• Journal of the Korean Ceramic Society
• /
• v.32 no.1
• /
• pp.106-112
• /
• 1995

In order to examine the effect of CuO and Al2O3 addition on the electrical conductivity of ZnO, both Al2O3 (0, 1, 2, 5, 10at.%) and CuO (1, 5at.%) were added to ZnO. Al2O3 addition (~2at.% Al) increased the total electrical conductivity of ZnO which was already decreased by CuO doping effect Above solid solubility of Al (~2at.%), ZnAl2O4 formed and the total electrical conductivity decreased due to the decrease of sintered density. Impedance measurements were used to know the reason and degree of contribution of three resistive elements, ZnO grain, ZnO/CuO, and ZnO/ZnO grain boundaries, to the total electrical conductivity changed.

• Applied Chemistry for Engineering
• /
• v.35 no.1
• /
• pp.1-7
• /
• 2024

Mn-M/Al₂O₃ (M = Cu, Fe, Co, and Ce) catalysts were prepared for simultaneous oxidation of NO, CO, and CH₄, and their oxidation activities were compared. The Mn-Cu/ Al₂O₃ catalyst with the best simultaneous oxidation activity was characterized by XRD, Raman, XPS, and O₂-TPD analysis. The result of XRD indicated that Mn and Cu existed as complex oxides in the Mn-Cu/Al₂O₃ catalyst. Raman and XPS results showed that electron transfer between Mn ions and Cu ions occurred during the formation of the Mn-O-Cu bond in the Mn-Cu/Al₂O₃ catalyst. The XPS O 1s and O₂-TPD analyses showed that the Mn-Cu/Al₂O₃ catalyst has more adsorbed oxygen species with high mobility than the Mn/Al₂O₃ catalyst. The high simultaneous oxidation activity of the Mn-Cu/Al₂O₃ catalyst is attributed to these results. Gas-phase NO promotes the oxidation reactions of CO and CH₄ in the Mn-Cu/Al₂O₃ catalyst while suppressing the NO oxidation reaction. These results were presumed to be because the oxidized NO was used as an oxidizing agent for CO and CH₄. On the other hand, the oxidation reactions of CO and CH₄ competed on the Mn-Cu/Al₂O₃ catalyst, but the effect was not noticeable because the catalyst activation temperature was different.

• Journal of the Korean Chemical Society
• /
• v.30 no.5
• /
• pp.415-422
• /
• 1986

The metal-support interaction of copper oxide supported on ${\gamma}$-alumina and silica was studied by X-ray diffraction (XRD) and temperature-programmed reduction(TPR). It was found that XRD pattern of CuO can not be observed up to 5.0wt % copper content for CuO/${\gamma}-Al_2O_3$ while CuO/$SiO_2$ sample shows the CuO pattern even at 2.5wt% copper content. $H_2-$TPR of CuO/${\gamma}-Al_2O_3$ system shows four major peaks at 145${\circ}C$, 185${\circ}C$, 210${\circ}C$, and 250${\circ}C$. In the case of CuO/$SiO_2$, a large peak at 250${\circ}C$ was appeared accompanying a small peak at 425${\circ}C$. Comparing the TPR peaks with that of copper aluminate which was prepared from the calcination of CuO/${\gamma}-Al_2O_3$ at 1000${\circ}C$, the peaks at around 145${\circ}C$, 200${\circ}C$ (185${\circ}C$ and 210${\circ}C$), and 250${\circ}C$ were corresponded to $Cu^+$ ion in CuO interacting ${\gamma}-Al_2O_3$, $Cu^+$ ions in defect sites of ${\gamma}-Al_2O_3$ and $Cu^{2+}$ ion in the bulk CuO layer, respectively. From the results, it was concluded that there is considerable metal-support interaction in CuO on ${\gamma}-Al_2O_3$ and the interaction results in a stabilization of $Cu^+$ ion in the system.

• Tribology and Lubricants
• /
• v.27 no.1
• /
• pp.1-6
• /
• 2011

The possibility of Cu-Al-Ni intermetallic coating on the mild steel through the combustion synthesis has been investigated. In particular, the effect of the ball milling energy on the microstructure of the coating layer was examined to obtain the best coating condition. Experimental results show that Cu-Al-Ni powder compact was explosively synthesized and successfully coated with the steel matrix. It was revealed that the formation of $Cu_9Al_4$ intermetallic decreased with increase in the ball milling energy. This result supports that the high energy ball milling would be effective for obtaining the most suitable microstructure for Cu-Al-Ni coating layer. However, the excessive ball milling energy seems to decrease the bonding strength between the coating layer and the matrix.

• Transactions of Materials Processing
• /
• v.7 no.5
• /
• pp.465-473
• /
• 1998

The effect of alloying elements of Ag-Cu-Zr-X brazing alloy on the microstructure and the bond strength of $Al_2O_3/Ni-Cr$ brazed steel joint was investigated. The reaction layer, $ZrO_2$ (a=5.146 ${\AA}$ , b=5.213 ${\AA}$ , c=5.311 ${\AA}$ )was formed at the interface of $Al_2O_3/Ni-Cr$ steel joint by the redox reaction between alumina and Zr. The addition of An and Al to the Ag-Cu-Zr brazing alloy gave rise to changes in the thickness of the reaction product layer and the morphology of the brazement. Sn caused the segregation of Zr was decreased b Al the $ZrO_2$ layer formed at the Ag-Cu-Zr-Al alloy was thinner than that of $ZrO_2$ formed at the Ag-Cu-Zr-An alloy. The fracture shear strength was strongly dependent on the microstructure of the brazement. Brazing with Ag-Cu-Zr-Sn alloy resulted in a better bond strength than with Ag-Cu-Zr or Ag-Cu-Zr-Al alloy.

• Korean Journal of Chemical Engineering
• /
• v.36 no.2
• /
• pp.191-196
• /
• 2019

The phase of Cu,Zn,Al precursors strongly affects the activity of their final catalysts. Herein, the Cu,Zn,Al precursor was prepared by precipitation of $Al^{3+}$ onto primitive, amorphous Cu,Zn precipitate. This precursor turned out to be a phase mixture of zincian malachite and hydrotalcite in which the latter phase was less abundant compared to the co-precipitated precursor. The final catalyst derived from this precursor exhibited a little higher copper surface area and methanol synthesis activity than the co-precipitated counterpart. Therefore, the two precursor phases need to be mixed in an adequate proportion for the preparation of active $Cu/ZnO/Al_2O_3$ catalyst.

• Journal of Powder Materials
• /
• v.16 no.4
• /
• pp.280-284
• /
• 2009

The pressureless sintering behavior of $Al_2O_3$/Cu powder mixtures, prepared from $Al_2O_3$/CuO and $Al_2O_3$/Cu-nitrate, has been investigated. Microstructural observation revealed that $Al_2O_3$ powders with nano-sized Cu particles could be synthesized by hydrogen reduction method. The specimens, pressureless-sintered at $1400^{\circ}C$ for 4 min using infrared heating furnace with the heating rate of $200^{\circ}C$/min, showed the relative density of above 90%. Maximum hardness of 16.1 GPa was obtained in $Al_2O_3$/MgO/Cu nanocomposites. The nanocomposites exhibited the enhanced fracture toughness of 4.3-5.7 $MPa{\cdot}m^{1/2}$, compared with monolithic $Al_2O_3$. The mechanical properties were discussed in terms of microstructural characteristics.

• Journal of the Korean Society for Heat Treatment
• /
• v.7 no.2
• /
• pp.96-102
• /
• 1994

The present work was aimed to examine the changes of the shape and particle size distribution(PSD) of ${\delta}^{\prime}$ particles on ageing in Al-Li-(Cu, Zr) alloys which had low density, high specific strength and stiffness, Increasing ageing time and temperature resulted in particles whose aspect ratio tended toward 1. The aspect ratio of ${\delta}^{\prime}$ particles was not dependent upon the ageing temperature and time in Al-Li-Cu alloy but was dependent upon them in Al-Li-Zr alloy. The PSD of ${\delta}^{\prime}$ particles in Al-Li-Zr alloy skewed to the right hand compared with that in Al-Li-Cu alloy, because $Al_3Zr$ phase in Al-Li-Zr alloy formed before ageing promoted the precipitation and growth of ${\delta}^{\prime}$ phase. Therefore, the PSD of the ${\delta}^{\prime}$ particles was found to be affected by the presence of $Al_3Zr$ particles. The growth rate of ${\delta}^{\prime}$ phase was not affected by the existence of the third transition phase $T_1$ formed by the addition of Cu in Al-Li alloy but was affected by the existence of $Al_3Zr$ formed by the addition of Zr in Al-Li alloy.

• Journal of Korea Foundry Society
• /
• v.17 no.5
• /
• pp.480-487
• /
• 1997

Particle reinforced metal matrix composites(MMCs) via a centrifugal spray-cast deposition(CSD) process were fabricated by injecting second phase particles($Al_2O_3$<40${\mu}m$, W<17.3${\mu}m$) into copper melt on the atomizing disc. Compositing modes were investigated by combining microstructures and mathematical modeling between Cu droplets and the reinforced particles injected. The $Cu/W_P$ powders were shown that the W particles penetrate and get embedded in the Cu droplets. It is considered that the W particles composite preferentially in Cu melt on the atomizing disc. On the other hand, the $Al_2O_3$, particles did not penetrate into the Cu droplets on the atomizing disc but get attached in surface of Cu droplets during the flight. It is considered that the compositing may be attained in the flight distance which the relative velocity between Cu droplet and $Al_2O_3$, particle is maximum. The microstructure of the $Cu/W_P$ and the $Cu/(Al_2O_3)_p$ composite preform was strongly influenced by compositing modes of droplets, and after subsequent deposition it was comprised as it is called the dispersed type and the cell type of microstructure, respectively.

• Journal of the Korean Society for Heat Treatment
• /
• v.33 no.6
• /
• pp.284-289
• /
• 2020

Since the dissimilar bonded interface usually consists of intermetallic compounds (IMCs) layer and cracks, their mechanical and electrical properties can be influenced by microstructure at interface between two different metals. In this study, the friction welded Cu-Al busbar, which is widely used to connect a secondary battery and their component, is selected to analyze the influence of interfacial characteristic on their tensile strength and electric conductivity. Then, the electrical characteristics of Cu busbar and Cu-Al busbar were investigated by thermal flow analysis and temperature rise test. In addition, the relationship between the maximum saturation temperature and the electrical conductivity were discussed in terms of interfacial characteristics of the friction welded Cu-Al busbar.