
• /
• v.10 no.12
• /
• pp.793-798
• /
• 2000

The age-hardening behavior of unreinforced 6061 Al alloy and SiCp/6061 Al alloy composites reinforced with different size of SiC particle (average diameter ; 0.7$\mu\textrm{m}$ and 7.0$\mu\textrm{m}$) was investigated by hardness measurement, calorimetric technique and transmission electron microscopy. At 17$0^{\circ}C$ isothermal aging treatment, the peak aging time of 0.7$\mu\textrm{m}$SiCp/6061Al alloy composite and 7.0$\mu\textrm{m}$SiCp/6061Al alloy composite is shorter than that of unreinforced 6061Al alloy, and the aging of 7.0$\mu\textrm{m}$SiCp/6061Al alloy composite is accelerated more than that of 0.7$\mu\textrm{m}$SiCp/6061Al alloy composite. This acceleration is due to the increase of dislocation density by the compositeness with SiCp and the SiC particle size. In the peak aged condition, the major strengthening phase of these materials is intermediate $\beta$ phase(Mg$_2$Si), and the activation energy for the formation of $\beta$ phase is considerably decreased by the compositeness with SiCp and the increasing of SiC Particle site.