• Journal of Welding and Joining
• /
• v.34 no.2
• /
• pp.36-45
• /
• 2016

Recent developing tendency for technologies of high efficient brazing are studied by searching of NDSL, Science Direct, KIPRIS, PCT and so on. Active metal brazing, arc brazing, fluxless brazing, brazing with low melting point, reactive air brazing, laser brazing, laser droplet brazing are investigated. By optimal selecting of the above mentioned technologies, it needs to investigate an economical metallurgical design and the advanced brazing methods. To improve the embrittlement of intermetallic compound at brazing interface, it must be studied the inexpensive variant metals including nonmetals and the heat sources(MIG, TIG, Laser) by hybrid techniques.

• Journal of Welding and Joining
• /
• v.9 no.4
• /
• pp.17-27
• /
• 1991

The direct brazing technology which could be used for the simplification of brazing process and the improvement of brazed joint quality was studied with $Al_2O_3$ and stainless steels. The brazing of $Al_2O_3$ to STS304 or STS430 was performed under different brazing conditions such as brazing filler metal, temperature, heating rate and brazing time. Microstructural observation and chemical analysis be SEM/EPAM were carried out to verify the quality of brazed joints. 4-point bending strength of brazed joints was also measured to find the optimal brazing conditions. The results showed that, in brazing of $Al_2O_3$, the mixed oxide layer resulted from the reaction between Ti in filler metal and oxide layer on the material surface to be brazed was found to be bery important for the joint quality. The width of oxide layer varied with the brazing conditions such as brazing time, heating rate and chemical composition of filler metals. The strength of brazed joints was more affected by the type of materials and their thermal properties than by brazing heat cycle.

• Proceedings of the KWS Conference
• /
• 1991.11a
• /
• pp.15-17
• /
• 1991

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.253-254
• /
• 2009

본 연구는 다결정 알루미나 소결체와 사파이어웨이퍼(sapphire wafer)의 견고한 접합을 위해 활성금속 Ti가 함유된 Active Filler Metal을 사용하였고, 이를 브레이징한 후 접합 반응층과 Ti 거동 특성에 관한 것이다. 브레이징 (brazing)은 Ar 분위기 종에 $850^{\circ}C$에서 이행하였으며. 이때 다결정 알루미나, 사파이어와 Active Filler Metal 사이의 접합 반응층을 확인하였다. Active Filler Metal 내어| 존재하는 Ti가 접할 반응층의 양계면에 집중되는 것을 SEM을 이용하여 확인하였다. 또한 EDS Line Scanning을 실시하여 접합부에서 원소들의 분포를 관찰하였다.

• Journal of Welding and Joining
• /
• v.32 no.1
• /
• pp.66-70
• /
• 2014

In Ti active brazing of YSZ to STS 430 using Ag-Cu Filler Metal, the effect of Ti contents on the shear bonding strength were investigated together with the effect of brazing temperature and holding time. The addition of Ti in Ag-Cu Filler Metal increased the bonding strength up to 4.68% Ti, followed by the decrease with further addition. This seems to be caused by formation of TixOy at the reaction layer. Brazing temperature was optimized at $960^{\circ}C$ among a given temperature ranges. The addion of Sn to Ag-Cu filler metal brought the decrease of its melting temperature its melting temperature without a significant decrease of bonging strength.

• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.3
• /
• pp.1-7
• /
• 2011

Active brazing of ceramic to metal is reviewed in this paper. As one of the key aspect in joint techniques, active brazing has been developed to simplify the manufacturing procedure of brazed joints between ceramic and metal. The active filler metal includes Ag-Cu-Ti series, Cu-Ti series, Co-Ti series and so on. The active filler metal which supplies the chemical bonds between ceramic and metal, enhances the wetting of filler metal on ceramic surface and eliminates the need for metallization treatments. The residual stress caused by difference of coefficient of thermal expansion between ceramic and metal, holds a direct influence on the bonding strength and even results in a fracture. Good joints of ceramic to metal promote the miniaturization and simplicity of electronic components with multifunction.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.381-387
• /
• 2000

Si3N4/stainless steel 316 joints with Ni buffer layer were fabricated by direct active brazing method (DIB) using Ag-Cu-Ti brazing alloy only and double brazing method (DOB) using Ag-Cu brazing alloy with Si3N4 pretreated with Ag-Cu-Ti brazing alloy. For the joint brazed by DIB method, Ti was segregated at the Si3N4/brazing alloy interface, but was not enough to form a stable joint interface. In addition, large amounts of Ni-Ti inter-metallic compounds were formed in tehbrazing alloy near the joint interface, which could deplete the contents of Ti involved in the interfacial reaction. However, for the joint brazed by DOB method, segregation of Ti at the joint interface were enough to enhance the formation of stable interfacial reaction products such as TiN and Ti-Si-Ni-N-(Cu) multicompounds, which restricted the formation of Ni-Tio inter-metallic compounds in the brazing alloy during brazing with Ni buffer layer. Fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was much improved by using DOB method rather than DIB method. It could be deduced that the differences of fracture strength of the joint with Ni buffer layer depending on brazing process adapted were directly affected by the formation of stable joint interface and the change in microstructure of the brazing alloy near the joint interface. It was found that fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was gradually reduced as the thickness of interface. It was found that fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was gradually reduced as the thickness of Ni buffer layer in the joint was increased from 0.1 mm to 10 mm. It seems to due to the increased residual stress in the joint as the thickness of Ni buffer layer is increased. The maximum fracture strength of Si3N4/S.S 316 joints with Ni buffer layer was 386 MPa, and the fracture of joint was originated at Si3N4/brazing alloy joint interface and propagated into Si3N4 matrix.

• Transactions of Materials Processing
• /
• v.7 no.5
• /
• pp.481-488
• /
• 1998

The active metal brazing was applied to bond Alumina and Ni-Cr steel by Ag-Cu-Zr-Sn alloy and the interfacial microstructure and reaction mechanism were investigated. Polycrystalline monoclinic $ZrO_2$ with a very fine grain of 100-150 nm formed at the alumina grain boundary contacted with Zr segregation layer at the interface. The $ZrO_2$ layer containing the inclusions and cracks were developed at the boundary of inclusion/$ZrO_2$ due to the difference in specific volume. The development of $ZrO_2$ at the interface was successfully explained by the preferential penetration of $ZrO_2$ at the interface was successfully explained by the preferential penetration of Zr atoms a higher concentration of oxygen and a high diffusion rate of Al ions into molten brazing alloy.

• Journal of Welding and Joining
• /
• v.13 no.3
• /
• pp.134-146
• /
• 1995

Aluminium nitride(AlN) is currently under investigation as potential candidate for replacing alumium oxide(Al$_{2}$ $O_{3}$) as a substrate material for for electronic circuit packaging. Brazing of aluminium nitride(AlN) to Cu with Ag base active alloy containing Ti has been investigated in vacuum. Binary Ag$_{98}$ $Ti_{2}$(AT) and ternary At-1wt.%Al(ATA), AT-1wt.%Ni(ATN), AT-1wt.% Mn(ATM) alloys showed good wettability to AlN and led to the development of strong bond between brate alloy and AlN ceramic. The reaction between AlN and the melted brazing alloys resulted in the formation of continuous TiN layers at the AlN side iterface. This reaction layer was found to increase by increase by increasing brazing time and temperature for all filler metals. The bond strength, measured by 4-point bend test, was increased with bonding temperature and showed maximum value and then decreased with temperature. It might be concluded that optimum thickness of the reaction layer was existed for maximum bond strength. The joint brazed at 900.deg.C for 1800sec using binary AT alloy fractured at the maximum load of 35kgf which is the highest value measured in this work. The failure of this joint was initiated at the interface between AlN and TiN layer and then proceeded alternately through the interior of the reaction layer and AlN ceramic itself.

• Journal of Mechanical Science and Technology
• /
• v.16 no.9
• /
• pp.1078-1083
• /
• 2002

Ceramics are significantly used in many industrial applications due to their excellent mechanical and thermal properties such as high temperature strength, low density, high hardness, low thermal expansion, and good corrosion resistive properties, while their disadvantages are brittleness, poor formability and high manufacturing cost. To combine advantages of ceramics with those of metals, they are often used together as one composite component, which necessiates reliable joining methods between metal and ceramic. Direct brazing using an active filler metal has been found to be a reliable and simple technique, producing strong and reliable joints. In this study, the fracture characteristics of Si$_3$N$_4$ ceramic joined to ANSI 304L stainless steel with a Ti-Ag-Cu filler and a Cu (0.25-0.3 mm) interlayer are investigated as a function of strain rate and temperature. In order to evaluate a local strain a couple of strain gages are pasted at the ceramic and metal sides near joint interface. As a result the 4-point bending strength and the deflection of interlayer increased at room temperature with increasing strain rate. However bending strength decreased with temperature while deflection of interlayer was almost same. The fracture shapes were classified into three groups ; cracks grow into the metal-brazing filler line, the ceramic-brazing filler line or the ceramic inside.