• Elastomers and Composites
• /
• v.44 no.2
• /
• pp.175-181
• /
• 2009

The solution polymerization was conducted to synthesize pressure sensitive adhesive for polarizer film using acrylic monomers. 2-Ethylhexyl acrylate, butyl acrylate, acrylic acid were used as acrylic monomers, benzoyl peroxide as initiator, ethyl acetate as solvent. The ratio of monomers was 2-ethylhexyl acrylate: butyl acrylate: acrylic acid = 25:50:3.6 reflecting $-40^{\circ}C$ of glass transition temperature in the pressure sensitive adhesive. The amount of initiator was determined as 0.09% to monomer considering wetting power and initial tackiness. The ratio of monomer to solvent was determined as 1:1.7 considering wetting power and transmissivity. The transmissivity of pressure sensitive adhesive increased with decreasing both viscosity and molecular weight due to reducing of refractive index by low entanglement between molecules. In the measurement of pot life, it was found that the storage stability was good at 1:1.7 of monomer: solvent without large change of viscosity during 200 min.

• Journal of Adhesion and Interface
• /
• v.10 no.1
• /
• pp.1-10
• /
• 2009

The waterborne acrylic pressure-sensitive adhesive in the basis of butylacylate (BA) and 2-Ethylhexylacrylate (2-EHA) was synthesized and the methyl methacrylate (MMA) have been used to give the rigidity perfroamce. The polymreric latex was synthesized using butyl acrylate (BA), 2-ethylhexyl acrylate (EHA), methyl methacrylate (MMA) and each 1, 2, 3% of various functional monomers. The dimethyl-2-imidazlidon acrylate and 2-acrylamido-2-methyl-1-propanesulfonate was used in order to increase the wetting properties of acrylic emulsion. To study of properties of functional monomer, The polymreric latex was synthesized various functional monomers each 1, 2, 3%. The 2-acrylamido-2-methyl-1-propanesulfonate showed the best properties. Latex with acrylic acid and dimethyl-2-imidazlidon acrylate had good peel strength, holding power, but it showed that they didn't separate from adhered cleanly by weak cohesion strength. The adhesion performance was increased by increasing amount of 2-acrylamido-2-methyl-1-propanesulfonate however latexes with upper 7% 2-acrylamido-2-methyl-1-propanesulfonate showed that the properties of PSA decreased.

• Journal of the Korean Applied Science and Technology
• /
• v.25 no.1
• /
• pp.1-14
• /
• 2008

To prepare weather-resistant modified silane acrylic resin coatings for an architectural purpose, tetrapolymers were synthesized by radical polymerization. 3-Methacryloxypropyltrimethoxysilane (MPTS) as a silicone monomer and n-butyl acrylate, methyl methacrylate, and n-butyl methacrylate as acrylic monomers were used. The composition of monomers was adjusted to fix the glass transition temperature of acrylic polymer for $20^{\circ}C$. The composition of MPTS in the synthesized polymer were varied from 10 wt% to 30 wt%. On the basis of synthesized resin amber paints were prepared and their physical properties and effects on weatherability were examined. The presence of MPTS in modified silane acrylic resins generally resulted in low molecular weight and broad molecular weight distribution, and also lowered the viscosity of the copolymers. The coated films prepared from these resins showed good and balanced properties in general. Adhesion to the substrate was outstanding in particular. Weatherability tests were carried out in three different types such as outdoor exposure, QUV, and SWO. The test results showed that the modified silane acrylic resins containing 30 wt% of MPTS had superior weathering properties.

• Journal of the Korean Applied Science and Technology
• /
• v.37 no.6
• /
• pp.1627-1634
• /
• 2020

In this study, water-based acrylic adhesives as copolymers with acrylic acid, 2-hydroxyethyl acrylate were synthesized using ethyl acrylate, 2-ethylhexyl acrylate, and lauryl methacrylate as the main monomers. Prepared water-based acrylic adhesive was compared to physical properties such as solid content, average particle size distribution, initial adhesive force, maximum adhesive force, peel strength, and heat resistance.

• Journal of Adhesion and Interface
• /
• v.9 no.1
• /
• pp.16-21
• /
• 2008

Hybrid emulsions consisting of polyurethane and acrylic polymer were prepared by emulsion polymerization of acrylic monomers and polyurethane water dispersions (PUD) as an emulsifier. At first, cationic type of PUD was synthesized with IPDI, PTMG1000, MDEA, and acetic acid. Then, acrylic monomers, such as MMA and n-BA, were copolymerized with the PUD without adding further surfactant. The tensile properties and water resistance increased with increasing acrylic monomer ratio. The hybrid emulsions showed better properties than the emulsions simply blended with the PUD and the acrylic emulsions.

• Korean Chemical Engineering Research
• /
• v.52 no.4
• /
• pp.451-458
• /
• 2014

Waterborne polyurethane dispersion (WPUD) was prepared from polycarbonate diol (PCD), isophorone diisocyanate (IPDI) and dimethylol propionic acid (DMPA) as starting materials. Then, waterborne acrylic polyurethane dispersion (AUD) was synthesized by reacting the WPUD with different types of acrylate monomers, such as methyl methacrylate (MMA), 2-hydroxyethyl methacrylate (HEMA) and butyl acrylate (BA). Subsequently, the AUD was mixed with multi-walled carbon nanotube (MWCNT) to yield a conductive coating solution, and the mixture was coated on the polycarbonate substrate. The pencil hardness, abrasion resistance and chemical resistance of the coating films from AUD were improved than those from WPUD, while the electrical conductivity of the coating films from AUD was decreased than that of WPUD. Also, the effect of acrylate types on the properties of coating films was investigated. The AUD obtained from HEMA showed the strongest pencil hardness, while the AUD obtained from MMA exhibited the strongest abrasion resistance, chemical resistance and electrical conductivity among several types of acrylate monomers.

• KSBB Journal
• /
• v.16 no.1
• /
• pp.82-86
• /
• 2001

Glyco-acrylate and methacrylate were synthesized by lipase-catalyzed glycosylation of acrylic acid, methacrylic acid and their vinyl esters with $\beta$-methyl fructoside and glycerol in t-butanol as a reaction medium. At the optimum conditions for enzymatic glycosylation of acrylic acid and vinyl methacrylate, we attained up to 80% conversion for glyco-acrylate from acrylic acid and 90% conversion for glyco-methacrylate from vinyl methacrylate. The polymerizable glyco-acrylates and methacrylate have biomedical application as hydrophilic monomers and hydration modifiers to be use for hydrogel contact lens formulation.

• Korean Chemical Engineering Research
• /
• v.50 no.4
• /
• pp.639-645
• /
• 2012

Waterborne polyurethane dispersion (PUD) was synthesized by capping the NCO groups of polyurethane prepolymers, prepared from isophorone diisocyanate, polycarbonate diol and dimethylol propionic acid, with aminopropyl triethoxysilane (APS). Subsequently, silylated acrylic polyurethane dispersion was synthesized by reacting the PUD with the mixture of acrylate monomers, 2-hydroxyethyl methacrylate and methyl methacrylate. The average particle size of silylated acrylic polyurethane dispersion, measured by the dynamic light scattering method, was increased from 39.0 nm to 399.8 nm by increasing the addition amounts of APS. Also, the pencil hardness of coating films of silylated acrylic polyurethane dispersion was enhanced from B grade to F grade with increasing APS content.

• Korean Chemical Engineering Research
• /
• v.49 no.5
• /
• pp.548-553
• /
• 2011

NCO terminated polyurethane prepolymers were synthesized from isophorone diisocyanate(IPDI), polycarbonate diol(PCD) and dimethylol propionic acid(DMPA). Subsequently, acrylic terminated polyurethanes were prepared by capping the NCO groups of polyurethane prepolymers with different types of acrylate monomers, such as 2-hydroxyethyl methacrylate(HEMA), 2-hydroxyethyl acrylate(HEA) and pentaerythritol triacrylate(PETA). The average particle sizes of the acrylic terminated polyurethane solutions were increased by capping acrylate monomers. Also, the prepared coating films showed better abrasion resistance and pencil hardness than those of pure waterborne polyurethanes. The coating film with PETA exhibited the best abrasion resistance and pencil hardness of coating films prepared with three acrylate monomers.

• Journal of the Korean Applied Science and Technology
• /
• v.22 no.3
• /
• pp.289-297
• /
• 2005

In order to improve resistant properties of water-borne acrylic pressure sensitive adhesives(PSAs) for automobiles, this study was carried out. Removable PSAs for automobiles were synthesized by emulsion polymerization of monomers, n-butyl acrylate(BA), n-butyl methacrylate(BMA), acrylonitrile(AN), acrylic acid(AA) and 2-hydroxyethyl methacrylate(2-HEMA), and AA and 2-HEMA could act as functional monomers for crosslink. Emulsion polymerization was carried out in a semi-batch type reactor. Water resistance, heat resistance, acid resistance, alkali resistance and smoke resistance were examined. As a result, water resistance increased with the amount of BMA, however, the effect of BMA content on the water resistance was insignificant at a range of over 14 wt%. The water resistance also increased with the amount of functional monomers, AA and 2-HEMA. The prepared PSAs satisfied all the standard for automobiles except heat resistance. However, the heat resistance comes nearly up to the standard. Also, acid resistance, alkali resistance and smoke resistance of the prepared PSAs satisfied with the standard.