• 한국주조공학회지
• /
• 제25권2호
• /
• pp.88-94
• /
• 2005

The microstructure and mechanical property of the ceramic reinforced AC4C matrix composites processed by squeeze casting were investigated. In this study Kaowool and Saffil fiber which are ceramic reinforcements are used as preform materials. As a matrix material, Al-7wt.%Si-0.3wt.%Mg(AC4C) has been used. In case of Kaowool and Saffil/AC4C composites, 7.5 MPa squeezing pressure and minimum 7.0% binder amount are needed to produce sound composite materials. The tensile strength of Kaowool/ AC4C composite is lower than the matrix metal and this can be explained by the melt unfilling due to formed cluster of Kaowool reinforcements. But the mechanical properties of hardness, wear resistance and thermal expansion are better than the matrix materials due to the strengthening effect of ceramic reinforcements.

• 한국세라믹학회지
• /
• 제27권4호
• /
• pp.457-464
• /
• 1990

This paper presents the influence of the loading rate on the room temperature fracture toughness of a brittle Al2O3 and a SiC whisker reinforced Al2O3 composite. Dynamic fracture toughness tests were conduced using compressive fatigue pre-cracked notched round bars loaded in tension to produce a stress intensity rate K1=106 MPa√m/sec. The experimental results show that for each loading rate the fracture toughness values obtained for the ceramic matrix composite are higher than the corresponding values for the single phase alumina. In addition, both the reinforced and unreinforced ceramic are singnificantly tougher under dynamic loading than static loading. This dynamic and quasi-static fracture initiation behaviro can be interpreted by identifying quantitatively the mode of fractuer initiation as a function of loading rate.

• 한국재료학회지
• /
• 제15권12호
• /
• pp.791-795
• /
• 2005

In this study, aluminum borate whisker reinforced Mg-3Al-2Ag-1Zn matrix composites were fabricated by the squeeze infiltration technique. The purpose is to develop materials for elevated temperature applications. Microstructure observation revealed successful fabrication of the metal matrix composites, namely no cast defects such as porosity and matrix/reinforcement interface delamination etc. High temperature hardness and creep rupture properties were improved significantly with addition of Ag to the Al borate whisker reinforced Mg alloy composite. $Mg_3Ag$ phase formed during aging heat treatment could improve creep properties of the Mg matrix composites.

• 한국재료학회지
• /
• 제31권6호
• /
• pp.339-344
• /
• 2021

Composite materials offer distinct and unique properties that are not naturally inherited in the individual materials that make them. One of the most attractive composites to manufacture is the aluminum alloy matrix composite, because it usually combines easiness of availability, light weight, strength, and other favorable properties. In the current work, Powder Metallurgy Method (PMM) is used to prepare Al2024 matrix composites reinforced with different mixing ratios of yttrium oxide (Y₂O₃) particles. The tests performed on the composites include physical, mechanical, and tribological, as well as microstructure analysis via optical microscope. The results show that the experimental density slightly decreases while the porosity increases when the reinforcement ratio increases within the selected range of 0 ~ 20 wt%. Besides this, the yield strength, tensile strength, and Vickers hardness increase up to a 10 wt% Y₂O₃ ratio, after which they decline. Moreover, the wear results show that the composite follows the same paradigm for strength and hardness. It is concluded that this composite is ideal for application when higher strength is required from aluminum composites, as well as lighter weight up to certain values of Y₂O₃ ratio.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 1999년도 춘계학술발표대회 논문집
• /
• pp.109-113
• /
• 1999

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 1999년도 춘계학술발표대회 논문집
• /
• pp.193-196
• /
• 1999

• 한국세라믹학회지
• /
• 제31권7호
• /
• pp.703-714
• /
• 1994

Sintering and microstructure of Ce-TZP/Al2O3 composite with $\alpha$-Al2O3 matrix containing dispersed 5~50 vol% ZrO2 were discussed. Sintered density was increased with elevating forming pressure in range of 6~300 MPa and about >99.2% of theoretical density was obtained at 1$600^{\circ}C$ for 2h in case of 300 MPa of 6~300 MPa uniaxially cold-pressed compacts containing 20 vol% ZrO2. All kinds of different batch composition exhibited nearly the same shrinkage behaviour with end-point shrinkage between 20 and 24%, and had the maximum shrinkage rate (0.41~0.54%/min) around 140$0^{\circ}C$. Grain growth was occurred faster in $\alpha$-Al2O3 than in {{{{ gamma }}-Al2O3 starting matrix during sintering at 1$600^{\circ}C$. Bimodal pore size distribution of interaglomerate pores with size of 0.03~0.2 ${\mu}{\textrm}{m}$ and of interaglomerate pores with size of around 60 ${\mu}{\textrm}{m}$ was obtained in Ce-TZP/$\alpha$-Al2O3 composite sintered at 130$0^{\circ}C$. But unimodal pore size distribution with around 0.1 ${\mu}{\textrm}{m}$ was observed in Ce-TZP/{{{{ gamma }}-Al2O3 composite sintered at the same temperature. Microcracks were occurred due to the tlongrightarrowm transformation of ZrO2 on cooling process.

• 한국주조공학회지
• /
• 제18권6호
• /
• pp.534-540
• /
• 1998

6061Al-matrix composite with TiNi shape memory fiber as reinforcement has been fabricated by Permanent Mold Casting to investigate the mechanical properties of the smart composites. The composites have showed good interface bonding as a result of the analysis of SEM and EDX. The smartness of composite is given due to the shape memory effect of the TiNi fiber which generates compressive residual stresses in the matrix material when heated after being prestrained. The tensile strength of the composites was tested at temperatures between $90^{\circ}C$ and room temperature with increasing amount of pre-strain, and it showed that the tensile strength at $90^{\circ}C$ was higher than that of the room temperature. Especially, the tensile strength of the composite increases with increasing pre-strain. It showed that hardness of matrix was higher than that of common 6061Al alloy.

• Korean Chemical Engineering Research
• /
• 제58권1호
• /
• pp.64-68
• /
• 2020

본 연구에서는, 열 전도성 충진제로 충진 된 에폭시복합체를 사용하여 금속 구리판에 이를 코팅한 기판이 제조되었다. 에폭시 복합체의 열전도도를 향상시키기 위해서는 에폭시 매트릭스에 있는 전도성 필러의 최적 분산을 통한 전도성 네트워크를 형성하게 하고, 인접한 필러 입자들 사이에서 열 저항 접합의 수를 감소시키는 것이 중요한 요소이다. 이는 에폭시는 열전도도가 0.2~0.3 W 밖에 안되기 때문에 높은 열전도도를 유지하기 위해선 열전도성 필러가 서로 연결되어 입자간에 갭이 적어야 열저항을 감소시킬수 있기 때문이다. 본 연구의 목적은 에폭시 수지에 Al₂O₃와 Boron Nitride (BN) 충진제를 균일하게 분산시켜 고방열 에폭시 복합체를 개발하는 데 있다. 그 결과, Al₂O₃와 Boron nitride Filler가 에폭시 수지 매트릭스에 서로 연결되어 에폭시 수지와 알루미나/Boron nitride 하이브리드 필러 간에 계면 공극 없이 분산되어 열전도도 특성 향상을 확인 할 수 있었고, 표면 처리한 s-BN 필러가 에폭시 수지의 매트릭스의 계면접착력을 향상시켰으며, 계면 공극을 최소화함에 따라 높은 열전도도 특성을 확보 할 수 있었다.

• 한국주조공학회지
• /
• 제15권6호
• /
• pp.566-573
• /
• 1995

In this study, the microstructural characteristics such as primary silicon, eutectic silicon, $SiC_p$ dispersion behavior, compound amount and Si solubility in $Al/SiC_p$ composite fabricated by the squeeze casting under various conditions were investigated systematically. As applied pressure(MPa) increases, cooling rate and compound amount are increased. In gravity casting, the cooling rate of hypereutectic composite is slower than of hypoeutectic composite by exothermic reaction of primary Si crystallization. But the cooling rate of hypereutectic composite is faster than that of hypoeutectic composite fabricated by same applied pressure, because amount of primary Si crystallization in hypereutectic composite was decreased, on the contrary, primary ${\alpha}-Al$ in hypoeutetic composite was increased due to increase of Si solubility in matrix by applied pressure. The crystalized primary silicon in hypereutectic composite fabricated by squeeze casting become more fine than that in non-pressure casting This is because mush zone became narrow due to increase of Si content of eutectic composition by pressure and time for growth of primary silicon got shorter according to applied pressure. It is turned out that eutectic temperature and liquidus are decreased by the increasing of squeeze pressure in all the composite due to thermal unstability of matrix owing to increasing of Si solubility in matrix by the increasing of applied pressure, as indicated in thermal anaiysis(DSC) results.