• Journal of the Korea Institute of Building Construction
• /
• v.7 no.4
• /
• pp.145-151
• /
• 2007

In this paper, tests are carried out in order to investigate the strength development of concrete under various binder types, W/B and curing temperature ranged from $5{\sim}20^{\circ}C$. Fly ash and blast furnace slag were incorporated by as much as 30%, respectively. Strength development of concrete are estimated using Logistic model and strength ratio of concrete at 28days to that at early age are also investigated. According to experimental results, it is found that good agreements are obtained between measured values and calculated ones using logistic model below $20^{\circ}C$. Strength ratio of concrete at 28days to that at early age increases in case W/B decreases and curing temperature increases. Tables and graphs for strength ratio of concrete are provided in this paper. It is capable of obtaining and predicting the periods to attain design strength by considering increment factor of strength easily with the table and graphs presented in this paper. This paper presents the reference data to decide removal time of form, time to reach target strength and strength inspection of remicon whether the test specimens meet the specified criteria of compressive strength. Multi regression models with respect to the relationship between 7days compressive strength and 28 days compressive strength depending on W/B and admixture types are presented.

• The Journal of Engineering Geology
• /
• v.25 no.2
• /
• pp.179-188
• /
• 2015

Although permeating injection is ideal for grouting reservoir embankments, it is usually combined with fracturing injection for grouting, which can disturb the original soil. Compaction with low expansive pressure followed by grout injection can overcome this problem. An expansive compaction (EC) packer was developed in this work to easily apply sequential injection and compaction at a work site. Furthermore, to achieve compaction around the grouting hole, a mixture of expansive admixtures and grout was injected with the EC packer to trigger an increase in volume of the grout material. This work verifies the compaction effect of the EC packer and the expansive admixture. It reports the concepts of the EC packer, the range of expansive compaction, the effectiveness of injection, and the results of indoor tests performed to verify the effectiveness of the expansive admixtures. The indoor testing comprised a preparatory test and the main test. The preparatory test assessed the admixtures for their compaction effects, while the main test measured and analyzed the admixtures' expansive force, pressure, and compaction effect with a mold to verify the effectiveness of the compaction effect.

• Journal of the Korea Concrete Institute
• /
• v.12 no.1
• /
• pp.79-88
• /
• 2000

Usually, the expansive additives is used to prevent the occurrence of drying shrinkage in concrete. However it may sometimes be over-added in field due to the insufficient cognition of constructor's, which may cause the serious problems in concrete structures. In this study the experiments are performed to present the expansion properties of concrete by varying the water to binder ratios, unit contents of expansive additives and curing conditions. By the results, the strength showed an increase with the addition of expansion additives from 30kg/㎥ up to 50kg/㎥, and a great decrease by contraries if the larger amount are added. Also the more the expansion additives were used, the more length change occurred in concrete. In view of the curing conditions, the concrete by air cured appeared a little expansion even the unit expansion additives increased, which showed an opposite inclination of that with standard curing. This could be explained by the less occurrence of hydration in air condition which also lead to the little expansion of concrete. Hence the expansion concrete to be cured in water or moisture condition became an especial important thing. concrete using expansive additives showed that high expansion was taken place with the rise of temperature.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.6
• /
• pp.566-574
• /
• 2012

To address the problem of global warming, consumption of cement, the main material of concrete, should be decreased. Unfortunately, when industrial by-products are used in large quantities as admixture, the early age strength of concrete will be decreased, reducing its viability for use in concrete structures. Therefore, in this study, the application of an ionization accelerator and alkaline activator as addition agent of superplasticizer were investigated to secure a similar early age strength to that of normal concrete, thus increasing the viability of low cement concrete. Through the investigation, it was found that specimens that used a combination of Alkaline-activator (Na2Sio3) and ionization accelerator (Amine) had the highest early and long-age compressive strength. From this, we can determine an appropriate range of application of superplasticizer to improve early-age compressive strength of low cement concrete.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.05a
• /
• pp.146-147
• /
• 2014

In this study, as the resistance of the carbonation for high volume admixture incorporating concrete, coating effect of using refined cooking oil in the surface of high volume admixture incorporating concrete has been tested. The following results could be made as the conclusion. For the fresh concrete, the slump and air content has been identified as satisfying the target range. For the hardened concrete, comparing with specimen of Plain, specimen with coating showed better long age compressive strength. For the carbonation speed, the specimen of FA30 showed highest speed and the specimen of BS60 showed higher speed than specimen of Plain. For all the specimens coated with RCO, as the decrease of capillary pores inside the concrete, the carbonation speed has been obviously decreased and with even better effect than using PEP coating. It could be identified that specimens with coating by RCO showed good effect on refrain the speed of carbonation.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.05a
• /
• pp.240-241
• /
• 2014

The environmental pollution problem the globally related to global warming arises. In the construction industry the cement mostly use material, generates the great quantity of CO₂ among the fired process and the global warming is more aggravated. In addition, the polysilicon that is the main raw material used in the solar power generation, produces 1 ton and the industrial by-product of 2 tons is generated. In this way, the arising sludge there is not method recycling and it is all discarded. Therefore, in this research, try to present as the fundamental research material for using the polysilicon sludge as the admixture of the cement in order to reduce the amount of the cement. The based on 'KS L ISO 679' was progressed mortar test. the liquidity, air flow rate, setting time, water absorption ratio, flexural and compression strength was measured. According to, appropriate replacement ratio of the polysilicon sludge tries to analyze.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.11a
• /
• pp.269-272
• /
• 2003

This study is intended to investigate the properties of concrete using AE Water Reducing Agent of Early-Strength Type. According to the results, as for the replacing method of mineral admixture, setting time is shortened faster in order of replacement for fine aggregate, combination and replacement for cement, and when AE Water Reducing Agent of Early-Strength Type is used, it is shortened by about 4 hours, compared with normal AE Water Reducing Agent Compressive strength is lower in the case of replacement for fine aggregate, but higher in the other case than that of plain concrete. And When AE Water Reducing Agent of Early-Strength Type is used, early compressive strength is very high in comparison to normal AE Water Reducing Agent. Early strength development is very favorable by the use of AE Water Reducing Agent of Early-Strength Type regardless of the replacing method of mineral admixture at $20^{\circ}C$, but at $l0^{\circ}C$, it is effective for Early strength development that W/B is lowered to below 45%, BS of 20% is replaced for fine aggregate, and AE Water Reducing Agent of Early-Strength Type is used.

• Journal of Environmental Science International
• /
• v.21 no.9
• /
• pp.1059-1068
• /
• 2012

The purpose of this study was to develope the environmentally favorable method of roller compacted soil concrete pavement using industrial waste red mud. Red mud was the major solid waste produced in the process of alumina extraction from bauxite(Bayer process). For recycling purpose, red mud was treated and applied to use as concrete admixtures. To this end, laboratory test such as compressive strength of soil concrete, and field test such as construction characteristics of soil concrete pavement, had been conducted. From the study results, the compressive strength of soil concrete was strongly related to its matrix proportion and compaction energy. The optimum mix proportion was comprised of cement 300 $kg/m^3$, water 110 $kg/m^3$, fine aggregate 600 $kg/m^3$, course aggregate 1400 $kg/m^3$, red mud admixture 50 $kg/m^3$ and compaction energy above 2.86 $cm-kgf/m^3$. The $7^{th}$-day and $28^{th}$-day mean compressive strength of soil concrete were 43.8 MPa and 53.3 MPa each under the optimum condition. Pavement application of soil concrete using red mud admixture indicated that the proposed method was simple in case of construction and showed a good surface texture.

• Proceedings of the IEEK Conference
• /
• 2001.10a
• /
• pp.549-554
• /
• 2001

The authors have proposed that waste glass, which is crushed to pieces, can be used as a concrete aggregate. At the present time, recycled-glass concrete is used for sidewalk concrete blocks and pavement as glass is ornamental. However, in cases where recycled-glass concrete is used for structural concrete, strength and durability are required as structural concrete is exposed to the weather. Glass that is used generally is a mixture of SiO$_2$, Na$_2$O and CaO. SiO$_2$is the most likely cause of alkali-aggregate reaction when waste glass was used for concrete aggregate. In this study, an alkali-aggregate reaction test that is one of the important tests related to durability of aggregate was carried out far discussion of utilization of waste glass for concrete aggregate. From the results of the tests, it is found that glass is a reactive aggregate. The pessimum proportion of glass is about 75%. Then the cases of using fly ash, blast furnace slag and artificial zeolite for admixture materials were also examined for the purpose of prevention of alkali-aggregate reaction. from the results of the test, it was found that using them is an effective way to prevent alkali-aggregate reaction. The compressive strength in the cases of using admixture materials is larger than that without admixture materials.

• Asian-Australasian Journal of Animal Sciences
• /
• v.28 no.1
• /
• pp.14-19
• /
• 2015

The genetic diversity of native chicken populations from Myanmar, Thailand, and Laos was examined by using 102 insertion and/or deletion (indels) markers. Most of the indels loci were polymorphic (71% to 96%), and the genetic variability was similar in all populations. The average observed heterozygosities ($H_O$) and expected heterozygosities ($H_E$) ranged from 0.205 to 0.263 and 0.239 to 0.381, respectively. The coefficients of genetic differentiation (Gst) for all cumulated populations was 0.125, and the Thai native chickens showed higher Gst (0.088) than Myanmar (0.041) and Laotian (0.024) populations. The pairwise Fst distances ranged from 0.144 to 0.308 among populations. A neighbor-joining (NJ) tree, using Nei's genetic distance, revealed that Thai and Laotian native chicken populations were genetically close, while Myanmar native chickens were distant from the others. The native chickens from these three countries were thought to be descended from three different origins (K = 3) from STRUCTURE analysis. Genetic admixture was observed in Thai and Laotian native chickens, while admixture was absent in Myanmar native chickens.