• 공업화학
• /
• 제5권4호
• /
• pp.630-636
• /
• 1994

열화처리 후 고무와 황동이 피복된 강선코드의 접박계면 변화를 오제 광전자 분광기와 주사 전자현미경으로 조사하였다. 열열화 후에는 접착층의 부분 산화와 추가 성장이, 습윤열화 후에는 접착층과 황동의 부분 소실이, 동적열화 후에는 접착층의 파괴와 철심의 부식이 관찰되었다. 이러한 접착계면의 변화를 인장시험에서 측정된 접착 성질과 관련지어 고찰하였다.

• 한국주조공학회지
• /
• 제36권3호
• /
• pp.88-94
• /
• 2016

We investigated the effect of heat treatment on an ADC12 alloy produced using diecasting. The heat treatment used in this study was a typical T6 process: a solid solution treatment followed by an artificial aging treatment. As-cast specimens were solid-solution-treated at $500^{\circ}C$ and $530^{\circ}C$ for 1-16 hr, and aged at $160^{\circ}C$ and $180^{\circ}C$ for 1-8 hr. Microstructural changes in the alloy during the heat treatment were observed. Changes in mechanical properties of the alloy were measured using a micro-Vickers hardness tester. Finally, we determined the optimal heat treatment conditions for the diecast ADC12 alloy.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2002년도 춘계학술대회 논문집
• /
• pp.21-24
• /
• 2002

One of the factors influences on microstructure of semi-solid product is forging pressure. Generally, the more forging pressure makes the more fine microstructure in semi-solid compression test. The microstructure and mechanical properties were investigated according to the forging pressure. The applied pressure is 110MPa, 140MPa and 170MPa, respectively. Heat treatment conditions also influence to the microstructure and mechanical properties of semi-solid product. T6 heat treatment was performed and the evaluation of microstructure and mechanical properties was investigated according to the aging time in T6 heat treatment.

• 한국주조공학회지
• /
• 제1권2호
• /
• pp.10-18
• /
• 1981

In this paper tensile strength and fatigue propagation rate were investigated by aging treatment $(T_6)$ and thermomechanical treatment (TMT) of 7075-Al Alloy specimen. The results of teat showed that TMT improved tensile strength and fatigue crack propagation due to bomogenization of microstructure. In TMT, the results of comparison between T-H' AHA and T-AHA and $T-AH{\cdot}{\cdot}{\cdot}$and $T-HA{\cdot}{\cdot}{\cdot}$were showed that T-AHA and $T-AH{\cdot}{\cdot}{\cdot}$treatments, after solution treatment, which are aging treated before rolling have higher tensile strength. Our investigation on high temperature stability at the Specimen for $T_6$, T-AHA, $T-AH{\cdot}{\cdot}{\cdot}$treatments resulted in rapid reduction of tensile strength over $150^{\circ}C$, but the reduction of tensile strength for specimen of TMT was smoothed than $T_6$.

• Macromolecular Research
• /
• 제12권6호
• /
• pp.608-614
• /
• 2004

Isotactic polypropylene (PP) surfaces were modified with argon and oxygen plasmas using a radio­frequency (RF) glow discharge at 240 mTorr and 40 W. The changes in topography and surface structure were investigated by atomic force microscopy (AFM) in conjunction with specular reflectance of infrared (IR) microspectroscopy. Under our operating conditions, the AFM image analysis revealed that longer plasma treatment resulted in significant ablation on the PP surface, regardless of the kind of plasma employed, but the topography was dependent on the nature of the gases. Specular reflectance IR spectroscopic analysis indicated that the constant removal of surface material was an important ablative aspect when using either plasma, but the nature of the ablative behavior and the resultant aging effects were clearly dependent on the choice of plasma. The use of argon plasma resulted in a negligible aging effect; in contrast, the use of oxygen plasma caused a noticeable aging effect, which was due to reactions of trapped or isolated radicals with oxygen in air, and was partly responsible for the increased surface area caused by ablation. The use of oxygen plasma is believed to be an advantageous approach to modifying polymeric materials with functionalized surfaces, e.g., for surface grafting of unsaturated monomers and incorporating oxygen-containing groups onto PP.

• 열처리공학회지
• /
• 제12권1호
• /
• pp.21-30
• /
• 1999

The present study were investigated changes of precipitation behaviour of laves phase in ferrite single phase and ferrite-martensite dual phase and precipitation of laves phase under stress. Hardness changes in ferrite phase appeared two hardness peaks by precipitation of initial fine precipitator and laves phase in 3Mo-0.3Si and 3Mo-0.3Si-C specimens, respectively. Hardness changes in martensite phase of 3Mo-0.3Si-C specimen was lower in the initial stage of aging by carbide precipitation and after this, increased by re-hardening due to precipitation of laves phase. In the ferrite phase, laves phase was mainly precipitated, whereas in the martensite phase, carbide was preferentially formed during the initial stage of aging and with increasing aging time, laves phase and carbide were simultaneously precipitated by precipitation of laves phase at around carbide. In the ferrite-martensite interface, laves phase was mainly precipitated and carbide was mainly formed at boundary of lath martensite than grain boundary. Adding the stress in aging, fine precipitator of inital precipitation of laves phase precipitated in (100) of perpendicular to tensile direction and has grown to only followed<010>direction and also, volume fraction of laves phase increased. Consequently, the stress added was accelerated initial precipitation of laves phase.

• 펄프종이기술
• /
• 제43권5호
• /
• pp.1-10
• /
• 2011

In this study, 13 water soluble polymers(6 natural polymer, 7 synthetic polymer) were treated on Hanji. Mechanical properties, morphology and oxidation index with thermal aging were measured on the aged Hanji, dewaxed Hanji and polymer treated Hanji. 3 natural polymer(such as CMC, EC, MC) and 3 synthetic polymers(such as PVA 1500, 2000, PEG 1500) treated Hanji had higher strength than other polymer treated Hanji. The oxidation index of 3% methyl cellulose solution treated Hanji did a little increase with thermal aging. Finally, methyl cellulose was found to be the most efficient method for strengthening the dewaxed Hanji. The best aging safety and thermal stability were obtained at the methyl cellulose 3% water solution.

• 펄프종이기술
• /
• 제45권1호
• /
• pp.1-5
• /
• 2013

Printing papers published in between 1950's and 1990's were treated with three methods such as distilled water washing, $CaCO_3$ solution washing and methyl cellulose solution coating for improving their conservational properties. Accelerated aging with $80^{\circ}C$ and 80% RH for 14 days was applied to the testing papers. Results showed that distilled water and $CaCO_3$ washing kept increased pH even after accelerated aging, but did not improve folding endurances for 1950's-60's papers. Methyl cellulose treatment did not increased pH of the old papers, but increased folding endurances remarkably for 1950's-60's papers even after accelerated aging. It suggests that methyl cellulose treatment after $CaCO_3$ washing should give improvements both in pH and folding endurance.

• 한국원자력학회:학술대회논문집
• /
• 한국원자력학회 1996년도 춘계학술발표회논문집(3)
• /
• pp.79-84
• /
• 1996

Small punch test was performed on CF8 duplex stainless steel aged at 370 and 400$^{\circ}C$ up to 5,000 h to evaluate the degree of the thermal aging embrittlement. At room temperature, the SP load-displacement curve was in a similar shape to those of ferritic steels and had a good reproducibility in spite of two-phase structure. The aging heat treatment resulted in a slight increase of the yield strength. As test temperature was lowered, the SP load showed a sudden drop followed by serrations before the SP specimen was fractured, resulting from the cracking of ferrite phase. The extent of thermal embrittlement was assessed in terms of the SP energy. Aging treatment at higher temperature led to a larger shift in the transition temperature and the corresponding change in the fracture mode. The main cause of the degradation was the embrittlement of ferrite phase. Additionally the phase boundary separation profoundly contributed to the degradation of the specimen aged at 400$^{\circ}C$.

• Asian-Australasian Journal of Animal Sciences
• /
• 제22권2호
• /
• pp.282-288
• /
• 2009

The present paper describes the effects of pressure and post-mortem aging treatments on in situ proteasome activity in rabbit and bovine skeletal muscles. Synthetic peptide hydrolyzing activity of rabbit proteasomes remained in the muscle after exposure to pressures up to 100 MPa. However, when a pressure of 400 MPa or more was applied, proteasomes were markedly inactivated. The extraction of proteasomes from excessively pressurized muscle appeared to be difficult. Proteasomes in aged muscle remained relatively stable throughout the aging process, with activity after 168 h (7 days) being 35%, 48%, 53% and 31% of the 0 h post-mortem LLVY, LSTR, AAF and LLE total hydrolyzing activities, respectively. The synthetic peptide hydrolyzing activities of bovine muscle proteasomes were similar to those of rabbit skeletal muscle proteasomes. The results suggest that synthetic peptide hydrolyzing activity remains in muscle exposed to relatively low pressures. Furthermore, it is known that high-pressure treatment induces fragmentation of myofibrils, modification of actin-myosin interaction and activation of intramuscular proteinases, cathepsins and calpains. Thus, proteasomes are probably involved in the tenderization process in combination with other intramuscular proteinases under high-pressure conditions. Our findings confirmed that proteasomes play a role in meat tenderization induced by high-pressure treatment or aging.