• Journal of Korea Foundry Society
• /
• v.26 no.6
• /
• pp.249-257
• /
• 2006

The effects of alloying element and the condition of heat-treatment on the strength of squeeze-cast Al-3.0 wt%Si alloy were investigated. The strength of the alloy without grain refinement was increased with increase Cu content upto 3.0 wt% and rather decreased beyond that. The tensile strength of the alloy with grain refinement increased with Cu content upto 3.0 wt% and not changed beyond that. The strength of the alloy without grain refinement increased with the Mg content. The tensile strength with grain refinement increased with the Mg content upto 0.50 wt% and then decreased beyond that. The strength of the grain refined alloy increased by individual and simultaneous additions of Cu and Mg and the maximum strength was obtained with Al-3.0 wt%Si-4.5 wt%Cu-0.50 wt%Mg alloy. The optimum heat-treatment condition for this alloy was obtained.

• Journal of Korea Foundry Society
• /
• v.41 no.6
• /
• pp.528-534
• /
• 2021

To confirm effects of natural and artificial aging of precipitate on thermal diffusivity and hardness, the studied Al-Mg-Si alloy were manufactured by gravity casting method with 0.6 wt% and 1.0 wt% additional Cu element. The samples were used for measuring thermal diffusivity and hardness. The addition of Cu, promoted by intermediates such as Q'' and θ'' phases, contributing to the improvement of hardness and high-temperature thermal diffusivity. The natural aging decreased the hardness of the Al-Mg-Si-Cu alloys with increasing time, but did not affect the thermal diffusivity.

• Journal of Korea Foundry Society
• /
• v.5 no.3
• /
• pp.19-26
• /
• 1985

This study has been carried out to examine into wettability of Cu-5%Sn alloy in $Al_2O_3$, MgO, $SiO_2$ and graphite, respectively and investigated into the change in macrostructure of Cu-5%Sn alloy according to kind and mixing rate of mold-coating. The results obtained from the experiment are summerized as follows; 1. Cu Cu-5%Sn alloy, wettabilities of $Al_2O_3$ and MgO were good, on the other hand, wettabilities of $SiO_2$ and graphite were bad. 2. The fine equiaxed zone was created because of the role of $Al_2O_3$ and MgO as preferential nucleation sites. 3. Notwithstanding change of mixing rate of $SiO_2$ in mold coating the equixed zone was not created. 4. The area of equiaxed zone was varied according to mixing rate in the case of using $Al_2O_3$ and MgO in mold-coating.

• Journal of the Korean Society for Heat Treatment
• /
• v.7 no.1
• /
• pp.17-24
• /
• 1994

The evaluation and analysis of diffusivity of lithium for coarsening and coarsening kinetics of ${\delta}^{\prime}$ precipitate in Al-Li-Cu-Mg-Zr alloy aged at $170^{\circ}C$ have been investigated by transmission electron microscopy. With ageing time, ${\delta}^{\prime}$ precipitate coaesened to followed $\bar{\gamma}{\propto}t^{1/3}$ and coarsening kinetics was found to be obeyed to the Lifshitz-Slyozov-Wagner(LSW) theory and diffusivity of lithium for coarsening of ${\delta}^{\prime}$ precipitate in Al-Li-Cu-Mg-Zr alloy was obtained to be $5.85{\times}10^{-17}{\sim}1.53{\times}10^{-16}$ by experimental coarsening rate constant and various coarsening kinetic theory. Diffusivity of lithium measured by using various model but MLSW and Tsumuraya (VI) et al. model in Al-Li-Cu-Mg-Zr alloy is similar to that calculated by the Costas's diffusivity equation. It was, therefore, suggested that additing to the Cu, Mg and Zr element in Al-Li system have no great effect on diiffusivity of lithium for coarsening of ${\delta}^{\prime}$ This suggest that in matrix.

• Journal of Korea Foundry Society
• /
• v.41 no.1
• /
• pp.3-10
• /
• 2021

In the compound casting between the aluminum alloy and the cast iron, the iron component may be dissolved from the cast iron during the process and mixed into the aluminum melt, thereby forming various iron-containing intermetallic compounds and significantly deteriorating the tensile properties of the aluminum alloy. On the other hand, unlike Fe, which is added as an impurity, Cu is added to improve the mechanical properties of the aluminum alloy. In this study, the change in microstructure and tensile properties of aluminum alloys due to the addition of Fe and Cu was investigated. A large amount of iron-containing compounds such as coarse Al₅FeSi phases were formed when the iron content was 1% or more, and the tensile properties were significantly reduced. In the case of the aluminum alloy to which Cu was added, an Al₂Cu phase was additionally formed and the tensile strength was clearly improved.

• Transactions of Materials Processing
• /
• v.29 no.3
• /
• pp.135-143
• /
• 2020

Low-cost alloying elements were added to a modified Al-6.5Si alloy and its microstructure, tensile and impact toughness properties were investigated. The alloying elements added were Mg, Zn, and Cu, and two kinds of alloy A (Mg:0.5, Zn:1, Cu:1.5 wt.%) and alloy B (Mg:2, Zn:1.5, Cu:2 wt.%) were prepared. In the as-cast Al-6.5Si alloys, Si phases were distributed at the dendrite interfaces, and Al₂Cu, Mg₂Si, Al₆ (Fe,Mn) and Al₅ (Fe,Mn)Si precipitates were also observed. The size and fraction of casting defects were measured to be higher for alloy A than for alloy B. The secondary dendrite arm spacing of alloy B was finer than that of alloy A. It was confirmed by the JMatPro S/W that the cooling rate of alloy B could be more rapid than alloy A. The alloy B had higher hardness and strength compared to the values of alloy A. However, the alloy A showed better impact toughness than alloy B. Based on the above results, the deformation mechanism of Al-6.5Si alloy and the improving method for mechanical properties were also discussed.

• Journal of Welding and Joining
• /
• v.15 no.4
• /
• pp.166-177
• /
• 1997

The high strength AlZnMgCu0.5 alloy is a light metal with good age hardenability, and has a high tensile and yielding strength. Therefore, it can be used for structures requiring high speciple strength. Even though high strength AlZnMgCu alloy has good mechanical properties, it has a lot of problems in TIG and MIG welding processes. Since lots of high heat absorption is introduced into the weldment during TIG and MIG processes, the microstructural variation and hot cracks take place in heat affected zone. Therefore, the mechanical properties of high strength AlZnMgCu0.5 alloy can be degraded in weldment and heat affected zone. Welding process utilizing high density heat source such as electron beam should be developed to reduce pore and hot cracking, whichare usually accompanied by MIG and TIG welding processes. In this work, electron beam welding process were used with or without AlMg4.5Mn as filler material to avoid the degradation of mechanical properties. Mechanical and metallurgical characteristics were also studied in electron beam weldment and heat affected zone. Moreover hot cracking mechanism was also investigated.

• Journal of Korea Foundry Society
• /
• v.31 no.3
• /
• pp.145-151
• /
• 2011

Metallic foam has been known as a functional material which can be used for absorption properties of energy and sound. The unique characteristics of Al foam of mechanical, acoustic, thermal properties depend on density, cell size distribution and cell size, and these characteristics expected to apply industry field. Al-Zn-Mg-Cu alloy foams was fabricated by following process; firstly melting the Al alloy, thickening process of addition of Ca granule to increased of viscosity, foaming process of addition of titanium hydride powder to make the pores, holding in the furnace to form of cooling down to the room temperature. Metal foams with various porosity level were manufactured by change the foaming temperature. Compressive strength of the Al alloy foams was 2 times higher at 88% porosity and 1.2 times higher at 92% porosity than pure Al foams. It's sound and vibration absorption coefficient were higher than pure Al foams and with increasing porosity.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.382-387
• /
• 2004

Nanoindentation technique has been used to measure the mechanical properties of aluminium alloy foam cell walls. Al-Si-Cu-Mg alloy foams of different compositions and different cell morphologies were produced using powder metallurgical method. Cell morphology of the foam was controlled during production by varying foaming time and temperature. Mechanical properties such as hardness and Young's modulus were calculated using two different methods: a continuous stiffness measurement (CSM) and an unloading stiffness measurement (USM) method. Experimental results showed that hardness and Young's modulus of Al-5%(wt.)Si-4%Cu-4%Mg (544 alloy) precursor and foam walls are higher than those of Al-3%Si-2%Cu-2%Mg (322 alloy) precursor and foam walls. It was noticed that mechanical properties of cell wall are different from those of precursor materials.

• Applied Microscopy
• /
• v.36 no.2
• /
• pp.47-55
• /
• 2006

In this paper a transmission electron microscope (TEM) observation of fine Cu precipitates distributed randomly in Al-2.5Cu-1.5Mg wt.% alloy is first reported. This new observation happened to occur when an ion milling was peformed to remove oxides on the specimen, particularly, aged 100 hours at $150^{\circ}C$. Meanwhile the oxides were identified to be $Cu_2O$ particles. For this work involved with analysis of diffraction rings, the formulation of the electron diffraction rings pattern for powder particles was made. Finally the significance of this unexpected ion milling effort on the alloy was discussed