• 한국자동차공학회논문집
• /
• 제7권9호
• /
• pp.138-145
• /
• 1999

Surface hardening of AC4C aluminium alloy with TiC powders was obtained by plasma transferred are (PTA) method, Bead appearance, microstrucutre and wear behavior were characterized in relation to the torch current, powder feed rate and wear condition. The width and the depth of bead were mainly increased with increasing torch current. The comparison of wear behavior between AC4C alloy and PTA treated AC4C alloy showed the remarkable enhancement of wear resistance.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1996년도 추계학술대회 논문집
• /
• pp.46-50
• /
• 1996

Die sinking Electrical Discharge Machining(EDM) of TiC/Al$_2$O$_3$Ceramic Matrix Composite(CMC) was conducted for positive and negative polarity according to the change of current and Duty Factor(DF). Also FEM analysis about temperature distribution of workpiece by one spark was executed. Maximum surface roughness( R$_{max}$ ) and SEM photographs of the EDMed surface for different conditions were evaluated. Higher Material Removal Rate(MRR) was obtained for negative polarity than positive one. Better surface morphology was found as the current is decreased, but the MRR was also decreased. From the SEM photographs, the size of melt cavity due to one spark is about 100 to 150${\mu}{\textrm}{m}$ in diameterer

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1142-1143
• /
• 2006

Kinik Company pioneered diamond pad conditioners protected by DLC barrier ($DiaShield^{(R)}$ Coating) back in 1999 (Sung & Lin, US Patent 6,368,198). Kink also evaluated Cermet Composite Coating (CCC or $C^3$, patent pending) with a composition that grades from a metallic (e.g. stainless steel) interlayer to a ceramic (e.g. $Al_2O_3$ or SiC) exterior. The metallic interlayer can form metallurgical bond with metallic matrix on the diamond pad conditioner. The ceramic exterior is both wear and corrosion resistant. The gradational design of $C^3$ coating will assure its strong adherence to the substrate because there is no weak boundary between coating and substrate.

• Steel and Composite Structures
• /
• 제45권4호
• /
• pp.535-546
• /
• 2022

The memory response of nonlocal systematical formulation size-dependent coupling of viscoelastic deformation and thermal fields for piezoelectric materials with dual-phase lag heat conduction law is constructed. The method of the matrix exponential, which constitutes the basis of the state-space approach of modern control theory, is applied to the non-dimensional equations. The resulting formulation together with the Laplace transform technique is applied to solve a problem of a semi-infinite piezoelectric rod subjected to a continuous heat flux with constant time rates. The inversion of the Laplace transforms is carried out using a numerical approach. Some comparisons of the impacts of nonlocal parameters and time-delay constants for various forms of kernel functions on thermal spreads and thermo-viscoelastic response are illustrated graphically.

• 한국주조공학회지
• /
• 제11권6호
• /
• pp.475-481
• /
• 1991

In this study the fabrication technology and mechanical properties of AC8A/$Al_2O_3$ Composites by squeeze casting process were investigated to develope for application as the piston materials that require good friction, wear resistance, and thermal stability. AC8A/$Al_2O_3$ composistes without a porosity and the break of preform were fabricated at the melt temperature of $740^{\circ}C$, the preform temperature of $500^{\circ}C$, and mold temperature of $400^{\circ}C$ under the applied pressure of $1200kg/cm^2$ as the results of the observation of microstructures. As the results of this study, the tensile strength of AC8A/$Al_2O_3$ composites was not increased linearly with $Al_2O_3$ volume fraction and so it seemed not to agree with the rule of mixture, which had been used often in metal matrix composite. Also the tensile strength after thermal fatigue test was little different from that before the test. Consequently it was thought that AC8A/$Al_2O_3$ composites fabricated under our experimental conditions had a good thermal stability and subsequently a good interface bonding. Wear rate(i.e., volume loss per unit sliding distance) of AC8A/$Al_2O_3$ composites was decreased with $Al_2O_3$ volume fraction and the sliding speed at both room temperature and $250^{\circ}C$ and so there was a good correlation between wear rate and hardness. Also the wear rate of AC/8A20% $Al_2O_3$ composities was obtained the value of $1.65cm^3/cm$ at sliding speed of 1.14m/sec as compared with about $3.0\;{\times}10^{-8}cm^3/cm$ hyereutectie Al-Si alloy(Al-16%Si-2%Cu-1%Fe-1%Ni), which applied presently for piston materials. The wear behavior of $Al_2O_3$ composites was observed to a type of abrasive wear by the SEM view of wear surface.

• 비파괴검사학회지
• /
• 제19권3호
• /
• pp.180-188
• /
• 1999

SiC 입자강화 2124Al 금속복합재료의 강화재 부피분율에 따른 탄성 stiffness를 초음파 공명 스펙트로스코피(resonant ultrasound spectroscopy: RUS) 방법을 이용하여 측정하였다. RUS 방법은 한 개의 소형 시편으로 9개의 독립변수를 가진 사방정계(orthorhombic) 탄성계수를 간단한 실험으로 측정 가능함을 보여주었다. SiC 강화재 부피분율 변화에 따른 탄성계수를 측정하였는데 이 경우 초기 추정 탄성계수를 구하기 위해서 부피 분율에 따른 미세조직 사진으로부터 강화재의 형상(aspect ratio)과 방향을 고려한 유효 aspect ratio 개념을 도입하였고. Mori-Tanaka 이론식에 의한 계산결과를 이용하였다. 이로부터 계산된 공진주파수와 RUS의 측정 공진주파수 사이를 최소화함으로 정확한 탄성계수를 측정하였다. 측정된 stiffnesses로부터 공학적 탄성계수인 Young's modulus를 계산하였으며, 계산된 Young's modulus와 압출방향으로 인장 시험한 Young's modulus를 비교분석 하였다. SiC 입자의 부피분율이 증가함에 따라 탄성계수가 증가함을 나타내었고, 탄성 stiffness의 거동은 강화재가 많이 첨가될수록 횡등방성(transversely isotropic)이 강하게 나타났으며 이것은 압출공정에 의해 강화재 입자의 방향성 재배열에 기인한다. 한편 일정크기 시편에 있어서 기본 공진주파수가 강화재 부피분율에 따라 고주파수 영역으로 이동하는 현상이 관찰되었으며, 이로 부터 비파괴적으로 강화재 부피분율을 예측할 수 있는 가능성을 제시하였다.

• Composites Research
• /
• 제16권1호
• /
• pp.1-12
• /
• 2003

본 연구는 보강재의 부피분율이 49%, 56%, 63%첨가된 패키징용 SiC/Al복합재료를 가압주조법을 통해 개발하였다. SiC/Al복합재료는 0.8%의 무기성형제와 $Al_2$O$_3$섬유가 SiC입자에 비해 부피비 1:10의 비율로 첨가되었으며 새로이 고안된 몰드에서 제조되었다. 제조된 SiC/Al복합재료에 대해 30-300 구간에서 열팽창 계수를 측정하고, FEM수치해석과 비교하여 온도에 따른 특성을 분석하였다. 실험결과 SiC/Al복한재료의 열팽창계수는 혼합법칙, Turner모델의 중간값을 가졌으며 상온에서는 Turner모델에 가깝다가 온도가 높아질수록 혼합법칙에 가까와졌다. 이러한 특성은 모재의 소성변형 및 잔류응력에 의한 것으로 본 연구에서 제안한 모재와 보강재 사이에 작용하는 평균응력 차이로부터 분석이 된다. 해석결파 모재의 소성변형이 시작되는 온도에서 SiC/Al복합재료의 열팽창계수가 급격히 증가하였으며, 가공 잔류응력은 이러한 소성변형의 시작온도를 고온으로 이동시킴으로써 열팽창계수에 영향을 끼침을 밝혔다. 이러한 일련의 연구를 통해 온도에 따른 열팽창 특성은 복수입자모델에 의한 2차인 해석을 통해 성공적으로 분석됨을 보였다.

• Composites Research
• /
• 제22권5호
• /
• pp.15-23
• /
• 2009

가압주조법으로 제조한 $Al_2O_3$ 섬유와 SiC 입자 혼합 보강 금속복합재료(MMCs)의 상온과 고온에서 윤활마모특성을 조사하였다. 마모시험은 거리와 온도의 변화에 따라 속도를 고정시켜 25Kgf의 하중하에서 수행하였으며 MMCs의 시험편은 가압의 수평(PR)방향과 수직(N)방향에서 채취하였다. 혼합비의 영향을 관찰한 결과 상온에서는 20%섬유만 보강한 PR방향 MMCs의 마모거동은 N방향 보다 우수한 결과를 보였으나, 혼합보강 MMCs는 반대로 나타내었다. 고온($100^{\circ}C$)에는 모든 MMCs에서 PR방향의 마모거동이 N 방향보다 우수한 결과를 보인 것은 보강재와 마찰면간 윤활필름이 강호작용에 기인한 것으로 밝혀졌다. $150^{\circ}C$에서는 혼합 MMCs의 마모거동은 온도영향으로 PR이 N 보다 우수한 결과를 보였다.

• 멤브레인
• /
• 제25권6호
• /
• pp.496-502
• /
• 2015

촉진수송은 기존의 고분자 막에서는 힘든, 투과도와 선택도를 동시에 향상시킬 수 있는 기술 중 한 가지이다. 촉진수송 분리막을 이용한 올레핀/파라핀 분리는 기존의 증류공정을 대체할 수 있는 기술로써 많은 관심을 받아왔다. 본 연구에서는 테트라플루오로붕산은/질산알루미늄의 혼합염이 포함된 고분자 블렌드 기반의 촉진수송 올레핀 분리막을 제조하였다. 자유 라디칼중합법을 이용하여 폴리다이메틸실록세인-g-폴리옥시에틸렌 메타크릴레이트 가지형 공중합체를 합성하였다. 또한, 폴리다이메틸실록세인-g-폴리옥시에틸렌 메타크릴레이트 매질에 폴리에틸렌옥사이드를 다양한 비율로 혼합하였다. 폴리에틸렌옥사이드를 폴리다이메틸실록세인-g-폴리옥시에틸렌 메타크릴레이트 가지형 공중합체 질량 대비 70%를 혼합하였을 때, 혼합기체 선택도 및 투과도는 5.6 및 10.05 GPU에 도달하였다. 이와 같은 복합막의 올레핀 분리 성능이 향상된 이유는, 분리막에 첨가된 은이온이 올레핀 기체분자의 선택적인 촉진 수송을 하였고, 또한 고투과성의 고분자 블렌드가 사용되었기 때문이다. 또한 은이온의 은나노입자로의 환원을 억제시키는 질산알루미늄의 첨가로 인해 복합막의 장시간 안정도를 향상시킬 수 있었다.

• Composites Research
• /
• 제23권2호
• /
• pp.10-16
• /
• 2010

가압주조법으로 제조된 알루미나 섬유와 SiC 입자 혼합금속복합재료의 마찰특성을 조사하였다. 핀 형태의 마모 시험편은 전체 부피비 20%에 섬유와 입자의 서로 다른 비를 갖고 있다. 혼합금속복합재료의 윤활마모시험은 핀과 디스크 타입의 마모시험기를 사용하여 수행되었는데, 상온과 고온 $100^{\circ}C$와 $150^{\circ}C$.에서의 건식마찰특성을 각각 수행하였다. 마모면의 미시분석은 주사전자현미경(SEM)으로 조사하여 마찰특성과 마모거동을 분석하였다. 시험 결과 마모저항은 상온에서는 섬유와 같은 방향인 (PR) 방향에서는 SiC입자의 증가에 따라 향상되었다. 고온에서는 섬유와 수직한 방향(N)의 마모특성은 PR방향의 섬유가 마모면으로 전체적으로 쉽게 뽑히기 때문에 PR방향의 금속보합재료의 마모특성보다 우수하였다. 한편 마찰계수는 온도증가에 따라 감소하였다.