• 대한치과보철학회지
• /
• 제45권5호
• /
• pp.601-610
• /
• 2007

Statement of problem: The adhesion between titanium and ceramic is less optimal than conventional metal-ceramic bonding, due to reaction layer form on cast titanium surface during porcelain firing. Purpose: This study characterized the effect of titanium-ceramic adhesion after gold and TiN coating on cast and wrought titanium substrates. Material and method: Six groups of ASTM grade II commercially pure titanium and cast titanium specimens$(13mm{\times}13mm{\times}1mm)$ were prepared(n=8). The conventional Au-Pd-In alloy served as the control. All specimens were sandblasted with $110{\mu}m\;Al_2O_3$ particles and ultrasonically cleaned for 5min in deionized water and dried in air before porcelain firing. An ultra-low-fusing dental porcelain (Vita Titankeramik) was fused on titanium surfaces. Porcelain was debonded by a biaxial flexure test at a cross head speed of 0.25mm/min. The excellent titanium-ceramic adherence was exhibited by the presence of a dentin porcelain layer on the specimen surface after the biaxial flexure test. Area fraction of adherent porcelain (AFAP) was determined by SEM/EDS. Numerical results were statistically analyzed by one-way ANOVA and Student-Newman-Keuls test at ${\alpha}=0.05$. Results: The AFAP value of cast titanium was greatest in the group 2 with TiN coating, followed by group 1 with Au coating and the group 3 with $Al_2O_3$ sandblasting. Significant statistical difference was found between the group 1, 2 and the group 3 (p<.05). The AFAP value of wrought titanium was greatest in the group 5 with TiN coating, followed by the group 4 with Au coating and the group 6 with $Al_2O_3$ sandblasting. Conclusion: No significant difference was observed among the three groups (p>.05). The AFAP values of the cast titanium and the wrought titanium were similar. However the group treated with $Al_2O_3$ sandblasting showed significantly lower value (p<.05).

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2009년도 춘계학술대회 논문집
• /
• pp.310-313
• /
• 2009

오스테나이트계 고질소 스테인레스강 4 가지 후보강종인 HNS C1, C2, C3, C4에 대해 질소함량, 가압조건 따른 단조재와 온도 및 동일한 가압조건에서 Ni 합금원소 첨가유무에 따른 용체화 처리재(HNS C1, C3)의 물성평가와 실제 냉연 공정의 pass schedule 검증을 위한 모사실험을 통해 다음과 같이 요약 하였다. 1) 가압증가에 따른 질소함량의 증가로 강도 및 경도가 동시 상승하며, 결정립의 미세화 및 기계적 쌍정 발생이 많았다. 동일한 가압조건에서 Ni 첨가된 HNS C3가 Ni 미첨가한 HNS C1 보다 강도-연성 조합평가에서 열/냉간 가공성 등의 특성이 우수하였다. 2) 고질소강 스테인레스강의 적정한 용체화 처리온도 범위는 상용화된 AIS1304와 유사한 $1050^{\circ}C{\sim}1100^{\circ}C$이며, 용체화처리 후냉각방법의 변경(수냉과 공냉)에 따른 경도의 편차는 없었다. 냉연 pass schedule 검증을 위한 모사실험에서 초기 압연의 최적조건은 roll 속도 5mpm, pass당 압연율 $15{\sim}17%$였다.

• 대한환경공학회지
• /
• 제31권10호
• /
• pp.901-908
• /
• 2009

음식물류 폐수를 생활 폐기물 소각로에 직접 분사하여 소각처리 하는 방안에 대하여 검토하였다. 소각설비는 연속 스토카식 실증플랜트를 이용하였다. 그 결과 암모니아성 질소($NH_3$-N)가 다량 함유된 음식물류 폐수를 분사 소각함으로써 질소산화물($NO_x$) 농도저감과 동시에 질소산화물($NO_x$) 저감을 위해 선택적 비촉매 환원장치(selective non-catalytic reduction ; SNCR)에서 사용되는 암모니아($NH_3$)의 사용량을 절감하는 효과를 가져왔다. 또한, 음식물류 폐수를 분사하여 2차 연소실 출구온도를 적정온도인 870~$950^{\circ}C$로 유지하여 소각량을 최대화하는 한편 폐열회수 보일러의 수관외벽 막힘현상 개선을 통한 로의 안정성 확보 및 연속운영기간의 연장을 실현하였다. 질소산화물($NO_x$), 황산화물($SO_x$) 및 다이옥신 등 대기오염물질 26개 항목에 대하여 측정을 실시한 결과 모두 배출허용 기준치 이하의 값을 나타내었다.

• Korean Chemical Engineering Research
• /
• 제49권6호
• /
• pp.790-797
• /
• 2011

삼상유동층에서 수력학적 유사성을 규모인자(scaling factor)를 이용하여 해석하였다. 규모인자는 직경이 다른 두 종류의 삼상유동층간의 기체, 액체, 그리고 고체입자의 체류량과 단위면적당 유효부피흐름속도를 기준으로 정의하였다. 두 종류 삼상유동층의 직경은 각각 0.102 m와 0.152 m이었다. 여과된 압축공기, 물 그리고 밀도가 2,500 kg/$m^3$인 유리구슬을 각각 기체, 액체 그리고 유동고체입자로 사용하였다. 각 삼상유동층에서 각 상들의 체류량은 정압강하법에의해 결정하였다. 기체 및 액체의 유속 그리고 고체유동입자의 크기가 각 상들을 기준으로한 규모인자와 유효부피흐름속도를 기준으로한 규모인자에 미치는 영향을 검토하였다. 직경이 다른 두 삼상유동층에서 기체 체류량의 편차는 기체와 액체의 유속이 증가함에 따라 감소하였으나 유동입자의 크기가 증가함에 따라 증가하였다. 직경이 다른 두 종류 삼상유동층에서 액체 체류량 편차는 기체와 액체 그리고 고체유동입자의 크기가 증가함에 따라 감소하였다. 두 종류 삼상유동층에서 고체입자 체류량 편차는 기체유속과 유동입자의 크기가 증가함에 따라 증가하였으나 액체의 유속이 증가함에 따라 감소하였다. 직경이 다른 두 종류 삼상유동층에서 유효부피흐름속도를 매개로 한 규모인자는 기체유속과 유동입자의 크기가 증가함에 따라 감소하였으나 액체의 유속이 증가함에 따라 증가하였다. 본 연구에서 정의된 규모인자는 삼상유동층 공정의 수력학적 유사성을 해석하는데 효과적으로 사용될 수 있었다.

• Restorative Dentistry and Endodontics
• /
• 제20권2호
• /
• pp.399-422
• /
• 1995

The purpose of this study was to investigate a fragment of possibility of pulpotomy with the Nd-YAG laser by the observation of pulpal healing process and the fine structural changes of the fibroblasts of the remaining pulpal tissues. Class V cavities on !55 teeth from 4 adult dogs were prepared and the pulp chambers were opened with a sterilized round bur. In the control group(19 teeth), the exposed coronal pulps were excised by a sharp excarvator. After bleeding was controlled with the sterilized cotton pellets, calcium hydroxide powder was applied on the remaining pulpal tissues and the cavities were sealed with Z.O.E. In the experimental group 1 : the pulpotomy with laser-calcium hydroxide powder application group(l9 teeth), the exposed coronal pulps were excised by Nd-YAG laser(10 watts power, 2 psi water, 20 psi air) for 2 or 3 seconds and calcium hydroxide powder was applied on the remaining pulpal tissues and the cavities were sealed with Z.O.E. In the experimental group 2 : the pulpotomy with laser-no calcium hydroxide powder application group(17 teeth), after amputating the coronal pulps with Nd-YAG laser as the experimental group 1, the remaining pulpal tissues were covered with stenilized aluminum foil and the cavities were filled with Z.O.E. The animals were sacrificed at the intervals of 1, 2, 3 and 4 weeks. All the teeth were rouutinely processed and the remaining pulpal tissues were observed by the light microscope and electron microscope. The results were as follows : 1. In light microscopic findings, there was no significant difference of the inflammatory response in the remaining pulpal tissues between the control group and the experimental groups. In both of the experimental group 1 : pulpotomy with laser-calcium hydroxide powder application group and the control group, the dentin bridges were observed after 2 weeks and the structure of the dentin bridge was almost same. In the experimental group 2 : pulpotomy with laser-no calcium hydroxide powder application group, the fibrous layers instead of dentin bridge were observed on the superficial portion of the remaining pulpal tissues after 2 weeks and they were consisted with densely crowded active fibroblasts. 2. In the electronmicroscopic findings, the active fibroblasts in the experimental groups were more frequently observed than in the control group at 1 week. But active fibroblasts were found with same frequency after 2 weeks in all of the control group and the experimental groups. 3. General distortions of the cell such as loss of the cell membrane, vaculoization of the cell etc. were observed at the suberficial layer of the remaining pulpal tissues and the carbonization was found in the dentinal wall in 1 week of the experimental groups. 4. In the experimental group 2 : pulpotomy with laser-no calcium hydroxide powder application group, the activity and the density of the fibroblasts in the fibrous layer were more than those in the deep portion of the remaining pulpal tissues after 2 weeks. 5. In the control group, bacteria such as cocci and bacilli were observed frequently, but in the experimntal groups, they could not be observed.

• 한국도로학회논문집
• /
• 제4권4호
• /
• pp.13-21
• /
• 2002

본 연구에서는 아스팔트 혼합물의 특성을 평가하는 대표적인 방법인 마샬안정도와 간접인장강도 시험시 양생온도와 양생시간 및 시험온도에서의 처리시간이 결과에 미치는 영향을 비교분석 하였다. 마샬안정도 시험은 공시체를 $60^{\circ}C$로 유지되는 수조에 30분 수침 후 수행하지만, 공시체의 양생시간에 관한 기준은 없다. 간접인장강도 시험의 경우는 시험온도는 $25^{\circ}C$라고 정해져 있지만 마샬안정도 시험과 마찬가지로 양생시간에 관한 기준은 없다. 또한 간접인장강도 시험을 하기 전 공시체의 온도를 $25^{\circ}C$로 맞추기 위하여 항온항습기 등과 같은 장치에 일정시간 보관해야 하는데 이것 역시 정해진 규정이 없다. 연구결과, 공시체의 양생온도에 따라 안정도와 간접인장강도 값은 많은 차이를 나타냈다. 따라서, 실험실 온도가 $25^{\circ}C$보다 높거나 낮으면, 혼합물의 양생이 제대로 되지 않아 시험결과의 신뢰성이 떨어질 것이다. 양생온도 변화에 따른 시험값 변화를 최소화하기 위하여. 마샬안정도 시험시 공시체를 $60^{\circ}C$ 수조에 수침해야 하는 시간과 간접인장강도 시험 전 공시체를 $25^{\circ}C$에 보관해야 하는 시간을 제안하였다.

• 농업생명과학연구
• /
• 제53권5호
• /
• pp.153-165
• /
• 2019

이 논문은 농업의 공익적 가치 확산의 일환으로 추진되고 있는 농업환경보전 프로그램의 성공적 도입을 위해 농업환경보전 실천기술 도입의 우선순위를 분석하고, 지역 환경에 적합한 맞춤형 농업환경보전실천기술 패키지를 제시하는데 목적이 있다. 농업환경보전 실천기술은 토양·용수·대기 3개 분야, 9개의 세부분야, 30개의 실천기술로 이루어져 있다. 우선순위 분석을 위해 AHP와 BWS의 이점을 적절하게 사용하여, 3개 분야와 9개 세부분야는 AHP기법으로, 분야별 실천기술은 BWS기법으로 우선순위를 측정하여 연구의 차별성 및 완성도를 높였다. 또한, 실천기술 우선순위 평가를 위한 기준은 환경효과성과 기술적용의 용이성을 이용하였다. 우선순위 종합 평가결과, '토양검정 및 비료·가축분뇨 사용량 감축' 활동이 가장 높은 우선순위를 가지는 것으로 평가되었다. 이러한 실천기술에 대한 우선순위 결과를 바탕으로 영농형태별 및 환경조건별 맞춤형 실천기술 패키지의 사례를 제시하였다.

• 한국건설순환자원학회논문집
• /
• 제10권3호
• /
• pp.195-203
• /
• 2022

본 논문에서는 바텀애시 골재의 크기 구성과 가압다짐이 다공성 콘크리트의 열전도도에 미치는 영향을 분석하였다. 본 실험연구에서는 바텀애시를 두 가지 입도의 골재를 섞은 SA와 한 가지 입도만을 갖는 DA를 사용하여 골재 특성을 파악한 후, 다공성 콘크리트 골재로 활용하였다. 물-바인더 비는 0.30으로 고정하고, 가압다짐을 0.5, 1.5 및 3.0 MPa을 콘크리트 시편에 적용하였다. 단위중량, 총 공극률 및 열전도도를 측정하고 분석을 수행하였다. 가압다짐이 증가할 때 단위중량과 열전도도는 증가하고 총공극률은 감소하였다. DA 사용 콘크리트에 비해 SA 사용 콘크리트의 단위중량과 열전도도는 크고 총공극률은 작게 나타난다. 또한, 오븐건조상태 시편의 열전도도가 기건상태 시편의 열전도도보다 낮은 결과를 나타냈다. 회귀분석을 통해 다공성 콘크리트의 단위중량, 총 공극률 및 열전도도와의 상관관계를 제시하였다. 열전도도와 단위중량은 서로 비례하는 상관관계를 나타내며, 열전도도와 총공극률은 서로 반비례하는 상관관계를 나타냈다.

• 한국어류학회지
• /
• 제34권1호
• /
• pp.57-63
• /
• 2022

2016년 4월, 경남 통영시 신봉천에서 채집한 어미 사백어(평균전장 4.6 mm, n=16)를 모래와 돌을 바닥에 깐 실험 수조(60 (L)×30 (W)×30 (H) cm)에 수용하고, 산란행동 및 수정난의 발생과 부화자어의 형태를 관찰하였다. 사백어 어미는 모래 위의 돌 아래에 구멍을 파고 들어가 산란하고, 부화할 때까지 수정난을 보호하는 행동을 보였다. 수정난은 곤봉형(장경 3.2~3.4 mm, 단경 0.6~0.8 mm, n=10)이며 지름이 2~3 cm (원형 또는 타원형)인 난괴를 이루어 돌의 천정에 매달려서 발생하였다. 수온 18~20℃하에서 눈이 생긴 수정난(eyed egg)은 168시간 후에 부화하였다. 부화자어는 투명하며 전장이 4.1~4.4 mm (n=5)이고, 배에는 투명한 난황을 가지고 있었으며 32~33개 (12~13+20)의 근절이 발달해 있었다. 부화 후 3일째, 전장 4.9 mm 자어는 머리의 아래쪽에 입이 열리며 직장이 발달하였다. 전장 난황을 흡수한 전장 5.2 mm 후기자어는 부레 등쪽과 직장 위에 흑색소포가 발달하며 꼬리의 아래 정중선을 따라서 흑색소포가 줄지어 발달하였다.

• 한국식품위생안전성학회지
• /
• 제27권2호
• /
• pp.152-160
• /
• 2012

본 연구에서는 경남에 소재한 토마토 토경재배농장 3곳 (A, B, C)과 양액재배농장 3곳 (D, E, F)을 대상으로 토마토 재배단계의 재배환경과 개인위생에 대하여 생물학적 및 화학적 (중금속) 위해요소를 분석하였다. 생물학적 위해요소를 분석한 결과 재배환경에서 위생지표세균의 경우 토경재배농장의 토양에서 일반세균과 대장균군이 최대7.2 및 6.1 log CFU/g 검출되었고, 관개용수에서는 1.7 log CFU/mL 이하로 검출되었으며, E. coli의 경우 B농장의 토양에서만 1건 검출되었다. 양액재배농장의 양액과 관개용수에서는 일반세균만 최대 1.4 및 1.8 log CFU/mL수준으로 검출되었다. 개인위생의 경우 일반세균과 대장균군이 토경재배농장에서는 0.4-4.6 log CFU/hand, 100 $cm^2$ 수준으로, 양액재배농장에서는 0.4-5.4 log CFU/hand, 100 $cm^2$ 수준으로 검출되었다. 병원성 미생물은 B. cereus만 토경재배농장의 토양에서 최대 4.4 log CFU/g, 관개용수에서 0.5 log CFU/mL, 개인위생에서 1.0-2.9 log CFU/hand, 100 $cm^2$ 검출되었고, 양액재배농장의 개인위생에서 0.5-2.8 log CFU/hand, 100 $cm^2$ 수준으로 검출되었다. 화학적 위해요소인 중금속(Cd, Cu, As, Hg, Pb, Cr, Zn 및 Ni)은 분석 결과 모두 허용기준치 이하 또는 불검출로 나타났다. 따라서 토마토의 재배단계에서 미생물의 오염으로 인한 위해를 확인할 수 있었으며, 안전성을 확보하기 위해서는 최종산물로까지 발생할 수 있는 모든 위해요소를 파악하고 이를 효율적으로 차단시키기 위한 체계적인 관리방안이 모색되어야 할 것으로 판단된다.