• Applied Chemistry for Engineering
• /
• v.26 no.4
• /
• pp.394-399
• /
• 2015

In this study, the Cu catalyst decorated with activated carbon fibers were prepared for improving $SO_2$ adsorption properties. Flame retardant and heat treatments of Lyocell fibers were carried out to obtain carbon fibers with high yield. The prepared carbon fibers were activated by KOH solution for the high specific surface area and controlled pore size to improve $SO_2$ adsorption properties. Copper nitrate was also used to introduce the Cu catalyst on the activated carbon fibers (ACFs), which can induce various reactions in the process; i) copper nitrate promotes the decomposition reaction of oxygen group on the carbon fiber and ii) oxygen radical is generated by the decomposition of copper oxide and nitrates to promote the activation reaction of carbon fibers. As a result, the micro and meso pores were formed and Cu catalysts evenly distributed on ACFs. By Cu-impregnation process, both the specific surface area and micropore volume of carbon fibers increased over 10% compared to those of ACFs only. Also, this resulted in an increase in $SO_2$ adsorption capacity over 149% than that of using the raw ACF. The improvement in $SO_2$ adsorption properties may be originated from the synergy effect of two properties; (i) the physical adsorption from micro, meso and specific surface area due to the transition metal catalyst effect appeared during Cu-impregnation process and ii) the chemical adsorption of $SO_2$ gas promoted by the Cu catalyst on ACFs.

• Carbon letters
• /
• v.5 no.4
• /
• pp.186-190
• /
• 2004

In this work, a nickel metal (Ni) electroplating on the activated carbon fiber (Ni/ACFs) surfaces was carried out to remove the toxic hydrogen chloride (HCl) gas. The surface properties of the treated ACFs were determined by using nitrogen adsorption isotherms at 77 K, SEM, and X-ray diffraction (XRD) measurements. HCl removal efficiency was confirmed by a gas-detecting tube technique. As a result, the nickel metal contents on the ACF surfaces were increased with increasing the plating time. And, it was found that the specific surface area or the micropore volume of the ACFs studied was slightly decreased as increasing the plating time. Whereas, it was revealed that the HCl removal efficiency containing nickel metal showed higher efficiency values than that of untreated ACFs. These results indicated that the presence of nickel metal on the ACF surfaces played an important role in improving the HCl removal over the Ni/ACFs, due to the catalytic reactions between nickel and chlorine.

• Korean Chemical Engineering Research
• /
• v.45 no.3
• /
• pp.277-285
• /
• 2007

The adsorption characteristics of multi-component solvent vapors including poorly-adsorbable chemicals such as toluene-xylene-MEK and toluene-MEK-IPA on the activated carbonaceous adsorbents were investigated in a stainless steel fixed bed of 10.2 cm ID and 50 cm in height in order to identify those carbons for eliminating and recovering solvent vapors from industrial emission sources. The used activated carbonaceous adsorbents were pelletized commercial activated carbons and activated carbon fiber. Breakthrough curves and adsorption capacity at atmospheric pressures were obtained. It has been found that non-polar and larger molecules have been adsorbed better than polar and smaller molecules. In special, alcohols and ketones were poorly adsorbed caused by competitive adsorbability in multi-component mixture system. However, it could be overcome by profitable employment of organization of cooperative system which was composed of different porosity activated carbonaceous adsorbents appropriately.

• Journal of the Korean Ceramic Society
• /
• v.42 no.7 s.278
• /
• pp.469-474
• /
• 2005

Activated Carbon Fibers (ACFs) are widely used as adsorbents in technologies related to pollution abatement due to their highly porous structure and large adsorption capacity. The porous structure and surface area of ACFs depends strongly on both the activation processes arid the nature .of the precursors. The chemical activation with hydroxides has recently been, of great interest as it permits the preparation of activated carbon fibers with highly developed porosity. In this work, OXI-PAN fiber used as precursor for the preparation of activated carbon fibers by chemical activation with KOH and NaOH. The affects of several activation conditions on the surface properties, pore size distribution and adsorption capacity of Ag ion and Iodine ion on ACFs studied.

• Applied Chemistry for Engineering
• /
• v.29 no.3
• /
• pp.318-324
• /
• 2018

In this study, PAN (polyacrylonitrile) based activated carbon fibers were prepared by water vapor activation method which is a physical activation method. Activation was performed with temperature and time as parameters. When the activation temperature reached 700, 750 and $800^{\circ}C$, the activation was carried out under the condition of a water vapor flow rate of 200 ml/min. In order to analyze the pore structure of activated carbon fibers, the specific surface area ($S_{BET}$) was measured by the adsorption/desorption isotherm of nitrogen gas and AFM analysis was performed for the surface analysis. Tensile tests were also conducted to investigate the effect of the pore structure on mechanical properties of fibers. As a result, the $S_{BET}$ of fibers after the activation showed a value of $448{\sim}902m^2/g$, the tensile strength decreased 58.16~84.92% and the tensile modulus decreased to 69.81~83.89%.

• Applied Chemistry for Engineering
• /
• v.28 no.3
• /
• pp.299-305
• /
• 2017

Activated carbon fibers (ACFs) were surface-modified by electron beam (E-beam) irradiation and used as a gas sensor electrode to investigate the effect of E-beam on nitric oxide (NO) gas sensing performance. XPS results showed that the oxygen component of ACFs surface treated by E-beam decreased and $sp^2$ bonded carbon of ACFs surface increased. These results were attributed to the structural transformation of ACFs surface irradiated by E-beam. NO gas sensitivity of the electrode composed of ACFs irradiated by100 kGy increased from about 4% to 8%, and the response time was also meaningfully enhanced from 360 s to 120 s. This is due to the fact that the $sp^2$ carbon bond increased by E-beam irradiation of activated carbon fibers, which significantly affects the resistance change of the electrode in NO gas sensing.

• Carbon letters
• /
• v.15 no.1
• /
• pp.71-76
• /
• 2014

Activated carbon nanofibers (ACNF) were prepared from polyacrylonitrile (PAN)-based nanofibers using $CO_2$ activation methods with varying activation process times. The surface and structural characteristics of the ACNF were observed by scanning electron microscopy and X-ray diffraction, respectively. $N_2$ adsorption isotherm characteristics at 77 K were confirmed by Brunauer-Emmett-Teller and Dubinin-Radushkevich equations. As experimental results, many holes or cavernous structures were found on the fiber surfaces after the $CO_2$ activation as confirmed by scanning electron microscopy analysis. Specific surface areas and pore volumes of the prepared ACNFs were enhanced within a range of 10 to 30 min of activation times. Performance of the porous PAN-based nanofibers as an electrode for electrical double layer capacitors was evaluated in terms of the activation conditions.

• Carbon letters
• /
• v.11 no.1
• /
• pp.28-33
• /
• 2010

In this study, $TiO_2$-Activated carbon (AC) complex fibers were prepared by electrospinning for the synergetic effect of adsorption and degradation of organic pollutant. The average diameter of these fibers increased with increasing the amount of AC added, except for 1AC-TOF (AC$/TiO_2$ =1/40 mass ratio). After calcinations at $500^{\circ}C$, long as-spun fibers were broken and their average diameter was slightly decreased. The resultant fibers after calcination had rough surface and sphere shapes like a peanut. From XRD results, it was confirmed that as-spun fibers were changed to anatase $Ti_O2$ fiber after calcinations at $500^{\circ}C$. The prepared $TiO_2$-AC complex fibers could remove procian blue dyes by solar light irradiation with high removal property of 94~99%. The PB dye was rapidly removed by adsorption during the initial 5 minutes. But after 5 minutes, dye removal was occurred by photodegradation. In this study, the most efficient AC/$TiO_2$ ratio of $TiO_2$-AC complex fibers was 5/40, showing the synergetic effect of adsorption and photodegradation. It is expected that the $TiO_2$-AC complex fibers can be used to remove of organic pollutants in water system.

• 한국전기화학회:학술대회논문집
• /
• 2004.04a
• /
• pp.15-16
• /
• 2004

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1999.05a
• /
• pp.76-76
• /
• 1999