• The Journal of Korean Academy of Prosthodontics
• /
• v.21 no.1
• /
• pp.9-26
• /
• 1983

In order to investigate the biocompatibility of silver-palladium alloys, gingival fibroblast was obtained from a healthy human gingival and cultured in MEM medium with the addition of silverpalladium alloys. Four different mixture of silver-palladium alloys comprising of Ag-Pd-Au, Ag-Pd-In and Ag-Sn were tested. Results were assessed by calculating the cell multiplication rate per millimeter of medium and morphological changes in cells were also observed and noted.The obtained results were as follows; 1. Ag-Pd-Au alloy was indicated to be most biocompatible with gingival fibroblast. Also there was a decrease in cytotoxicity of the alloy as the concentration of gold increased. 2. Ag-Pd alloy showed a decrease in cell multiplication rate as compared to Ag-Pd~Au alloy. 3. Silver-palladium alloy supplemented with Indium increased the cell multiplication rate. 4. Among the alloys tested, Ag-Sn alloy was indicated to be the most cytotoxic and the least biocompatible with human gingival fibroblast.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.97-97
• /
• 2017

This study investigated the corrosion protection by electrodeposited copper layer on AZ31 Mg alloy with and without additional silver layer by immersion test, salt spray test, OCP transient and potentiodynamic polarization experiment. The single electrodeposited Cu layer on AZ31 Mg alloy showed a nodular structure with many imperfections of crevices between the nodules, which resulted in the fast initiation of pitting corrosion within first few hours of immersion. Double-layer coating of Cu and outer Ag layer slightly increased the initiation time for pitting corrosion. Triple-layer coatings of Cu/Ag/Cu exhibited the most efficient corrosion protection of AZ31 Mg alloy, compared to the single- and double-layer coatings. Surface morphology of the outer Cu layer in the triple-layer was changed from the nodular structure to fine particle structure with no crevices due to the presence of an additional Ag layer. Thus, the improved corrosion resistance of AZ31 Mg alloy by electrodeposited Cu/Ag or Cu/Ag/Cu layers is readily ascribed to the decreased number of imperfections in the electrodeposited layers due to the additional silver layer. It is concluded that the additional silver layer provides many nucleation sites for the second Cu plating, resulting in the formation of finer and denser structure than the first Cu electrodeposit.

• The Journal of Advanced Prosthodontics
• /
• v.7 no.5
• /
• pp.392-399
• /
• 2015

PURPOSE. The aim of this study was to evaluate the effect of metal primers on the bonding of dental alloys and veneer resin. Polyvinylpyrrolidone solution's tarnish effect on bonding strength was also investigated. MATERIALS AND METHODS. Disk-shape metal specimens (diameter 8 mm, thickness 1.5 mm) were made from 3 kinds of alloy (Co-Cr, Ti and Au-Ag-Pd alloy) and divided into 4 groups per each alloy. Half specimens (n=12 per group) in tarnished group were immersed into polyvinylpyrrolidone solution for 24 hours. In Co-Cr and Ti-alloy, Alloy Primer (MDP + VBATDT) and MAC-Bond II (MAC-10) were applied, while Alloy Primer and V-Primer (VBATDT) were applied to Au-Ag-Pd alloys. After surface treatment, veneering composite resin were applied and shear bond strength test were conducted. RESULTS. Alloy Primer showed higher shear bond strength than MAC-Bond II in Co-Cr alloys and Au-Ag-Pd alloy (P<.05). However, in Ti alloy, there was no significant difference between Alloy Primer and MAC-Bond II. Tarnished Co-Cr and Au-Ag-Pd alloy surfaces presented significantly decreased shear bond strength. CONCLUSION. Combined use of MDP and VBATDT were effective in bonding of the resin to Co-Cr and Au-Ag-Pd alloy. Tarnish using polyvinylpyrrolidone solution negatively affected on the bonding of veneer resin to Co-Cr and Au-Ag-Pd alloys.

• Journal of Korea Foundry Society
• /
• v.28 no.4
• /
• pp.184-189
• /
• 2008

Ag-Cd alloy has been widely used as an electrical contact material, since Ag-Cd alloy has a good wear resistance and stable contact resistance. But nowadays Ag-Cd alloy is not considered as electrical contact material any more due to detrimental effect on environments. Currently, active researches are being performed on ($Ag-SnO_2$ and $Ag-SnO_{2}-In_{2}O_{3}$) as an alternative solution which can fix the remaining environmental problems. However, $In_{2}O_{3}$ is relatively expensive and Ag-Sn alloy has low wear resistance. Our recent research results show that Ag-X%Zn-Y%Sn has similar physical and chemical properties. In the present study, so we tried to change and to optimize the Zn oxide content to over 6 wt% and Sn oxide content with 0.5, 1.0, 1.5 wt%. Results obtained from the experiments on the Ag-X%ZnO-Y%$SnO_2$ are discussed.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.3
• /
• pp.286-300
• /
• 2016

Pd-Ag alloy membranes have attracted a great deal of attention for their use in hydrogen purification and separation due to their high theoretical permeability, infinite selectivity and chemical compatibility with hydro-carbon containing gas streams. For commercial application, Pd-based membranes for hydrogen purification and separation need not only a high perm-selectivity but also a stable long-term durability. However, it has been difficult to fabricate thin, dense Pd-Ag alloy membranes on a porous stainless steel metal support with surface pores free and a stable diffusion barrier for preventing metallic diffusion from the porous stainless steel support. In this study, thin Pd-Ag alloy membranes were prepared by advanced Pd/Ag/Pd/Ag/Pd multi-layer sputter deposition on the modified porous stainless steel support using rough polishing/$ZrO_2$ powder filling and micro-polishing surface treatment, and following Ag up-filling heat treatment. Because the modified Pd-Ag alloy membranes using rough polishing/$ZrO_2$ powder filling method demonstrate high hydrogen permeability as well as diffusion barrier efficiency, it leads to the performance improvement in hydrogen perm-selectivity. Our membranes, therefore, are expected to be applicable to industrial fields for hydrogen purification and separation owing to enhanced functionality, durability and metal support/Pd alloy film integration.

• Journal of the Korean Vacuum Society
• /
• v.16 no.4
• /
• pp.291-297
• /
• 2007

The field emission properties of CNT-emitters coated with Ag-Cu alloy have been investigated. The vertical aligned multi-walled CNTs were synthesized by dc-plasma enhanced chemical vapor deposition (dc-PECVD) and the Ag-Cu alloy was coated by using dc-magnetron sputter. The morphology of alloy-coated and un-coated CNT-emitters was observed by using SEM and their field emission properties were also measured. Annealing the AgCu-coated CNTs at temperature more than ${\sim}700^{\circ}C$, the Ag-Cu alloy was diffused to and aggregated on the top of the CNT as a Q-tip. A significant progress on the field emission was not observed with coating Ag-Cu alloy on the CNTs, but a certain improvement in a resistance against oxygen gas was made confirmation. It seems to be due to inertness of Ag-Cu alloy on the CNTs.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.6
• /
• pp.549-554
• /
• 2003

The purpose of this paper is to investigate the solder properties by the change of P mass percentage. Tension test, wetting balance test, spread test, and analysis of intermetallic compound after isothermal aging of Sn-2.5Ag-0.7Cu-0.005P, Sn-2.5Ag-0.7Cu-0.01P, Sn-2.5Ag-0.7Cu-0.02P, Sn-0.7Cu-0.005P were performed. Adding P in the solder alloys resulted in improvement of tensile strength, reduction of intermetallic compound growth, reduction of oxidization in fusible solders under wave soldering. After comparing solder alloy containing P with tin-lead eutectic solder alloy, P contained solders alloys showed much better solder properties than eutectic solder alloy. Furthermore, this solder alloy presented remarkable properties than any other lead-free solder alloy.

• The Journal of Korean Academy of Prosthodontics
• /
• v.33 no.4
• /
• pp.645-661
• /
• 1995

As the mechanical property of composite resin improved, composite resin has been widely used esthetic dentistry. In the field of esthetic dentistry, the color of prosthetic material is very important. The purpose of this study was to evaluate the color difference of specimens, by the types of alloys and gold electrodeposit. Experimental groups were as follows : Group Prec : Au-Pt alloy with no gold coating and no resin veneer. Group Semi : Pd-Ag alloy with no gold coating and no resin veneer. Group BAse : Ni-Cr alloy with no gold coating and no resin veneer. Group Gsem : Pd-Ag alloy with no gold coating and no resin veneer. Group Gbas : Ni-Cr alloy with no gold coating and no resin veneer. Group PreR : Resin veneer on the Pd-Ag alloy without gold coating. Group SemR : Resin veneer on the Pd-Ag alloy without gold coating. Group GbsR : Resin veneer on the Ni-Cr alloy with gold coating Group BasR : Resin veneer on the Ni-Cr alloy without gold coating. In this study, colors of metal surfaces and veneered resins were evaluated by the CIE $L^{*}a^{*}b$ system. The results obtained were as follows : 1. different alloy types and gold coating make the $L^{*}a^{*}b$ system. 2. The ${\Delta}E^*$ab value between groups semi and Base was less than 1.5 and there was no $a^*$ and $b^*$ value difference between groups Gsem and Gbas 3. The values of $L^*$ and $a^*$ ain groups GsemR and GbasR were so similar that the ${\Delta}E^*$ab value was as small as 0.58. 4. In resin specimens with gold coated semiprecious or base alloys showed yellower and redder deviation than the resin specimens with precious alloy. 5. The ${\Delta}E^*$ab values between goups PreR-GsemR and groups PreR-GbasR were as small as 2.68 and 2.22 respectively.

• Korean Journal of Metals and Materials
• /
• v.46 no.7
• /
• pp.443-448
• /
• 2008

Contact materials are used in many electrical devices. Ag-Cd alloy has been widely used in electrical part, because Ag-Cd alloy has a good wear resistance and stable contact resistance. But nowadays Ag-Cd alloy isn't being used because of environmental challenges. Currently new research is being done on ($Ag-SnO_2$ and $Ag-SnO_2-In_2O_3$) as an alternative solution to fix any remainly environmental challenges. However $In_2O_3$ is more expensive and Ag-Sn alloy has low wear resistance. According to our research data Zn has a similar physical and chemical property. In this work, so we changed and optimized the Zn oxide to over 4 and added Sn oxide ratio 0.5, 1.0, 1.5wt%. Conclusions from the data recorded from the experiment of $Ag-ZnO-SnO_2$ are as follows.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.640-644
• /
• 2000

The microstructure, wettability, shear strength and aging effect of Sn-3.5Ag/Cu and Alloy42 lead-frame solder joints were measured for comparison. In the case of Sn-3.5Ag/Cu, Ag$_3$Sn and Cu$\sub$6/Sn$\sub$5/ phases in the matrix Sn and 1∼2$\mu\textrm{m}$ thick Cu$\sub$6/Sn$\sub$5/ Phase at the interface of solder/lead-frame were formed. In the case of Sn-3.5AAg/A11oy42, only Ag$_3$Sn Phase of low density in the matrix Sn and 0.5∼1.5$\mu\textrm{m}$ thick FeSn$_2$phase at the interface of solder/lead-frame were formed. Comparing to Cu, Alloy42 shear strength of Alloy 42 solder joints was smaller than that of Cu and all declined after aging. After aging at 180$^{\circ}C$ for 1 week, η-Cu$\sub$6/Sn$\sub$5/ layer was formed on Cu lead-frame, while AgSn$_3$ phase in the matrix and thickened FeSn$_2$at the interface were formed on Alloy42 lead-frame.