• Transactions on Electrical and Electronic Materials
• /
• 제14권4호
• /
• pp.165-171
• /
• 2013

Nanostructured pure a-C and nitrogen doped a-C: N thin films with small particle size of, ~50 nm were obtained by Aerosol-assisted CVD method from the natural precursor camphor oil. Five samples were prepared for the a-C and a-C: N respectively, with the deposition temperatures ranging from $400^{\circ}C$ to $600^{\circ}C$. At high temperature, the AFM clarifies an even smoother image, due to the increase of the energetic carbon ion bombardment at the surface of the thin film. An ohmic contact was acquired from the current-voltage solar simulator characterization. The higher conductivity of a-C: N, of ${\sim}{\times}10^{-2}Scm^{-1}$ is due to the decrease in defects since the spin density gap decrease with the nitrogen addition. Pure a-C exhibit absorption coefficient, ${\alpha}$ of $10^4cm^{-1}$, whereas for a-C:N, ${\alpha}$ is of $10^5cm^{-1}$. The high ${\sigma}$ value of a-C:N is due to the presence of more graphitic component ($sp^2$ carbon bonding) in the carbon films.

• Bulletin of the Korean Chemical Society
• /
• 제27권10호
• /
• pp.1572-1576
• /
• 2006

A dimeric precursor, $[Cu(dmae)(OCOCH_3)(H_2O)]_2$ for the CVD of copper metal films, (dmaeH = N,N-dimethylaminoethanol) was synthesized by the reaction of copper(II) acetate monohydrate ($Cu(OCOCH_3)_2{\cdot}H_2O$) and dmaeH in toluene. The product was characterized by m.p. determination, elemental analysis and X-ray crystallography. Molecular structure of $[Cu(dmae)(OCOCH_3)(H_2O)]_2$ shows that a dimeric unit $[Cu(dmae)(OCOCH_3)(H_2O)]_2$ is linked to another through hydrogen bond and it undergoes facile decomposition at 300 C to deposit granular copper metal film under nitrogen atmosphere. The decomposition temperature, thermal behaviour, kinetic parameters, evolved gas pattern of the complex, morphology, and the composition of the film were also investigated.

• Progress in Superconductivity
• /
• 제12권1호
• /
• pp.68-73
• /
• 2010

Y123 films have been deposited on $LaAlO_3$ (100) single-crystal and IBAD substrates by spray pyrolysis method using nitrate precursors. Ultrasonic atomization was adopted to decrease the droplet size, spraying angle and its moving velocity toward substrate for introducing the preheating tube furnace in appropriate location. A small preheating tube furnace was installed between spraying nozzle and substrate for fast drying and enhanced decomposition of precursors. C-axis oriented films were obtained on both LAO and IBAD substrates at deposition temperature of around $710{\sim}750^{\circ}C$ and working pressures of 10~15 torr. Thick c-axis epitaxial film with the thickness of $0.3{\sim}0.6\;{\mu}m$ was obtained on LAO single-crystal by 10 min deposition. But the XRD results of the film deposited on IBAD template at same deposition condition showed that the buffer layers of the IBAD metal substrate was affected by long residence of metal substrate at high temperature for YBCO deposition.